CN1168530A - 耐火合成云母带及其生产工艺 - Google Patents

耐火合成云母带及其生产工艺 Download PDF

Info

Publication number
CN1168530A
CN1168530A CN 96119156 CN96119156A CN1168530A CN 1168530 A CN1168530 A CN 1168530A CN 96119156 CN96119156 CN 96119156 CN 96119156 A CN96119156 A CN 96119156A CN 1168530 A CN1168530 A CN 1168530A
Authority
CN
China
Prior art keywords
synthetic mica
mica tape
alkali
free glass
paper
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 96119156
Other languages
English (en)
Other versions
CN1044647C (zh
Inventor
陈云生
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN96119156A priority Critical patent/CN1044647C/zh
Publication of CN1168530A publication Critical patent/CN1168530A/zh
Application granted granted Critical
Publication of CN1044647C publication Critical patent/CN1044647C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

一种绝缘材料及其生产工艺，特别是合成云母带及其生产工艺，合成云母带分单面合成云母带和双面合成云母带，经在合成云母纸上面层涂以经稀释粘结剂(单面)或上下面层涂以粘结剂(双面)，再在上面层或上、下面层压入无碱玻璃布，辊压，烘干，收卷，切割检验即得。采用本发明的耐火合成云母带制作的耐火电线电缆，对于消除由于电线电缆短路引起的火灾起到非常积极的作用。利用其耐高温及优良的绝缘性能，在电热器具中应用可延长产品的寿命和提高安全性能，可广泛应用于耐火电线电缆、电加热器具、高温消防手套、服装等领域。本发明的生产工艺简单、合理。

Description

耐火合成云母带及其生产工艺
本发明涉及一种绝缘材料及其生产工艺，特别是合成云母(晶体云母)带及其生产工艺。
由于电力供应紧张，超负荷用电等原因，给安全防火工作带来一定的隐患，目前最行之有效的解决该隐患的办法就是采用耐火电线电缆，其基本原理是在导体外层加上防火云母带，避免短路时过热而向外燃烧。耐火云母带多为有机硅玻璃金云母带，它是天然云母与有机硅玻璃布粘接而成，这种金云母带在840℃以下，具有较好的绝缘性和不燃性，属于国际耐火云母带B级，但它存在耐高温、耐火效果略差的缺点。
本发明的目的在于提供一种耐火、耐高温效果更好的合成云母带及其生产工艺。
本发明是这样实现的。
合成云母带分单面与双面合成云母带，单面云母带结构为三层，依次为无碱玻璃布层、粘胶层、合成云母纸层，双面云母带结构为五层，依次为无碱玻璃布层、粘胶层、合成云母纸层、粘胶层、无碱玻璃布层，其中无碱玻璃布的成分是SiO2(54.1±0.7)、Al2O3(15.0±0.5)、CaO(16.5±0.5)、MgO(4.5±0.5)、B2O3(9.0±0.5)、Na2O＜0.5，可采用上海耀华玻璃厂生产的Q-40、Q-30、Q-25型；粘胶层采用的粘结剂为有机硅树脂，它是以硅氧键(Si-O-)为主链的聚合物，产地为日本信越化学工业株式会社，以型号为KR101-10、T102、Y3344型为佳，耐高温600℃以上，合成云母纸单体为鳞片状晶体结构，经制浆，造纸而得，它的成分为(重量百分比)SiO2 38.37％、Al2O312.11％、Fe2O3 1.02％、MgO 28.43％、K2O 11.16％、Na2O 0.02％、F 8.89％。
单面合成云母带的粘结剂的胶浓度为13～16％，双面合成云母带的胶浓度为9～26％，以甲苯、异丙醇为溶剂，增加吹干剂过氧化苯酰来溶解稀释；合成云母带成品厚度为0.09～0.20mm。粘结剂用量是9～30g/m2，单面合成云母带云母纸含量70～220g/m2，厚度0.04～0.14mm，无碱玻璃布含量23～31g/m2，双面合成云母带云母纸含量70～220g/m2，厚度0.04～0.14mm，无碱玻璃布含量是28～51g/m2。
本发明的生产工艺为，取无碱玻璃布，在无碱玻璃布上涂以经稀释的粘结剂，再压入合成云母纸(单面带云母纸在上方，双面带云母纸在中间，上、下方均有无碱玻璃布)，辊压，压力为1.5～2.5kg/m2，在100～280℃烘干，收卷，切割机切割，经检验合格后，即得。
本发明的合成云母带将自然云母带(耐温750～800℃)的耐温提高到950～1200℃，耐火等级从国际耐火云母带B级提高到A级。
经机械工业部广州电器科学研究所检验，采用管型喷灯，通过液化石油气燃烧，用长1200mm、规格0.09mm云母带绕在导体上，使三根线呈三角形集束，制成试验电缆，喷口与本发明的耐火云母带试样表面距离75mm，燃烧时间90min，火焰温度975℃，施加试验电压0.6KV的情况下，3A熔丝未熔断，符合A级水平；1000℃/1h，云母无脱落分层现象；高温绝缘电阻试验，厚度为0.09mm样品500℃实测800MΩ；燃烧性试验，移去火焰后即熄灭。
采用本发明的耐火合成云母带制作的耐火电线电缆，对于消除由于电线电缆短路引起的火灾起到非常积极的作用。利用其耐高温及优良的绝缘性能，在电热器具中应用可延长产品的寿命和提高安全性能，可广泛应用于耐火电线电缆、电加热器具、高温消防手套、服装等领域。本发明的生产工艺简单、合理。
下面叙述实施例。
实施例1：单面合成云母带
合成云母纸为鳞片状晶体结构，其中80目以上占68～95％，经制浆，制成合成云母纸。云母纸含量为70～220g/m2，厚度为0.04～0.14mm。
在无碱玻璃布上面层涂以13～16％和过氧化苯酰为吹干剂的有机硅树脂粘结剂，如日本信越化学工业株式会社生产的KR101-10、T102、Y3344型树脂，用量为9～30g/m2，其中溶剂为甲苯或异丙醇。
在无碱玻璃布下压入合成云母纸，无碱玻璃布含量为23～31g/m2，经辊压，压力为1.5～2.5kg/m2，在100～280℃烘干，收卷，切割机切割，经检验合格后，即得。
实施例2：双面合成云母带
合成云母纸为鳞片状晶体结构，其中80目以上占68～95％，经制浆、制成合成云母纸。云母纸含量为70～220g/m2，厚度为0.04～0.14mm。
在无碱玻璃布上涂以9～26％的过氧化苯酰为吹干剂的有机硅树脂粘结剂，如日本信越化学工业株式会社生产的KR101-10、T102、Y3344型树脂，用量为9～30g/m2，其中溶剂为甲苯或异丙醇。
在云母纸上、下面压入无碱玻璃布，粘连剂面朝向云母纸，无碱玻璃布含量28～51g/m2，经辊压，压力为1.5～2.5kg/m2，在100～280℃烘干，收卷，切割机切割，经检验合格后，即得。

Claims (7)

1.一种绝缘材料，为合成云母带，合成云母带分单面与双面合成云母带，单面云母带结构为三层，依次为无碱玻璃布层、粘胶层、合成云母纸层，双面云母带结构为五层，依次为无碱玻璃布层、粘胶层、合成云母纸层、粘胶层、无碱玻璃布层，其中无碱玻璃布的成分是SiO2(54.1±0.7)、Al2O3(15.0±0.5)、CaO(16.5±0.5)、MgO(4.5±0.5)、B2O3(9.0±0.5)、Na2O＜0.5，可采用上海耀华玻璃厂生产的Q-40、Q-30、Q-25型；粘胶层采用的粘结剂为有机硅树脂，它是以硅氧键(Si-O-)为主链的聚合物，产地为日本信越化学工业株式会社，以型号为KR101-10、T102、Y3344型为佳，耐高温600℃以上，合成云母纸单体为鳞片状晶体结构，经制浆，造纸而得，它的成分为(重量百分比)SiO2 38.37％、Al2O3 12.11％、Fe2O3 1.02％、MgO 28.43％、K2O 11.16％、Na2O 0.02％、F8.89％。
2.根据权利要求1所述的绝缘材料，其特征在于合成云母带厚度为0.09～0.20mm。
3.根据权利要求1所述的绝缘材料，其特征在于合成云母带粘结剂用量为9～30g/m2。
4.根据权利要求1所述的绝缘材料，其特征在于合成云母带云母纸含量为70～220g/m2，厚度为0.04～0.14mm。
5.根据权利要求1所述的绝缘材料，其特征在于合成云母带无碱玻璃布含量为单面合成云母带23～31g/m2，双面合成云母带28～51g/m2。
6.一种如权利要求1所述绝缘材料的生产工艺，有以下步骤：取无碱玻璃布，在无碱玻璃布上涂以经稀释的粘结剂，再压入合成云母纸(单面带云母纸在上方，双面带云母纸在中间，上、下方均有无碱玻璃布)，辊压，烘干，收卷，切割机切割，经检验合格后，即得。
7.根据权利要求6所述的绝缘材料的生产工艺，其特征在于辊压压力为1.5～2.5kg/m2，在100～280℃烘干。
CN96119156A 1996-02-14 1996-10-07 耐火合成云母带及其生产工艺 Expired - Fee Related CN1044647C (zh)