CN116874279B - 具有镂空绿纹的粉底釉面陶瓷及其制备方法 - Google Patents
具有镂空绿纹的粉底釉面陶瓷及其制备方法 Download PDFInfo
- Publication number
- CN116874279B CN116874279B CN202310877742.1A CN202310877742A CN116874279B CN 116874279 B CN116874279 B CN 116874279B CN 202310877742 A CN202310877742 A CN 202310877742A CN 116874279 B CN116874279 B CN 116874279B
- Authority
- CN
- China
- Prior art keywords
- parts
- green body
- glaze
- green
- hollowed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及陶瓷制备技术领域，具体涉及一种具有镂空绿纹的粉底釉面陶瓷及其制备方法，陶瓷包括坯体和面釉，所述坯体上雕刻有贯通坯体的纹路，所述面釉覆盖于坯体表面并填充坯体的纹路，纹路内的面釉呈现绿色，坯体为白瓷，面釉为透明釉，涂抹于坯体釉面上的低浓度着色氧化物使得釉面呈现淡粉色，釉烧过程中坯体内部高浓度的着色氧化物使镂空纹路内的釉面呈现绿色，陶瓷顶部设有透光孔，加上镂空纹路本身也会透光，将外界光线引入坯体内，整体形成具有镂空绿纹的粉底釉面陶瓷，镂空绿纹为透明纹路，晶莹剔透，独具美感。
Description
技术领域
本发明涉及陶瓷制备技术领域，具体的涉及具有镂空绿纹的粉底釉面陶瓷及其制备方法。
背景技术
釉是一种硅酸盐，陶瓷器上所施的釉一般以石英、长石、粘土为原料，经研磨、加水调制后，涂敷于坯体表面，经一定温度的焙烧而熔融，温度下降时，形成陶瓷表面的玻璃质薄层。它使陶瓷器增加机械强度、热稳定性、介电强度和防止液体、气体的侵蚀。釉还有增加瓷器美观和便于洗拭、不被尘土粘染等作用。现有的釉面若想要呈现不同颜色的釉面交织，特别是在具有底色的面釉上实现不同颜色的纹路，往往是通过先在坯体上施加彩绘，再施加面釉来实现，但是该纹路不具有透光性，釉面表现形式较为单一，有鉴于此，本案由此产生。
发明内容
本发明的一个目的是通过具有镂空绿纹的粉底釉面陶瓷及其制备方法解决至少上述问题。
为解决上述技术问题，本发明采用的技术方案如下：具有镂空绿纹的粉底釉面陶瓷，其特征在于：包括坯体和面釉，所述坯体上雕刻有贯通坯体的纹路，所述面釉覆盖于坯体表面并填充坯体的纹路，纹路内的面釉呈现绿色，所述面釉的原料以重量份计，包括如下组分：霞石正长石30-40份、硅矿石15-20份、碳酸钙15-20份、硼酸钙10-15份、高岭土15-20份、氧化锌5-8份、膨润土6-8份、球土3-5份、燧石5-6份，所述坯体的原料以重量份计，包括如下组分：德化高岭土45-55份、钾长石20-25份、黏土10-15份、燧石10-15份、石英12-16份、菱镁石14-18份、碳酸钙5-10份。
优选的，所述面釉的原料以重量份计，包括如下组分：霞石正长石35份、硅矿石18份、碳酸钙18份、硼酸钙13份、高岭土18份、氧化锌7份、膨润土7份、球土4份、燧石5.5份，所述坯体的原料以重量份计，包括如下组分：德化高岭土50份、钾长石23份、黏土13份、燧石14份、石英14份、菱镁石16份、碳酸钙8份。
优选的，所述面釉的原料以重量份计，包括如下组分：霞石正长石30份、硅矿石15份、碳酸钙15份、硼酸钙10份、高岭土15份、氧化锌5份、膨润土6份、球土3份、燧石5份，所述坯体的原料以重量份计，包括如下组分：德化高岭土45份、钾长石20份、黏土10份、燧石10份、石英12份、菱镁石14份、碳酸钙5份。
优选的，所述面釉的原料以重量份计，包括如下组分：霞石正长石40份、硅矿石20份、碳酸钙20份、硼酸钙15份、高岭土20份、氧化锌8份、膨润土8份、球土5份、燧石6份，所述坯体的原料以重量份计，包括如下组分：德化高岭土55份、钾长石25份、黏土15份、燧石15份、石英16份、菱镁石18份、碳酸钙10份。
上述的具有镂空绿纹的粉底釉面陶瓷的制备方法，包括如下步骤：
步骤a、成型坯体，坯体底部设有开口，干燥坯体；
步骤b、在坯体上雕刻镂空的纹路，该镂空的纹路贯穿坯体的内外表面，坯体顶部开设透光孔；
步骤c、在镂空纹路和透光孔内填充石蜡；
步骤d、在坯体表面上面釉，烘干；
步骤e、施釉的坯体进行釉烧前放置于釉烧底座上，釉烧底座顶部的中心设有用于容纳着色混合物的腔体，往腔体内填充高浓度着色混合物后，将坯体放置于釉烧底座上，使腔***于坯体底部的开口内；
步骤f、在釉面上涂抹低溶度的着色混合物；
步骤g、在坯体放置于釉烧底座上一起进入窑炉釉烧，釉烧过程中，坯体内部的高浓度着色混合物在高温下挥发，挥发的着色氧化物附着于坯体内部以及镂空纹路内的面釉内侧，高浓度的着色氧化物使镂空纹路内的面釉内侧呈现绿色；涂抹于坯体表面的着色氧化物溶度较低，釉烧后呈淡粉色；
步骤h、釉烧后取出陶瓷，陶瓷的釉面呈现淡粉色、并分布有绿色纹路。
优选的，所述步骤d中，施釉的坯体先自然干燥，然后入烘干线烘干，并将石蜡挥发。
优选的，所述步骤d中，所述烘干线上设有移动的托盘，所述托盘的中心设有通风口，所述施釉后的坯体放置于托盘上，所述托盘中心的通风口位于坯体底部的开口内，所述托盘下方设有向上鼓风的风扇，施釉后的坯体在通过烘干线时，坯体内部的石蜡经加热后挥发，并通过底部的开口挥发至坯体外部，鼓风机往坯体内部鼓风加速石蜡挥发。
优选的，所述步骤e中，在釉烧底座的顶部设有环形限位槽，所述坯体底部设有圈足，所述环形限位槽与圈足形状匹配，所述坯体放置于釉烧底座上时，其圈足嵌入所述环形限位槽内。
优选的，所述着色混合物的原料以重量份计，包括如下组分：氧化锡60-70份、氧化铬20-30份、氧化硅10-15份。
优选的，所述釉烧过程中，放置于位于坯体内部的高浓度着色混合物的质量含水率为20-30％，所述釉烧过程中，涂抹于坯体外部的低浓度着色混合物的质量含水率为70-80％。
由上述描述可知，本发明提供的具有镂空绿纹的粉底釉面陶瓷及其制备方法具有如下有益效果：坯体为白瓷，面釉为透明釉，涂抹于坯体釉面上的低浓度着色氧化物使得釉面呈现淡粉色，釉烧过程中坯体内部高浓度的着色氧化物使镂空纹路内的釉面呈现绿色，陶瓷顶部设有透光孔，加上镂空纹路本身也会透光，将外界光线引入坯体内，整体形成具有镂空绿纹的粉底釉面陶瓷，镂空绿纹为透明纹路，晶莹剔透，独具美感。
具体实施方式
以下通过具体实施方式对本发明作进一步的描述。
为使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施方式，进一步阐述本发明。
本发明具有镂空绿纹的粉底釉面陶瓷，包括坯体和面釉，坯体上雕刻有贯通坯体的纹路，面釉覆盖于坯体表面并填充坯体的纹路，纹路内的面釉呈现绿色，面釉的原料以重量份计，包括如下组分：霞石正长石30-40份、硅矿石15-20份、碳酸钙15-20份、硼酸钙10-15份、高岭土15-20份、氧化锌5-8份、膨润土6-8份、球土3-5份、燧石5-6份，坯体的原料以重量份计，包括如下组分：德化高岭土45-55份、钾长石20-25份、黏土10-15份、燧石10-15份、石英12-16份、菱镁石14-18份、碳酸钙5-10份。
作为优选实施例，面釉的原料以重量份计，包括如下组分：霞石正长石35份、硅矿石18份、碳酸钙18份、硼酸钙13份、高岭土18份、氧化锌7份、膨润土7份、球土4份、燧石5.5份，坯体的原料以重量份计，包括如下组分：德化高岭土50份、钾长石23份、黏土13份、燧石14份、石英14份、菱镁石16份、碳酸钙8份。
作为优选实施例，面釉的原料以重量份计，包括如下组分：霞石正长石30份、硅矿石15份、碳酸钙15份、硼酸钙10份、高岭土15份、氧化锌5份、膨润土6份、球土3份、燧石5份，坯体的原料以重量份计，包括如下组分：德化高岭土45份、钾长石20份、黏土10份、燧石10份、石英12份、菱镁石14份、碳酸钙5份。
作为优选实施例，面釉的原料以重量份计，包括如下组分：霞石正长石40份、硅矿石20份、碳酸钙20份、硼酸钙15份、高岭土20份、氧化锌8份、膨润土8份、球土5份、燧石6份，坯体的原料以重量份计，包括如下组分：德化高岭土55份、钾长石25份、黏土15份、燧石15份、石英16份、菱镁石18份、碳酸钙10份。
上述的具有镂空绿纹的粉底釉面陶瓷的制备方法，包括如下步骤：
步骤a、成型坯体，坯体底部设有开口，干燥坯体；
步骤b、在坯体上雕刻镂空的纹路，该镂空的纹路贯穿坯体的内外表面，坯体顶部开设透光孔；
步骤c、在镂空纹路和透光孔内填充石蜡；
步骤d、在坯体表面上面釉，烘干；
步骤e、施釉的坯体进行釉烧前放置于釉烧底座上，釉烧底座顶部的中心设有用于容纳着色混合物的腔体，往腔体内填充高浓度着色混合物后，将坯体放置于釉烧底座上，使腔***于坯体底部的开口内；
步骤f、在釉面上涂抹低溶度的着色混合物；
步骤g、在坯体放置于釉烧底座上一起进入窑炉釉烧，釉烧过程中，坯体内部的高浓度着色混合物在高温下挥发，挥发的着色氧化物附着于坯体内部以及镂空纹路内的面釉内侧，高浓度的着色氧化物使镂空纹路内的面釉内侧呈现绿色；涂抹于坯体表面的着色氧化物溶度较低，釉烧后呈淡粉色；坯体内部空间较小，加上着色氧化物的溶度较高，因此挥发后的坯体内部的着色氧化物浓度高，附着于镂空纹路的面釉内侧的氧化物溶度也就比较高，而高溶度的氧化铬、氧化锡混合物在釉烧中呈现绿色；而釉面表面涂抹低浓度的着色混合物，由于在加热过程中会挥发至整个窑炉内，因此釉烧后附着于面釉上的着色混合物含量少，使釉面呈现淡淡的粉色。
步骤h、釉烧后取出陶瓷，陶瓷的釉面呈现淡粉色、并分布有绿色纹路。坯体为白瓷，面釉为透明釉，涂抹于坯体釉面上的低浓度着色氧化物使得釉面呈现淡粉色，陶瓷顶部设有透光孔，加上镂空纹路本身也会透光，将外界光线引入坯体内，镂空纹路呈现绿色，形成具有镂空绿纹的粉底釉面陶瓷，镂空绿纹为透明纹路，晶莹剔透，整体独具美感。
步骤d中，施釉的坯体先自然干燥，然后入烘干线烘干，并将石蜡挥发。纹路内的石蜡经烘干线的加热后挥发，在后续的釉烧过程中，着色氧化物能够附着于纹路的釉面内侧。
步骤d中，烘干线上设有移动的托盘，托盘的中心设有通风口，施釉后的坯体放置于托盘上，托盘中心的通风口位于坯体底部的开口内，托盘下方设有向上鼓风的风扇，施釉后的坯体在通过烘干线时，坯体内部的石蜡经加热后挥发，并通过底部的开口挥发至坯体外部，鼓风机往坯体内部鼓风加速石蜡挥发。
步骤e中，在釉烧底座的顶部设有环形限位槽，坯体底部设有圈足，环形限位槽与圈足形状匹配，坯体放置于釉烧底座上时，其圈足嵌入环形限位槽内。
着色混合物的原料以重量份计，包括如下组分：氧化锡60-70份、氧化铬20-30份、氧化硅10-15份。
釉烧过程中，放置于位于坯体内部的高浓度着色混合物的质量含水率为20-30％，釉烧过程中，涂抹于坯体外部的低浓度着色混合物的质量含水率为70-80％。当着色混合物浓度较高时，其附着于釉面上形成绿色，当着色氧化物浓度较高时，其附着于釉面上形成淡粉色，附着釉面上的着色混合物的含量高低除了跟初始着色氧化物的浓度有关，还跟其所处的空间大小有关，由于坯体内部的空间密闭，其最终附着于纹路内釉面内的着色氧化物含量较高，使其纹路呈现绿色，反之，釉面上的着色氧化物含量较低，则呈现淡粉色。
上述仅为本发明的若干具体实施方式，但本发明的设计构思并不局限于此，凡利用此构思对本发明进行非实质性的改动，均应属于侵犯本发明保护范围的行为。
Claims (4)
1.具有镂空绿纹的粉底釉面陶瓷，其特征在于：包括坯体和面釉，所述坯体上雕刻有贯通坯体的纹路，所述面釉覆盖于坯体表面并填充坯体的纹路，纹路内的面釉呈现绿色，所述面釉的原料以重量份计，包括如下组分：霞石正长石30-40份、硅矿石15-20份、碳酸钙15-20份、硼酸钙10-15份、高岭土15-20份、氧化锌5-8份、膨润土6-8份、球土3-5份、燧石5-6份，所述坯体的原料以重量份计，包括如下组分：德化高岭土45-55份、钾长石20-25份、黏土10-15份、燧石10-15份、石英12-16份、菱镁石14-18份、碳酸钙5-10份；
所述的具有镂空绿纹的粉底釉面陶瓷的制备方法，包括如下步骤：
步骤a、成型坯体，坯体底部设有开口，干燥坯体；
步骤b、在坯体上雕刻镂空的纹路，该镂空的纹路贯穿坯体的内外表面，坯体顶部开设透光孔；
步骤c、在镂空纹路和透光孔内填充石蜡；
步骤d、在坯体表面上面釉，烘干；
步骤e、施釉的坯体进行釉烧前放置于釉烧底座上，釉烧底座顶部的中心设有用于容纳着色混合物的腔体，往腔体内填充高浓度着色混合物后，将坯体放置于釉烧底座上，使腔***于坯体底部的开口内；
步骤f、在釉面上涂抹低溶度的着色混合物；
步骤g、在坯体放置于釉烧底座上一起进入窑炉釉烧，釉烧过程中，坯体内部的高浓度着色混合物在高温下挥发，挥发的着色氧化物附着于坯体内部以及镂空纹路内的面釉内侧，高浓度的着色氧化物使镂空纹路内的面釉内侧呈现绿色；涂抹于坯体表面的着色氧化物溶度较低，釉烧后呈淡粉色；
步骤h、釉烧后取出陶瓷，陶瓷的釉面呈现淡粉色、并分布有绿色纹路；
所述步骤d中，施釉的坯体先自然干燥，然后入烘干线烘干，并将石蜡挥发；
所述步骤d中，所述烘干线上设有移动的托盘，所述托盘的中心设有通风口，所述施釉后的坯体放置于托盘上，所述托盘中心的通风口位于坯体底部的开口内，所述托盘下方设有向上鼓风的风扇，施釉后的坯体在通过烘干线时，坯体内部的石蜡经加热后挥发，并通过底部的开口挥发至坯体外部，鼓风机往坯体内部鼓风加速石蜡挥发；
所述步骤e中，在釉烧底座的顶部设有环形限位槽，所述坯体底部设有圈足，所述环形限位槽与圈足形状匹配，所述坯体放置于釉烧底座上时，其圈足嵌入所述环形限位槽内；
所述着色混合物的原料以重量份计，包括如下组分：氧化锡60-70份、氧化铬20-30份、氧化硅10-15份；
所述釉烧过程中，放置于位于坯体内部的高浓度着色混合物的质量含水率为20-30%，所述釉烧过程中，涂抹于坯体外部的低浓度着色混合物的质量含水率为70-80%。
2.根据权利要求1所述的具有镂空绿纹的粉底釉面陶瓷，其特征在于：所述面釉的原料以重量份计，包括如下组分：霞石正长石35份、硅矿石18份、碳酸钙18份、硼酸钙13份、高岭土18份、氧化锌7份、膨润土7份、球土4份、燧石5.5份，所述坯体的原料以重量份计，包括如下组分：德化高岭土50份、钾长石23份、黏土13份、燧石14份、石英14份、菱镁石16份、碳酸钙8份。
3.根据权利要求1所述的具有镂空绿纹的粉底釉面陶瓷，其特征在于：所述面釉的原料以重量份计，包括如下组分：霞石正长石30份、硅矿石15份、碳酸钙15份、硼酸钙10份、高岭土15份、氧化锌5份、膨润土6份、球土3份、燧石5份，所述坯体的原料以重量份计，包括如下组分：德化高岭土45份、钾长石20份、黏土10份、燧石10份、石英12份、菱镁石14份、碳酸钙5份。
4.根据权利要求1所述的具有镂空绿纹的粉底釉面陶瓷，其特征在于：所述面釉的原料以重量份计，包括如下组分：霞石正长石40份、硅矿石20份、碳酸钙20份、硼酸钙15份、高岭土20份、氧化锌8份、膨润土8份、球土5份、燧石6份，所述坯体的原料以重量份计，包括如下组分：德化高岭土55份、钾长石25份、黏土15份、燧石15份、石英16份、菱镁石18份、碳酸钙10份。