DE102010008650A1

DE102010008650A1 - Bearing ring for roller bearing, is provided with continuous circumferential tracks, in whose region roller contact takes place

Info

Publication number: DE102010008650A1
Application number: DE102010008650A
Authority: DE
Inventors: Klaus Daut; Sergej Dr. Schwarz; Patrick Mirring; Bernd Gombert; Werner Dr. Trojahn
Original assignee: Schaeffler Technologies AG and Co KG
Current assignee: Schaeffler Technologies AG and Co KG
Priority date: 2009-08-14
Filing date: 2010-02-20
Publication date: 2011-02-17

Abstract

The bearing ring is provided with the continuous circumferential tracks (5,6), in whose region a roller contact takes place. The bearings (7,9) have a relative wall thickness relative to the wall thickness of the total corpus of bearing rings. The material of the former bearing has certain compressive strength. The material of the former bearing has a module of certain elasticity. An independent claim is also included for a roller bearing.

Description

Gebiet der ErfindungField of the invention

Die Erfindung betrifft einen Lagerring nach dem Oberbegriff des Anspruchs 1 für ein Wälzlager, einen Lagerring mit einem Träger und einer Laufbahn nach Anspruch 11, sowie ein Wälzlager nach Anspruch 12.The The invention relates to a bearing ring according to the preamble of the claim 1 for a rolling bearing, a bearing ring with a Carrier and a track according to claim 11, and a rolling bearing according to claim 12.

Aus der Praxis sind Lagerringe bekannt, die eine Laufbahn als Oberflächenabschnitt des Korpus des Lagerrings aufweisen, wobei im Bereich der Laufbahn ein Kontakt mit einem anderen Bestandteil des Lagers auftritt. Dieser andere Körper des Lagers ist für den Fall des Wälzlagers ein Wälzkörper, der im Bereich der Laufbahn des Wälzlager-Lagerrings in Wälzkontakt mit der Oberfläche des Korpus des Wälzlager-Lagerrings tritt.Out In practice, bearing rings are known which have a track as a surface section having the body of the bearing ring, wherein in the region of the raceway a contact with another component of the warehouse occurs. This other body of the camp is in the case of Rolling bearing a rolling element, in the field the raceway of the rolling bearing bearing ring in rolling contact with the surface of the body of the rolling bearing race occurs.

Für Wälzlager ist bekannt, dass die Lagerringe ein Korpus aufweisen, das massiv aus einem Stahl, insbesondere einem Wälzlagerstahl, besteht, wobei der den Anforderungen des Wälzlagers entsprechende Stahl, speziell der Wälzlagerstahl, aufgrund seiner mechanischen und tribologischen Eigenschalten für den Bereich der Laufbahn des Lagerrings als Material für das gesamte Korpus des Lagerrings gewählt wird, um den im Bereich der Laufbahn des Lagerrings, also nur einem Teilbereich der Oberfläche des Korpus des Lagerrings auftretenden Betriebsbedingungen, Rechnung zu tragen. Stahl, speziell Wälzlagerstahl, weist eine hohe Dichte auf, so dass Lagerringe für insbesondere Großlager, also für Lager mit einem Durchmesser von mehr als ca. 1000 Millimeter, ein hohes Gewicht erhalten. Stahl und der aus Stahl hergestellte Wälzlagerstahl können zeitweilig knappe und damit teure Rohstoffe darstellen.For Rolling bearing is known that the bearing rings have a body, the massive one steel, in particular a bearing steel, which corresponds to the requirements of the rolling bearing Steel, especially bearing steel, due to its mechanical properties and tribological peculiarities for the field of career of the bearing ring as material for the entire body of the Bearing ring is chosen to be in the range of the raceway Lagerrings, so only a portion of the surface of the Body of the bearing ring occurring operating conditions, invoice to wear. Steel, especially bearing steel, has a high Density, so that bearing rings for especially large storage, So for bearings with a diameter of more than about 1000 millimeters, get a high weight. Steel and made of steel Rolled bearing steel can be temporarily scarce and thus represent expensive raw materials.

US 5,866,647 A beschreibt einen Lagerring für ein Wälzlager, wobei das gesamte Korpus des Lagerrings aus einem faserverstärkten Kunststoff hergestellt ist, so dass auch im Bereich der Laufbahn der faserverstärkte Kunststoff den Reibpartner für den Wälzkontakt ausbildet. Faserverstärkte Kunststoffe können unter hohen mechanischen Belastungen ihre Eigenschaften ändern, so dass bei Betrieb des Lagerrings dessen Eigenschaften schwer vorhersehbar sind. US 5,866,647 A describes a bearing ring for a rolling bearing, wherein the entire body of the bearing ring is made of a fiber-reinforced plastic, so that also in the region of the raceway, the fiber-reinforced plastic forms the friction partner for the rolling contact. Fiber-reinforced plastics can change their properties under high mechanical loads, so that its properties are difficult to predict when the bearing ring is in operation.

DE 101 24 534 A1 beschreibt einen Lagerring für ein Wälzlager bzw. für ein Gleitlager, wobei das Korpus des Lagerrings eine Laufbahn aus einem Glas bzw. aus einer Glaskeramik umfasst, und das Glas auf einen metallischen Körper als Träger aufgespritzt ist. Hierbei tritt bei Betrieb des Lagers der Kontakt mit dem Glas bzw. mit der Glaskeramik auf, deren Verschleißeigenschaften deutlich von denen des insoweit gut bekannten Wälzlagerstahls abweichen. DE 101 24 534 A1 describes a bearing ring for a rolling bearing or a sliding bearing, wherein the body of the bearing ring comprises a raceway of a glass or of a glass ceramic, and the glass is sprayed onto a metallic body as a carrier. In this case occurs during operation of the bearing of the contact with the glass or with the glass ceramic, the wear properties of which differ significantly from those of the well-known rolling bearing steel.

DE 202 00 241 U1 beschreibt einen Lagerring für ein Wälzlager, wobei ein Träger aus einem Kunststoff oder einem Faserverbundstoff vorgesehen ist, und wobei an dem Träger ein Korpus einer Laufbahn angeordnet ist. Das Korpus der Laufbahn umfasst jeweils einen Laufdraht aus Stahldraht, auf dem ein Wälzkontakt mit einem Wälzkörper stattfindet, wobei der Laufdraht wesentlich dünner als der Träger ist. Eine derartige Anordnung weist insbesondere auf den Fall von Großwälzlagern übertragen keine ausreichende Stabilität auf, um die beim Betrieb des Großwälzlagers auf die Laufbahn übertragenen Kräfte dauerhaft aufnehmen zu können. DE 202 00 241 U1 describes a bearing ring for a rolling bearing, wherein a carrier made of a plastic or a fiber composite material is provided, and wherein on the carrier a body of a track is arranged. The body of the track each comprises a running wire of steel wire, on which a rolling contact with a rolling element takes place, wherein the running wire is substantially thinner than the carrier. Such an arrangement has in particular in the case of large rolling bearings do not transmit sufficient stability to accommodate the forces transmitted to the career during operation of the large rolling bearing permanently.

DE 10 2007 062 145 A1 beschreibt einen Lagerring für insbesondere Großwälzlager, wobei der Lagerring durch aneinander gefügte Segmente ausgebildet ist, so dass zwei benachbarte Segmente eine Fügestelle ausbilden, was insbesondere im Wälzkontakt zu einer Laufunruhe führt. DE 10 2007 062 145 A1 describes a bearing ring for particular slewing bearings, wherein the bearing ring is formed by segments joined together, so that two adjacent segments form a joint, which leads in particular in Wälzkontakt to a rough running.

Aufgabe der ErfindungObject of the invention

Es ist die Aufgabe der Erfindung, einen Lagerring anzugeben, der die Eigenschaften des Stahls im Bereich der Laufbahn beibehält und verbesserte, insbesondere auf den konkreten Betriebsfall anpassbare, Eigenschaften erhält.It The object of the invention to provide a bearing ring, the Properties of the steel in the area of the track maintains and improved, in particular adaptable to the specific case of operation, Features get.

Zusammenfassung der ErfindungSummary of the invention

Diese Aufgabe wird erfindungsgemäß durch einen Lagerring mit den Merkmalen des Anspruchs 1 bzw. 11 für ein Wälzlager nach Anspruch 12 gelöst.These Task is inventively by a bearing ring with the features of claim 1 or 11 for a rolling bearing solved according to claim 12.

Die Maßgaben des Kennzeichens des Anspruchs 1 stellen sicher, dass der Lagerring zweiteilig, nämlich aus der Laufbahn und dem Träger, ausgebildet ist, so dass der sich insgesamt ergebende Lagerring Eigenschaften aufweist, die mindestens den betriebsrelevanten Eigenschaften entsprechen, die ein vollständig aus Stahl, insbesondere Wälzlagerstahl ausgebildeter Lagerring zeigt. Für die Auswahl des Materials des Trägers bzw. für die Bemessung des Trägers besteht jeweils ein Freiheitsgrad, der ausgenutzt werden kann, um einen zweiteiligen oder mehrteiligen Lagerring zu erhalten, dessen Eigenschaften gegenüber dem vollständig aus Stahl, insbesondere vollständig aus Wälzlagerstahl, hergestellten Lagerring verbessert sind.The The provisions of the characterizing portion of claim 1 ensure that that the bearing ring in two parts, namely from the raceway and the wearer, is formed so that the total resulting bearing ring has properties that at least the operational Properties that are completely made of steel, especially bearing steel trained bearing ring shows. For the selection of the material of the carrier or for the design of the carrier exists respectively a degree of freedom that can be exploited to form a two-part or to obtain a multi-part bearing ring whose properties are opposite completely made of steel, in particular completely from bearing steel, produced bearing ring improved are.

Die Maßgabe, dass der Träger als Kreisring ausgebildet ist und eine relative Wandstärke, bezogen auf die Wandstärke des gesamten Korpus des Lagerrings, von mindestens ca. 0,44, insbesondere mindestens ca. 0,55, aufweist, stellt insbesondere für den Anwendungsfall des Wälzlagers sicher, dass die bei der Überrollung der Laufbahn auftretenden Kräfte aufgenommen werden können, da diese Kräfte bis in eine Tiefe von mindestens ca. 50% der gesamten Dicke des Lagerrings eingetragen werden können. Der Träger muss daher nur verhältnismäßig geringe Kräfte aufnehmen und kann hinsichtlich seines Materials dahingehend ausgewählt werden, dass er leichtbauend bzw. kostengünstig herstellbar zugleich ist.The proviso that the carrier is formed as a circular ring and a relative wall thickness, based on the wall thickness of the entire body of the bearing ring, of at least about 0.44, in particular at least about 0.55, has, in particular for the application of the rolling bearing certain that the forces occurring during the rolling over of the raceway can be absorbed, since these forces are to a depth of at least approximately 50% of the total Di can be registered bridge of the bearing ring. Therefore, the carrier must absorb only relatively small forces and can be selected in terms of its material to the effect that it is easy to build and inexpensive to produce at the same time.

Die Maßgabe, dass das Material des Trägers eine Druckfestigkeit von mindestens ca. 480 MPa, insbesondere mindestens ca. 600 MPa, aufweist, stellt sicher, dass entlang der Kontaktfläche zwischen dem Korpus des Trägers und dem Korpus des Lagerrings auftretende Zug- oder Druckkräfte von dem Träger so weit aufgenommen werden können, dass das Material des Trägers unbeschädigt bleibt und das Lager im Betriebsfall die gleiche Belastbarkeit aufweist wie ein vollständig aus dem Material der Laufbahn hergestelltes Lager.The Provided that the material of the carrier is a compressive strength of at least about 480 MPa, in particular at least about 600 MPa, has, ensures that along the contact surface between the body of the carrier and the body of the bearing ring occurring tensile or compressive forces from the carrier can be absorbed so far that the material of the Carrier remains undamaged and the bearing in case of operation the same load capacity as a complete bearing made of the material of the raceway.

Die Maßgabe, dass das Material des Trägers ein Elastizitätsmodul von mindestens ca. 40 GPa, insbesondere mindestens ca. 50 GPa, aufweist, stellt sicher, im Bereich der Kontaktfläche zwischen dem Korpus des Trägers und dem Korpus des Lagerrings auftretende Tangentialspannungen sicher aufgenommen werden können, so dass der Verbund aus dem Träger und dem Lagerring dauerhaft stabil ist und das Lager nach außen hin eine vergleichbare Steifigkeit aufweist.The Provided that the material of the carrier has a modulus of elasticity of at least about 40 GPa, in particular at least about 50 GPa, ensures in the area of the contact surface between the body Tangential stresses occurring in the carrier and the body of the bearing ring can be safely taken, so that the composite out the carrier and the bearing ring is permanently stable and the bearing has a similar stiffness to the outside.

Die Erfindung umfasst weiter einen Lagerring, umfassend eine Laufbahn mit einem Korpus aus einem aufgestickten, martensitischen Kaltarbeitsstahl, insbesondere aus einem martensitisch härtbaren stickstofflegierten Stahl mit je mindestens 0,2% Kohlenstoff und Stickstoff sowie mindestens 13% Chrom, einen Träger aus einem Vergütungsstahl, einem Einsatzstahl oder einem austenitischen Stahl, wobei das Korpus der Laufbahn an dem Träger befestigt ist. Ein derartiger Lagerring bietet, auch für den Fall, dass die relative Wandstärke des Trägers, bezogen auf die Wandstärke des gesamten Lagerrings weniger als ca. 0,44 beträgt, eine sichere Aufnahme für die bei dem Betrieb mit der Überrollung auftretenden Kräfte. Ein derartiger Lagerring ist vorzugsweise für den Fall vorgesehen, dass der Durchmesser des Lagerringes einige Dezimeter (wie für Bahnlager beispielsweise bekannt) oder einige Meter (wie für Anwendungen bei Windkraftanlagen geläufig) beträgt. Vorzugsweise ist ein derartiger Lagerring Teil eines Wälzlagers, das weiter Wälzkörper aus einem keramischen Material umfasst. Alternativ zu dem Korpus der Laufbahn aus dem Kaltarbeitsstahl ist vorgesehen, dass das Korpus der Laufbahn aus einem Schnellarbeitsstahl, insbesondere einem pulvermetallurgisch hergestellten Schnellarbeitsstahl, hergestellt ist.The The invention further comprises a bearing ring comprising a raceway with a body made of an embroidered, martensitic cold-work steel, in particular from a martensitic hardenable nitrogen-alloyed Steel containing at least 0.2% carbon and nitrogen and at least 13% chromium, a carrier made of a tempered steel, a case hardening steel or an austenitic steel, wherein the body the raceway is attached to the carrier. Such a Bearing ring provides, even in the event that the relative Wall thickness of the carrier, based on the wall thickness of the entire bearing ring is less than about 0.44, one safe absorption for those occurring during operation with the rollover Forces. Such a bearing ring is preferably for provided the case that the diameter of the bearing ring some Decimeter (as known for railway camp, for example) or a few meters (as for wind turbine applications common). Preferably, such is Bearing ring part of a rolling bearing that continues rolling elements made of a ceramic material. Alternative to the body The raceway made of cold-work steel is intended to be the body the track of a high-speed steel, in particular a powder metallurgical manufactured high-speed steel.

Vorzugsweise ist vorgesehen, dass das Material des Trägers in Bezug auf das Material des Lagerrings, nämlich in Bezug auf Stahl und insbesondere Wälzlagerstahl so gewählt ist, dass die Dichte des Materials des Trägers deutlich geringer ist als die Dichte des Materials der Laufbahn. Der insgesamt erhaltene Lagerring weist damit ein geringeres Gewicht auf als der vollständig aus dem Stahl, insbesondere dem Wälzlagerstahl, hergestellte Lagerring. Vorzugsweise ist für das Material der Laufbahn vorgesehen, dass dass das Material der Laufbahn einen aufgestickten, martensitischen Kaltarbeitsstahl, insbesondere einen martensitisch härtbaren stickstofflegierten Stahl mit je mindestens 0,2% Kohlenstoff und Stickstoff sowie mindestens 13% Chrom, umfasst. Das Material des Trägers kann in besonders bevorzugter Ausgestaltung einen Kunststoff, eine Keramik, ein Leichtmetall, speziell Aluminium oder Titan, oder ein Faserverbundwerkstoff, speziell ein Kohlenstofffaser-, ein Keramikfaser- oder ein Glasfaserverstärkter Kunststoff, umfassen. Besteht der Träger insbesondere aus dem Faserverbundwerkstoff, kann der Träger auf den Außenumfang des Korpus der Laufbahn durch einen Wickelprozess aufgetragen sein, bei dem die Fasern von der Matrix durchtränkt den Umfang der Laufbahn lagenweise umlaufend aufgebracht werden und im folgenden eine Aushärtung abläuft, so dass eine feste Verbindung zwischen dem Korpus der Laufbahn und dem Träger stattfindet, die insbesondere eine form- und kraftschlüssige Verbindung im Bereich der gemeinsamen Kontaktfläche ausbildet. Der Träger aus dem Kunststoff bzw. der Keramik lässt sich beispielsweise aufspritzen oder abscheiden, das Leichtmetall sowie der Kunststoff, die Keramik bzw. der Faserverbundwerkstoff als vorgefertigter Kreisring bereitstellen, der mit dem kreisringförmigen Korpus des Lagerrings formschlüssig bzw. reib- oder kraftschlüssig, beispielsweise mittels Aufschrumpfen, zu einem festen Verbund gefügt wird.Preferably is provided that the material of the wearer in relation on the material of the bearing ring, namely in relation to steel and in particular bearing steel is chosen so that the density of the material of the carrier is significantly lower is considered the density of the material of the track. The total surviving Bearing ring thus has a lower weight than the complete made of steel, in particular bearing steel Bearing ring. Preferably, for the material of the career provided that that the material of the career one embroidered, martensitic cold work steel, in particular a martensitic hardenable nitrogen-alloyed steel with at least 0.2% each Carbon and nitrogen and at least 13% chromium. The material of the carrier can in a particularly preferred embodiment a plastic, a ceramic, a light metal, especially aluminum or titanium, or a fiber composite, especially a carbon fiber, a ceramic fiber or a glass fiber reinforced plastic, include. If the carrier consists in particular of the fiber composite material, The carrier may be on the outer circumference of the carcass the career be applied by a winding process, in which the fibers from the matrix saturate the circumference of the raceway be applied circumferentially in layers and in the following curing expires, leaving a firm connection between the body the career and the carrier takes place in particular a positive and non-positive connection in the field of forms common contact surface. The carrier from the plastic or the ceramic can be, for example spray or deposit the light metal as well as the plastic that Ceramics or the fiber composite material as a prefabricated circular ring provide with the annular body of the Bearing ring with positive locking or frictional or force-locking, For example, by means of shrinking, is joined to a solid composite.

Vorzugsweise ist hinsichtlich der Auswahl des Materials des Trägers vorgesehen, dass das Material des Trägers einen Eisenwerkstoff umfasst, insbesondere einen Grauguss. Der Träger kann beispielsweise vollständig als Kreisring aus einem Grauguss hergestellt sein, wobei das Korpus des Trägers form- oder reibschlüssig an dem Korpus des Lagerrings befestigt ist.Preferably is with regard to the selection of the material of the carrier provided that the material of the carrier is a ferrous material includes, in particular a gray cast iron. The carrier may, for example completely manufactured as a circular ring from a gray cast iron be, with the body of the carrier positive or frictional attached to the body of the bearing ring.

Als Alternative zu einem Träger aus einem Eisenwerkstoff wie Grauguss ist vorzugsweise vorgesehen, dass das Material des Trägers einen Vergütungsstahl, einen Einsatzstahl oder einen austenitischen Stahl umfasst.When Alternative to a carrier made of a ferrous material such as Cast iron is preferably provided that the material of the carrier a tempered steel, a case hardening steel or an austenitic one Steel covers.

Vorzugsweise ist vorgesehen, dass das Material des Trägers ein Glas, insbesondere ein technisches Glas wie ein Bor-Silikat-Glas oder ein Quarzglas, umfasst. Das Korpus des Trägers kann insbesondere vollständig aus dem Glas, speziell aus dem technischen Glas wie dem Bor-Silikat-Glas bzw. dem Quarzglas, bestehen, wobei der Träger als Glasring bereitgestellt wird, der form- oder reibschlüssig an dem Korpus der Laufbahn befestigt ist. Es versteht sich, dass das Glas auch mittels eines Sol-Gel-Prozesses oder eines naßchemischen Abscheideverfahrens auf das Korpus der Laufbahn aufgetragen sein kann.It is preferably provided that the material of the carrier comprises a glass, in particular a technical glass such as a borosilicate glass or a quartz glass. The body of the carrier may in particular consist entirely of the glass, especially of the technical glass such as the boron-silicate glass or quartz glass, wherein the carrier is a glass ring is provided, which is positively or frictionally secured to the body of the track. It is understood that the glass may also be applied to the body of the raceway by means of a sol-gel process or a wet-chemical deposition process.

Vorzugsweise ist vorgesehen, dass das Material des Trägers Kohlenstoff in Form von Nanoröhrchen umfasst. Diese Nanoröhrchen können beispielsweise dem Glas, dem Kunststoff, der Keramik bzw. dem Faserverbundwerkstoff zugesetzt sein; alternativ hierzu können die Nanoröhrchen als verpresstes Pulver bereitgestellt werden.Preferably is provided that the material of the carrier carbon in the form of nanotubes. These nanotubes For example, the glass, the plastic, the ceramic or be added to the fiber composite material; Alternatively, you can provided the nanotubes as compressed powder become.

Vorzugsweise ist vorgesehen, dass der Lagerring für ein Großwälzlager vorgesehen ist, insbesondere, dass der Lagerring einen Durchmesser von mehr als ca. 1000 Millimetern aufweist, so dass sich insbesondere die Gewichtsersparnis vorteilhaft auswirkt.Preferably is provided that the bearing ring for a slewing bearing is provided, in particular, that the bearing ring has a diameter of more than about 1000 millimeters, so in particular the weight savings advantageous.

Hinsichtlich des Wälzlagers ist vorgesehen, dass mindestens einer der beiden Lagerringe, bevorzugt beide Lagerringe so ausgebildet sind, dass eine Laufbahn und ein als Kreisring ausgebildeter, an der Laufbahn befestigter Träger vorgesehen ist, wobei für das Material des Trägers die oben hinsichtlich des Elastizitätsmoduls bzw. Druckspannungen angegebenen Parameterbereiche eingehalten werden, und wobei die relative Wandstärke des Trägers, bezogen auf die Wandstärke des gesamten Lagerrings, mindestens ca. 0,44, insbesondere mindestens ca. 0,55 beträgt.Regarding of the rolling bearing is provided that at least one of both bearing rings, preferably both bearing rings are designed so that a track and a trained as a circular ring, on the track fixed support is provided, wherein for the Material of the carrier the up in terms of elastic modulus or compressive stresses specified parameter ranges are met, and wherein the relative wall thickness of the carrier, based on the wall thickness of the entire bearing ring, at least about 0.44, in particular at least about 0.55.

Weitere Vorteile und Merkmale der Erfindung ergeben sich aus den abhängigen Ansprüchen sowie aus der Beschreibung von Ausführungsbeispielen.Further Advantages and features of the invention will become apparent from the dependent Claims and from the description of exemplary embodiments.

Die Erfindung wird im folgenden unter Bezugnahme auf die anliegenden Zeichnungen näher beschrieben und erläutert.The Invention will be described below with reference to the appended Drawings described and explained in detail.

Kurze Beschreibung der ZeichnungenBrief description of the drawings

1 zeigt eine schematische Darstellung eines ersten Ausführungsbeispiels eines erfindungsgemäßen Lagerrings in einem ersten Ausführungsbeispiel eines erfindungsgemäßen Lagers, und 1 shows a schematic representation of a first embodiment of a bearing ring according to the invention in a first embodiment of a bearing according to the invention, and

2 zeigt eine schematische Darstellung eines zweiten Ausführungsbeispiels eines erfindungsgemäßen Lagerrings in einem zweiten Ausführungsbeispiel eines erfindungsgemäßen Lagers. 2 shows a schematic representation of a second embodiment of a bearing ring according to the invention in a second embodiment of a bearing according to the invention.

Detaillierte Beschreibung der ZeichnungenDetailed description the drawings

1 zeigt ein Wälzlager 1, das einen ersten Lagerring 2, der als Außenring des Wälzlagers 1 ausgebildet ist, und einen zweiten Lagerring 3, der als Innenring des Wälzlagers 1 ausgebildet ist, umfasst. Das Wälzlager 1 umfasst weiter zylindrische Wälzkörper 4, die an einer ersten Laufbahn 5 an dem Außenring 2 sowie an einer zweiten Laufbahn 6 an dem Innenring 3 abrollen, so dass ein Wälzkontakt zu den beiden Laufbahnen 5, 6, im Betrieb des Lagers 1 auftritt. Der Innenring 3 weist einen Lagerbord auf, der die Wälzkörper 4 in axialer Richtung, also in Richtung der Drehachse des Wälzlagers 1, nämlich senkrecht zu der Papierebene in der Darstellung von 1, sichert. 1 shows a rolling bearing 1 that has a first bearing ring 2 , the outer ring of the rolling bearing 1 is formed, and a second bearing ring 3 , the inner ring of the rolling bearing 1 is formed comprises. The rolling bearing 1 further comprises cylindrical rolling elements 4 who are on a first career 5 on the outer ring 2 as well as on a second career 6 on the inner ring 3 unroll, leaving a rolling contact with the two raceways 5 . 6 , in the operation of the warehouse 1 occurs. The inner ring 3 has a bearing board, which the rolling elements 4 in the axial direction, ie in the direction of the axis of rotation of the rolling bearing 1 , namely perpendicular to the plane of the paper in the representation of 1 , secures.

Die beiden Laufbahnen 5, 6 der beiden Lagerringe 2, 3 sind jeweils als kreisringförmiges Korpus ausgebildet, wobei die Kontaktfläche zu den Wälzkörpern 4, an der der Wälzkontakt stattfindet, einen Teilabschnitt der auf die Wälzkörper 4 weisenden Oberfläche des jeweiligen Korpus ausbildet. Das jeweilige Korpus der beiden Laufbahnen 5, 6 ist vollständig aus einem Stahl, insbesondere aus einem Wälzlagerstahl, ausgebildet, so dass der Wälzkontakt der Wälzkörper 4 mit dem Wälzlagerstahl der beiden Laufbahnen 5, 6 stattfindet.The two careers 5 . 6 the two bearing rings 2 . 3 are each formed as an annular body, wherein the contact surface to the rolling elements 4 , at which the rolling contact takes place, a partial section of the rolling elements 4 forming surface of the respective body. The respective body of the two raceways 5 . 6 is formed entirely of a steel, in particular of a bearing steel, so that the rolling contact of the rolling elements 4 with the rolling bearing steel of the two raceways 5 . 6 takes place.

Das Wälzlager 1 ist als Großwälzlager ausgebildet, so dass jeder der beiden Lagerringe 2, 3 einen Durchmesser von mehr als 1000 Millimetern aufweist.The rolling bearing 1 is designed as a slewing bearing, so that each of the two bearing rings 2 . 3 has a diameter of more than 1000 millimeters.

Im folgenden wird insbesondere der erste Lagerring 2, also der Außenring des Wälzlagers 1, mit der ersten Laufbahn 5, näher beschrieben, mit dem Verständnis, dass die Angaben entsprechend auf den zweiten Lagerring 3, also den Innenring des Wälzlagers 1, mit der zweiten Laufbahn 6 zu übertragen sind.In the following, in particular, the first bearing ring 2 , ie the outer ring of the rolling bearing 1 , with the first career 5 , described in more detail, with the understanding that the information corresponding to the second bearing ring 3 , ie the inner ring of the rolling bearing 1 , with the second career 6 to be transferred.

Der Lagerring 2 umfasst zusätzlich zu der Laufbahn 5 einen Träger 7, der als kreisringförmiges Korpus umfasst, das an dem Korpus der Laufbahn 5 entlang einer gemeinsamen Kontaktfläche 9 befestigt ist. Der Lagerring 2 ist damit zweiteilig aufgebaut und besteht aus der Laufbahn 5 sowie aus dem an der Laufbahn 5 befestigten Träger 7. Dabei ist die auf die Laufbahn 5 weisende Seite des Trägers 7 an der auf den Träger 7 weisenden Seite der Laufbahn 5 so befestigt, dass die entlang des Umfangs des Kreisrings durchgehende Kontaktfläche 8 zu dem Träger 7 ausgebildet ist, und zwar derart, dass zwischen dem Träger 7 und dem Korpus der Laufbahn 5 kein Hohlraum ausgebildet ist. Der Träger 7 sowie die Laufbahn 5 sind somit in Umfangsrichtung des Lagerrings 2 ungeteilt ausgebildet. Ebenso sind der Träger 7 und die Laufbahn 5 in Richtung der Drehachse des Lagerrings 2, also in der Darstellung von 1 senkrecht zu der Papierebene, einteilig ausgestaltet.The bearing ring 2 includes in addition to the career path 5 a carrier 7 which comprises an annular body attached to the body of the track 5 along a common contact surface 9 is attached. The bearing ring 2 is thus constructed in two parts and consists of the track 5 as well as from the on the career 5 fastened carrier 7 , It is the on the career 5 pointing side of the vehicle 7 at the on the carrier 7 pointing side of the track 5 fixed so that the along the circumference of the annulus continuous contact surface 8th to the carrier 7 is formed, in such a way that between the carrier 7 and the corpus of the career 5 no cavity is formed. The carrier 7 as well as the career 5 are thus in the circumferential direction of the bearing ring 2 undivided trained. Likewise, the carrier 7 and the career 5 in the direction of the axis of rotation of the bearing ring 2 , ie in the presentation of 1 perpendicular to the plane of the paper, one-piece.

Der Träger 7 ist aus einen Faserverbundwerkstoff, speziell einem Glasfaserverstärkten Kunststoff, ausgebildet, wobei zum Aufbringen des Trägers 7 auf die nach außen weisende Seite der Laufbahn 5 die mit dem Harz getränkten Fasern um die nach außen weisende Seite gewickelt wurden, so dass sich ein mehrlagiger Verbund ergibt, der bei einer anschließenden Aushärtung fest an der Laufbahn 5 verbleibt. Die Wandstärke des Trägers 7 beträgt ca. zwei Drittel der gesamten Wandstärke des Lagerrings 2.The carrier 7 is made of a fiber composite material, especially a glass fiber reinforced plastic, formed, for applying the carrier 7 on the outward facing side of the track 5 the fibers soaked with the resin were wound around the outward-facing side, resulting in a multi-layered composite, which firmly adheres to the raceway during subsequent curing 5 remains. The wall thickness of the carrier 7 is about two-thirds of the total wall thickness of the bearing ring 2 ,

Der zweite Lagerring 3 weist ebenfalls einen Träger 9 auf, der an einer gemeinsamen Kontaktfläche 10 zu der zweiten Laufbahn 6 in Umlaufrichtung ohne dazwischen liegende Hohlräume befestigt ist. Der Träger 9 besteht ebenfalls aus einem Faserverbundwerkstoff, insbesondere aus dem gleichen Material wie der Träger 7 des ersten Lagerrings 2. Der zweite Träger 9 weist ebenfalls eine Wandstärke auf, die ca. 50% der Wandstärke des zweiten Lagerrings 3 beträgt, gemessen an einer Stelle, an der keiner der Borde vorgesehen ist.The second bearing ring 3 also has a carrier 9 on, at a common contact area 10 to the second career 6 is fixed in the direction of rotation without intermediate cavities. The carrier 9 also consists of a fiber composite material, in particular of the same material as the carrier 7 of the first bearing ring 2 , The second carrier 9 also has a wall thickness, which is about 50% of the wall thickness of the second bearing ring 3 is, measured at a point where none of the shelves is provided.

Durch das Faserverbundwerkstoff-Material der beiden Träger 7, 9 weisen die beiden Lagerringe 2, 3 jeweils ein Gewicht auf, das deutlich geringer ist als das Gewicht eines Lagerrings, der bei gleichen äußeren Abmessungen vollständig aus dem Stahl, insbesondere dem Wälzlagerstahl ausgebildet ist.Through the fiber composite material of the two carriers 7 . 9 have the two bearing rings 2 . 3 in each case a weight which is significantly lower than the weight of a bearing ring, which is completely formed with the same outer dimensions of the steel, in particular the bearing steel.

Bei dem vorstehend beschriebenen ersten Ausführungsbeispiel waren die aus dem Faserverbundwerkstoff hergestellten Träger 7, 9 durch einen Wickelprozess auf die von dem Wälzkörpern 4 fort weisende Seite der jeweiligen Laufbahnen 5, 6 aufgetragen worden. Es versteht sich, dass die Träger 7, 9 auch als vorgefertigte Formteile ausgebildet sein können, in die die Laufbahnen 5, 6 eingefügt werden, so dass sich eine form- bzw. reib- oder kraftschlüssige Verbindung zwischen dem jeweiligen Träger 7, 9 und der jeweiligen Laufbahn 5, 6 ausbildet.In the first embodiment described above, the carriers made of the fiber composite material were 7 . 9 by a winding process on the of the rolling elements 4 continuing side of the respective raceways 5 . 6 been applied. It is understood that the carrier 7 . 9 can also be designed as prefabricated moldings into which the raceways 5 . 6 be inserted so that a positive or frictional or non-positive connection between the respective carrier 7 . 9 and the respective career 5 . 6 formed.

Sofern der Träger 7, 9 als vorgefertigtes Formteil ausgebildet ist, versteht es sich ferner, dass der Träger aus einem Kunststoff, einer Keramik, einem Glas oder einem Metall, insbesondere einem Leichtmetall wie Titan oder Aluminium, oder einem metallischen Werkstoff auf Eisenbasis wie Grauguss hergestellt sein kann.Unless the carrier 7 . 9 is designed as a prefabricated molded part, it is further understood that the carrier may be made of a plastic, a ceramic, a glass or a metal, in particular a light metal such as titanium or aluminum, or an iron-based metallic material such as gray cast iron.

Ist der Träger insbesondere aus Kunststoff, Keramik oder Glas hergestellt, versteht es sich, dass der Träger durch eine Spritzprozess bzw. durch ein Abscheideverfahren, insbesondere ein naßchemisches Abscheideverfahren, auf die Laufbahn aufgetragen sein kann.is the carrier in particular made of plastic, ceramic or glass made, it is understood that the carrier by a Injection process or by a deposition method, in particular a Wet chemical deposition, applied to the track can be.

Bei dem vorstehend beschriebenen ersten Ausführungsbeispiel bestand der Träger 7, 9 jeweils ausschließlich aus dem Faserverbundwerkstoff. Es versteht sich, dass der Träger mehrere Komponenten umfassen kann, insbesondere kann der Träger selbst zwei oder mehrere aneinander befestigte Lagen umfassen. Es versteht sich weiter, dass dem Material des Trägers Zusätze wie Kohlenstoff-Nanoröhrchen beigesetzt sein können.In the first embodiment described above, the carrier was 7 . 9 in each case exclusively from the fiber composite material. It is understood that the carrier may comprise a plurality of components, in particular the carrier itself may comprise two or more mutually attached layers. It is further understood that additives such as carbon nanotubes may be added to the material of the carrier.

Bei dem im folgenden beschriebenen zweiten Ausführungsbeispiel (2) bezeichnen gleiche Bezugsziffern gleiche oder in ihrer technischen Funktion vergleichbare Elemente.In the second embodiment described below ( 2 ) denote like reference numerals the same or comparable in their technical function elements.

2 zeigt einen Längsschnitt durch ein Wälzlager 1, das einen ersten Lagerring 2, der als Außenring des Wälzlagers 1 ausgebildet ist, und einen zweiten Lagerring 3, der als Innenring des Wälzlagers 1 ausgebildet ist, umfasst. Das Wälzlager 1 umfasst weiter zylindrische Wälzkörper 4 aus einem keramischen Material. 2 shows a longitudinal section through a rolling bearing 1 that has a first bearing ring 2 , the outer ring of the rolling bearing 1 is formed, and a second bearing ring 3 , the inner ring of the rolling bearing 1 is formed comprises. The rolling bearing 1 further comprises cylindrical rolling elements 4 from a ceramic material.

Der erste Lagerring 2 umfasst eine Laufbahn 5, an deren zu dem Wälzkörper 4 weisenden Oberflächenabschnitt ein Wälzkontakt zu den Wälzkörpern 4 auftritt. Der erste Lagerring 2 umfasst weiter einen Träger 7. Das kreisringförmige Korpus der Laufbahn 5 ist an dem kreisringförmigen Korpus des Trägers 7 befestigt, nämlich mittels Aufschrumpfen des Trägers 7 auf das Korpus der Laufbahn 5. Die Dicke des Trägers 7 beträgt ca. zwei Drittel der Dicke des gesamten ersten Lagerrings 2, damit weist der Träger 7 eine relative Dicke von ca. 0,67 auf. Das kreisringförmige Korpus der Laufbahn 5 ist aus einem martensitisch härtbaren stickstofflegierten Stahl mit je mindestens 0,2% Kohlenstoff und Stickstoff sowie mindestens 13% Chrom ausgebildet. Das kreisringförmige Korpus des Trägers 7 ist aus Vergütungsstahl ausgebildet. Anstelle von Vergütungsstahl könnte des Korpus des Trägers 7 auch aus Einsatzstahl oder aus austenitischen Stahl ausgebildet sein.The first bearing ring 2 includes a career 5 , to whose to the rolling elements 4 pointing surface portion a rolling contact with the rolling elements 4 occurs. The first bearing ring 2 further comprises a carrier 7 , The circular body of the track 5 is on the annular body of the wearer 7 fastened, namely by shrinking the carrier 7 on the corpus of the career 5 , The thickness of the carrier 7 is about two thirds of the thickness of the entire first bearing ring 2 that's what the wearer points to 7 a relative thickness of about 0.67. The circular body of the track 5 is made of a martensitic hardenable nitrogen-alloyed steel with at least 0.2% carbon and nitrogen and at least 13% chromium. The circular body of the carrier 7 is made of tempered steel. Instead of tempered steel could be the body of the wearer 7 also be made of case hardened steel or austenitic steel.

Der zweite Lagerring 3 umfasst eine zweite Laufbahn 6, deren kreisringförmiges Korpus eine auf den Wälzkörper 4 weisende Oberfläche aufweist, an der der Wälzkontakt mit dem Wälzkörper 4 auftritt. Der zweite Lagerring 3 umfasst weiter einen zweiten Träger 9, dessen kreisringförmiges Korpus an dem Korpus der zweiten Laufbahn 6 befestigt ist. Das Korpus der zweiten Laufbahn 6 ist an dem zweiten Träger 9 mittels Aufschrumpfen befestigt. Die zweite Laufbahn 6 besteht aus einem martensitisch härtbaren stickstofflegierten Stahl mit je mindestens 0,2% Kohlenstoff und Stickstoff sowie mindestens 13% Chrom. Weiter besteht der zweite Träger 9 aus einem Einsatzstahl, alternativ zu dem Einsatzstahl aus einem Vergütungsstahl oder einem austenitischen Stahl. Die relative Dicke des zweiten Trägers 9, bezogen auf die Dicke des gesamten zweiten Lagerrings 3, beträgt ca. 0,67.The second bearing ring 3 includes a second career 6 , whose annular body one on the rolling elements 4 having facing surface on which the rolling contact with the rolling elements 4 occurs. The second bearing ring 3 further comprises a second carrier 9 , whose toroidal body on the body of the second career 6 is attached. The corpus of the second career 6 is on the second carrier 9 attached by shrinking. The second career 6 consists of a martensitic hardenable nitrogen-alloyed steel, each with at least 0.2% carbon and nitrogen, and at least 13% chromium. Next, there is the second carrier 9 made of case-hardened steel, alternatively to case-hardening steel made of tempered steel or austenitic steel. The relative thickness of the second carrier 9 , based on the thickness of the entire second bearing ring 3 , is about 0.67.

Das ist 2 schematisch dargestellte Wälzlager 1 weist einen Außendurchmesser von einigen Dezimetern auf, so dass das Wälzlager 1 die Abmessungen von typischen Bahnlagern aufweist. Das Wälzlager 1 könnte auch Abmessungen von ca. einem Meter oder einigen Metern aufweisen, so dass in diesem Fall das Wälzlager 1 die Abmessungen von typischen Lagern für beispielsweise Windkraftanlagen aufweist.This is 2 schematically illustrated bearings 1 has an outer diameter of a few decimeters, so that the rolling bearing 1 the Ab has measurements of typical railroad bearings. The rolling bearing 1 could also have dimensions of about one meter or a few meters, so in this case the rolling bearing 1 the dimensions of typical bearings for example, wind turbines has.

Das Lager 1 umfasst weiter noch eine Seitenscheibe 11, die die Stirnflächen der beiden Lagerringe 2, 3 überdeckt. Die Seitenscheibe 11 ist mittels Befestigungsschrauben 12 an dem Träger 7 des ersten Lagerrings 2 befestigt. Diesen Befestigungsschrauben 12 bietet der Einsatzstahl des Trägers 7 einen sicheren Halt.The warehouse 1 also includes a side window 11 covering the end faces of the two bearing rings 2 . 3 covered. The side window 11 is by means of fastening screws 12 on the carrier 7 of the first bearing ring 2 attached. These fixing screws 12 offers the case-hardening steel of the carrier 7 a secure hold.

Die Erfindung wurde vorstehend anhand eines zweiten Ausführungsbeispiels beschrieben, bei dem die relative Dicke des Trägers 7 bzw. 9 ca. 0,67 betrug, so dass der Träger 7, 9 dicker als die Laufbahn 5, 6 ist. Von der Erfindung mit umfasst soll der Fall sein, dass der Träger 7, 9 eine geringere Dicke als die Laufbahn 5, 6 aufweist, eingeschlossen den Fall, dass der Träger 7, 9 eine relative Dicke von weniger als ca. 0,44 aufweist.The invention has been described above with reference to a second embodiment in which the relative thickness of the carrier 7 respectively. 9 about 0.67, so the carrier 7 . 9 thicker than the track 5 . 6 is. To be covered by the invention is to be the case that the carrier 7 . 9 a smaller thickness than the raceway 5 . 6 includes, including the case that the carrier 7 . 9 has a relative thickness of less than about 0.44.

Die Erfindung wurde vorstehend anhand eines zweiten Ausführungsbeispiels beschrieben, bei dem das Korpus der Laufbahn 5, 6 aus einem martensitisch härtbaren stickstofflegierten Stahl mit je mindestens 0,2% Kohlenstoff und Stickstoff sowie mindestens 13% Chrom ausgebildet war. Es versteht sich, dass das Korpus der Laufbahn 5, 6 aus einem anderen aufgestickten, martensitischen Kaltarbeitsstahl bestehen kann.The invention has been described above with reference to a second embodiment in which the body of the track 5 . 6 was formed from a martensitic hardenable nitrogen-alloyed steel, each with at least 0.2% carbon and nitrogen and at least 13% chromium. It is understood that the corpus of the career 5 . 6 may consist of another embossed, martensitic cold work steel.

Bei dem vorstehend beschriebenen zweiten Ausführungsbeispiel war das Korpus der Laufbahn 5, 6 aus einem martensitisch härtbaren stickstofflegierten Stahl mit je mindestens 0,2% Kohlenstoff und Stickstoff sowie mindestens 13% Chrom ausgebildet. Alternativ hierzu kann vorgesehen sein, dass das Korpus der Laufbahn 5, 6 aus einem Schnellarbeitsstahl, insbesondere einem pulvermetallurgisch hergestellten Schnellarbeitsstahl, hergestellt ist.In the second embodiment described above, the body was the raceway 5 . 6 formed from a martensitic hardenable nitrogen-alloyed steel, each with at least 0.2% carbon and nitrogen and at least 13% chromium. Alternatively, it may be provided that the body of the raceway 5 . 6 is made of a high-speed steel, in particular a high-speed steel produced by powder metallurgy.

BezugszeichenlisteLIST OF REFERENCE NUMBERS

11: Wälzlagerroller bearing
22: Außenringouter ring
33: Innenringinner ring
44: Wälzkörperrolling elements
55: erste Laufbahnfirst career
66: zweite Laufbahnsecond career
77: Trägercarrier
88th: Kontaktflächecontact area
99: zweiter Trägersecond carrier
1010: zweite Kontaktflächesecond contact area
1111: Seitenscheibeside window
1212: Befestigungsschraubenmounting screws

ZITATE ENTHALTEN IN DER BESCHREIBUNGQUOTES INCLUDE IN THE DESCRIPTION

Diese Liste der vom Anmelder aufgeführten Dokumente wurde automatisiert erzeugt und ist ausschließlich zur besseren Information des Lesers aufgenommen. Die Liste ist nicht Bestandteil der deutschen Patent- bzw. Gebrauchsmusteranmeldung. Das DPMA übernimmt keinerlei Haftung für etwaige Fehler oder Auslassungen.This list The documents listed by the applicant have been automated generated and is solely for better information recorded by the reader. The list is not part of the German Patent or utility model application. The DPMA takes over no liability for any errors or omissions.

Zitierte PatentliteraturCited patent literature

- US 5866647 A [0004] US 5866647 A [0004]
- DE 10124534 A1 [0005] - DE 10124534 A1 [0005]
- DE 20200241 U1 [0006] - DE 20200241 U1 [0006]
- DE 102007062145 A1 [0007] DE 102007062145 A1 [0007]

Claims

Lagerring für ein Wälzlager (1), umfassend eine durchgehend umlaufende Laufbahn (5, 6), in deren Bereich ein Wälzkontakt stattfindet, wobei das Material im Bereich der Laufbahn ein für Wälzanwendungen geeigneter Stahl, insbesondere ein Wälzlagerstahl, ist, und einen Träger (7, 9) aus einem von dem Material der Laufbahn (5, 6) abweichenden Material, wobei die Laufbahn (5, 6) an dem Träger (7, 9) befestigt ist, dadurch gekennzeichnet, dass der Träger (7, 9) eine relative Wandstärke, bezogen auf die Wandstärke des gesamten Korpus des Lagerrings (2, 3), von mindestens ca. 0,44, insbesondere mindestens ca. 0,55, aufweist, dass das Material des Trägers (7, 9) eine Druckfestigkeit von mindestens ca. 480 MPa, insbesondere mindestens ca. 600 MPa, aufweist, und dass das Material des Trägers (7, 9) ein Elastizitätsmodul von mindestens ca. 40 GPa, insbesondere mindestens ca. 50 GPa, aufweist.Bearing ring for a rolling bearing ( 1 ), comprising a continuous circulating track ( 5 . 6 ), in the region of which a rolling contact takes place, wherein the material in the region of the track is suitable for rolling applications steel, in particular a rolling bearing steel, and a carrier ( 7 . 9 ) from one of the material of the track ( 5 . 6 ) different material, the track ( 5 . 6 ) on the carrier ( 7 . 9 ), characterized in that the carrier ( 7 . 9 ) a relative wall thickness, based on the wall thickness of the entire body of the bearing ring ( 2 . 3 ), of at least about 0.44, in particular at least about 0.55, that the material of the carrier ( 7 . 9 ) has a compressive strength of at least about 480 MPa, in particular at least about 600 MPa, and that the material of the carrier ( 7 . 9 ) has a modulus of elasticity of at least about 40 GPa, in particular at least about 50 GPa.

Lagerring nach Anspruch 1, dadurch gekennzeichnet, dass die Dichte des Materials des Trägers (7, 9) deutlich geringer ist als die Dichte des Materials der Laufbahn (2, 3), insbesondere, dass das Material des Trägers (7, 9) einen Kunststoff, eine Keramik, ein Leichtmetall, speziell Aluminium oder Titan, oder ein Faserverbundwerkstoff, speziell ein Kohlenstofffaser-, ein Keramikfaser- oder ein Glasfaserverstärkter Kunststoff, umfassen.Bearing ring according to claim 1, characterized in that the density of the material of the carrier ( 7 . 9 ) is significantly less than the density of the material of the track ( 2 . 3 ), in particular, that the material of the carrier ( 7 . 9 ) comprise a plastic, a ceramic, a light metal, especially aluminum or titanium, or a fiber composite material, especially a carbon fiber, a ceramic fiber or a glass fiber reinforced plastic.

Lagerring nach Anspruch 1 oder 2, dadurch gekennzeichnet, dass das Material des Trägers (7, 9) einen Eisenwerkstoff umfasst, insbesondere ein Grauguss.Bearing ring according to claim 1 or 2, characterized in that the material of the carrier ( 7 . 9 ) comprises an iron material, in particular a gray cast iron.

Lagerring nach Anspruch 1 oder 2, dadurch gekennzeichnet, dass das Material des Trägers (7, 9) einen Vergütungsstahl, einen Einsatzstahl oder einen austenitischen Stahl umfasst.Bearing ring according to claim 1 or 2, characterized in that the material of the carrier ( 7 . 9 ) comprises a tempered steel, a case hardening steel or an austenitic steel.

Lagerring nach Anspruch 1 oder 2, dadurch gekennzeichnet, dass das Material des Trägers (7, 9) ein Glas, insbesondere ein technisches Glas wie ein Bor-Silikat-Glas oder Quarzglas, umfasst.Bearing ring according to claim 1 or 2, characterized in that the material of the carrier ( 7 . 9 ) comprises a glass, in particular a technical glass such as borosilicate glass or quartz glass.

Lagerring nach einem der Ansprüche 1 bis 5, dadurch gekennzeichnet, dass das Material des Trägers (7, 9) Kohlenstoff in Form von Nanoröhrchen umfasst.Bearing ring according to one of claims 1 to 5, characterized in that the material of the carrier ( 7 . 9 ) Comprises carbon in the form of nanotubes.

Lagerring nach einem der Ansprüche 1 bis 6, dadurch gekennzeichnet, dass der Lagerring (2, 3) für ein Großwälzlager vorgesehen ist, insbesondere, dass der Lagerring (2, 3) einen Durchmesser von mehr als ca. 1000 Millimetern aufweist.Bearing ring according to one of claims 1 to 6, characterized in that the bearing ring ( 2 . 3 ) is provided for a slewing bearing, in particular that the bearing ring ( 2 . 3 ) has a diameter of more than about 1000 millimeters.

Lagerring nach einem der Ansprüche 1 bis 7, dadurch gekennzeichnet, dass der Träger und das Korpus der Laufbahn reib- oder kraftschlüssig, insbesondere mittels Aufschrumpfen, aneinander befestigt sind.Bearing ring according to one of claims 1 to 7, characterized in that the carrier and the body friction or frictionally, especially by means of the career Shrink, attached to each other.

Lagerring nach einem der Ansprüche 1 bis 8, dadurch gekennzeichnet, dass das Korpus der Laufbahn (2, 3) als Kreisring ausgebildet ist, wobei entlang des Umfangs des Kreisrings eine durchgehende Kontaktfläche (8, 10) zu dem Träger (7, 9) ausgebildet ist, insbesondere derart, dass zwischen dem Träger (7, 9) und dem Korpus der Laufbahn (5, 6) kein Hohlraum ausgebildet ist.Bearing ring according to one of claims 1 to 8, characterized in that the body of the track ( 2 . 3 ) is formed as a circular ring, wherein along the circumference of the circular ring a continuous contact surface ( 8th . 10 ) to the carrier ( 7 . 9 ), in particular such that between the carrier ( 7 . 9 ) and the corpus of the career ( 5 . 6 ) no cavity is formed.

Lagerring nach einem der Ansprüche 1 bis 9, dadurch gekennzeichnet, dass das Material der Laufbahn (5, 6) einen aufgestickten, martensitischen Kaltarbeitsstahl, insbesondere einen martensitisch härtbaren stickstofflegierten Stahl mit je mindestens 0,2% Kohlenstoff und Stickstoff sowie mindestens 13% Chrom, oder einen Schnellarbeitsstahl, insbesondere einem pulvermetallurgisch hergestellten Schnellarbeitsstahl umfasst.Bearing ring according to one of claims 1 to 9, characterized in that the material of the track ( 5 . 6 ) comprises an embroidered, martensitic cold work steel, in particular a martensitic hardenable nitrogen-alloyed steel, each with at least 0.2% carbon and nitrogen and at least 13% chromium, or a high-speed steel, in particular a high-speed steel produced by powder metallurgy.

Lagerring, umfassend eine Laufbahn (5, 6) mit einem Korpus aus einem aufgestickten, martensitischen Kaltarbeitsstahl, insbesondere aus einem martensitisch härtbaren stickstofflegierten Stahl mit je mindestens 0,2% Kohlenstoff und Stickstoff sowie mindestens 13% Chrom, oder einem Schnellarbeitsstahl, insbesondere einem pulvermetallurgisch hergestellten Schnellarbeitsstahl, einen Träger (7, 9) aus einem Vergütungsstahl, einem Einsatzstahl oder einem austenitischen Stahl, wobei das Korpus der Laufbahn (5, 6) an dem Träger (7, 9) befestigt ist.Bearing ring comprising a raceway ( 5 . 6 ) comprising a body of an embossed martensitic cold work steel, in particular of a martensitic hardenable nitrogen-alloyed steel each having at least 0.2% carbon and nitrogen and at least 13% chromium, or a high-speed steel, in particular a high-speed steel produced by powder metallurgy, a support ( 7 . 9 ) of a tempered steel, case-hardening steel or austenitic steel, the body of the track ( 5 . 6 ) on the carrier ( 7 . 9 ) is attached.

Wälzlager, umfassend einen Lagerring (2, 3) nach einem der Ansprüche 1 bis 11.Rolling bearing comprising a bearing ring ( 2 . 3 ) according to one of claims 1 to 11.

Wälzlager nach Anspruch 12, dadurch gekennzeichnet, dass beide Lagerringe (2, 3) nach einem der Ansprüche 1 bis 8 ausgebildet sind, und dass die Träger (7, 9) beider Lagerringe (2, 3) aus dem gleichen Material bestehen.Rolling bearing according to claim 12, characterized in that both bearing rings ( 2 . 3 ) are formed according to one of claims 1 to 8, and that the carrier ( 7 . 9 ) of both bearing rings ( 2 . 3 ) consist of the same material.

Wälzlager nach einem der Ansprüche 12 oder 13, weiter umfassend Wälzkörper (4) aus einem keramischen Material.Rolling bearing according to one of claims 12 or 13, further comprising rolling elements ( 4 ) made of a ceramic material.