CN1291942C - Functional ball of nano level composite porous ceramic material and its production process - Google Patents
Functional ball of nano level composite porous ceramic material and its production process Download PDFInfo
- Publication number
- CN1291942C CN1291942C CN 200510045991 CN200510045991A CN1291942C CN 1291942 C CN1291942 C CN 1291942C CN 200510045991 CN200510045991 CN 200510045991 CN 200510045991 A CN200510045991 A CN 200510045991A CN 1291942 C CN1291942 C CN 1291942C
- Authority
- CN
- China
- Prior art keywords
- zeolite
- organism
- tourmalinite
- loess
- gac
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a functional ball made from a composite porous ceramic material in a nanometer level, which is characterized in that the functional ball is made from tourmaline, maifanite, zeolite, yellow soil, activated carbon, an organic matter expanding agent and an adhesive, wherein the functional ball has the components according to the proportion by weight: 20 to 40% of tourmaline, 10 to 25% of maifanite, 2 to 10% of zeolite, 8 to 15% of yellow soil, 20 to 35% of activated carbon, 1 to 5% of organic matter expanding agent and 5 to 10% of adhesive. Compared with the prior art, the present invention has the characteristics of reasonable proportioning, long-time use, good air purification effect, multi-function, etc. The present invention can continuously release negative ions and far infrared to be adsorbed by heavy metal ions to make the fixed detoxification, so the water can be in a negative ion state and have weak alkalinity instantly, and the air quality in a room or a vehicle completely reach the standard regulated by the China. The present invention can excite the cytoactive of a human body, promote the growing and the development of a plant, and have the certain capability of radiation prevention. According to the detection of the geological experiment center in the China, the formaldehyde eliminating capability of the present invention can reach 58.3% in 20 minutes and can reach 81.4% in 500 minutes. Thereby, the present invention is an environmental protection product with great significance and wide market prospects.
Description
(1) technical field
The present invention relates to a kind of matrix material that is used for indoor, car inner air-cleaning, water demineralization, particularly relate to a kind of porous ceramic matrix material functional ball.
(2) background technology
The room, office, the Air quality in the car is subjected to the great attention of national government and people's common concern, and Air quality present situation indoor, that car is interior is made us very worry, and indoor environment is administered the project verification content of having listed nation-building portion in.CCTV's " telling the truth " column is reported in September, 2002 that compatriots have and is in sub-health state more than 70%, people's office, study, live between the chamber more than the 60%-90%, particularly national pupils and students account for population about 1/4, their academic environment dust pollution, atmospheric pollution is worrying, how to guarantee that healthy full of vitality the finishing school of several hundred million students is a major issue.Country is that content has been assigned a series of laws and regulations with indoor environment improvement, has worked out IAQ (indoor air quality) and has executed standard, and country organizes a large amount of manpower and materials project verification tackling key problem, is intended to improve the environment in indoor human settlements, office, the classroom.Air quality more causes people's common concern and attention in the particularly indoor car.Now on the market in the decontamination chamber, the product of the interior air of car is dazzled, what have plays better action really, have plenty of disposable sprays, but have do not have an effect of purifying air at all, but covered peculiar smell and air inferior in the indoor car with some aromatoising substances.That also have in addition not only can not the decontamination chamber in, air in the car, brought pollution on the contrary, the discovery as yet of infringement people's health, the environment-friendly type of the employing natural materials of real meaning efficient for a long time (such as using 1-3) air clearing product to air.
(3) summary of the invention
The object of the present invention is to provide a kind of environment-friendly type porous ceramic matrix material functional ball, sustainable release negative ion of this functional ball and far infrared rays, air in can the decontamination chamber, in the car, formaldehyde in the absorbed air, benzene, ammonia do not have oxyradical to poison, remove other various peculiar smell, antibacterial sterilizations such as stink, cigarette, and can make water softening purify the moment negative ionization.
The technical scheme that adopts is:
Porous ceramic matrix material functional ball, be to be wrapped up with stupalith by the ball that tourmalinite, medical stone, zeolite, loess, gac, organism expanding agent, binding agent are made to constitute, the ingredients by weight per-cent of tourmalinite, medical stone, zeolite, loess, gac, organism expanding agent, binding agent is again: tourmalinite 20-40%,, medical stone 10-25%, zeolite 2-10%, loess 8-15%, gac 20-35%, organism expanding agent 1-5%, binding agent 5-10%.
Above-mentioned organism expanding agent can select for use wood powder, granularity below 1.8 μ m.Binding agent is an aluminium colloidal sol etc.
The production technique of porous ceramic matrix material functional ball is: get tourmalinite, medical stone, zeolite, loess, gac, organism expanding agent, binding agent by above-mentioned ratio of components, earlier with tourmalinite, medical stone, zeolite, four kinds of raw material extra-fine grindings of loess to the ultrafine powder below the 2 μ m, mix with gac, organism expanding agent then, stir, add tackiness agent and make ball, wrap up with stupalith again, promptly can be made into porous ceramic matrix material functional ball through 400 ℃ of-600 ℃ of very low temperature calcinings.
The present invention compared with prior art, have batching rationally, use characteristics such as permanent, good air purification effect, function are many, this product can continue to discharge negative ion, far infrared rays, heavy metal ion adsorbed fixation devirus, make instant water negative ionization, weak baseization, make Air quality indoor, that car is interior reach state specified standards fully.In addition, this product can also the exciting human cytoactive, promotes growth and development of plants, has certain radiation protection ability.This product detects through the National Geology experimental center, and it removes the formaldehyde ability and reached 58.3% at 20 minutes in the clock time, reaches 81.4% in 500 minutes, is the environmentfriendly products of real meaning, has vast market prospect.
(4) embodiment
Embodiment one
Porous ceramic matrix material functional ball of the present invention, it is the ball of making by tourmalinite, medical stone, zeolite, loess, gac, organism expanding agent and binding agent, wrap up through calcining with stupalith and form, the ingredients by weight per-cent of tourmalinite, medical stone, zeolite, loess, gac, organism expanding agent and binding agent is: tourmalinite 15%,, medical stone 20%, zeolite 8%, loess 10%, gac 34%, organism expanding agent alfalfa meal 5%, binding agent aluminium colloidal sol 8%.
The production technique of porous ceramic matrix material functional ball is: by above-mentioned ratio of components with tourmalinite, medical stone, zeolite, four kinds of raw material extra-fine grindings of loess to 1.5 μ m sodium meter level ultrafine powders, add gac and organism expanding agent by ratio of components then, stir after the mixing, add tackiness agent by ratio of components again and make ball, behind balling-up outsourcing pottery, after 350 ℃ of low temperature calcinations, stir, add the tackiness agent balling-up by ratio of components at last.
Embodiment two
Porous ceramic matrix material functional ball of the present invention, its tourmalinite, medical stone, zeolite, loess, gac, organism expanding agent and weight of binder ratio of components are: tourmalinite 40%,, medical stone 10%, zeolite 5%, loess 8%, gac 30%, organism expanding agent wood powder 2%, binding agent aluminium colloidal sol 5%.
The production technique of porous ceramic matrix material functional ball is: by above-mentioned ratio of components with tourmalinite, medical stone, zeolite, four kinds of raw material extra-fine grindings of loess to 1.6 μ m nano level superfine powder, add gac and organism expanding agent by ratio of components then, stir after the mixing, add tackiness agent by ratio of components again and make ball, behind balling-up outsourcing stupalith, promptly made finished product in 180 minutes through 500 ℃ of low temperature calcinations.
Embodiment three
Porous ceramic matrix material functional ball of the present invention, its tourmalinite, medical stone, zeolite, loess, gac, organism expanding agent and weight of binder ratio of components are: tourmalinite 28%, medical stone 20%, zeolite 2%, loess 15%, gac 25%, organism expanding agent alfalfa meal 3%, binding agent aluminium colloidal sol 7%.
The production technique of porous ceramic matrix material functional ball is: by above-mentioned ratio of components with tourmalinite, medical stone, zeolite, four kinds of raw material extra-fine grindings of loess to 1.8 μ m nano level superfine powder, add gac and organism expanding agent by ratio of components then, stir after the mixing, add tackiness agent by ratio of components again and make ball, behind balling-up outsourcing pottery, promptly made finished product in 120 minutes through 600 ℃ of low temperature calcinations.
Claims (5)
1, porous ceramic matrix material functional ball, be to wrap up with stupalith by the ball that tourmalinite, medical stone, zeolite, loess, gac, organism expanding agent, binding agent are made to constitute, it is characterized in that the ingredients by weight per-cent of tourmalinite, medical stone, zeolite, loess, gac, organism expanding agent, binding agent is: tourmalinite 20-40%,, medical stone 10-25%, zeolite 2-10%, loess 8-15%, gac 20-35%, organism expanding agent 1-5%, binding agent 5-10%.
2, porous ceramic matrix material functional ball according to claim 1 is characterized in that its ingredients by weight per-cent is: tourmalinite 15%,, medical stone 20%, zeolite 8%, loess 10%, gac 34%, organism expanding agent alfalfa meal 5%, binding agent aluminium colloidal sol 8%.
3, porous ceramic matrix material functional ball according to claim 1 is characterized in that its ingredients by weight ratio is: tourmalinite 40%,, medical stone 10%, zeolite 5%, loess 8%, gac 30%, organism expanding agent wood powder 2%, binding agent aluminium colloidal sol 5%.
4, porous ceramic matrix material functional ball according to claim 1 is characterized in that its ingredients by weight ratio is: tourmalinite 28%, medical stone 20%, zeolite 2%, loess 15%, gac 25%, organism expanding agent alfalfa meal 3%, binding agent aluminium colloidal sol 7%.
5, the production technique of porous ceramic matrix material functional ball according to claim 1, it is characterized in that getting tourmalinite, medical stone, zeolite, loess, gac, organism expanding agent, binding agent by ratio of components, earlier with tourmalinite, medical stone, zeolite, four kinds of raw material extra-fine grindings of loess to the ultrafine powder below the 2 μ m, mix with gac, organism expanding agent then, stir, add tackiness agent and make ball, wrap up with stupalith again, promptly can be made into the porous ceramic film material functional ball through 400 ℃ of-600 ℃ of very low temperature calcinings.