CN1524647A - 镁钙质中间包涂料 - Google Patents

镁钙质中间包涂料 Download PDF

Info

Publication number
CN1524647A
CN1524647A CNA031156053A CN03115605A CN1524647A CN 1524647 A CN1524647 A CN 1524647A CN A031156053 A CNA031156053 A CN A031156053A CN 03115605 A CN03115605 A CN 03115605A CN 1524647 A CN1524647 A CN 1524647A
Authority
CN
China
Prior art keywords
calcareous
magnesium
tundish
paint
tundish paint
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA031156053A
Other languages
English (en)
Inventor
张金明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANGHAI HUIJI NEW MATERIAL CO Ltd
Original Assignee
SHANGHAI HUIJI NEW MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANGHAI HUIJI NEW MATERIAL CO Ltd filed Critical SHANGHAI HUIJI NEW MATERIAL CO Ltd
Priority to CNA031156053A priority Critical patent/CN1524647A/zh
Publication of CN1524647A publication Critical patent/CN1524647A/zh
Pending legal-status Critical Current

Abstract

本发明是一种镁钙质中间包涂料，其特征在于含有65－85％的高钙镁砂、5－25％的低钙镁砂、1－5％的结合剂、1－5％的增塑剂和0.2－3％的硅微粉。本发明用于钢铁冶炼中连铸中间包的工作衬涂料，具有净化钢水、抗冲刷、耐侵蚀和使用寿命长的优点。

Description

镁钙质中间包涂料
技术领域
本发明涉及的是连铸中间包涂料，特别是镁钙质中间包涂料。
背景技术
连铸中间包是钢铁冶炼接触的最后一个容器，其内衬从外到内依次是钢壳、隔热衬保温材料、永久衬耐火砖或浇注料、工作衬涂料。其中工作衬涂料直接与中间包内钢水、熔渣接触，在使用过程中工作衬涂料受到钢水的冲刷和熔渣的侵蚀，这就要求中间包涂料具有良好的耐侵蚀性、涂抹性，良好的抗冲击性，良好的净化钢水作用以及使用后残余物具有较好的剥离性。
目前常用的中间包工作衬涂料有镁质和镁钙质，镁质涂料没有净化钢水作用；镁钙质涂料所用主要原料为石灰石，高温下分解为CaO和CO2气体，CaO具有净化钢水的作用，但高温下CaCO3分解后会导致镁钙涂料气孔率增大，烧后线变化率大，因而其抗钢水冲刷性、耐熔渣侵蚀性会大大降低。例如A钢厂生产优质钢时，为了净化钢水而使用了镁钙涂料，由于镁钙涂料抗钢水冲刷性、耐熔渣侵蚀性差，所以就采用了双层涂料(即内涂镁质涂料外涂镁钙涂料的方法)，不得不依靠镁质涂料而提高使用寿命。
发明内容
本发明提供一种镁钙质中间包涂料，其含有65-85％的高钙镁砂、5-25％的低钙镁砂、1-5％的结合剂、1-5％的增塑剂和0.2-3％的硅微粉。
其中，高钙镁砂中CaO占38-45％，MgO+CaO不低于94％，且其颗粒体积密度不低于3.10g/cm3。
低钙镁砂中CaO占15-25％，MgO+CaO不低于94％，且其颗粒体积密度不低于3.10g/cm3。
结合剂为三聚磷酸钠或六偏磷酸钠，结合剂是为了增加涂料的强度；增塑剂为粘土，可增加涂料的塑性，便于涂料的涂抹和喷涂。
硅微粉为防水化剂不仅能降低氧化钙水化，还有减少加水量的作用，平均粒径D50不大于140nm。
另外，为达到高钙镁砂不水化的目的，本发明对该高钙镁砂预先进行过表面处理以隔离空气，即将97.9％的高钙镁砂升温至150℃-210℃，加入1.5％的氯化苯并***，表面处理数分钟，再加入0.6％的有机油。
上述有机油为甲基硅油或乙基硅油。
为了增加涂料的涂抹性，喷补附着率以及防爆裂，该镁钙质中间包涂料还可含有0.2-2％的有机纤维。
上述有机纤维为乙烯纤维或丙纶纤维。
将合格的原料按比例称量混和均匀即可。
本发明中所称百分比为重量百分比。
本发明是生产、施工、解体方便，具有净化钢水，抗冲刷耐侵蚀，使用寿命长的镁钙质涂料。
具体实施方式
下面用非限制性实施例进一步描述本发明。
实施例一：在A钢厂中间包施工现场，将组分为：表面处理过的高钙原料65％，低钙镁砂25％，三聚磷酸钠2％，粘土5％，硅微粉3％的涂料混和物倒入泥浆搅拌机内加水15％搅拌15分钟后进行中间包的涂抹，养生3小时后烘烤到1100℃开始受钢，钢种为优质钢，连浇6炉，受钢时间420分钟，熔损不明显，冷却后自动解体。
实施例二：在A钢厂中间包施工现场，将组分为：表面处理过高钙原料85％，低钙镁砂5％，六偏磷酸钠5％，粘土2.8％，硅微粉0.2％，纸纤维2％的涂料混和物倒入泥浆搅拌机内加水18％搅拌15分钟后进行中间包的涂抹，养生3小时后烘烤到1100℃开始受钢，钢种为普通钢，连浇11炉，受钢时间600分钟，熔损明显，冷却后自动解体。
实施例三：在A钢厂中间包施工现场，将组分为：表面处理过高钙原料79.6％，低钙镁砂18％，三聚磷酸钠1％，粘土1％，硅微粉0.2％，纸纤维0.2％的涂料混和物倒入泥浆搅拌机内加水16％搅拌15分钟后进行中间包的涂抹，养生3小时后烘烤到1100℃开始受钢，钢种为普通钢，连浇10炉，受钢时间550分钟，熔损不明显，冷却后自动解体。
实施例四：在A钢厂中间包施工现场，将组分为：表面处理过的高钙原料67％，低钙镁砂20％，六偏磷酸钠3％，粘土5％，硅微粉3％，纸纤维2％的涂料混和物倒入泥浆搅拌机内加水15％搅拌15分钟后进行中间包的涂抹，养生3小时后烘烤到1100℃开始受钢，钢种为优质钢，连浇8炉，受钢时间480分钟，熔损不明显，冷却后自动解体。
实施例五：在A钢厂中间包施工现场，将组分为：表面处理过高钙原料85％，低钙镁砂7％，三聚磷酸钠5％，粘土2.8％，硅微粉0.2％的涂料混和物倒入泥浆搅拌机内加水18％搅拌15分钟后进行中间包的涂抹，养生3小时后烘烤到1100℃开始受钢，钢种为普通钢，连浇10炉，受钢时间580分钟，熔损明显，冷却后自动解体。
实施例六：在A钢厂中间包施工现场，将组分为：表面处理过高钙原料80％，低钙镁砂16％，六偏磷酸钠1％，粘土1％，硅微粉2％的涂料混和物倒入泥浆搅拌机内加水16％搅拌15分钟后进行中间包的涂抹，养生3小时后烘烤到1100℃开始受钢，钢种为普通钢，连浇11炉，受钢时间600分钟，熔损不明显，冷却后自动解体。
在上述所有实施例中高钙镁砂产于辽宁华银集团，该高钙镁砂预先进行过表面处理，即将97.9％的高钙镁砂升温至150℃-210℃，加入1.5％的氯化苯并***，表面处理数分钟，再加入0.6％的有机油；低钙镁砂产于山东镁矿；粘土选用广西维罗泥或宜兴泥；硅微粉平均粒径要求不大于140nm。

Claims (10)

1、一种镁钙质中间包涂料，其特征在于含有65-85％的高钙镁砂、5-25％的低钙镁砂、1-5％的结合剂、1-5％的增塑剂和0.2-3％的硅微粉。
2、根据权利要求1所述的镁钙质中间包涂料，其特征在于该高钙镁砂中CaO占38-45％，MgO+CaO不低于94％，且其颗粒体积密度不低于3.10g/cm3。
3、根据权利要求1所述的镁钙质中间包涂料，其特征在于该低钙镁砂中CaO占15-25％，MgO+CaO不低于94％，且其颗粒体积密度不低于3.10g/cm3。
4、根据权利要求1所述的镁钙质中间包涂料，其特征在于该结合剂为三聚磷酸钠或六偏磷酸钠。
5、根据权利要求1所述的镁钙质中间包涂料，其特征在于该增塑剂为粘土。
6、根据权利要求1所述的镁钙质中间包涂料，其特征在于该硅微粉平均粒径不大于140nm。
7、根据权利要求1或2所述的镁钙质中间包涂料，其特征在于该高钙镁砂预先进行过表面处理，即将97.9％的高钙镁砂升温至150℃-210℃，加入1.5％的氯化苯并***，表面处理数分钟，再加入0.6％的有机油。
8、根据权利要求7所述的镁钙质中间包涂料，其特征在于该有机油为甲基硅油或乙基硅油。
9、根据权利要求1-6中任一权利要求所述的镁钙质中间包涂料，其特征在于还含有0.2-2％的有机纤维。
10、根据权利要求9所述的镁钙质中间包涂料，其特征在于该有机纤维为乙烯纤维或丙纶纤维。
CNA031156053A 2003-02-28 2003-02-28 镁钙质中间包涂料 Pending CN1524647A (zh)