CN1900200A - 喷胶及其制作工艺 - Google Patents
喷胶及其制作工艺 Download PDFInfo
- Publication number
- CN1900200A CN1900200A CN 200510035847 CN200510035847A CN1900200A CN 1900200 A CN1900200 A CN 1900200A CN 200510035847 CN200510035847 CN 200510035847 CN 200510035847 A CN200510035847 A CN 200510035847A CN 1900200 A CN1900200 A CN 1900200A
- Authority
- CN
- China
- Prior art keywords
- spray glue
- organic solvent
- grams
- thermoplastic elastomer
- rosin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种喷胶,按重量百分比计该喷胶含有:热塑性弹性体SBS 5-20%、有机溶剂10-30%、6号抽提溶剂油10-55%、801树脂2-15%、松香10-40%。其制作工艺为:a、将有机溶剂和6号抽提溶剂油总量的一半加入反应釜,启动反应釜电机;b、分别将热塑性弹性体SBS和801树脂加入反应釜,搅拌3-4小时;c、加入松香和剩余的6号抽提溶剂油,再搅拌3-4小时。本发明无污染、对人体无害,且胶粘能力强、不易开胶、不易老化、耐高温、耐寒。本发明的喷胶主要用于沙发、转椅、屏风、箱包、保温材料等行业。
Description
【技术领域】
本发明涉及一种粘合剂,尤其是涉及一种喷胶及其制作工艺。
【背景技术】
目前市场上出现的热塑性弹性体SBS溶剂型喷胶,都不同比例的含有三苯(苯、甲苯、二甲苯)及卤代氢类剧毒、高毒性溶剂,三苯属致癌物质,卤代氢类能影响人体新陈代谢及造成肝脏中毒,无论是长时间接触或短时问接触,都会不同程度地造成人体的急、慢性中毒,同时给周围环境造成严重的污染。并且胶粘能力低、易开胶、易老化、不耐高温、不耐寒。
【发明内容】
本发明所要解决的技术问题在于提供一种喷胶其制作工艺,无污染、对人体无害,且胶粘能力强、不易开胶、不易老化、耐高温、耐寒。
为解决上述技术问题,本发明所采用的技术方案是:一种喷胶,其特征在于:按重量百分比计该喷胶含有:热塑性弹性体SBS 5-20%、有机溶剂10-30%、6号抽提溶剂油10-55%、801树脂2-15%、松香10-40%。
上述技术方案的进一步改进在于:
所述的热塑性弹性体SBS为411号。
所述的有机溶剂为二氯甲烷。
所述的有机溶剂为三氯乙烯。
所述的有机溶剂为丙酮。
所述的有机溶剂为二氯甲烷、三氯乙烯、丙酮的混合物。
该喷胶的重量配比中还包括氢化松香2-5%。
该喷胶的重量配比中还包括异丙醇1-3%。
该喷胶的重量配比中还包括松香树脂1-5%。
一种上述喷胶的工艺方法,包括如下步骤:
a、将有机溶剂和6号抽提溶剂油总量的一半加入反映釜,启动反映釜电机;
b、分别将热塑性弹性体SBS和801树脂加入反映釜,搅拌3-4小时;
c、加入松香和剩余的6号抽提溶剂油,再搅拌3-4小时。
本发明的有益效果是:本发明的喷胶无污染、对人体无害,且胶粘能力强、干燥快,可以耐高低、气味小、喷涂均匀、初粘能力强、粘力持久、耐老化、固含量高,比普通同类产品用量节约10-30%,正确使用对人体无害。
【具体实施方式】
下面结合具体实施方式对本发明做进一步描述:
实施例一:配制3630克喷胶,组分及重量配比为:
411号热塑性弹性体SBS 280克;
二氯甲烷350克;
三氯乙烯50克;
丙酮50克;
6号抽提溶剂油1900克;
801树脂150克;
松香850克。
其中二氯甲烷、三氯乙烯、丙酮为有机溶剂,可以使用其中的一种、两种或者三种,有机溶剂总量达到450克即可。
工艺方法为:
a、将有机溶剂(二氯甲烷、三氯乙烯、丙酮)和6号抽提溶剂油总量的一半即950克加入反映釜,启动反映釜电机;
b、分别将热塑性弹性体SBS 280克和801树脂150克加入反映釜,搅拌3-4小时;
c、加入松香850克和剩余的6号抽提溶剂油950克,再搅拌3-4小时。
实施例二:配制3770克喷胶,组分及重量配比为:
411号热塑性弹性体SBS 260克;
二氯甲烷540克;
三氯乙烯60克;
丙酮50克;
6号抽提溶剂油1740克;
801树脂70克;
松香870克;
氢化松香130克;
异丙醇50克。
其中二氯甲烷、三氯乙烯、丙酮为有机溶剂,可以使用其中的一种、两种或者三种,有机溶剂总量达到650克即可。
工艺方法为:
a、将有机溶剂(二氯甲烷、三氯乙烯、丙酮)和6号抽提溶剂油总量的一半即870克加入反映釜,启动反映釜电机;
b、分别将热塑性弹性体SBS 260克和801树脂70克加入反映釜,搅拌3-4小时;
c、加入松香870克和剩余的6号抽提溶剂油870克,加入氢化松香130克、异丙醇50克,再搅拌3-4小时。
本实施例根据不同季节需要加入了氢化松香和异丙醇,可以在10月至3月份使用。
实施例三:配制3680克喷胶,组分及重量配比为:
411号热塑性弹性体SBS 260克;
二氯甲烷300克;
三氯乙烯50克;
丙酮50克;
6号抽提溶剂油1950克;
801树脂100克;
松香870克;
松香树脂100克。
其中二氯甲烷、三氯乙烯、丙酮为有机溶剂,可以使用其中的一种、两种或者三种,有机溶剂总量达到400克即可。
工艺方法为:
a、将有机溶剂(二氯甲烷、三氯乙烯、丙酮)和6号抽提溶剂油总量的一半即975克加入反映釜,启动反映釜电机;
b、分别将热塑性弹性体SBS 260克和801树脂100克加入反映釜,搅拌3-4小时;
c、加入松香870克和剩余的6号抽提溶剂油975克,再加入松香树脂100克,再搅拌3-4小时。
本实施例根据不同季节需要加入了松香树脂,可以在4月至6月份使用。
Claims (10)
1、一种喷胶,其特征在于:按重量百分比计该喷胶含有:热塑性弹性体SBS 5-20%、有机溶剂10-30%、6号抽提溶剂油10-55%、801树脂2-15%、松香10-40%。
2、如权利要求1所述的喷胶,其特征在于:所述的热塑性弹性体SBS为411号。
3、如权利要求1所述的喷胶,其特征在于:所述的有机溶剂为二氯甲烷。
4、如权利要求1所述的喷胶,其特征在于:所述的有机溶剂为三氯乙烯。
5、如权利要求1所述的喷胶,其特征在于:所述的有机溶剂为丙酮。
6、如权利要求1所述的喷胶,其特征在于:所述的有机溶剂为二氯甲烷、三氯乙烯、丙酮的混合物。
7、如权利要求1所述的喷胶,其特征在于:该喷胶的重量配比中还包括氢化松香2-5%。
8、如权利要求1所述的喷胶,其特征在于:该喷胶的重量配比中还包括异丙醇1-3%。
9、如权利要求1所述的喷胶,其特征在于:该喷胶的重量配比中还包括松香树脂1-5%。
10、一种如权利要求1所述的喷胶的工艺方法,其特征在于:该方法包括如下步骤:
a、将有机溶剂和6号抽提溶剂油总量的一半加入反映釜,启动反映釜电机;
b、分别将热塑性弹性体SBS和801树脂加入反映釜,搅拌3-4小时;
C、加入松香和剩余的6号抽提溶剂油,再搅拌3-4小时。