CN1338435A - Process for treating cyclic cooling water - Google Patents
Process for treating cyclic cooling water Download PDFInfo
- Publication number
- CN1338435A CN1338435A CN 00121549 CN00121549A CN1338435A CN 1338435 A CN1338435 A CN 1338435A CN 00121549 CN00121549 CN 00121549 CN 00121549 A CN00121549 A CN 00121549A CN 1338435 A CN1338435 A CN 1338435A
- Authority
- CN
- China
- Prior art keywords
- acid
- accordance
- water
- add
- test
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A process for treating cyclic cooling water features that the alkaline substance is added to the cyclic cooling water to regulate its pH value to 9.4-14. Its advantages include low cossion and scaling, low pollution, simple operation and low cost.
Description
The present invention relates to the method for cycle of treatment water, exactly, is to be used to suppress the burn into fouling of circulating water system and the method for microbial reproduction.
The processing of recirculated cooling water 20th century the '30s be to prevent tosca by simply adding acid (recirculated water pH value is controlled at 6.5~7.5), to five, the sixties bring into use special-purpose water conditioner to carry out scale inhibition, inhibition and germicidal treatment.The beginning of the eighties, along with continuous research and development to water treatment agent, the water treatment scheme is also being updated, natural pH value (pH is 7.5~9.5) operating scheme that sour operating scheme develops into multiple formulations that adds by early stage poly-phosphate water conditioner, proposing in order to humic acid as CN1067230A is that the water treatment prescription of host is handled and contained ammonia recirculated water, the corrosion of suppression equipment and fouling preferably, operation also is simplified; It is main raw material that SU1175879 adopts the waste material of producing caprolactam, obtains a kind of water conditioner through pyroreaction, can reduce Corrosion rate in Carbon Steel etc. effectively.
But, the present corrosion inhibiting and descaling agent that uses is carbon containing, phosphoric all, these carbon sources and phosphorus source all are the good nutrition sources of microorganism, and above-mentioned pH scope helps microbial growth, and microorganism is bred in a large number, causes circulating water system to produce a large amount of biological clays and is deposited on the interchanger, the heat exchange efficiency of interchanger is reduced significantly, can not satisfy industrial requirement, cause the heavy corrosion and the perforation of equipment simultaneously, and form vicious cycle.Mainly by adding biocide, as chlorine, hypochlorite, dioxide peroxide etc., required dosage is higher, and still loses control of the breeding of microorganism sometimes to the microbiological manipulation of recirculated water for prior art.Biological clay to circulating water system formation, prior art generally is to add to have quaternary ammonium salts such as surface-active material such as dimethyl benzyl tetradecyl ammonium chloride, or biological enzyme formulation such as Shu Erguo (Surgo) etc. peel off and clean, though these methods all have certain peeling off and cleaning performance to biological clay, all can not degrade and kill biological clay.In addition, also there is foaming problem such as serious in quaternary ammonium salt, and there is problem such as cost an arm and a leg in Shu Erguo.When hardness in the water and basicity sum during less than 50mg/L, existing corrosion inhibiting and descaling agent ACU corrosive difficulty is bigger on the other hand, and when hardness in the water and basicity sum during greater than 250mg/L, the difficulty of ACU fouling is bigger.These problems not only make the circulating water treatment effect undesirable, and contaminate environment, waste water resource and increased the expense of handling.
The objective of the invention is to overcome the above-mentioned defective of prior art, a kind of method of simple, effective, economic cycle of treatment water coolant is provided, solve corrosion of circulating water system water cooler and fouling, microbial reproduction and biological clay such as grow at problem.
The method of cycle of treatment water coolant provided by the invention comprises: add alkaline matter and make its pH value reach 9.5~14 in recirculated cooling water.
The said alkaline matter of the present invention can be oxide compound, oxyhydroxide, carbonate or supercarbonate or its mixture of lithium, sodium and potassium, for example, can be NaOH, KOH, Na
2CO
3, K
2CO
3, NaHCO
3, KHCO
3, Na
2O, K
2O, Li
2O, LiOH, Li
2CO
3And LiHCO
3One of or two or more mixture wherein.Preferred NaOH and KOH.The concentration that adds of alkaline matter is 50~2000mg/L, preferred 150~800mg/L.In above-mentioned concentration range, the pH value of recirculated water is controlled at 9.5~14, and preferred 10.0~13.0.
Adopt the inventive method, in recirculated water, also can add other water conditioner in right amount, as inhibiter, Scale inhibitors and biocide etc., with problems such as the burn into fouling of further control generation in service and microbial growth.
Said inhibiter can be 1-Hydroxy Ethylidene-1,1-Diphosphonic Acid, hydroxyl phosphino-acetate, amido three methene phosphonic acids, ethylene diamine tetra methylene phosphonic acid, benzotriazole copper inhibitor etc.The consumption of inhibiter can be 0~300mg/L, preferred 50~100mg/L.
Said Scale inhibitors can be that the consumption of the terpolymer Scale inhibitors of copolymer, vinylformic acid and the AMPS of copolymer, vinylformic acid and AMPS (2-acrylamido-2-methyl propane sulfonic acid) of polyacrylic acid or salt, polymaleic anhydride, vinylformic acid and acrylate and maleic anhydride can be 0~300mg/L, preferred 50~100mg/L.
Said biocide can be selected from one of chlorine, clorox, potassium hypochlorite, Losantin, DICHLOROISOCYANURIC ACID, trichloroisocyanuric acid, dioxide peroxide, bromine, sodium hypobromite, potassium hypobromite, hypobromous acid calcium, quaternary ammonium salt and quaternary alkylphosphonium salt or two or more mixture wherein.Preferred clorox or DICHLOROISOCYANURIC ACID or trichloroisocyanuric acid, adding concentration is 0~300mg/L, preferred 5~50mg/L.
During with the inventive method cycle of treatment water, when recirculated water discharges, only need add mineral acid, regulate pH value to 6.5~8.5 and can discharge, free from environmental pollution.
The inventive method place all is suitable for greater than the various water quality of 25mg/L firmly to calcium.
Characteristics of the present invention are cycle of treatment water coolant under high pH value.As everyone knows, the pH value of recirculated water all has material impact to corrodibility, fouling tendency and the microbial reproduction of recirculated water.Prior art thinks that under low pH value, the corrodibility of water is strong, a little less than the fouling tendency, microorganism is easy to breeding, and next opposite in high pH value, a little less than the corrodibility of water, fouling tendency is strong, microorganism is difficult for breeding, and it is generally acknowledged that the pH value is higher than at 9.5 o'clock, and fouling tendency is difficult to control, therefore, do not retrieve the method that the pH value is higher than 9.5 cycle of treatment water as yet.
The present invention adopts the high pH value cycle of treatment water 9.5~14, has overcome the prejudice of prior art, has reached goal of the invention.This be because, under the low pH value that prior art adopts,, be deposited on the wall hard scale that formation is difficult to remove gradually because lime carbonate, magnesiumcarbonate formation speed are slower.And under the high pH value that the present invention adopts, circulating water flow absorbs a large amount of carbonic acid gas from air when water cooling tower, generate the soft dirt that lime carbonate, magnesiumcarbonate etc. suspend in water rapidly with calcium hydroxide in the water, magnesium hydroxide etc., along with mobile being easy to of recirculated water caught and be removed by the filter screen in the pipeline, the fouling tendency of water is reduced significantly.
Therefore, the present invention has following outstanding advantage:
1. destroyed the environment of microbial growth and breeding, can make in the recirculated water microorganism concn be controlled at 105/below the mL.
2. greatly reduce the corrodibility of recirculated water, corrosion of carbon steel speed can be controlled at below the 0.075mm/a.
3. greatly reduce the fouling degree on calcium in the water, magnesium ion concentration and the water cooler heat-transfer surface, adhere to speed and can be controlled at 20mg/cm
2.mon. in.
In addition, the inventive method is simple to operate, and processing costs is low, and is free from environmental pollution.
The invention will be further described below by embodiment, but therefore do not limit the present invention.
Embodiment 1
Present embodiment is the rotary hanging plate corrosion test, carries out with reference to HG/T2159-91.
Test water quality: the hard 25mg/L of calcium, the hard 10mg/L of magnesium, total alkalinity 30mg/L.
Add different concns NaOH in above-mentioned water quality, test-results sees Table 1.
The Corrosion results that table 1 obtains with the test of soft water quality
Embodiment 2 present embodiments are the rotary hanging plate corrosion test, carry out with reference to HG/T2159-91.Test water quality: the hard 80mg/L of calcium, the hard 30mg/L of magnesium, total alkalinity 110mg/L.Add different concns NaOH in above-mentioned water quality, test-results sees Table 2.
Embodiment 3 present embodiments are the rotary hanging plate corrosion test, carry out with reference to HG/T2159-91.Test water quality: the hard 250mg/L of calcium, the hard 110mg/L of magnesium, total alkalinity 310mg/L.Add different concns NaOH in above-mentioned water quality, test-results sees Table 3.
Embodiment 4
Present embodiment is tested firmly for calcium in the reduction water.
Test water quality: the hard 80mg/L of calcium, the hard 30mg/L of magnesium, total alkalinity 110mg/L.
Get 5 250mL Erlenmeyer flasks, add the NaOH of above-mentioned water quality of 200mL and different concns respectively, shake up, at room temperature left standstill 4 hours, use filter paper filtering, get filtrate with reference to calcium ion concn in the GB/T14636-93 methods analyst water.Test-results sees Table 4.
5 examples of embodiment are dynamic analog test.Test water quality: according to embodiment 2 preparations, add NaOH and make concentration reach 300mg/L, stir, at room temperature left standstill 24 hours, extract the make up water that supernatant liquid is done dynamic analog test.
Test is carried out with reference to HG/T2160-91 standard " water coolant dynamic simulation experiment method ".The 20# carbon steel test tube of 2 φ 10 * 1 * 530mm carries out parallel test, and test water is walked tube side.The heating of test tube external application saturated vapor, 30 ± 1 ℃ of control test water inflow temperatures, 10 ℃ of exit port water temperature difference, the recirculated water cycles of concentration is controlled at 3~4, and test was carried out 400 hours continuously.The erosion rate that obtains test tube is 0.031mm/a, adheres to speed 10.6mg/ (cm
2.mon.), in the water microorganism concn less than 10
5Individual/ml.
Claims (10)
1. the method for a cycle of treatment water coolant comprises: add alkaline matter and make its pH value reach 9.5~14 in recirculated cooling water.
2. in accordance with the method for claim 1, it is characterized in that said alkaline matter is selected from oxide compound, oxyhydroxide, carbonate and supercarbonate or its mixture of lithium, sodium and potassium.
3. in accordance with the method for claim 1, it is characterized in that the concentration that adds of said alkaline matter is 50~2000mg/L.
4. according to claim 1 or 3 described methods, it is characterized in that said pH value reaches 10~13.
5. in accordance with the method for claim 1, it is characterized in that to add the biocide that concentration is 0~300mg/L.
6. in accordance with the method for claim 5, it is characterized in that, said biocide is selected from one of chlorine, clorox, potassium hypochlorite, Losantin, DICHLOROISOCYANURIC ACID, trichloroisocyanuric acid, dioxide peroxide, bromine water, sodium hypobromite, potassium hypobromite, hypobromous acid calcium, quaternary ammonium salt and quaternary alkylphosphonium salt, or two or more mixture wherein.
7. in accordance with the method for claim 1, it is characterized in that, also can add the inhibiter of 0~300mg/L.
8. in accordance with the method for claim 7, it is characterized in that said inhibiter is selected from 1-Hydroxy Ethylidene-1,1-Diphosphonic Acid, hydroxyl phosphino-acetate, amido three methene phosphonic acids, ethylene diamine tetra methylene phosphonic acid and benzotriazole copper inhibitor.
9. in accordance with the method for claim 1, it is characterized in that, also can add the Scale inhibitors of 0~300mg/L.
10. in accordance with the method for claim 9, it is characterized in that said Scale inhibitors is selected from the terpolymer of copolymer, vinylformic acid and 2-acrylamido-2-methyl-propanesulfonic acid and maleic anhydride of copolymer, vinylformic acid and the 2-acrylamido-2-methyl-propanesulfonic acid of polyacrylic acid or salt, polymaleic anhydride, vinylformic acid and acrylate.