Anion environmental protection ceramic material
Technical field
The present invention relates to ceramic material, more particularly, to a kind of anion environmental protection ceramic material.
Background technology
Development and the raising of people's living standard along with society, increasingly focus on environmental protection with healthy, particularly in terms of article of everyday use, common domestic ceramics can not meet people's requirement to health properties, and anion ceramic material is due to the negative ion releasing function of its uniqueness, health and field of Environment Protection can be preferably applied for.
Summary of the invention
It is an object of the invention to provide a kind of anion environmental protection ceramic material, capable of releasing negative ion, more environmentally-friendly health.
The object of the invention is achieved by the following technical programs:
A kind of anion environmental protection ceramic material is provided, is made up of each component of following weight fraction: build 35~54 parts of soil, tourmaline 22~33 parts, Maifanitum 16~21 parts, activated carbon 4~11 parts, kieselguhr 2~9 parts, meerschaum 2~15 parts, activated bauxite 0.5~1.3 parts, kieselguhr 1~3 parts.
Preferably, described anion environmental protection ceramic material is made up of each component of following weight fraction: build 45 parts of soil, 29 parts of tourmaline, Maifanitum 18 parts, activated carbon 7 parts, 8 parts of kieselguhr, meerschaum 6 parts, activated bauxite 1 part, kieselguhr 2 parts.
The preparation method of described anion environmental protection ceramic material, preparation process is as follows: by formula dispensing, with material: ball: water=1:2:0.7 enters ball milling, crosses 200 mesh sieves and tails over 0.2%, old 24h, obtains anion environmental protection ceramic material.
Owing to the burst size of anion is relevant with tourmaline content, increasing along with the increase of tourmaline content, therefore, the present invention have selected most suitable tourmaline content proportioning, to reach the anion burst size of maximum.
Compared with prior art, the method have the advantages that
The invention provides a kind of anion environmental protection ceramic material, capable of releasing negative ion, more environmentally-friendly health, can be widely applied to the industries such as health care, environmental protection.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is further illustrated.
Embodiment 1
Present embodiment discloses a kind of anion environmental protection ceramic material, be made up of each component of following weight fraction: build 45 parts of soil, 29 parts of tourmaline, Maifanitum 18 parts, activated carbon 7 parts, 8 parts of kieselguhr, meerschaum 6 parts, activated bauxite 1 part, kieselguhr 2 parts.
Embodiment 2
Present embodiment discloses a kind of anion environmental protection ceramic material, be made up of each component of following weight fraction: build 35 parts of soil, 33 parts of tourmaline, Maifanitum 16 parts, activated carbon 11 parts, 9 parts of kieselguhr, meerschaum 15 parts, activated bauxite 1.3 parts, kieselguhr 1 part.
Embodiment 3
Present embodiment discloses a kind of anion environmental protection ceramic material, be made up of each component of following weight fraction: build 54 parts of soil, 22 parts of tourmaline, Maifanitum 21 parts, activated carbon 4 parts, 2 parts of kieselguhr, meerschaum 2 parts, activated bauxite 0.5 part, kieselguhr 3 parts.
Embodiment 4
Present embodiment discloses a kind of anion environmental protection ceramic material, be made up of each component of following weight fraction: build 39 parts of soil, 25 parts of tourmaline, Maifanitum 17 parts, activated carbon 9 parts, 6 parts of kieselguhr, meerschaum 9 parts, activated bauxite 0.8 part, kieselguhr 2 parts.
Embodiment 5
Present embodiment discloses a kind of anion environmental protection ceramic material, its preparation method comprises the following steps:
By embodiment 1~4 formula dispensing, with material: ball: water=1:2:0.7 enters ball milling, cross 200 mesh sieves and tail over 0.2%, old 24h, obtain anion environmental protection ceramic material.
Embodiment 6
Present embodiment discloses a kind of anion environmental protection pottery, its preparation method comprises the following steps:
The anion environmental protection ceramic material of Example 5, by tradition grouting process injection forming, enters kiln 1050 DEG C and fires 22h, obtains anion environmental protection pottery.Owing to the highest meeting of sintering temperature causes anion burst size to reduce on the contrary, therefore sintering temperature is controlled at about 1050 DEG C, available maximum anion burst size.