CN1715460A - α－MnO2单晶纳米棒的制备方法 - Google Patents

α－MnO2单晶纳米棒的制备方法 Download PDF

Info

Publication number
CN1715460A
CN1715460A CN 200410020888 CN200410020888A CN1715460A CN 1715460 A CN1715460 A CN 1715460A CN 200410020888 CN200410020888 CN 200410020888 CN 200410020888 A CN200410020888 A CN 200410020888A CN 1715460 A CN1715460 A CN 1715460A
Authority
CN
China
Prior art keywords
manganese dioxide
mno
sulfuric acid
potassium permanganate
single crystal
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200410020888
Other languages
English (en)
Other versions
CN1312330C (zh
Inventor
成会明
陈永
刘畅
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Institute of Metal Research of CAS
Original Assignee
Institute of Metal Research of CAS
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Institute of Metal Research of CAS filed Critical Institute of Metal Research of CAS
Priority to CNB2004100208881A priority Critical patent/CN1312330C/zh
Publication of CN1715460A publication Critical patent/CN1715460A/zh
Application granted granted Critical
Publication of CN1312330C publication Critical patent/CN1312330C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及二氧化锰纳米棒的制备技术，具体地说是一种小直径α－MnO2单晶纳米棒的制备方法。采用硫酸溶液中加入高锰酸钾，在加热的条件下使硫酸和高锰酸钾反应，反应温度为70－95℃。二氧化锰纳米棒的直径可通过调节硫酸溶液的浓度，高锰酸钾的加入量和温度等工艺参数得到控制。本发明具有所需要的化学药品种类少，工艺简单、操作方便易于控制，不需要昂贵的设备。二氧化锰是单晶α－MnO2；二氧化锰纳米棒的直径小，长度短且比较均匀，比表面积高。本发明所制备的产品具有广阔的应用前景，可用于催化剂，离子筛、锌锰电池和锂离子电池中的电极材料等。

Description

α-MnO2单晶纳米棒的制备方法
技术领域
本发明涉及二氧化锰纳米棒的制备技术，具体地说是一种小直径α-MnO2单晶纳米棒的制备方法。
背景技术
由于纳米材料本身所具有的量子尺寸效应，表面效应及量子隧道效应等，在电、磁、声、光、传感和催化等方面都展现出许多常规材料所不具备的特殊的性质。因此，受到人们的广泛的关注。
氧化锰由于具有离子交换、分子吸附、催化、电化学和磁学等优良特性，被广泛的应用于催化剂，分子筛和超级电容器。此外，它具有成本低，能量适中，环境友好的特性，作为Li/MnO2电池中的电极材料。而且，二氧化锰价格低廉，资源丰富，具有很大的应用前景和价值。
氧化锰的特性不仅和锰的价态有关，还取决于二氧化锰的形态结构。因此，科研人员用不同的方法制备了不同形态的二氧化锰纳米结构。如：MnO2纳米颗粒，α-、β-、γ-、δ-MnO2纳米线和纳米棒。
发明内容
本发明的目的是提供一种操作相对简单的制备α-MnO2单晶纳米棒的方法，工艺简单，不需要复杂而昂贵的设备，反应易于控制。所制备的α-MnO2单晶纳米棒的直径较小，可达到4nm。
为了实现上述目的，本发明的技术方案是：采用硫酸溶液中加入高锰酸钾，在加热的条件下使硫酸和高锰酸钾反应，待反应结束后，自然冷却，而后，加入去离子水冲洗干净并干燥。其中：硫酸溶液的浓度为0.1mol/l到3mol/l；反应温度为70-95℃。二氧化锰纳米棒的直径可通过调节硫酸溶液的浓度、高锰酸钾的加入量和温度等工艺参数得到控制。
本发明高锰酸钾加入量较佳为每100毫升的硫酸溶液加入高锰酸钾0.5～4g。本发明硫酸溶液的浓度较佳为1～3M。
与其它方法制备二氧化锰纳米棒相比，本发明更具有如下有益效果：
1、工艺简单。本发明采用仅在硫酸溶液中加入高锰酸钾，再在加热的条件下制备出直径较小且均匀α-MnO2单晶纳米棒，所需要的化学药品种类少，反应简单易于控制，不需要昂贵的设备，操作方便、工艺简单。
2、二氧化锰纳米棒的直径小，长度短且比较均匀。二氧化锰纳米棒的直径范围为：5-20nm，长度范围为：80-300nm。
3、纳米棒比表面积高达165.8m2/g。
4、二氧化锰纳米棒是α-MnO2单晶。
5、具有广阔的应用前景。本发明可用于催化剂，离子筛、锌锰电池和锂离子电池中的电极材料等。
附图说明
图1a为本发明一个实施例1的二氧化锰纳米棒的透射电镜照片。
图1b为本发明一个实施例1的二氧化锰纳米棒[110]面的高分辨电镜照片。
图1c为本发明一个实施例1的二氧化锰纳米棒的X光衍射图谱(XRD)。
图1d为本发明一个实施例1的二氧化锰纳米棒的电子能量损失谱(EDS)。
图2为本发明实施例2二氧化锰纳米棒的透射电镜照片。
图3a为本发明实施例3二氧化锰纳米棒的扫描电镜照片。
图3b为本发明实施例3二氧化锰纳米棒的高倍扫描电镜照片。
图3c为本发明实施例3二氧化锰纳米棒的透射电镜照片。
图3d为本发明实施例3二氧化锰纳米棒的吸附等温线。
具体实施方式
实施例1
采用硫酸溶液中加入高锰酸钾，硫酸溶液的浓度为3mol/l；每100毫升的硫酸溶液加入高锰酸钾2g；在加热的条件下使硫酸和高锰酸钾反应，反应温度为70℃。待反应结束后，自然冷却，而后，加入去离子水洗干净并干燥。二氧化锰纳米棒的直径约为20nm，长度范围为80-150nm。如图1a所示二氧化锰纳米棒的透射电镜照片。如图1b～图1c所示，经过X射线衍射(XRD)和高分辨电镜分析，所得到二氧化锰是α-MnO2单晶。如图1d所示，电子能量损失谱(EDS)表明产物主要元素是氧和锰。
实施例2
与实施例1不同之处在于：
采用硫酸溶液中加入高锰酸钾，硫酸溶液的浓度为2mol/l；每100毫升的硫酸溶液加入高锰酸钾1.5g；在加热的条件下使硫酸和高锰酸钾反应，反应温度为80℃。待反应结束后，自然冷却，而后，加入去离子水洗干净并干燥。二氧化锰纳米棒的直径约为8nm，长度范围为150-200nm，如图2所示二氧化锰纳米棒的透射电镜照片。
实施例3
与实施例1不同之处在于：
采用硫酸溶液中加入高锰酸钾，硫酸溶液的浓度为1mol/l；每100毫升的硫酸溶液加入高锰酸钾2.5g；在加热的条件下使其反应，反应温度为90℃。待反应结束后，自然冷却，而后，加入去离子水洗干净并干燥。如图3a～图3b所示，扫描电镜表明二氧化锰纳米棒聚集成1-2μm的颗粒，扫描电镜表明二氧化锰纳米棒的直径约为4nm。如图3c所示二氧化锰纳米棒的透射电镜照片。如图3d所示二氧化锰纳米棒的氮吸附等温线，从图中可以看出二氧化锰纳米棒具有较大的外比表面积和较强的毛细凝聚现象。这是由于二氧化锰纳米棒直径小并聚集成团的原因。这种小直径的二氧化锰纳米棒的比表面积高达165.8m2/g。

Claims (4)

1、一种α-MnO2单晶纳米棒的制备方法，其特征在于：采用在硫酸溶液中加入高锰酸钾，再在加热的条件下使硫酸和高锰酸钾反应，待反应结束后，自然冷却，制备出直径较小且均匀的α-MnO2单晶纳米棒。
2、按照权利要求1所述α-MnO2单晶纳米棒的制备方法，其特征在于：所述反应温度为70-95℃。
3、按照权利要求1所述α-MnO2单晶纳米棒的制备方法，其特征在于：所述硫酸溶液的浓度为0.1mol/l到3mol/l。
4、按照权利要求1所述α-MnO2单晶纳米棒的制备方法，其特征在于：所得纳米棒加入去离子水冲洗干净并干燥。
CNB2004100208881A 2004-07-02 2004-07-02 α－MnO2单晶纳米棒的制备方法 Expired - Fee Related CN1312330C (zh)