DE2108184A1 - Zinklegierung - Google Patents
ZinklegierungInfo
- Publication number
- DE2108184A1 DE2108184A1 DE19712108184 DE2108184A DE2108184A1 DE 2108184 A1 DE2108184 A1 DE 2108184A1 DE 19712108184 DE19712108184 DE 19712108184 DE 2108184 A DE2108184 A DE 2108184A DE 2108184 A1 DE2108184 A1 DE 2108184A1
- Authority
- DE
- Germany
- Prior art keywords
- zinc
- zinc alloy
- exceed
- final rolling
- rare earths
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Description
PATENTANWALT 4 DÖSSELDORF-BENRATH 2108184
DlPL-ING. ULRICH PLÖGER BENRAWER SCHLOSSAUEE 89
REG. NR. 1771
CENTRE NATIONAL DE RECHERCHES METALLURGIQÜES, *
Association Sans But Lucratif, ™
47, rue Montoyer, Brüssel / BELGIEN
Zinklegierung
Die Erfindung bezieht sich auf eine Legierung mit Zink als
Grundmetall, bei welcher die mechanischen Eigenschaften, und zwar insbesondere die Dehnungseigenschaften, verbessert sind, J
speziell gegenüber denjenigen des reinen Zinks, wie es elektrolytisch oder thermisch erzeugt wird.
Es wird davon ausgegangen, daß die Metalle mit einer hexagonal dichten Struktur sich durch eine mindere Bildsamkeit kenn
zeichnen, welche Eigenschaft darüberhinaus noch durch die Mehr
zahl der ihnen gemachten Zusätze verschlechtert wird. Die»·· ist
BAO ORtQiNAL
109836/1008
b«in Zink der FaII, und die Veränderung seiner Bildsamkeit war
häufig durch seine verschiedenen Zusätze bedingt.
Überraschenderweise wurde nun gefunden, daß der Zusatz von den
zu den Seltenen Erden zählenden Elenenten bein Zink zu einer merklichen Verbesserung der Bildsamkeit dieses Metalls beiträgt, obgleich diese Elemente gleichfalls von einer hexagonal dichten Struktur sind.
Diese Eigenschaft hat sich vor allem für die binären Zink/Seltene Erden-Verbindungen als zutreffend erwiesen, welche eine
oder mehrere der folgenden Seltenen Erden enthalten; Dy, Er, Gd, Ho, Nd, Pr, La; der Anteil darf dabei für ein oder mehrere
Elemente 5 % und vorzugsweise 1 % je Eic—nt nicht fiberschreiten.
Besonders vorteilhafte Ergebnisse wurden bei binären Legierungen
erhalten, bei welchen der Gehalt des einen oder anderen Elementes der vorerwähnten Seltenen Erden in der Größenordnung von
0,1 % lag, wobei der Rest aus Zink mit seinen üblichen Verunreinigungen an Pb, Sn, Cd, Fe, In, Ag und dergleichen bestand.
Das Entstehen einer Verbesserung der Werte für die Bildsamkeit dieser Legierungen wird indessen durch durch die Merkmale des
abschließenden Walzens begünstigt, dem diese Legierungen unterworfen werden, wobei die genannte Verbesserung umso merklicher
ist, je mehr die Temperatur beim abschließenden Walzen der Umgebungstemperatur angenähert ist.
Die nachstehende Tafel zeigt im Vergleich die Ergebnisse des
Faltbiegeversuches einerseits für reines Elektrolyt-Zink und andererseits für eine Reihe von binären Legierungen der vorstehend genannten Art:
BAD
109836/1058
Endwalzung bei | Endwalzung bei | |
200° C | Umgebungstemperatur | |
Zn | 13 | 11 |
Zn + 0,1 1 | 9 | 28 |
Zn + 0,1 1 | 19 | 23 |
Zn + 0,1 1 | 18 | 26 |
Zn + 0,1 1 | 18 | 22 |
Zn ♦ 0,1 1 | 21 | 17 |
Zn + 0,1 1 | 13 | 20 |
ϊ Dy | ||
k Er | ||
i Gd | ||
i Ho | ||
t Nd | ||
k Pr |
Die dargestellten Zahlen stellen den Index der quer zur Wals» richtung vorgenommenen Biegung nach dem Verfahren des abwechselnden Biegens nach Amsler dar.
In Bereich der beim Zink durch Zusatz der obengenannten Elemente der seltenen Erden erzielten Verbesserungen muß festgestellt werden, daß diese Verbesserungen anhalten, wenngleich
in einer geringeren Höhe, wenn das Zink Magnesium in einem Anteil unter 0,1 % enthält.
109836/1008
Claims (2)
1. Binäre Zinklegierung, dadurch gekennzeichnet, daß sie
eine oder mehrere der aus der Gruppe Dy, Er, Gd, Ho, Nd, Pr, La ausgewählten seltenen Erden enthält, wobei
der gesamte Gewichtsanteil an diesen seltenen Erden nicht über S % und der Gewichteanteil für eine seltene
Erde nicht über 1 % liegt und der Rest aus Zink und seinen üblichen Verunreinigungen Pb, Sn, Cd, Fe, In, Ag
und dergleichen besteht.
2. Legierung nach Anspruch 1, dadurch gekennzeichnet, daß sie einer Endwalzung unterzogen ist, deren Temperatur
2000C nicht übersteigt und vorzugsweise in Nähe der Umgebungstemperatur
liegt.
109836/1008