DE3026605C2 - Säurefestes, hydrolytisch beständiges optisches und ophthalmisches Borosilikat-Glas geringer Dichte - Google Patents

Säurefestes, hydrolytisch beständiges optisches und ophthalmisches Borosilikat-Glas geringer Dichte

Info

Publication number
DE3026605C2
DE3026605C2 DE3026605A DE3026605A DE3026605C2 DE 3026605 C2 DE3026605 C2 DE 3026605C2 DE 3026605 A DE3026605 A DE 3026605A DE 3026605 A DE3026605 A DE 3026605A DE 3026605 C2 DE3026605 C2 DE 3026605C2
Authority
DE
Germany
Prior art keywords
glasses
resistance
glass
cao
refractive index
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
DE3026605A
Other languages
English (en)
Other versions
DE3026605A1 (de
Inventor
Volkmar 6500 Mainz Geiler
Georg Dipl.-Ing. Dr. Gliemeroth
Karl Dr. 6204 Taunusstein Mennemann
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Schott AG
Original Assignee
Schott Glaswerke 6500 Mainz
Schott Glaswerke AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Schott Glaswerke 6500 Mainz, Schott Glaswerke AG filed Critical Schott Glaswerke 6500 Mainz
Priority to DE3026605A priority Critical patent/DE3026605C2/de
Priority to GB8120313A priority patent/GB2083016B/en
Priority to IT67943/81A priority patent/IT1224100B/it
Priority to AR286061A priority patent/AR227552A1/es
Priority to JP56107220A priority patent/JPS5751149A/ja
Priority to BR8104446A priority patent/BR8104446A/pt
Priority to FR8113608A priority patent/FR2486516B1/fr
Priority to US06/282,787 priority patent/US4390638A/en
Priority to ES503911A priority patent/ES8206401A1/es
Publication of DE3026605A1 publication Critical patent/DE3026605A1/de
Priority to US06/384,462 priority patent/US4400473A/en
Application granted granted Critical
Publication of DE3026605C2 publication Critical patent/DE3026605C2/de
Expired legal-status Critical Current

Description

Die Erfindung bezieht sich auf ein leichtes, säurefestes, hydrolytisch beständiges, optisches und ophthaimisches Borsilikat-Glas mit einem Brechungsindex /ij^-1,69, einer Abbezahl vä>. 39 und einer Dichte i< 3,2Og/cm\
Das neue Glas ist ein Borosilikatglas im System SiO2-B2O3-CaO-TiO3.
Hochbrechende Gläser geringen Gewichtes, z. B. für die Augenoptik oder Tür optische Systeme sind beschrieben in der DE-AS 22 59 183. Diese Gläser mit einer Dichte von ca. 3,0 g/cm1 sind besonders geeignet für starke Korrekturen, haben aber den großen Nachteil einer starken Dispersion, was sich in der vergleichsweise niedrigen Abbe-Zahl <33 niederschlägt.
SiO2
B2O3
GeO2
AI2O3
24-32
5-14
O- 8
O- 6
wobei die Summe dieser 3- und 4wertigen Glasbildner 33-39 Gew.-% ausmacht.
Wie oben angeführt, kann durch den fünfwertigen Glasbildner P2O5 die Entglasungsstabilität verbessert werden, ebenso wie auch die chemische Beständigkeit; deshalb ist ein Zusatz von einigen Prozent P2O5 notwendig; die Summe der 3- und 4wertigen Glasbildner plus
P2O5 beträgt 37-43 Gew.-%.
Wie erwähnt, ist ein Alkalizusatz notwendig, um einer Entmischung vorzubeugen; für die einzelnen Alkalioxide gilt:
Na2O+ K2O = Gew,-%
Li2O 0- 7
Na2O 0- 8
KjO 0-1.1
Li2O + 4-14
Nb2O5 und WO1. Diese Oxide können in Mengen von
Als essentieller Bestandteil wird CaO hinzugefügt; CaO bewirkt eine deutliche Anhebung des Brechwertes, wobei eine hohe Abbe-Zahl gewährleistet wird und gleichzeitig die Dichte niedrig gehalten wird. Die Funktion des CaO kann bedingt innerhalb recht weiter Grenzen vom MgO übernommen werden. Die Anteile der leichten Erdalkalioxide MgO und CaO betragen:
MgO
CaO
MgO+ CaO =
Gew.-%
0-10 12-25
18-30
SrO
BaO
zugesetzt werden, ferner sind
Gew-%
0-6
0-6
ZnO
PbO
erlaubt, mit der Bedingung:
Gew.-%
0-8 0-5
SrO + BaO + ZnO + PbO < 8%,
da bei größeren Anteilen die Dichte stark ansteigt.
Ein weiterer unbedingter Bestandteil diesesGIases ist TiOj, das bekanntlich den Brechwert stark erhöht, die Dichte hingegen nur wenig. Ein Zusatz von 6-10 Gew.-% ist nötig, um den Brechwert auf den gewünschten Wert zu heben. Eine weitere positive Eigenschaft des TiO2 besteht darin, daß es die chemische Beständigkeit verbessert.
Ähnlich in den Eigenschaften wie TiO2 verhalten sich
Von den schweren Zrdalkalioxiden SrO und BaO können bei Bedarf
Gew.-%
Nb2O5 O- 8
WO3 0-10
zugesetzt werden. Die Summe dieser drei in ihren Eigenschaften ähnlichen Oxiden TiO2, Nb2O3, WO3 beträgt 13-19 Gew.-%.
Ein weiteres notwendiges Oxid ist das ZrO2; es erhöht den Brechwert stark, erniedrigt jedoch die Abbe-Zahl nur mäßig, und es verbessert die chemische Beständigkeit merklich. Es wird in Anteilen von 3-9 Gew.-% zugefügt.
Um das Glas weiter gegen Entglasung zu stabilisisieren, können erfindungsgemäß zugesetzt werden:
Gew.-%
La2O3 0-11
Y2O3 0-12
Gd2O3 O- 8
Yb2O3 O- 7
Weiterhin ist ein Zusatz von 0-7% Ta2O5 möglich.
r> HfO2 kann in Mengen von 0-5 Gew.-% zugesetzt werden, sowie 0-6 Gew.-% SnO2. Ein Teil der SauerstofT-ionen kann durch Fluorid ersetzt werden, indem statt eines Oxids ein Fluorid >n die Glasschmelze gegeben wird.
jo Die einzelnen Oxide können auch in komplexer Form eingebracht werden, z. B. das P2O3 gebunden an die Alkali- bzw. Erdalkalioxide, z. B. als CaPO3 oder Ca2P2O7. Auch ist es z. B. möglich, das SiO2 z. T. als CaSiO3 einzusetzen - bei geeigneter Umrechnung oder z. B. als ZrSiO4. Ebenfalls ist es möglich, geringe Mengen Fluorid einzubringen, z. B. als Alkali-Erdalka-Ii- bzw. Seltenerdftuoride. Zum Gemenge wird As2O3 bzw. Sb2O3 als Läutermittel hinzugefügt, anschließend wird es gut gemischt und bei ~ 14000C in Pt-Tiegel oder Keramikwanne in etwa 8 Stunden eingeschmolzen. Nach einer Läuterzeit von etwa 3 Stunden wird bis zur Auslauf- bzw. Gußtemperatur abgerührt. Das Glas wird in herkömmlicher Weise entweder in Gußformen gegossen oder verpreßt.
Die nachstehende Tabelle zeigt Zusammensetzungsbeispiele im Rahmen der Erfindung:
1 1,50 2 9,00 1,80 1,50 3 4 7,75 5
B2O3 12,50 3,10 24,05 3,00 8,00 11,60 28,60 12,95
SiO2 25,80 4,70 5,10 4,00 - 26,00 - 25,55
AI2O3 - 0,50 - 4,00 7,80 - - -
P2O5 - 24,75 19,50 - - 4,75
Li2O - - 1,45 4,45 7,00
Na2O 0,60 3,00 8,00 -
K2O 6,55 4,50 3,85 -
MgO - 4,40 15,20 -
CaO 7.95 15,05 - 23,00
BaO - - 3,05
ZnO - 2,00 -
La2O3 7,95 11,55 -
Y2O3 - 7,90 -
TiO2 9,75 9,40
5 1 6,10 30 26 2 6,60 605 7,50 6 4 4,40 S 6,40
.5,95 5,20 1,50 6,30 7,90
For! Setzung - - 7,30 - -
1,7005 1,6993 3 1,7015 1,6996 1,7030
ZrO2 40,5 39,3 39,0 40,2 40
Nb2O5. 3,12 3,17 3,20 3,18 3,06
WO3
nd
"rf
P

Claims (1)

  1. Patentanspruch:
    30 26 60$
    Optisches und ophthaimisches Borosilikat-Glas mit einenl· Brechungsindex >l,69, einem v^-Wert >39 und einer Dichte s < 3,2 g/cm3, das für eine kontinuierliche Fertigung genügend kristallisationsstabil ist und gleichzeitig den Mindestforderungen in bezug auf Säurefestigkeit sowie der Klimawechselbeständigkeit genügt, gekennzeichnet durch folgenden Zusamtnensetzungsbereich (Gew.-%):
    B2O3 5-14
    SiO, 24-32
    Al2O3 0- 6
    GeO2 0- 8
    B2O3 + SiO2 + Al2O3 + GeO2 = 33-39
    P2O5 0- 6
    B2O3 + SiO2 + Al2O3 + GeO2 + P2O5 = 37-43
    Li2O O- 7
    Na2O O- 8
    K2O 0-11
    Li2O + Na2O + K2O = 4-14
    MgO 0-10
    CaO 12-30
    MgO + CaO = 18-27 18-27
    ZnO 0- 8
    BaO 0- 6
    SrO 0- 6
    PbO 0- 5
    ZnO + BaO + SrO + PbO =0-8
    TiO2 6-10
    Nb2O5 0- 8
    WO3 0-10
    TiO3 + Nb2O5 + WOj = 13-19
    ZrO2 3- 9
    La2O3 0-11
    Y2O3 0-12
    Gd2O3 0- 8
    Yb:03 0- 7
    La2O3 + Y2O3 + Gd2O3 + Yb2O3 = 0-14
    Ta2O5 0- 7
    HfO2 0- 6
    SnO2 0- 6
    Dieseslarke Dispersion fuhrt dazu, daß ein Brillenträger durch Gläser dieser Art ausgeprägte Farbsäume sieht Deshalb wurde bereits versucht, die Dispersion zu verbessern bei gleicher bzw. nur geringfügig erhob's ter spezifischer Dichte (FR-PS 24 27 309), Auch diese neuen Gläser erfüllen jedoch nicht die Erfordernisse nach einem v^-Wert >39,
    Weitere Entwicklungen brachten zwar Fortschritte in bezug auf die Erhöhung der Abbe-Zahl, jedoch machen
    ίο die Kristallisationseigenschaften eine kontinuierliche Fertigung unmöglich, wie auch die chemische Beständigkeit (Säurefestigkeit und Klimawechselbeständigkeit) nicht den zu stellenden Anforderungen für ein Brillenglas genügt Gläser dieser Art sind beschrieben
    is in der DE-OS 28 09 409 und DE-AS 27 15 894 sowie der DE-AS 26 23 683. Die vorliegende Erfindung ermöglicht es, Brillenglas und optische Gläser mit genügender chemischer Beständigkeit (SäurefestigkeiJ end Wasserbeständigkeit) mit einem Brechwert von ca. 1,7 und
    einer Abbe-Zahl >39 bei einer Dichte <3,20 g/cm3 kontinuierlich herzustellen; gleichzeitig kann durch Einstellung eines Ausdehnungskoeffizienten von tf(20_30o) - 107 von 90-98 eine Verschmelzung mit handelsüblichem Brillenkronglas gewährleistet werden.
    Erfindungsgemäß wird als Grundglassystem ein Borsilikatglas gewählt, das sich bekanntlich durch eine gute chemische Beständigkeit auszeichnet. Gläser in diesem Grundglassystem, auch mit ähnlicher optischer Lage, sind bekannt aus der CH-PS 4 38 600 und aus der US-PS
    jo 34 77 863. Diese bekannten Gläser haben jedoch allein schon wegen ihres hohen BaO-Gehalts eine für den hier beabsichtigten Verwendungszweck zu hohe Dichte.
    Dem genannten Grundglassystem werden im Rahmen der vorliegenden Erfindung als brechwerterhöhende Komponenten vornehmlich die leichten Erdalkalioxide MgO und CaO zugesetzt, insbesondere CaO, sowie als stark den Brechwert erhöhende, aber die Abbe-Zahl nicht zu sehr verschlechternde Komponenten Nb2O5 und TiO2 sowie ZrO2. Um dieses System gegen
    ■to Entmischung zu stabilisieren, ist ein Zusatz von Alkalioxid notwendig.
    Es zeigt sich, daß dieses System, das nur mäßig stabil gegen Entglasung ist, und das des weiteren wegen des hohen Erdalkalioxid- sowie Alkalioxidgehaltes eine nicht genügende chemische Resistenz besitzt, in beiden genannten Eigenschaften - der Entglasungsstabilität und der chemischen Resistenz - verbessert werden kann, wenn P2O5 hinzugefugt wird.
    Das Glas gemäß Erfindung ist aus folgenden Kompo-
    nenten in den genannten Bereicher: zusammengesetzt (in Gew.-%):
DE3026605A 1980-07-14 1980-07-14 Säurefestes, hydrolytisch beständiges optisches und ophthalmisches Borosilikat-Glas geringer Dichte Expired DE3026605C2 (de)