DE2815520A1 - Polymermassen - Google Patents
PolymermassenInfo
- Publication number
- DE2815520A1 DE2815520A1 DE19782815520 DE2815520A DE2815520A1 DE 2815520 A1 DE2815520 A1 DE 2815520A1 DE 19782815520 DE19782815520 DE 19782815520 DE 2815520 A DE2815520 A DE 2815520A DE 2815520 A1 DE2815520 A1 DE 2815520A1
- Authority
- DE
- Germany
- Prior art keywords
- elastomer
- polymer
- ethylene
- ester
- thermoplastic polymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Description
dieses Material betreffen, sind in der Dupont-Broschüre
"Vamac ethylene/acrylic Elastomer - A new Class of Heat & Oil
Resistant Rubber" beschrieben.
nicht enthalten sein sollten, oder falls sie anwesend sind,
n= 6-40. Solche Polymere sind im Handel von Dupont Co.unter [ dem eingetragenen Warenzeichen "Hytrel" erhältlich. Informa- ; tionen hinsichtlich ihrer Struktur, ihrer Eigenschaften und j der Methoden zu ihrer Herstellung finden sich in den US-PS ; 3 023 192, 3 651 014, 3 763 109, 3 766 146 und 3 784 520 sowie! in der BE-PS 793 332. Zusätzliche Informationen liefert die [ Schrift "Segmented Polyether Ester Copolymers-A-New Generation; of Thermoplastic Elastomers" von G.K. Hoeschele, herausgegeben! von der Elastomer-Abteilung von Du Pont De Nemours, Inc., '· Wilmington,De.
Polymermasse als elektrisches Heizmaterial, z.B. in Heizbändern und Wasserbettheizungen. .
Banbury-Laboratoriums-Mischers hergestellt (alle Teile sind
Gew.Teile):
Physik.Eigenschaft | Dehnung % b.Raumtemp. |
Eigenschafter ASTM-Öl Nr. 2 |
nach Eintauchen in : bei 900C für 168 Std. . |
Sewichtszu- name % |
|
Thermoplast | Zugfestigk. ).Raumtemp. kg/cm2 |
530 | Zugfestigk. b.Raumtemp. kg/cm2 |
Dehnung % b.Raumtemp. |
20.3 |
HytreT 4055 | 120 | 16C | 94 | 400 | 86.7 |
DPD 6181 | 132 | 140 | 64.4 | 395 | 70.6 |
Vestolen A 4516 |
120 | 175 | 82.8 | 395 | 95.5 |
DYNH | 133 | 110 | 65 | 380 | 35.9 |
Surlyn A 1707 | 181 | 153 | 420 |
Physik. Eigenschaft | Dehnung % b.Raumtemp. |
Eigenschaften nach Eintauchen in ASTM-ΟΊ Nr.2 bei 900C für 168 Std |
Dehnung % b.Räumt. |
Gewichts zunahme % |
|
Thermoplast | Zugfestigk. b.Raumtemp. MPa |
320 250 |
Zugfestigk. b.Raumtemp. MPa |
330 250 |
5.4 6.0 |
Hytrel Manolen 5203 |
8.5 12.2 |
10.1 12.1 |
Physik.Eigenschaft | Dehnung % ο.Räumt. |
Eigenschaften nach Eintauchen in ASTM-öl Nr.2 bei 9O0C für 158 Std. |
Dehnung % b.Räumt. |
Gewichtszu nahme & |
Zugfestigk. b.Raumtemp. MPa |
440 | Zugfestigk. b.Raumtemp. MPa |
400 | 8.S |
12.9 | 10.4 |
Elastomer | Thermoplast |
Zugfestigk
).Raumtemp. MPa |
Dehnung
b.Räumt. |
Hitzeschocfc bei |
4Std. ■ 2000C, |
Zugfest.b.
Räumt.(MPa) |
Dehnung | ||||
Vynathene
EY907 |
Hytrel 4056" | 12.3 | 460 | 5.5 | b.Räumt |
Vamac N123 | Hytrel 4056 | 12.8 | 430 | 10.3 | j 220 | |
Vamac N123 | Manolen5203 | 13.9 | 295 | 12.5 | 310 ! |
Vamac N123 | Surlyn 1560* | 15.3 | 275 | 18.3 | 230 j |
165 ! i |
Elastomer | Thermoplast | 4056 | Gewichtsaufnahme Eintauchen in Di bei 900C für 24 |
in % nach eselöl Std. |
Vynathene EY 907 |
Hytrel | 4056 | 23.1 | |
Vamac N123 | Hytrel | ι 5203 | 15.8 | |
Vamac N123 | Manoler | 1560 | 12.9 | |
Vamac N123 | Surlyn | 38.4 |
von Äthylen und Methacrylsäure, Löslichkeitsparameter 8,9
(Hersteller: Dupont)
Massen gute Beständigkeit gegen Kohlenwasserstoff-Lösungsmit- ■ tel und eine gute Beibehaltung ihrer physikalischen Eigenschaften bei der Wärmealterung zeigen. Insbesondere werden die her-j vorragenden Ergebnisse demonstriert, die mit Mischungen'erhal-,
und Dieselöl durch Eintauchen in diese Flüssigkeiten bei 9O0C
Thermoplasti
sches Polymer |
Physik.Eng«
Zugfestigk. }.Raumtemp. MPa |
nschaften
Dehnung % b.Räumt. |
Physik.Eigens
4Std. bei 200 Zugfestigk. b.Raumtemp. MPa |
chaften nad
0C Dehnung % b.Raumtemf |
NYNH verzweigtes Poly
äthylen niedr.Dichte |
9.6 | 385 | 9.7 | 260 |
*Sclai r-Harz,Schmelz-
index 5, Dichte 0,922 |
11,3 | 410 | 11.2 | 350 |
Sclair-Harz, Schmelz
index 5, Dichte 0,930 |
9.0 | 360 | 10.8 | 315 |
Sclair-Harz, Schmelz
index 2,7,Dichte 0,932 |
13.5 | 430 | 11.4 | 340 |
Sclair-Harz, Schmelz
index 2,7,Dichte 0,937 |
10.5 | 340 | 10.7 | 210 |
Sclair-Harz, Schmelz
index 3,3,Dichte 0,950 |
9.9 | 215 | 10.7 | 81 |
Sclair-Harz, Schmelz
index 3,3,Dichte 0,922 Manolen 5203 |
12.9
13.9 |
: 455
295 |
10.2
12.5 |
255
230 |
Thermoplastisches
Polymer |
Gewichtsaufnahm« ASTM-Ol Nr. 2 |
ί (X) nach 24 Std. bei 900C Dieselöl |
DYNH | 16 | 74 |
* Sclair-Harz, Schmelzin dex 5, Dichte 0.922 |
7.8 | 40 |
Sclair-Harz, Schmelzin dex 5, Dichte 0.930 |
5.0 | 25 |
Sclair-Harz, Schmelzin- dex 2,7, Dichte 0.932 |
5.2 | 24 |
Sclair-Harz, Schmelzin- dex 2,7, Dichte 0.937 |
3.7 | 19 |
Sclair-Harz, Schmelzin dex 2,7, Dichte 0.950 |
3.6 | 16 |
Sclair-Harz, Schmelzin- dex 3.3, Dichte 0.922 |
8.5 | 35 |
Manolen 5230 | 2.9 | 13 |
Claims (1)
- Patentansprüche1) Polymermasse, enthaltend eine vernetzbare oder vernetzte
Mischung aus einem Elastomeren und einem thermoplastischen i Polymeren, wobei das Elastomere ein Polymeres von Äthylen
mit einem äthylenisch ungesättigten aliphatischen Ester ; enthält oder daraus besteht und Elastomeres und thermo- ! plastisches Polymeres im wesentlichen frei von halogenhaltigen Substituenten sind.2) Masse nach Anspruch 1, dadurch gekennzeichnet, daß das
Elastomer ein Äthylen/Acrylester-Polymeres oder einÄthylen/Vinylacetat-Polymeres ist, wobei das Polymere we- · nigstens 3,6 Mole Äthylen pro 1000 g Polymeres enthält.3) Masse nach Ansprüchen 1 oder 2, dadurch gekennzeichnet, daß das Elastomere enthält:a) ein Äthylen/Alkylacrylat- oder Äthylen/Alkyl-Methacrylat-Copolymeres, worin die Alkylgruppe 1 bis 4 Kohlenstoffatome aufweist und der Anteil des Acrylsäureesters 2,4
bis 8 Molen Estergruppen pro 1000 g des Copolymeren
äquivalent ist oder · ;b) ein Terpolymeres von Äthylen mit Alkylacrylat oder -Methacrylat, worin die Alkylgruppe 1 bis 4 Kohlenstoff- \ atome aufweist und einer der folgenden Verbindungen '■ als drittem copolymerisierbarem Monomeren: ,i ein C1-C12-AIkYImOnOeStCr oder -diester einer ! Butendicarbonsäure ;ii Acrylsäure ;iii Methacrylsäure IiV Kohlenmonoxid jv Acrylnitril !vi ein Vinylester ;809843/0712ORIGINAL INSPECTEDvii ein Alkyiacrylat oder Alkylmethacrylat, wobei der Älkylrest wenigstens 5 Kohlenstoffatome aufweistviii Maleinsäureanhydrid,wobei der Anteil des Acrylesters 2,5 bis 8 Molen Estergruppen pro 1000 g des Polymeren äquivalent ist und der Anteil des dritten Monomeren nicht höher als 10 Gew.% des Polymeren beträgt oderc) ein Äthylen/Vinylacetat-Copolyneres mit einem Gehalt von wenigstens 35 Gew.% Vinylacetat.4) Masse nach einem der Ansprüche 1 bis 3, dadurch gekennzeichnet, daß das Elastomere ein Terpolymeres aus Äthylen, Me-; thylacrylat und einem carboxylgruppenhaltigen Monomeren enthält oder daraus besteht.5) Masse nach einem der Ansprüche 1 bis 4, dadurch gekennzeichnet, daß das Elastomere einen Schmelzindex von 0,5 bis 15 nach ASTM Nr. D-1238-52T hat.6) Masse nach einem der Ansprüche 1 bis 5, dadurch gekennzeichnet, daß das thermoplastische Polymere ein Polyester, ein Polyamid, ein Copolymeres eines Olefins mit einem ungesättigten Ester mit einem Gehalt von weniger als 25% an ungesättigtem Ester, ein Ionomeres oder ein Polyäthylen ist.7) Masse nach einem der Ansprüche 1 bis 6, dadurch gekenn-zeichnet, daß das thermoplastische Polymere ein segmentiertes Copolyester-Porymeres enthält, das im wesentlichen aus wiederkehrenden intralinearen langkettigen Estereinheiten und kurzkettigen Estereinheiten besteht, die regellos von Kopf zu Schwanz über Esterbindungen verbunden sind, wobei die langkettigen Estereinheiten die allgemeine Formel809843/0712ο σB Ι»-O-G-O-C-R-C-und die kurzkettigen Estereinheiten die allgemeine FormelO Otr it-o-b-o-c-r-c-worin G ein zweiwertiger Rest ist, der nach der Entfernung von endständigen Hydroxyl-Gruppen aus wenigstens einem langkettigen Glykol eines Molekulargewichts von bis 6000 verbleibt; R ein zweiwertiger Rest ist, der nach Entfernung der Carboxylgruppen aus wenigstens einer Dicarbonsäure eines Molekulargewichts von weniger als 300 verbleibt; D ein zweiwertiger Rest ist, der nach der Entfernung der Hydroxylgruppen aus wenigstens einem niedermolekularen : Mol eines Molekulargewichts von weniger als 250 verbleibt.8. Masse nach einem der Ansprüche 1 bis 7, dadurch gekennzeichnet, daß das thermoplastische Polymer ein segmentiertes PoIyätherester-Copolymeres ist, daß sich von Terephthalsäure, Polytetramethylenätherglxkol und 1,4-Butandiol ableitet und· die wiederkehrenden Einheiten. -OC-O OS098U/07122S155,sowie- Ρ (CH, )-0C-</ A-C-V/aufweist, worin η * 6 bis 40 ist. ;9) Masse nach einem der Ansprüche 1 bis 8, dadurch gekenn- : zeichnet, daß der Löslichkeitsparameter des Elastomeren größer als 9 ist.10) Masse nach einem der Ansprüche 1 bis 9, dadurch gekennzeichr net, daß der Löslichkeitsparameter des Elastomeren und des thermoplastischen Polymeren um nicht mehr als 0,5 differie-'ren. '.11) Masse nach einem der Ansprüche 1 bis 10, dadurch gekenn- ; zeichnet, daß Elastomer und thermoplastisches Polymer in '. einem Gewichtsverhältnis von 2,5:1 bis 1:2,5 vorliegen. '12) Masse nach einem der Ansprüche 1 bis 11, dadurch gekenn- ! zeichnet, daß sie eine Mischung aus einea Äthylen/Acrylesterj-Elastomeren und einem segmentierten Copolyester als thermoplastischen Polymeren in Anteilen von 5 bis 50 Gew.Teilen i des Äthylen/Acrylester-Elastomeren pro 100 Gew.Teile des [ segmentierten Copolyesters enthält . ι13) Masse nach einem der Ansprüche 1 bis 12, dadurch gekenn- : zeichnet, daß sie mittels Strahlung hoher Energie vernetzt worden ist.14) Draht oder Kabel, gekennzeichnet durch eine Ummantelung aus: einem Material, welches Massen nach einem der Ansprüche 1809843/0712ORIGINAL INSPECTED5 :bis 13 enthält. j. 15) -Wärmerückstellfähiger Gegenstand, enthaltend eine Polymer- : masse, die eine vernetzte Mischung aus einem Elastomeren und einem thermoplastischen Polymeren enthält oder daraus besteht, wobei das Elastomer ein Polymeres von Äthylen mit jeinem äthylenisch ungesättigten aliphatischen Ester enthält' und das Elastomere sowie das thermoplastische Polymere im ; wesentlichen frei von halogenhaltigen Substituenten sind, j16) Wärmerückstellfähiger Gegenstand nach Anspruch 15, gekenn- j zeichnet durch einen Gehalt an Polymermassen nach einem der]Ansprüche 2 bis 13. '17) Wärmerückstellfähiger Gegenstand, enthaltend ein Elastomeres aus Äthylen/Acrylester und ein thermoplastisches Polymeres.;18) Kabelbaum für Drähte und Kabel, enthaltend einen Gegenstand nach Ansprüchen 15 bis 17. <19) Vernetzte Masse nach einem der Ansprüche 1 bis 13, gekennr- ' zeichnet durch eine ölaufnähme von 10 Gew.% oder weniger j nach Eintauchen in ASTM-Öl Nr. 2 bei einer Temperatur von j 900C für 163 Stunden.20) Polymermasse, gekennzeichnet durch einen Gehalt an einem Elastomeren aus Äthylen/AcryIester und einem thermoplastischen Polymeren.21) Masse nach Anspruch 20, dadurch gekennzeichnet, daß der Acrylester Methylacrylat ist.22) Polymermasse, gekennzeichnet durch einen Gehalt an einem Äthylen/Acrylester-Elastomeren und einem thermoplastischen Polymeren, wobei Elastomeres und thermoplastischen Polymere* im wesentlichen frei von halogenhaltigen Substituenten sind.809843/0712 cw,._ ,23) Wärmerückstellfähiger Gegenstand, gekennzeichnet durch einen Gehalt an einem Elastomeren aus Äthylen/Acrylsäureester und einem thermoplastischen Polymeren mit einem Elastizitätsmodul von mehr als 30 N/m2.24) Polymermasse,enthaltend eine vernetzbare oder vernetzte Mischung aus einem Elastomeren und einem thermoplastischen Polymeren, wobei das Elastomere ein Terpolymeres aus Äthylen, Methylacrylat und einem carboxylgruppenhaltigen Mono- . meren enthält und das thermoplastische Polymere ein von Terephthalsäure, Polytetramethylenätherglykol und 1,4-Butandiol abgeleitetes segmentiertes Polyätherester-Copolymeres mit den wiederkehrenden Einheitenund-OC-// A-c-worin N * 6 bis 40 ist, oder ein lineares Polyäthylen enthält und wobei Elastomer und thermoplastisches Polymer im wesentlichen frei von halogenhaltigen Substituenten sind. '.25) Polymermasse nach Anspruch 1, dadurch gekennzeichnet, daß das thermoplastische^Polymer ein lineares Polyäthylen ist.809843/0712