CN1927968A - 基于有机硅丙烯酸环氧酯水分散体的水性工业涂料及其制备方法 - Google Patents
基于有机硅丙烯酸环氧酯水分散体的水性工业涂料及其制备方法 Download PDFInfo
- Publication number
- CN1927968A CN1927968A CN 200610037496 CN200610037496A CN1927968A CN 1927968 A CN1927968 A CN 1927968A CN 200610037496 CN200610037496 CN 200610037496 CN 200610037496 A CN200610037496 A CN 200610037496A CN 1927968 A CN1927968 A CN 1927968A
- Authority
- CN
- China
- Prior art keywords
- water dispersion
- epoxide acrylate
- consumption
- acrylate water
- organosilicon epoxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
项目 | 指标值 | |
储存期(年)> | 1 | |
固体分(%)≥ | 55 | |
25℃干燥时间 | 表干(h)≤ | 2 |
实干(h)≤ | 12 | |
有机挥发物含量(VOC,g/L)≤ | 60 | |
耐老化试验时间(h)≥ | 1000 | |
耐盐雾试验时间(h)≥ | 800 | |
吸水率(%)≤ | 2.5 | |
附着力(级)不小于 | 1 | |
耐冲击性kg·cm | 50 | |
摆杆硬度≥ | 0.60 |
组分 | 投料量(公斤) |
有机硅丙烯酸环氧酯水分散体 | 450 |
氧化铁红 | 140 |
三聚磷酸铝 | 50 |
WD-D-500型复合铁钛防锈颜料 | 30 |
滑石粉 | 100 |
硫酸钡 | 60 |
BYK-P104 | 4 |
Tego Wet KL 245 | 2.5 |
RW-8 | 3 |
异锌酸钴 | 15 |
Acticide MKA | 2 |
Acticide THP | 3 |
BYK-022 | 0.8 |
2-氨基-2-甲基-1-丙醇 | 2.5 |
去离子水 | 137.2 |
合计(公斤) | 1000 |
项目 | 指标值 | |
储存期 | 1.5年无变化 | |
固体分,(%) | 57.3 | |
25℃干燥时间 | 表干(h) | 1.5 |
实干(h) | 10 | |
有机挥发物含量(VOC,g/L) | 47 | |
耐老化试验 | 1100小时无异常 | |
耐盐雾试验 | 850小时无异常 | |
吸水率(%) | 1.8 | |
附着力(级) | 1 | |
耐冲击性kg·cm | 50 | |
摆杆硬度 | 0.63 |
组分 | 投料量(公斤) |
有机硅丙烯酸环氧酯水分散体 | 500 |
氧化铁红 | 150 |
三聚磷酸铝 | 40 |
WD-D-500型复合铁钛防锈颜料 | 40 |
滑石粉 | 80 |
硫酸钡 | 50 |
BYK-P104 | 2 |
Tego Wet KL 245 | 1.5 |
RW-8 | 4 |
异锌酸钴 | 20 |
Acticide MKA | 3 |
Acticide THP | 2 |
BYK-022 | 0.6 |
2-氨基-2-甲基-1-丙醇 | 2 |
去离子水 | 104.9 |
合计(公斤) | 1000 |
项目 | 指标值 | |
储存期 | 1.5年无变化 | |
固体分,(%) | 59.6 | |
25℃干燥时间 | 表干(h) | 1.2 |
实干(h) | 11 | |
有机挥发物含量(VOC,g/L) | 51 | |
耐老化试验 | 1050小时无异常 | |
耐盐雾试验 | 900小时无异常 | |
吸水率(%) | 2.0 | |
附着力(级) | 1 | |
耐冲击性kg·cm | 50 | |
摆杆硬度 | 0.65 |
组分 | 投料量(公斤) |
有机硅丙烯酸环氧酯水分散体 | 550 |
氧化铁红 | 110 |
三聚磷酸铝 | 60 |
WD-D-500型复合铁钛防锈颜料 | 50 |
滑石粉 | 70 |
硫酸钡 | 70 |
BYK-P104 | 3 |
Tego Wet KL 245 | 2 |
RW-8 | 5 |
异锌酸钴 | 25 |
Acticide MKA | 3 |
Acticide THP | 3 |
BYK-022 | 0.7 |
2-氨基-2-甲基-1-丙醇 | 2.4 |
去离子水 | 45.9 |
合计(公斤) | 1000 |
项目 | 指标值 | |
储存期 | 1.5年无变化 | |
固体分,(%) | 61.2 | |
25℃干燥时间 | 表干(h) | 1.6 |
实干(h) | 10 | |
有机挥发物含量(VOC,g/L) | 53 | |
耐老化试验 | 1200小时无异常 |
耐盐雾试验 | 850小时无异常 |
吸水率(%) | 1.6 |
附着力(级) | 1 |
耐冲击性kg·cm | 50 |
摆杆硬度 | 0.67 |
组分 | 投料量(公斤) |
有机硅丙烯酸环氧酯水分散体 | 500 |
云母氧化铁红 | 160 |
磷酸锌 | 40 |
WD-D-800型复合铁钛防锈颜料 | 30 |
绢云母粉 | 60 |
石英粉 | 80 |
Henkel 5040 | 3 |
BYK346 | 2 |
COATEX BR125P | 3.5 |
环烷酸锰 | 18 |
M-8 | 2 |
LXE | 3 |
SN313 | 0.8 |
2-氨基-2-甲基-1-丙醇 | 2.8 |
去离子水 | 94.9 |
合计(公斤) | 1000 |
项目 | 指标值 | |
储存期 | 1.5年无变化 | |
固体分,(%) | 59.1 | |
25℃干燥时间 | 表干(h) | 1.5 |
实干(h) | 12 | |
有机挥发物含量(VOC,g/L) | 54 | |
耐老化试验 | 1200小时无异常 | |
耐盐雾试验 | 800小时无异常 | |
吸水率(%) | 1.4 | |
附着力(级) | 1 | |
耐冲击性kg·cm | 50 | |
摆杆硬度 | 0.64 |
Claims (11)