CN1715359A - Animal protein external coated phase change energy storage microcapsule, preparing method and its use - Google Patents
Animal protein external coated phase change energy storage microcapsule, preparing method and its use Download PDFInfo
- Publication number
- CN1715359A CN1715359A CN 200510025903 CN200510025903A CN1715359A CN 1715359 A CN1715359 A CN 1715359A CN 200510025903 CN200510025903 CN 200510025903 CN 200510025903 A CN200510025903 A CN 200510025903A CN 1715359 A CN1715359 A CN 1715359A
- Authority
- CN
- China
- Prior art keywords
- phase change
- microcapsules
- change material
- storing energy
- animal proteinum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a kind of animal protein coated energy storing phase change microcapsule and its preparation process and use. The microcapsule has shell of animal protein and core of oil soluble organic phase change material with melting point in 10-90 deg c. It is prepared through physical coating process and has average size of 0.2-10 micron. The microcapsule may be used directly or after further acetalation, and is suitable for modifying flexible textile material through mixing, compounding, coating or grouting on flexible material.
Description
Technical field:
The present invention relates to outer microcapsules of storing energy through phase change, the preparation method and its usage that coats of a kind of animal proteinum.The method that system adopts physics to coat prepares the microcapsules of storing energy through phase change that shell is an animal proteinum, is used for the modification of flexible textile material.
Background technology:
Phase-changing energy storage material is to improve capacity usage ratio, and heat release adaptively and heat-retaining intelligent material, aspect environmental temperature regulate and control, demonstrated application prospect (old love English river is learned English Cao Xue and is increased. the progress of phase-changing energy storage material and application. material Leader .2003,17 (5): 42-44).Make building inner decorative material with phase-changing energy storage material, can make full use of environmental energy, obtain effect cool in summer and warm in winter (the beam yellow Xiang of just navigating, phase change material application under construction. building heat-energy air conditioner .2004,23 (4): 23-26).Be used for space station and the interior trim of wearing people's airship, not only can reduce the fluctuation of temperature in the cabin, obtain comfortable space environment, and can effectively reduce dissipation of energy, (strong Lu of leaf Four Modernizations Guo Yuan brightness Chen Ming of society just to save the energy, microencapsulated phase change material and application thereof, polymer material science and engineering .2004,20 (5): 6-9).
Along with people to increasing and diversification that clothes require, except clothes due external attractive in appearance and comfortable and easy to wear, there is also a desire for multiple function, such as functions such as far infrared, uvioresistant, negative ion, antibiotic, antimite, fire-retardant, radiation shielding, thermal isolations.And microcapsules of storing energy through phase change is a kind of coating of dress materials or basic material of weighting material of can be used for, can be used for regulating adaptively the human body envrionment temperature, be truly produce comfortable function and even intelligence effect take material (Cai Lihai opens emerging auspicious. the research of phase-change material micro-capsule and application. material Leader .2002,16 (12): 61-64).After wearing the clothes that this class contains microcapsules of storing energy through phase change, and when general room temperature environment entered the higher environment of temperature, the effect of the phase change material Yin Wendu in the microcapsule absorbed heat by solid-state liquefy, thus the rising of reducing human table temperature.Otherwise when when general room temperature environment enters lower temperature environment, phase change material changes from liquid to solid again, emits heat, thus the reduction of reducing human table envrionment temperature.Thus, human body is made at high and low temperature and still keep comfort.
Relevant for phase-changing energy storage material and Material Used thereof patent report is arranged, only United States Patent (USP) just has nearly 750 more; Domestic have nearly 150.About microcapsules of storing energy through phase change material and Material Used thereof and technology also have patent report, United States Patent (USP) has nearly 60; Domestic have only 6~7.Wherein, the report of the technology of preparing of relevant microcapsules of storing energy through phase change, quite limited both at home and abroad.Refusing aqueous solution separating husk as humans such as external K.K.Mistry is that polymkeric substance, core are the microparticle of phase transformation thing, method (the Mistry K K for preparing microcapsule, Preston J A, Symes K C, Particles, USP-6,753,083.Ciba SpecialtyChemicals Water Treatments Ltd., June 22,2004); The hot phase-change microcapsule of humans such as M.C.Magill is as mixture processing polycomponent phase change fiber (the Magill M C of fiber, Hartmann M H, Haggard J S, Multi-component fibers having enhanced reversible thermal properties and methods ofmanufacturing thereof, USP-6,855,422.February 15,2005); Human large capsules such as D.A.Davis coat the solid-solid phase change material that microcapsule form stable form, but yardstick 2~50 μ m and the content of only having carried microcapsule briefly can reach 80% (Davis D A, Hart R L, Work D E, et al., Macrocapsules containing microencapsulatedphase change materials, USP-6,835,334.Microtek Laboratories, Inc., December 28,2004); R.C Weston and H.R Dungworth have introduced with methyl-prop diluted acid polymer blend and have made shell, phase change material or other functional materialss are made microcapsule preparation method (the Weston R C of sandwich layer, Dungworth H R, Particulate compositionsand their manufacture, USP-6,716,526.Ciba Specialty Chemicals Water Treatments Ltd., April 6,2004); People such as D.P.Colvin have just stated, and can to prepare diameter be 1~100 μ m phase-change microcapsule material, and be used for absorbing heat and the hard and Resins, epoxy (the Colvin D P of heat release occasion, Bryant Y G, Mulligan J C, Method ofusing thermal energy absorbing and conducting potting materials, USP-5,224,356.TriangleResearch ﹠amp; Development Corp., July 6,1993); Chen and Eichelberger have introduced size at microcapsule 1/8~1 inch, that contain phase change material, and the preparation method of mechanical separation (Chen J C H, Eichelberger J L, Encapsulated phase change thermal energy storage materials and process, USP-4,513,053.Pennwalt Corporation, April 23,1985).As " a kind of microcapsule coated phase-change material and preparation method thereof (number of patent application: 03130587.3, open day: 2004.07.21) " of people such as domestic Wang Lixin, be with the technology of emulsification method with the polymer overmold phase change material; People's such as Zhang Xingxiang " autoamtic temp-regulating fibre and goods thereof (Chinese patent-ZL00105837.1, Granted publication day: on 03 19th, 2003) " is to adopt situ aggregation method synthetic cyst wall, and phase change material is the microcapsule of capsule-core, the preparation temperature-regulating fiber; People such as YG Bryant " adiabatic coating of use microencapsulated phase change material and method (Chinese patent-ZL98804081.6, open day: 2000.05.03) ", be method based on coating, be not the preparation method of microencapsulated phase change material.Obviously, to prepare shell be that the method for the microcapsules of storing energy through phase change of animal ceratin is not seen similar or similar patent report to the method that adopts physics to coat.
The phase-changing energy storage material that microcapsule method makes has the feature and the performance of solid-solid phase-change on the form.In general, cryogenic solid-solid phase-change energy-storage material because the end group of its molecular chain one or both ends is fixed, its transformation temperature can change, its unit mass phase transformation heat is lower than the phase change material of solid-liquid phase.Though and solid-liquid phase change material phase-change energy is bigger, the inefficacy of the leakage of easy generating material and whole mechanical property when liquid state, this is in particular for the application scenario of flexible textile material.
Utilize microcapsulary will in, low-temperature phase-change material is fixed on microcapsule inside, phase change material still freely, its transformation temperature and phase transformation calorific value can not change.Can not only keep the material appearance form, and bigger phase-change energy can be arranged.
Report physics in people such as big eastern Chen Li duckweed Zhang Yueting and coated the microcapsule technology of preparing, be to utilize wool keratin or other animal ceratins or fibroin solubilized performance in certain hydrophilic solvent, with organic water-insoluble phase transition temperature compound is core, with proteic non-solvent proteinosis is come out then, form the shell of the nuclear of ceasing to be faithful mutually, make phase-change microcapsule (" from wool the dissolving wool keratin auxiliary agent, and its production and use ", application number: 200410052924.2, the applying date: on July 16th, 2004; " preparation method of a kind of wool keratin and goods thereof, application number: 200410052922.3, the applying date: on July 16th, 2004).Key problem in technology of the present invention is to have a kind of solvent can dissolve wool keratin (comprising other animal ceratins or fibroin), and non-solvent can make Keratin sulfate deposit out and the dispersion of nuclear matter in protein solution containing of organically ceasing to be faithful mutually.
Summary of the invention:
The purpose of this invention is to provide the microcapsules of storing energy through phase change that a kind of animal proteinum coats.
Purpose of the present invention also provides a kind of method for preparing the microcapsules of storing energy through phase change of animal proteinum coating, is that the method that adopts physics to coat prepares the technology that shell is the microcapsules of storing energy through phase change of animal proteinum.
Another object of the present invention provides the purposes of above-mentioned microcapsules of storing energy through phase change.
Microcapsules of storing energy through phase change of the present invention is that a kind of shell is an animal proteinum, and core is oil-soluble fusing point at 10-90 ℃ organic phase change material, and the weight ratio of animal proteinum and organic phase change material is 1: 0.45~9.Described animal ceratin is wool keratin, fibroin, bristles Keratin sulfate, rabbit hair Keratin sulfate, camel hair Keratin sulfate or human hair keratin etc.; Described aldehyde is formaldehyde, acetaldehyde, oxalic dialdehyde or glutaraldehyde; Described organic phase change material is C
20~1000Cured, C
8~30Fatty Alcohol(C12-C14 and C12-C18), C
8~30Lipid acid and the ester of described lipid acid, wherein said wax can be alkane paraffin, ceresine, beeswax or their mixture; Described ester can be methyl esters, ethyl ester or glyceryl ester etc.
Microcapsules of storing energy through phase change of the present invention because coat protein is a kind of natural macromolecular material, have nontoxic, nuisanceless, contact comfortable etc. advantage with human body.Microcapsule size average out to 0.2-10um of the present invention can regulate arbitrarily.Organically phase change material has the long advantage of phase change transition validity period.Capsular protein coat can be made solvable or insoluble as required.
Main preparation methods of the present invention is as follows:
Is core with oil-soluble fusing point at 10-90 ℃ organic phase change material, with the animal proteinum is the outer cover polymer source, with the hydrophilic solvent that can dissolve animal proteinum is dispersion medium, with nonionic and anion surfactant is emulsifying agent, disperseing phase change material under 10-95 ℃ the temperature in this solution, formation contains the suspension of phase transformation particulate, makes proteinosis to the phase change material particulate with non-solvent, is the phase-change microcapsule of shell and get animal protein.
Described animal proteinum is 1: 0.45~9 with the weight ratio of face phase change material is arranged.
Described organic phase change material is alkane paraffin, ceresine, the beeswax of carbon number 20-1000, also can be the mixture of above-mentioned several waxes; And carbon number is the high fatty alcohol of 8-30; Carbon number is the lipid acid of 8-30 and methyl esters, ethyl ester, the glyceryl ester of lipid acid thereof, and its concentration expressed in percentage by weight is 10%-30%.
Described dispersion medium is a hydrophilic solvent, be the aqueous solution of dimethyl sulfoxide (DMSO), dimethyl formamide, amine oxide, trolamine or inorganic salt, wherein inorganic salt are Sodium Thiocyanate 99, potassium sulfocyanate, zinc chloride, and wherein the concentration expressed in percentage by weight of polar organic matter or inorganic salt solution is 20~60%.Animal protein is dissolved in to make protein wt concentration in this solvent be 5~30% solution.The concentration expressed in percentage by weight of this solution is the 70%-90% of whole suspension.
Described non-solvent is water, ethanol, methyl alcohol, acetone, acetonitrile, can be one or more mixture wherein.
Described dispersion protective material is:
Molecular formula is R (OCH
2CH
2)
nThe nonionogenic tenside of OH, wherein R is C
8-18Alkylphenol, alkyl and acyl alkyl, n is 3-20, and the nonionogenic tenside of taking charge of this series and tween series;
Molecular formula is R (OCH
2CH
2)
nOSO
3The anion surfactant of M, wherein R is C
8-18Alkylphenol, alkyl and acyl alkyl, n is 3-10, M is sodium, potassium, ammonium;
Molecular formula is RSO
3The anion surfactant of M, wherein R is C
8-18Alkylbenzene, alkyl, n is 3-10, M is sodium, potassium, ammonium;
Molecular formula is ROSO
3The anion surfactant of M, wherein R is C
8-18Alkylbenzene, alkyl, n is 3-10, M is sodium, potassium, ammonium;
These tensio-active agents can independent or compound use, and its weight concentration is the 0.01-0.5% of protein solution.
Described cladding process is under the temperature more than the melting temperature of phase change material, and the organic phase change material of required fusing point (fusing point 10-90 ℃) is dispersed in the hydrophilic solvent that contains emulsifying agent and animal proteinum, makes into the organic phase change material drop of certain particle diameter.Then under high-speed stirring, slowly add proteic non-solvent after, obtain the microcapsules of storing energy through phase change that animal proteinum coats.
Described aldolization, the fixedly animal proteinum of further carrying out.Used aldehyde can be formaldehyde, acetaldehyde, oxalic dialdehyde, glutaraldehyde.The concentration expressed in percentage by weight of its aqueous solution is 3%-8%, and treatment temp is 50-80 ℃, and the time is the 2-30 branch, and the pH value of treatment solution is adjusted to 2-3.
The average dimension of resulting microcapsules of storing energy through phase change can be adjusted arbitrarily between 0.2-10 μ m, sees shown in the accompanying drawing 1.Be specially adapted to the mixing of flexible textile material, the use of compound, coating.
Description of drawings:
Fig. 1 is the transmission electron microscope picture of phase-change microcapsule
Embodiment:
To help to understand the present invention by following examples, but not limit content of the present invention.
Adopt technology of the present invention, the organic phase change material of required fusing point (fusing point 10-90 ℃), under the temperature more than the melting temperature of phase change material (10-95 ℃), be dispersed in the hydrophilic solvent that contains tensio-active agent and wool keratin (animal ceratin or fibroin), make into the organic phase change material drop of certain particle diameter.Under high-speed stirring, slowly join in the proteinic non-solvent then, obtain the microcapsules of storing energy through phase change that wool keratin coats.The prescription of its concrete scheme, technology and result are as described below.
Raw materials usedly among the embodiment be commercial commodity, the title of tensio-active agent is the trade(brand)name of the above tensio-active agent.
Embodiment 1
The suspension that 20 gram stearyl alcohol is become to contain the phase change material particulate in the solder(ing)acid that is distributed to 80 grams that contain fibroin and tensio-active agent under 80 ℃ of temperature, under high-speed stirring is floating, contains albumen 8 grams, zinc chloride 28 grams, tensio-active agent MOA in the aqueous solution of the protein-contg zinc chloride of 80 grams
30.03 gram and OP-10 0.01 gram, all the other are water.Cool to room temperature under agitation is poured in the water, and albumen is separated out the microparticle surfaces that is wrapped in stearyl alcohol, and the transformation temperature that obtains fibroin and be coating material is 58 ℃ a phase-change microcapsule.Its median size is 0.8 μ m.
Embodiment 2
The suspension that No. 30 phase-change wax of 18 grams is become to contain the phase change material particulate in the sodium thiocyanate water solution that is distributed to 82 grams that contain wool keratin and tensio-active agent under 50 ℃ of temperature, under high-speed stirring is floating, contains protein 10 gram, Sodium Thiocyanate 99 30 grams, tensio-active agent MOA in the aqueous solution of the protein-contg Sodium Thiocyanate 99 of 82 grams
50.02 gram and ABS 0.015 gram, all the other are water.Cool to room temperature under agitation is poured in the aqueous ethanolic solution of 60% concentration, and albumen is separated out the microparticle surfaces that is wrapped in No. 30 phase-change wax, and the transformation temperature that obtains wool keratin and be coating material is 30 ℃ a phase-change microcapsule.Its median size is 0.45 μ m.
Embodiment 3
The suspension that 24 gram lauric acid is become to contain the phase change material particulate in the dimethyl sulphoxide aqueous solution that is distributed to 76 grams that contain wool keratin and tensio-active agent under 75 ℃ of temperature, under high-speed stirring is floating, contain albumen 7 grams, dimethyl sulfoxide (DMSO) 30 grams, tensio-active agent TWEEN80 0.02 gram and SPAN60 0.02 gram in the aqueous solution of the protein-contg dimethyl sulfoxide (DMSO) of 76 grams, all the other are water.Cool to room temperature under agitation is poured in the aqueous acetone solution of 50% concentration, and albumen is separated out and is wrapped in lauric microparticle surfaces, and the transformation temperature that obtains wool keratin and be coating material is 44 ℃ a phase-change microcapsule.Its median size is 0.4 μ m.
Embodiment 4
The suspension that 15 gram glyceryl monostearates is become to contain the phase change material particulate in the aqueous solution of the trolamine that is distributed to 85 grams that contain bristles Keratin sulfate and tensio-active agent under 70 ℃ of temperature, under the ultrasonic wave effect is floating, contain protein 10 gram, trolamine 20 grams, tensio-active agent K12 0.03 gram and SPAN60 0.01 gram in the aqueous solution of the protein-contg trolamine of 85 grams, all the other are water.Cool to room temperature under agitation is poured in the methanol aqueous solution of 70% concentration, and albumen is separated out the microparticle surfaces that is wrapped in glyceryl monostearate, and the transformation temperature that obtains the bristles Keratin sulfate and be coating material is 60 ℃ a phase-change microcapsule.Its median size is 0.35 μ m.
Embodiment 5
The suspension that 29 grams, 60 degree paraffin is become to contain the phase change material particulate in the aqueous solution of the amine oxide that is distributed to 71 grams that contain tussah silk albumen and tensio-active agent under 70 ℃ of temperature, under the ultrasonic wave effect is floating, contain protein 20 gram, amine oxide 30 grams, surfactant A ES 0.16 gram in the aqueous solution of the protein-contg trolamine of 71 grams, all the other are water.Cool to room temperature under agitation is poured in the water, and albumen is separated out the microparticle surfaces that is wrapped in paraffin, and the transformation temperature that obtains the tussah fibroin and be coating material is 60 ℃ a phase-change microcapsule.Its median size is 0.22 μ m.Still mix with water with these microcapsule, volumetric mixture ratio is about 70: 30, puts into the hollow polyester fiber of degree of hollowness 50% then, vacuumizes the bubble that degass, and recovers normal pressure, and drying must pour into the tubular fibre of these microcapsule, and microcapsule weight reaches more than 35%.
Embodiment 6
The suspension that 10 grams, 90 degree South Africa waxes is become to contain the phase change material particulate in the aqueous solution of the potassium sulfocyanate that is distributed to 90 grams that contain rabbit hair Keratin sulfate and tensio-active agent under 95 ℃ of temperature, under the ultrasonic wave effect is floating, contain 45 grams, surfactant A ES 0.01 gram of albumen 5 grams, potassium sulfocyanate in the aqueous solution of the protein-contg potassium sulfocyanate of 90 grams, all the other are water.Cool to room temperature under agitation is poured in the water, and albumen is separated out the microparticle surfaces that is wrapped in paraffin, and the transformation temperature that obtains rabbit hair Keratin sulfate and be coating material is 90 ℃ a phase-change microcapsule.Its median size is 1.9 μ m.
Embodiment 7
The suspension that 12 grams, 75 degree paraffin is become to contain the phase change material particulate in the aqueous solution of the ammonium thiocyanate that is distributed to 88 grams that contain camel hair Keratin sulfate and tensio-active agent under 90 ℃ of temperature, under high-speed stirring is floating, contains 40 grams, the tensio-active agent MOA of protein 25 gram, ammonium thiocyanate in the aqueous solution of the protein-contg ammonium thiocyanate of 88 grams
30.05 gram and OP-15 0.01 gram, all the other are water.Be cooled to 40 ℃, under agitation be poured in the water, albumen is separated out the microparticle surfaces that is wrapped in paraffin, and the transformation temperature that obtains the camel hair Keratin sulfate and be coating material is 75 ℃ a phase-change microcapsule.Its median size is 0.42 μ m.
Embodiment 8
The suspension that No. 30 phase-change wax of 25 grams is become to contain the phase change material particulate in the aqueous solution of the dimethyl formamide that is distributed to 75 grams that contain human hair keratin and tensio-active agent under 45 ℃ of temperature, under the ultrasonic wave effect is floating, contain 44 grams, surfactant A BS 0.05 gram of protein 10 gram, dimethyl formamide in the aqueous solution of the protein-contg potassium sulfocyanate of 75 grams, all the other are water.Cool to room temperature under agitation is poured in the water, and albumen is separated out the microparticle surfaces that is wrapped in paraffin, and the transformation temperature that obtains human hair keratin and be coating material is 30 ℃ a phase-change microcapsule.Particle diameter is the phase-change wax bead of 0.6-0.8 μ m.Through separate, washing, be dispersed in after the lyophilize in the polyacrylate dispersion, be used for the bonding of gum sprayed cotton, can obtain containing the non-manufacturing cloth of phase transition temperature material, wallpaper that this non-manufacturing is fabric or wall paper can be used for room temp constant among a small circle.
Embodiment 9
The microcapsule that contain No. 30 phase-change wax of embodiment 2 are put into 60 ℃ 5% formalin, keep making in 15 minutes albumen generation acetalation.Obtain shell undissolvable transformation temperature in solvent and be 30 ℃ phase-change microcapsule.
Embodiment 10
Is the tussah silk albumen that contains No. 75 paraffin of embodiment 5 that the microcapsule of shell are put into 70 ℃ 6% glutaraldehyde water solution, keeps making in 20 minutes albumen generation acetalation.Obtain shell undissolvable transformation temperature in solvent and be 75 ℃ phase-change microcapsule.
Embodiment 11
Is the tussah silk albumen that contains No. 75 paraffin of embodiment 5 that the microcapsule of shell are put into 50 ℃ 4% glyoxal water solution, keeps making in 30 minutes albumen generation acetalation.Obtain shell undissolvable transformation temperature in solvent and be 75 ℃ phase-change microcapsule.
Embodiment 12
Containing of embodiment 3 lauric wool keratin be that the microcapsule of shell are put into 80 ℃ 8% acetaldehyde solution, keep making in 5 minutes albumen generation acetalation.Obtain shell undissolvable transformation temperature in solvent and be 44 ℃ phase-change microcapsule.Through separate, washing, be dispersed in after the lyophilize in the solvent based coating, this coating is used for making the brushing of the wall of the little occasion of temperature fluctuation in certain amplitude.
Claims (9)
1, a kind of microcapsules of storing energy through phase change, its shell are the acetal thing of animal proteinum or animal proteinum and aldehyde, and core is the fusing point that there is not dissolubility at 10-90 ℃ organic phase change material, and the weight ratio of animal proteinum and organic phase change material is 1: 0.45-9; Described organic phase change material is C
20-100Cured, C
8-30Fatty Alcohol(C12-C14 and C12-C18), C
8-30Lipid acid and ester thereof.
2, microcapsules of storing energy through phase change as claimed in claim 1 is characterized in that described micro-capsule mean size is 0.2-10 μ m.
3, microcapsules of storing energy through phase change as claimed in claim 1 is characterized in that described animal proteinum is wool keratin, fibroin, bristles Keratin sulfate, rabbit hair Keratin sulfate, camel hair Keratin sulfate or human hair keratin.
4, microcapsules of storing energy through phase change as claimed in claim 1 is characterized in that described C
8-30Fatty acid ester be C
8-30Fatty acid methyl ester, ethyl ester or glyceryl ester.
5, microcapsules of storing energy through phase change as claimed in claim 1, its feature is formaldehyde, acetaldehyde, oxalic dialdehyde or glutaraldehyde at described aldehyde.
6, the preparation method of microcapsules of storing energy through phase change as claimed in claim 1 is characterized in that adopting following (1) or (1) and (2) two kinds of methods to make:
(1) animal proteinum is the preparation of the microcapsules of storing energy through phase change of shell:
A. hydrophilic solvent dissolving animal proteinum becomes to contain the animal proteinum hydrophilic solvent solution of 5-30% weight;
Add organic phase change material in the solution of b.a, organic phase change material concentration is 5-30%;
C. add emulsifying agent and form suspension in the solution of b, this suspension contains the molten stream of b of 70-90% weight;
D. in the described suspension of c, add non-solvent, animal proteinum is deposited on the particulate;
Wherein, organic phase change material according to claim 1; Described hydrophilic solvent is the aqueous solution of its sulfoxide of diformazan, dimethyl formamide, amine oxide, trolamine or the inorganic salt of 20-60% weight; Inorganic salt are Sodium Thiocyanate 99, potassium sulfocyanate or zinc chloride; Described emulsifying agent is nonionic or anion surfactant; Described non-solvent is water, ethanol, methyl alcohol, third bronze medal, acetonitrile or their mixture;
(2) the acetal thing of animal proteinum and aldehyde is the preparation of the microcapsules of storing energy through phase change of shell:
Under 50-80 ℃, the product of above-mentioned (1) and pH are the reactant aqueous solution 2-30 branch that contains 1-8% weight aldehyde of 2-3; Wherein the weight ratio of the microcapsule of (1) and aldehyde is 1: 1~3; Described aldehyde is formaldehyde, acetaldehyde, oxalic dialdehyde or glutaraldehyde.
7, method according to claim 6, its feature at described emulsifying agent is:
Molecular formula is R (OCH
2CH
2)
nThe nonionogenic tenside of OH, wherein R is C
8-18Alkylphenol, alkyl and acyl alkyl, n is 3-20, and the nonionogenic tenside of taking charge of this series and tween series;
Molecular formula is R (OCH
2CH
2)
nOSO
3The anion surfactant of M, wherein R is C
8-18Alkylphenol, alkyl and acyl alkyl, n is 3-10, M is sodium, potassium, ammonium;
Molecular formula is RSO
3The anion surfactant of M, wherein R is C
8-18Alkylbenzene, alkyl, n is 3-10, M is sodium, potassium, ammonium;
Molecular formula is ROSO
3The anion surfactant of M, wherein R is C
8-18Alkylbenzene, alkyl, n is 3-10, M is sodium, potassium, ammonium;
One or more above-mentioned blended tensio-active agents.
8, method according to claim 6, it is characterized in that described method is under>10 ℃ of-95 ℃ of temperature, organic phase change material is dispersed in the described hydrophilic solvent that contains emulsifying agent and animal proteinum, become the organic phase change material drop, then under high-speed stirring, slowly add described non-solvent, obtain the microcapsules of storing energy through phase change that animal proteinum coats.
9, the purposes of the microcapsule of phase-change accumulation energy according to claim 1 is characterized in that being used for the mixing of flexible textile material, compound, coating, perfusion.