CN1385072A - Nano silicate antibiosis composition and process for preparing same - Google Patents
Nano silicate antibiosis composition and process for preparing same Download PDFInfo
- Publication number
- CN1385072A CN1385072A CN 02102183 CN02102183A CN1385072A CN 1385072 A CN1385072 A CN 1385072A CN 02102183 CN02102183 CN 02102183 CN 02102183 A CN02102183 A CN 02102183A CN 1385072 A CN1385072 A CN 1385072A
- Authority
- CN
- China
- Prior art keywords
- nano
- parts
- dispersant
- zeolite
- based oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a nano silicate antibacterial compound and its preparation method. Said invention adopts nano technology and utilizes the control of components and contents of Zn(No3)2, NH4NO3, AgNO3 and silicone base oxide, etc and steps of preparation method to obtain the invented antibacterial compound with stable colour, good antibacterial broad-spectrum property, good physical, mechanical and optical properties. It can be used in low-temp. materials of plastics, fibre and paint, etc. and can produce special antibacterial effect.
Description
Technical field: the present invention relates to a kind of inorganic antibacterial composition, particularly a kind of nano silicate antibiosis composition that is used for cryogenic material processing such as fiber, plastics, coating and preparation method thereof.
Background technology: the silicate bactericidal composition is a kind of maximum inorganic antiseptic of using, Japanese Yamamoto unit in 1994 controls etc. and to disclose a kind of alkali metal or metal oxide antibacterial agent patents (spy opens flat 7-268653 1995) such as AgO, CuO, ZnO, people such as a middle island and a man of virtue and ability disclose a kind of stable zeolite and preparation method thereof patent (JP91-131513), and people such as Li Bizhong disclose a kind of bactericidal composition and preparation method thereof (CN1253729A).Above-mentioned disclosed bactericidal composition all belongs to the inorganic antiseptic made from inorganic carrier appendix antibacterial metal oxide.The main active ingredient of inorganic antiseptic mostly is oxides such as silver, zinc, copper greatly, therefore is widely used in fields such as ecological environment material nd, engineering material, biomaterial, structural timber.But the ubiquitous problem of these antibacterial agents is owing to contained Ag in the main component
+To the lability of light, easily make antibacterial agent variable color in use, influence is used and sense organ.Next is that all antibacterial agents are just used with other material is compound, and compound process is the process to the material modification, and the material after the modification should possess except that antibiotic, has other concurrently and helps the combination property that material is used.Foregoing antibacterial agent does not all possess this function.
Summary of the invention: the present invention is based on the problems referred to above, the applying nano technology, new prescription of synthesis of nano silicate bactericidal composition and preparation method thereof is proposed, with the stability that solves color and luster in the cryogenic material processing such as fiber, plastics, coating, antibiotic broad spectrum activity, and the nano silicate antibiosis composition with performances such as physics, mechanics, optics, to improve the range of application and the application level of anti-biotic material.
Nano silicate antibiosis composition of the present invention is to realize by following proportioning and preparation method, and the component and the content of its proportioning is (weight portion): Zn (NO
3)
22～75 parts, NH
4NO
30.5～5 parts, AgNO
30.2 100 parts of～5 parts, 0.5～2 part of dispersant, nano zeolite or nano silicon-based oxides.Its component and content of optimizing proportioning is (weight portion): Zn (NO
3)
260 parts, NH
4NO
32 parts, AgNO
3100 parts of 3 parts, 2 parts of dispersants, nano zeolite or nano silicon-based oxides.The component and the content of its best proportioning is (weight portion): Zn (NO
3)
260 parts, NH
4NO
31.5 part, AgNO
3The nano zeolite that 3 parts, dispersant are 1.5 parts, 1000 parts.Its preparation method is to follow these steps to carry out (weight portion): (1) gets 100 parts of zeolite powder or silicon-base oxide powders, with the deionized water is medium, put powder in autoclave, 100 ℃～300 ℃ of reaction temperatures, reaction time 1～4h, reaction pressure 15MPa makes nano zeolite powder of the present invention or nano silicon-based oxide powder.(2) get 100 parts nano zeolite powder or nano silicon-based oxide powder by weight, put in the baking oven under 110 ℃ of conditions, dry 30min takes out, add deionized water furnishing pulpous state, be heated to 75 ℃, stir 30～120min to boiling, the degassing, add 0%～5% salpeter solution and water again, regulate pH=5～7, it is stand-by to make slurry.(3) in deionized water, add 0.2～5 part AgNO
3, 2～75 parts Zn (NO
3)
2, 0.5～5 part NH
4NO
3, make the ion exchange aqueous solution.(4) above-mentioned nano zeolite slurry of making or nano silicon-based oxide slurry (2) are mixed with the above-mentioned ion exchange aqueous solution of making (3), be heated to 40 ℃～60 ℃, under this temperature, keep 4～12h to carry out ion exchange.(5) after ion exchange finishes, filter, separate, spend deionised water non-metallic ion to the solution.(6) add 0.5～2 part of dispersant in above-mentioned slurries, nano silicate antibiosis composition is promptly made in oven dry, grinding.
The nano silicate antibiosis composition that the present invention makes all has good restraining and sterilizing bacteria effect to staphylococcus aureus, Escherichia coli, bacillus subtilis, streptococcus, aspergillus flavus, Mucor racemosus etc. after testing.Bacteriostasis rate to Escherichia coli, staphylococcus aureus in 1 hour and 2 hours is respectively 95%, 97% and 97%, 99%; To pathogenic escherichia coli, staphylococcus aureus minimal bactericidal concentration is 0.05 μ g/ml; Its safety per os acute toxicity experience belongs to actual innocuous substance; Skin irritation test shows, belongs to nonirritant; The present invention is through 200h, and the accelerated ageing of 4500W xenon lamp is tested, and the difference of value of chromatism and tester aberration is Δ E≤0.1.The nano silicate antibiosis composition that the present invention makes is in adding polyamide material, be injected into the standard batten, according to GB/T1039-92 " plastics mechanical test method " standard detection mechanical property, compare with un-added tester, its impact strength has improved 18 times, tensile strength improves 10%, and tensile stretch improves 1.5 times, and modulus improves 10%; Hot property: the nano silicate antibiosis composition of every interpolation 5% in material, the heat distortion temperature of material can improve 30 ℃～50 ℃.Because this nano silicate antibiosis composition has good dispersiveness, can directly add to and make anti-biotic materials such as antibiotic plastic, anti-bacterial fibre, antibiotic paint in the materials such as plastics, fiber, coating; Also can be prepared into masterbatch in advance, add to again in the materials such as plastics, fiber, coating and make various antibacterial products.
Embodiment: embodiment 1 (weight portion): (1) gets 100 parts zeolite powder, is medium with the deionized water, puts powder in the 250ml autoclave, 100 ℃～300 ℃ of reaction temperatures, reaction time 1～4h, reaction pressure 15MPa makes nano zeolite powder of the present invention.(2) get 100 parts nano zeolite powder, put in the baking oven dry 30min under 110 ℃ of conditions, add 100ml deionized water furnishing pulpous state, be heated to 80 ℃, stir 60min simultaneously, the degassing adds salpeter solution and the water of 50ml again, regulates pH=5～7, and it is stand-by to make slurry.(3) in deionized water, add 0.2 part AgNO
3, 2 parts Zn (NO
3), 0.5 part NH
4NO
3, make the ion exchange aqueous solution.(4) the above-mentioned nano zeolite slurry of making (2) is mixed with the above-mentioned ion exchange aqueous solution of making (3), be heated to 40 ℃～60 ℃, under this temperature, keep 4～12h to carry out ion exchange.(5) after ion exchange finishes, filter, separate, spend deionised water non-metallic ion to the solution.(6) add 0.5 part dispersant (ST-237) in above-mentioned slurries, oven dry is ground, and promptly makes nano silicate antibiosis composition.
Embodiment 2: the Zn (NO that, gets (weight portion) 75 parts according to the method for embodiment 1
3)
2, 5 parts NH
4NO
3, 5 parts AgNO
3, 2 parts dispersant (OX-N102), 100 parts nano zeolite.
Embodiment 3: according to the method for embodiment 1, optimization proportioning of the present invention is: the Zn (NO that gets (weight portion) 60 parts
3)
2, 2 parts NH
4NO
3, 3 parts AgNO
3, 2 parts dispersant (OX-N102), 100 parts nano zeolite.
Embodiment 4: according to the method for embodiment 1, best proportioning of the present invention is: the Zn (NO that gets (weight portion) 60 parts
3)
2, 1.5 parts NH
4NO
3, 3 parts AgNO
3, 1.5 parts dispersant (HDP-3000), 1000 parts nano zeolite.
Embodiment 5: the Zn (NO that, gets (weight portion) 2 parts according to the method for embodiment 1
3)
2, 0.5 part NH
4NO
3, 0.2 part AgNO
3, 0.5 part dispersant (OX-N102), 100 parts nano silicon-based oxide.
Embodiment 6: the Zn (NO that, gets (weight portion) 75 parts according to the method for embodiment 1
3)
2, 5 parts NH
4NO
3, 5 parts AgNO
3, 2 parts dispersant (ST-237), 100 parts nano silicon-based oxide.
Embodiment 7: according to the method for embodiment 1, optimization proportioning of the present invention is (weight portion): 60 parts Zn (NO
3)
2, 2 parts NH
4NO
3, 3 parts AgNO
3, 2 parts dispersant (HDP-3000), 100 parts nano silicon-based oxide.
Embodiment 8: according to the method for embodiment 1, best proportioning of the present invention is (weight portion): 60 parts Zn (NO
3)
2, 1.5 parts NH
4NO
3, 3 parts AgNO
3, 1.5 parts dispersant (HDP-3000), 100 parts nano silicon-based oxide.
Claims (4)
1. nano silicate antibiosis composition, its component and content are as follows:
Constituent content
Zn(NO
3)
2 2～75
NH
4NO
3 0.5～5
AgNO
3 0.2～5
Dispersant 0.5～2
Nano zeolite or nano silicon-based oxide 100
Above proportioning is weight portion
2. a kind of nano silicate antibiosis composition according to claim 1, its component and content are as follows:
Constituent content
Zn(NO
3)
2 2～60
NH
4NO
3 0.5～2
A
gNO
3 0.2～3
Dispersant 0.5～2
Nano zeolite or nano silicon-based oxide 100
Above proportioning is weight portion
3. a kind of nano silicate antibiosis composition according to claim 1, dispersant wherein are ST-237, OX-N102 or HDP-3000.
4. a kind of nano silicate antibiosis composition according to claim 1, the preparation method of said composition follows these steps to carry out:
(1) getting zeolite powder or silicon-base oxide powder, is medium with the deionized water, puts powder in autoclave, 100 ℃～300 ℃ of reaction temperatures, and reaction time 1～4h, reaction pressure 15MPa makes nano zeolite powder of the present invention or nano silicon-based oxide powder.
(2) get 100 parts of nano zeolite powders or nano silicon-based oxide powder by weight, put in the baking oven under 110 ℃ of conditions, dry 30min takes out, add deionized water furnishing pulpous state, be heated to 75 ℃, stir 30～120min to boiling, the degassing, add 0%～5% salpeter solution and water again, regulate pH=5～7, it is stand-by to make slurry.
(3) in deionized water, add 0.2～5 part AgNO
3, 2～75 parts Zn (NO
3)
2, 0.5～5 part NH
4NO
3, make the ion exchange aqueous solution.
(4) above-mentioned nano zeolite slurry of making or nano silicon-based oxide slurry (2) are mixed with the above-mentioned ion exchange aqueous solution of making (3), be heated to 40 ℃～60 ℃, under this temperature, keep 4～12h to carry out ion exchange.
(5) after ion exchange finishes, filter, separate, spend deionised water non-metallic ion to the solution.
(6) add 0.5～2 part of dispersant in above-mentioned slurries, stir, nano silicate antibiosis composition is promptly made in oven dry, grinding.