DE3243965A1 - Writing element for writing implements - Google Patents
Writing element for writing implementsInfo
- Publication number
- DE3243965A1 DE3243965A1 DE19823243965 DE3243965A DE3243965A1 DE 3243965 A1 DE3243965 A1 DE 3243965A1 DE 19823243965 DE19823243965 DE 19823243965 DE 3243965 A DE3243965 A DE 3243965A DE 3243965 A1 DE3243965 A1 DE 3243965A1
- Authority
- DE
- Germany
- Prior art keywords
- writing
- glass ceramic
- writing element
- glass
- oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Die Erfindung betrifft ein Schreibelement für Schreibgeräte,The invention relates to a writing element for writing implements,
wie es unter anderem als Kugel und Kugelfassung, als Feder, als Draht, Stift oder Docht oder als Schreib- oder Stützröhrchen in entsprechenden Schreibgeräten benützt wird.as it is, among other things, as a ball and ball socket, as a spring, as a wire, Pen or wick or as a writing or support tube in appropriate writing implements is used.
Diese Schreibelemente bestehen üblicherweise aus Metall oder aus Kunststoff.These writing elements are usually made of metal or plastic.
Besondere Probleme derartiger Schreibelement ergeben sich hauptsächlich durch die direkte reibende Berührung mit dem SchriTtträger während der bestimmungsgemäßen Benützung, sowie durch vers-chiedem aggressive Substanzen im Schreibmittel.Particular problems with such writing elements mainly arise through the direct rubbing contact with the step support during the intended use Use, as well as various aggressive substances in the writing material.
Es sind daher schon vielfach Vorschläge zur Verbesserung der Abriebfestigkeit und zur Erhöhung der Korrosionsbeständigkeit bekannt geworden.There are therefore already many suggestions for improving the abrasion resistance and become known to increase the corrosion resistance.
So wird beispielsweise in DE-PS 804 768 empfohlen, ein Schreibröhrchen a;us Sinteroxyden, z. B. aus Sintertonerde oder aus "Sintersaphir", herzustellen, nachdem u. a. Einsätze aus Saphir am Schreibende des Röhrchens sich nicht als zweckmäßig erwiesen hatten.For example, DE-PS 804 768 recommends a writing tube a; from sintered oxides, e.g. B. from sintered clay or from "sintered sapphire", after inter alia Sapphire inserts at the writing end of the tube are not found to be useful had proven.
Darüberhinaus sind Schreibelemente bekannt, die Einsätze aus Hartmetall aufweisen oder mit einer Hartchrom-Schicht überzogen sind, um die Abriebfestigkeit und gegebenenfalls auch die Korrosionsbes-tEndigkeit zu erhöhen, wofür in-der DE-PS eine zusätzliche "äußere Auskleidung" aus tintenbeständigen Legierungen vorgesehen ist.In addition, writing elements are known which have hard metal inserts have or are coated with a hard chrome layer to increase the abrasion resistance and if necessary also to increase the resistance to corrosion, for which the DE-PS an additional "outer lining" of ink-resistant alloys is provided is.
Alle bekannten Schreibelemente stellen jedoch bezüglich beider Kriterien noch keine optimale Lösung dar.However, all known writing elements represent both criteria is not yet an optimal solution.
Aufgabe der Erfindung ist es daher, bei Schreibelementen die Abriebfestigkeit und die Korrosionsbeständigkeit weiterhin zu erhöhen, um möglichst lange Stand- und Funktionszeiten zu erhalten.The object of the invention is therefore to improve the abrasion resistance of writing elements and to further increase the corrosion resistance in order to and to get functional times.
Diese Aufgabe wird mit den im Hauptanspruch 1 umfaßten Merkmalen auf überraschende Weise gelöst.This task is based on the features encompassed in the main claim 1 solved surprising way.
Durch die Verwendung von Glaskeramik als Material für das Schreibelement, für ein Teil von diesem oder für einen entsprechenden Überzug.an den kritischen Bereichen des Schreibelementes bzw. der Schreibspitze, wird sowohl eine extrem hohe Abriebfestigkeit, als auch eine.sehrgute Korrosionsbeständigkeit erreicht.By using glass ceramic as the material for the writing element, for part of this or for a corresponding coating. to the critical Areas of the writing element or the writing tip, both an extremely high Abrasion resistance as well as a very good corrosion resistance achieved.
Glaskeramik als solche ist seit vielen Jahren ganz allgemein bereits bekannt und wird vielfältig indWstriell angewandt.Glass-ceramic as such has been quite general for many years known and is widely used in industry.
Der Verwendung im Schreibgerätebereich stande aber offensichtlich - trotz konkretem Richtungshinweis durch die genannte DE-PS - erhebliche Bedenken der Fachwelt gegenüber.The use in writing implements was obvious - in spite of a concrete directional reference from the aforementioned DE-PS - considerable concerns to the professional world.
Insbesondere die allen aus Glas und/oder aus Keramik bestehenden Produkte üblicherweise eigene Sprödigkeit aufgrund der amorphen Struktur, spricht prinzipiell gegen eine entsprechende Anwendung bei Schreibgeräten, sowohl als reines Glas, als auch in modifizierter Form.In particular, all products made of glass and / or ceramics usually own brittleness due to the amorphous structure, speaks in principle against a corresponding use in writing implements, both as pure glass, as also in modified form.
Erst durch Überwindung dieser grundsätzlichen Bedenken konnte der Erfinder zu der vorgeschlagenen Lösung gelangen, wozu es aber dann noch weiterer Erkenntnisse und uberlegungen bedurfte, um aus der Vielzahl der auf der Basis von Glas und/oder von Keramik bekannten Materialien gerade zur vorgeschlagenen Glaskeramik zu gelangen.Only by overcoming these fundamental concerns could the Inventors arrive at the proposed solution, but then there are still others Knowledge and reflection needed to be drawn from the multitude of based on Glass and / or materials known from ceramics, especially for the proposed glass ceramics to get.
Hierbei zeigt sich überraschenderteise, daß trotz der Sprödigkeit von Glas bzw. von Keramik das 6tfindungsgemäße Schreibelement ausreichende Bruchfestigkeit aufweist und sich aufgrund der sehr hohes Abriebfestigkeit ç der guten Beständigkeit gegen Korrosion, besonders z. B. für die Verwendung auch von folienanibsenden (lösungsmittelhåt3tlBed) Pasten, Tinten oder Tuschen auf Folien und somit bevorzugt für den Einsatz in nummerisch gesteuerten (automatischen) Schreib- oder Zeichenanlagen, wie Plottern u. ä., sehr gut eignet.This surprisingly shows that despite the brittleness of glass or ceramic the writing element according to the invention has sufficient breaking strength and due to the very high abrasion resistance ç the good durability against corrosion, especially z. B. for the use of foil tags (solvent håt3tlBed) Pastes, inks or inks on foils and therefore preferred for use in numerical form controlled (automatic) writing or drawing systems, such as plotters and the like well suited.
Vorteilhafte Ausgestaltungen und Weiterbildungen des erfindungsgemäßen Schreibelementes sind in den weiteren Ansprüchen umfaßt.Advantageous refinements and developments of the invention Writing element are included in the further claims.
Wird nicht das gante Schreibelement aus Glaskeramik hergestellt, so sollen die diesbezüglichen Abschnitte, Zonen oder Beschichtungen bzw. Überzüge hauptsächlich im Bereich der Berührungszone mit der Schreibfläche und/oder im Bereich der Abstütz- oder Auflagezone, z. B. im Kugelbett der Fassung für eine Schreibkugel, vorhanden sein.If the entire writing element is not made of glass ceramic, then so the relevant sections, zones or coatings or coverings are mainly intended in the area of contact with the writing surface and / or in the area of the support or support zone, e.g. B. in the ball bed of the socket for a writing ball, available be.
Schreibkugeln, Schreibröhrchen, Drähte, Stifte oder Dochte als Schreibelement oder diesem zugeordnet, können ganz aus Glaskeramik bestehen oder partielle Bereiche oder auch Überzüge hiervon aufweisen.Writing balls, writing tubes, wires, pens or wicks as writing elements or assigned to it, can consist entirely of glass ceramic or partial areas or also have coatings thereof.
Sind die Schreibelemente lediglich mit Glaskeramik überzogen, so soll die Schichtdicke des Überzuges 0,05 bis 0,5 vorzugsweise 0,1 bis 0,3 mm betragen.If the writing elements are only covered with glass ceramic, then should the layer thickness of the coating is 0.05 to 0.5, preferably 0.1 to 0.3 mm.
Zur Erhöhung der Stabilität und zur Erleichterung der Bildung geschlossener Strukturen soll die zu verwendende Glaskeramik feinkörnige kristalline Struktur aufweisen.To increase the stability and to facilitate the formation of closed Structures, the glass ceramic to be used should have a fine-grain crystalline structure exhibit.
Ein derartiges feinkörniges Gefüge wird außer durch verfahrensmäßige Kriterien, wie z. B. durch Kristallisation bei ansteigender Temperatur, besonders durch eine der Glasmischung beigesetzte geringe Menge von Titanoxid, Chromoxid, Molybdänoxid, Vanadrumoxid, Phosphoroxid, Phosphaten, Sulfiden, Fluoriden oder anderen Keimbildnern erhalten.Such a fine-grain structure is not only due to the process Criteria such as B. by crystallization with increasing temperature, especially due to a small amount of titanium oxide, chromium oxide added to the glass mixture, Molybdenum oxide, vanadrum oxide, phosphorus oxide, phosphates, sulfides, fluorides or others Get nucleating agents.
Als Ausgangsmaterialien werden Gläser bz. Grundstoffsysteme vorgeschlagen, deren -X<ristallisationsvorgang kontrollierbar bleibt. Hierfür so-lDen u. q. Gläser aus den Systemen Lithiumoxid - Aluminiumox?Z1ci¼ Siliciumoxid; LithiumoRid - Zinkoxid -Siliciumoxid oder Magnesiumoxid - Aluminiumoxid - Siliciumoxid Anwendung finden.Glasses or basic material systems are suggested as starting materials, whose -X <crystallization process remains controllable. For this, so-lDen u. Q. Glasses from the systems lithium oxide - aluminum ox? Z1ci¼ silicon oxide; LithiumoRid - Zinc Oxide -Silicon Oxide or Magnesium Oxide - Aluminum Oxide - Silica Application Find.
Claims (6)