CN1244628C - 改良的聚氯乙烯丁腈橡胶电缆料 - Google Patents
改良的聚氯乙烯丁腈橡胶电缆料 Download PDFInfo
- Publication number
- CN1244628C CN1244628C CN 03131872 CN03131872A CN1244628C CN 1244628 C CN1244628 C CN 1244628C CN 03131872 CN03131872 CN 03131872 CN 03131872 A CN03131872 A CN 03131872A CN 1244628 C CN1244628 C CN 1244628C
- Authority
- CN
- China
- Prior art keywords
- polyvinyl chloride
- rubber
- cable material
- cable materials
- acrylonitrile butadiene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明是关于对聚氯乙烯丁腈橡胶电缆料的改进，其组成为：20-40%(重量)的聚氯乙烯树脂，5-15%的交联聚氯乙烯树脂，15-30%的增塑剂，5-15%的丁腈橡胶，20-40%的填充料，1.5-6%的无尘复合稳定剂。本发明电缆料既可获得橡胶的柔软性、良好的手感和亚光效果，而且还提高了机械物理和化学性能，耐油、耐磨、耐酸碱，使改性料具有塑料和橡胶的双重性能，不需硫化，用塑料在普通塑料挤出机就可挤出成型，且能得到与橡胶性能及外观相仿的亚光效果，可代替橡胶用于电线、电缆绝缘及护套。
Description
技术领域
本发明涉及一种电线、电缆料，尤其是具有橡胶外观特性的聚氯乙烯丁腈橡胶电缆料。
背景技术
普通橡胶电缆料，具有柔软、耐磨，因而被广泛用作移动场合电线、电缆绝缘和/或护套。然而，橡胶绝缘和/或护套成型对设备要求较高，设备投入成本大，成型工艺控制复杂，而且普通橡胶电缆料不耐油、不耐酸、碱。聚氯乙烯(PVC)护套虽成型工艺简单，但质地比较硬，而且不够耐磨，因此通常只能用作固定非移动场合电线、电缆绝缘和/或护套。人们为综合橡胶和聚氯乙烯两者优点，提出将两者混合改性，如《中国塑料制品配方大全》P101公开，由100份PVC、20-40份丁腈橡胶、5-10份活性碳酸钙、一定量稳定剂混合改性，制备电缆护套料和绝缘料。然而仅由PVC与丁腈橡胶混合改性，改性料的挤出温度偏高，不利于挤包成型，而且改性料表面光亮，达不到橡胶表面无光泽亚光效果。为达到消光效果，通常需另行采用砂磨工艺仿出橡胶外观亚光状态，后续工艺复杂；也有采用增加较大量的消光剂消光，然而单独采用增大消光剂消光措施，虽能降低光亮度，但又会导致材料疏松，混合物料间连接性变差，强度低，且较难挤包成型。
发明内容
本发明的目的在于克服上述已有技术的不足，提供一种具有橡胶特性及表面亚光效果，可加工性好的改良聚氯乙烯丁腈橡胶电缆料。
为达到上述目的，本发明改良的聚氯乙烯丁腈橡胶电缆料，其组成为：20-40wt％的聚氯乙烯树脂，5-15wt％的交联聚氯乙烯树脂，15-30wt％的增塑剂，5-15wt％的丁腈橡胶，20-40wt％的填充料，1.5-6wt％的无尘复合稳定剂。
此外本发明根据不同颜色要求，还可以外加适量颜料，如碳黑、碳白粉、及其它色料，形成各种颜色。
本发明中聚氯乙烯树脂(PVC)作为电缆料的基料，可以采用通常诸如分子量为1000-1300的中分子量聚氯乙烯树脂；也可以采用2500-4000的高分子量聚氯乙烯树脂，本发明中尤以采用高分子量聚氯乙烯树脂为好，有利于提高改善电缆料的柔软性。交联聚氯乙烯树脂(XLPVC)，与聚氯乙烯同作基料，主要可起到消光作用，产生亚光效果，同时其交联网状结构又可改善电缆料的机械物理性能。增塑剂，主要是降低树脂的熔化玻璃态温度，增加树脂流动性，以利于挤出成型，本发明为适应各种使用环境温度，使之在高温和低温下都具有较好的柔软性，一种较好方法是采用高温型和低温型增塑剂混合。丁腈橡胶用于改性聚氯乙烯，增加电缆料的柔软性，使之产生橡胶的柔软效果，同时可增强聚氯乙烯的耐油、耐酸碱和回弹性。填充料，与通常电缆填充料相仿，较常用的有活性碳酸钙和/或陶土，作护套料时，可以全部采用活性碳酸钙，以降低成本；作绝缘料，应掺以较大量的陶土或全部采用陶土填充料，以增强绝缘性能。无尘复合稳定剂，为通用稳定剂，主要起稳定作用。
本发明聚氯乙烯丁腈橡胶电缆料，由于采用交联聚氯乙烯树脂改性，不仅使电缆料可获得橡胶的柔软性、良好的手感和亚光效果，而且还提高了机械物理和化学性能，耐油、耐磨、耐酸碱，使改性料具有塑料和橡胶的双重性能，不需硫化，用塑料只要在普通塑料挤出机就可挤出成型，且能得到与橡胶性能及外观相仿的亚光效果，可代替橡胶用于电线、电缆绝缘及护套。
以下结合三个非限定性实施例，进一步说明本发明。
具体实施方式
实施例1：护套料，30份(重量)普通聚氯乙烯树脂，10份交联聚氯乙烯树脂，10份DOP，10份DOS或DOA，10份丁腈橡胶，25份活性碳酸钙，5份无尘复合稳定剂，少量色料。将物料称量经高速捏和混合，由双螺杆挤出机挤出造粒。
实施例2：绝缘料，20份普通聚氯乙烯树脂，8份交联聚氯乙烯树脂，12份的DOP，12份DOS或DOA，14份丁腈橡胶，15份活性碳酸钙，15份陶土，4份无尘复合稳定剂，少量色料。
实旋例3：绝缘料，35份分子量为2500-4000聚氯乙烯树脂，7份交联聚氯乙烯树脂，8份DOP，8份DOS或DOA，5份丁腈橡胶，17份活性碳酸钙，17份陶土，3份无尘复合稳定剂，少量色料。
Claims (6)
1、一种聚氯乙烯丁腈橡胶电缆料，其特征在于其组成为：20-40wt％的聚氯乙烯树脂，5-15wt％的交联聚氯乙烯树脂，15-30wt％的增塑剂，5-15wt％的丁腈橡胶，20-40wt％的填充料，1.5-6wt％的无尘复合稳定剂。
2、根据权利要求1所述聚氯乙烯丁腈橡胶电缆料，其特征在于外加有适量着色颜料。
3、根据权利要求1或2所述聚氯乙烯丁腈橡胶电缆料，其特征在于所说聚氯乙烯树脂为分子量2500-4000的高分子聚氯乙烯树脂。
4、根据权利要求3所述聚氯乙烯丁腈橡胶电缆料，其特征在于所说增塑剂为高温型和低温型混合增塑剂。
5、根据权利要求3所述聚氯乙烯丁腈橡胶电缆料，其特征在于所说填充料为活性碳酸钙和/或陶土。
6、根据权利要求4所述聚氯乙烯丁腈橡胶电缆料，其特征在于所说填充料为活性碳酸钙和/或陶土。