CN1974055A - Sae6427钢锻造加热工艺 - Google Patents

Sae6427钢锻造加热工艺 Download PDF

Info

Publication number
CN1974055A
CN1974055A CN 200610134609 CN200610134609A CN1974055A CN 1974055 A CN1974055 A CN 1974055A CN 200610134609 CN200610134609 CN 200610134609 CN 200610134609 A CN200610134609 A CN 200610134609A CN 1974055 A CN1974055 A CN 1974055A
Authority
CN
China
Prior art keywords
forging
sae6427
heating
heating process
temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200610134609
Other languages
English (en)
Other versions
CN100431736C (zh
Inventor
陈鉴
董绍国
孙春国
徐艳君
王雷
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JINGANG FORGE Co.,Ltd.
Original Assignee
JINGANG LARGE FORGE TENGAO SPECIAL ZONE ANSHAN
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JINGANG LARGE FORGE TENGAO SPECIAL ZONE ANSHAN filed Critical JINGANG LARGE FORGE TENGAO SPECIAL ZONE ANSHAN
Priority to CNB2006101346093A priority Critical patent/CN100431736C/zh
Publication of CN1974055A publication Critical patent/CN1974055A/zh
Application granted granted Critical
Publication of CN100431736C publication Critical patent/CN100431736C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及高合金的锻造加热技术SAE6427钢锻造加热工艺，该工艺包括如下步骤：1)毛坯装炉温度在550℃－600℃；2)在850℃之前缓慢加热，在850℃是进行120－180分钟的保温；3)在 850℃后快速加热至顶温1180℃，顶温下进行180－240分钟的保温；4)始锻温度在1150℃左右；大量变形在1000℃以上进行，锻造时要快速翻转，多次倒棱，送进量要小而勤。本发明的有益效果是：采用SAE6427钢作为连铸辊道辊的母材，可提高辊道辊使用寿命2倍以上；本发明可使SAE6427钢锻造连铸辊道辊的成品率由30％提高到80％以上。

Description

SAE6427钢锻造加热工艺
                          技术领域
本发明涉及高合金的锻造加热技术，特别是SAE6427钢的锻造加热技术。
                          背景技术
连铸辊道辊是连铸设备主要的耐热工作部件，质量的优劣直接影响连铸设备的工作效率，目前，国内广泛使用的连铸辊道辊不仅耐热性能差、易损坏，同时影响连铸设备的连续生产，根本原因是辊道辊的母材性能差，在高温、高承载的情况下容易产生断裂。采用SAE6427钢作为连铸辊道辊的母材，可以提高辊道辊使用寿命2倍以上，但其锻造成品率仅有30％左右。这严重制约了SAE6427钢应用于连铸辊道辊的推广。
                          发明内容
本发明的目的是提供一种SAE6427钢锻造加热工艺，该工艺通过改变传统工艺参数，可使SAE6427钢锻造连铸辊道辊的成品率由30％提高到80％以上。
为实现上述目的，本发明通过以下技术方案实现：
SAE6427钢锻造加热工艺，其特征在于该工艺包括如下步骤：
1)毛坯装炉温度在550℃-600℃；
2)在850℃之前缓慢加热，在850℃是进行120-180分钟的保温；
3)在850℃后快速加热至顶温1180℃，顶温下进行180-240分钟的保温；
4)始锻温度在1150℃左右；大量变形在1000℃以上进行，锻造时要快速翻转，多次倒棱，送进量要小而勤。
所述的步骤2)中，在850℃之前缓慢加热，加热时间要在180-240小时分钟之间。
本发明与现有技术相比的有益效果是：采用SAE6427钢作为连铸辊道辊的母材，可提高辊道辊使用寿命2倍以上；本发明可使SAE6427钢锻造连铸辊道辊的成品率由30％提高到80％以上。
                        附图说明
图1是SAE6427钢锻造加热工艺的加热曲线图。
                         具体实施方式
本发明SAE6427钢锻造加热工艺包括如下步骤：
1)毛坯装炉温度在550℃-600℃；
2)在850℃之前缓慢加热，加热时间要在180-240小时分钟之间；在850℃是进行120-180分钟的保温；
3)在850℃后快速加热至顶温1180℃，顶温下进行180-240分钟的保温；
4)始锻温度在1150℃左右；大量变形在1000℃以上进行，锻造时要快速翻转，多次倒棱，送进量要小而勤。

Claims (2)

1、SAE6427钢锻造加热工艺，其特征在于该工艺包括如下步骤：
1)毛坯装炉温度在550℃-600℃；
2)在850℃之前缓慢加热，在850℃是进行120-180分钟的保温；
3)在850℃后快速加热至顶温1180℃，顶温下进行180-240分钟的保温；
4)始锻温度在1150℃左右；大量变形在1000℃以上进行，锻造时要快速翻转，多次倒棱，送进量要小而勤。
2、根据权利要求1所述的SAE6427钢锻造加热工艺，其特征在于在850℃之前缓慢加热，加热时间要在180-240小时分钟之间。
CNB2006101346093A 2006-12-08 2006-12-08 Sae6427钢锻造加热工艺 Expired - Fee Related CN100431736C (zh)