CN1673175A - Functional ball of nano level composite porous ceramic material and its production process - Google Patents
Functional ball of nano level composite porous ceramic material and its production process Download PDFInfo
- Publication number
- CN1673175A CN1673175A CN 200510045991 CN200510045991A CN1673175A CN 1673175 A CN1673175 A CN 1673175A CN 200510045991 CN200510045991 CN 200510045991 CN 200510045991 A CN200510045991 A CN 200510045991A CN 1673175 A CN1673175 A CN 1673175A
- Authority
- CN
- China
- Prior art keywords
- porous ceramic
- loess
- zeolite
- organism
- tourmalinite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The functional ball is made with the nanometer level composite porous ceramic material comprising tourmaline, Chinese medicinal stone, zeolite, loess, active carbon, organic pore expanding agent and adhesive. Compared with available technology, the present invention has the features of reasonable material compounding, long service life, high air purifying effect, many functions, etc. The functional ball can release negative ion and far infrared ray continuously, adsorb heavy metal ions, purify air, activate body' cell, promote plant growth, and prevent radiation.
Description
(1) technical field
The present invention relates to a kind of matrix material that is used for indoor, car inner air-cleaning, water demineralization, particularly relate to a kind of functional ball of nano level composite porous ceramic material.
(2) background technology
The room, office, the Air quality in the car is subjected to the great attention of national government and people's common concern, and Air quality present situation indoor, that car is interior is made us very worry, and indoor environment is administered the project verification content of having listed nation-building portion in.CCTV's " telling the truth " column is reported in September, 2002 that compatriots have and is in sub-health state more than 70%, people's office, study, live between the chamber more than the 60%-90%, particularly national pupils and students account for population about 1/4, their academic environment dust pollution, atmospheric pollution is worrying, how to guarantee that healthy full of vitality the finishing school of several hundred million students is a major issue.Country is that content has been assigned a series of laws and regulations with indoor environment improvement, has worked out IAQ (indoor air quality) and has executed standard, and country organizes a large amount of manpower and materials project verification tackling key problem, is intended to improve the environment in indoor human settlements, office, the classroom.Air quality more causes people's common concern and attention in the particularly indoor car.Now on the market in the decontamination chamber, the product of the interior air of car is dazzled, what have plays better action really, have plenty of disposable sprays, but have do not have an effect of purifying air at all, but covered peculiar smell and air inferior in the indoor car with some aromatoising substances.That also have in addition not only can not the decontamination chamber in, air in the car, brought pollution on the contrary, the discovery as yet of infringement people's health, the environment-friendly type of the employing natural materials of real meaning efficient for a long time (such as using 1-3) air clearing product to air.
(3) summary of the invention
The object of the present invention is to provide a kind of environment-friendly type functional ball of nano level composite porous ceramic material, sustainable release negative ion of this functional ball and far infrared rays, air in can the decontamination chamber, in the car, formaldehyde in the absorbed air, benzene, ammonia do not have oxyradical to poison, remove other various peculiar smell, antibacterial sterilizations such as stink, cigarette, and can make water softening purify the moment negative ionization.
The technical scheme that adopts is:
Functional ball of nano level composite porous ceramic material is to be made by tourmalinite, medical stone, zeolite, loess, gac, organism expanding agent, binding agent, and its ingredients by weight per-cent is: tourmalinite 20-40%,, medical stone 10-25%, zeolite 2-10%, loess 8-15%, gac 20-35%, organism expanding agent 1-5%, binding agent 5-10%.
Above-mentioned organism expanding agent can select for use wood powder, granularity below 1.8 μ m.Binding agent is an aluminium colloidal sol etc.
The production technique of functional ball of nano level composite porous ceramic material is: get tourmalinite, medical stone, zeolite, loess, gac, organism expanding agent, binding agent by above-mentioned ratio of components, earlier with tourmalinite, medical stone, zeolite, four kinds of raw material extra-fine grindings of loess to the ultrafine powder below the 2 μ m, mix with activated carbon, organism expanding agent then, stir, add tackiness agent and make ball, wrap up with stupalith again, promptly can be made into porous ceramic nano composite material functional ball through 400 ℃ of-600 ℃ of very low temperature calcinings.
The present invention compared with prior art, have batching rationally, use characteristics such as permanent, good air purification effect, function are many, this product can continue to discharge negative ion, far infrared rays, heavy metal ion adsorbed fixation devirus, make instant water negative ionization, weak baseization, make Air quality indoor, that car is interior reach state specified standards fully.In addition, this product can also the exciting human cytoactive, promotes growth and development of plants, has certain radiation protection ability.This product detects through the National Geology experimental center, and it removes the formaldehyde ability and reached 58.3% at 20 minutes in the clock time, reaches 81.4% in 500 minutes, is the environmentfriendly products of real meaning, has vast market prospect.
(4) embodiment
Embodiment one
Functional ball of nano level composite porous ceramic material of the present invention, be to be formed by tourmalinite, medical stone, zeolite, loess, gac, organism expanding agent, binding agent calcining, its batching per-cent is: tourmalinite 15%,, medical stone 20%, zeolite 8%, loess 10%, gac 34%, organism expanding agent lucerne moss powder 5%, binding agent aluminium colloidal sol 8%.
The production technique of functional ball of nano level composite porous ceramic material is: by above-mentioned ratio of components with tourmalinite, medical stone, zeolite, four kinds of raw material extra-fine grindings of loess to 1.5 μ m sodium meter level ultrafine powders, add activated carbon and organism expanding agent by ratio of components then, stir after the mixing, add tackiness agent by ratio of components again and make ball, behind balling-up outsourcing pottery, after 350 ℃ of low temperature calcinations, stir, add the tackiness agent balling-up by ratio of components at last.
Embodiment two
Functional ball of nano level composite porous ceramic material of the present invention, its weight batching ratio is: tourmalinite 40%,, medical stone 10%, zeolite 5%, loess 8%, gac 30%, organism expanding agent wood powder 2%, binding agent aluminium colloidal sol 5%.
The production technique of functional ball of nano level composite porous ceramic material is: by above-mentioned ratio of components with tourmalinite, medical stone, zeolite, four kinds of raw material extra-fine grindings of loess to 1.6 μ m nano level superfine powder, add activated carbon and organism expanding agent by ratio of components then, stir after the mixing, add tackiness agent by ratio of components again and make ball, behind balling-up outsourcing stupalith, promptly made finished product in 180 minutes through 500 ℃ of low temperature calcinations.
Embodiment three
Functional ball of nano level composite porous ceramic material of the present invention, its weight batching ratio is: tourmalinite 28%, medical stone 20%, zeolite 2%, loess 15%, gac 25%, organism expanding agent wood moss powder 3%, binding agent aluminium colloidal sol 7%.
The production technique of functional ball of nano level composite porous ceramic material is: by above-mentioned ratio of components with tourmalinite, medical stone, zeolite, four kinds of raw material extra-fine grindings of loess to 1.8 μ m nano level superfine powder, add activated carbon and organism expanding agent by ratio of components then, stir after the mixing, add tackiness agent by ratio of components again and make ball, behind balling-up outsourcing pottery, promptly made finished product in 120 minutes through 600 ℃ of low temperature calcinations.
Claims (5)
1, functional ball of nano level composite porous ceramic material, it is characterized in that being made by tourmalinite, medical stone, zeolite, loess, gac, organism expanding agent, binding agent, its ingredients by weight per-cent is: tourmalinite 20-40%,, medical stone 10-25%, zeolite 2-10%, loess 8-15%, gac 20-35%, organism expanding agent 1-5%, binding agent 5-10%.
2, functional ball of nano level composite porous ceramic material according to claim 1 is characterized in that its batching per-cent is: tourmalinite 15%,, medical stone 20%, zeolite 8%, loess 10%, gac 34%, organism expanding agent wood moss powder 5%, binding agent aluminium colloidal sol 8%.
3, functional ball of nano level composite porous ceramic material according to claim 1 is characterized in that its weight batching ratio is: tourmalinite 40%,, medical stone 10%, zeolite 5%, loess 8%, gac 30%, organism expanding agent wood powder 2%, binding agent aluminium colloidal sol 5%.
4, functional ball of nano level composite porous ceramic material according to claim 1 is characterized in that its weight batching ratio is: tourmalinite 28%, medical stone 20%, zeolite 2%, loess 15%, gac 25%, organism expanding agent wood moss powder 3%, binding agent aluminium colloidal sol 7%.
5, the production technique of functional ball of nano level composite porous ceramic material, it is characterized in that: get tourmalinite, medical stone, zeolite, loess, gac, organism expanding agent, binding agent by ratio of components, earlier with tourmalinite, medical stone, zeolite, four kinds of raw material extra-fine grindings of loess to the ultrafine powder below the 2 μ m, mix with activated carbon, organism expanding agent then, stir, add tackiness agent and make ball, wrap up with stupalith again, promptly can be made into the porous ceramic film material functional ball through 400 ℃ of-600 ℃ of very low temperature calcinings.