CN102277641A - 黏胶冰凉纤维长丝及其生产方法 - Google Patents
黏胶冰凉纤维长丝及其生产方法 Download PDFInfo
- Publication number
- CN102277641A CN102277641A CN2010102002145A CN201010200214A CN102277641A CN 102277641 A CN102277641 A CN 102277641A CN 2010102002145 A CN2010102002145 A CN 2010102002145A CN 201010200214 A CN201010200214 A CN 201010200214A CN 102277641 A CN102277641 A CN 102277641A
- Authority
- CN
- China
- Prior art keywords
- viscose
- mica
- fiber filament
- sections
- cool fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种黏胶冰凉纤维长丝及其生产方法,其中云母锦纶冰凉纤维长丝按照重量百分比包括以下两种成分:纳米云母3-5%,黏胶4切片95-97%。本发明的云母黏胶冰凉纤维长丝相对于常规的黏胶纤维,不仅消除了原有的缺点,还增加了以下新的优点:(1)抗静电功能;(2)导热、吸水功能:由于云母本身为片状矽酸盐结构,其导热效果优于PA6本身,而脱层后的云母本身形成的水合效应,易形成一层水化膜,具有导热和含水的双重效果;(3)消臭功能:脱层云母的比表面积高于450M2/G,此种高比表面积,使其吸附异味的效果由于其他矿石甚至云母自身,高比表面积具有类似活性炭分解臭味分子效果,所以不需要香味就可以消臭。
Description
技术领域
本发明涉及一种纤维长丝及其生产方法,特别是涉及一种添加了纳米云母黏胶冰凉纤维长丝及其生产方法。
背景技术
锦纶纤维(PA)是合成纤维中工业化生产最早的品种,其品种很多,常用的主要有锦纶6(PA6)和锦纶66(PA66)。锦纶的产量仅次于涤纶,其产品以长丝为主,民用上主要用于做袜子、围巾、长丝织物及刷子的丝,还可用于织制地毯等;工业上可用于制造轮胎帘子线、绳索、渔网等;国防上主要用于织制降落伞等。锦纶纤维为熔体纺丝纤维。截面、纵形态与涤纶相似。它具有以下优点:(1)吸湿能力是常见合成纤维中较好的,在一般大气条件下回潮率可达4.5%左右,有些品种如锦纶4可达7%。(2)耐磨性好:是常见纺织纤维中最好的;(3)染色性能好,也具有如下缺点:(1)小负荷下容易变形,所以织物保形性和硬挺性不及涤纶织物;(2)耐热、耐晒性较差,晒后发黄发脆。遇火种会熔成小孔。
云母是一种无色透明的层状矽酸盐,本身化学性安定,其熔点高达1300度,且在高温550度以下性质完全不改变,其特点为:抗紫外线、耐高温、水合性强、具有珍珠光泽、折射亮度高。主要应用于化妆品、防火建材、塑胶、造纸、油漆涂料和焊材等方面。由于水合性强,即含水率极高,云母具有高吸热效果,另外云母由于其层状结构,当薄膜层的厚度减少,边界的散射效应对热传导的影响逐渐显著,垂直于薄膜方向的热传导系数降低,但薄膜横向的热传导系数却逐步上升,使得云母具有高吸热热传递率。
目前尚未有相关的将云母添加到黏胶中的产品及其生产方法。
发明内容
针对上述问题,本发明的主要目的在于提供一种成本低在黏胶4切片中添加了纳米云母的黏胶冰凉纤维长丝及其生产方法。
本发明是通过下述技术方案来解决上述技术问题的:黏胶冰凉纤维长丝,其特征在于:按照重量百分比包括以下两种成分:
纳米云母 3~5%
黏胶4切片 90~95%。
在一个具体实施例中,按照重量百分比包括以下两种成分:
纳米云母 3%
黏胶4切片 97%。
在另一个具体实施例中,按照重量百分比包括以下两种成分:
纳米云母 4%
黏胶4切片 96%。
在另一个具体实施例中,按照重量百分比包括以下两种成分:
纳米云母 5%
黏胶4切片 95%。
在另一个具体实施例中,按照重量百分比包括以下两种成分:
纳米云母 3.5%
黏胶4切片 96.5%。
在另一个具体实施例中,按照重量百分比包括以下两种成分:
纳米云母 4.5%
黏胶4切片 95.5%。
其中,云母黏胶冰凉纤维长丝的生产方法,其特征在于:通过熔体纺丝法进行纺丝,主要包括以下步骤:
(1)干燥:将黏胶4切片和纳米云母母粒进行干燥;
(2)制备纺丝流体:按照一定的比例,利用母粒输出注释泵精确地添加纳米云母母粒,与黏胶4切片混合熔融;
(3)纺丝:将熔融的成纤高聚熔体从喷丝头的喷丝孔中压出,在周围空气(或水)中冷却凝固成丝,在生产过程中,保持稳定的温度、湿度和压力,纺丝过程中的温度为200~258℃;
(4)后加工:将制成的纤维依次进行拉伸加捻、后加捻、压洗、干燥、热定型、平衡、倒筒、包装和检验工序,最终得到成品云母黏胶冰凉纤维长丝。
本发明的积极进步效果在于:本发明涉及的云母黏胶冰凉纤维长丝相对于常规的黏胶纤维,不仅消除了原有的缺点,还增加了以下新的优点:
(1).抗静电功能;
(2).导热、吸水功能:由于云母本身为片状矽酸盐结构,其导热效果优于PA6本身,而脱层后的云母本身形成的水合效应,易形成一层水化膜,具有导热和含水的双重效果;
(3).消臭功能:脱层云母的比表面积高于450M2/G,此种高比表面积,使其吸附异味的效果由于其他矿石甚至云母自身,高比表面积具有类似活性炭分解臭味分子效果,所以不需要香味就可以消臭。
具体实施方式
为使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施方式,进一步阐述本发明。
实施例1
在本实施例中,云母黏胶冰凉纤维长丝的原料组成及生产方法步骤如下:
1、原料及重量:
纳米云母 300g
黏胶4切片 9700g
2、方法:通过熔体纺丝法进行纺丝,主要包括以下步骤:
(1)干燥:将黏胶4切片和纳米云母母粒进行干燥;
(2)制备纺丝流体:按照一定的比例,利用母粒输出注释泵精确地添加纳米云母母粒,与黏胶4切片混合熔融;
(3)纺丝:将熔融的成纤高聚熔体从喷丝头的喷丝孔中压出,在周围空气(或水)中冷却凝固成丝,在生产过程中,保持稳定的温度、湿度和压力,纺丝过程中的温度为200~258℃;
(4)后加工:将制成的纤维依次进行拉伸加捻、后加捻、压洗、干燥、热定型、平衡、倒筒、包装和检验工序,最终得到成品云母黏胶冰凉纤维长丝。
实施例2
在本实施例中,云母黏胶冰凉纤维长丝的原料组成及生产方法步骤如下:
1、原料及重量:
纳米云母 400g
黏胶4切片 9600g
2、方法:与实施例1相同。
实施例3
在本实施例中,云母黏胶冰凉纤维长丝的原料组成及生产方法步骤如下:
1、原料及重量:
纳米云母 500g
黏胶4切片 9500g
2、方法:与实施例1相同。
实施例4
在本实施例中,云母黏胶冰凉纤维长丝的原料组成及生产方法步骤如下:
1、原料及重量:
纳米云母 350g
黏胶4切片 9650g
2、方法:与实施例1相同。
实施例5
在本实施例中,云母黏胶冰凉纤维长丝的原料组成及生产方法步骤如下:
1、原料及重量:
纳米云母 450g
黏胶4切片 9550g
2、方法:与实施例1相同。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内,本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (7)
1.一种黏胶冰凉纤维长丝,其特征在于:按照重量百分比包括以下两种成分:
纳米云母 3~5%
黏胶4切片 95~97%。
2.根据权利要求1所述的黏胶冰凉纤维长丝,其特征在于:按照重量百分比包括以下两种成分:
纳米云母 3%
黏胶4切片 97%。
3.根据权利要求1所述的黏胶冰凉纤维长丝,其特征在于:按照重量百分比包括以下两种成分:
纳米云母 4%
黏胶4切片 96%。
4.根据权利要求1所述的黏胶冰凉纤维长丝,其特征在于:按照重量百分比包括以下两种成分:
纳米云母 5%
黏胶4切片 95%。
5.根据权利要求1所述的黏胶冰凉纤维长丝,其特征在于:按照重量百分比包括以下两种成分:
纳米云母 3.5%
黏胶4切片 96.5%。
6.根据权利要求1所述的黏胶冰凉纤维长丝,其特征在于:按照重量百分比包括以下两种成分:
纳米云母 4.5%
黏胶4切片 95.5%。
7.一种权利要求1~6之一所述的黏胶冰凉纤维长丝黏胶冰凉纤维长丝的生产方法,其特征在于:通过熔体纺丝法进行纺丝,主要包括以下步骤:
(1)干燥:将黏胶4切片和纳米云母母粒进行干燥;
(2)制备纺丝流体:按照一定的比例,利用母粒输出注释泵精确地添加纳米云母母粒,与黏胶4切片混合熔融;
(3)纺丝:将熔融的成纤高聚熔体从喷丝头的喷丝孔中压出,在周围空气或水中冷却凝固成丝,在生产过程中,保持稳定的温度、湿度和压力,纺丝过程中的温度为200~258℃;
(4)后加工:将制成的纤维依次进行拉伸加捻、后加捻、压洗、干燥、热定型、平衡、倒筒、包装和检验工序,最终得到成品云母黏胶冰凉纤维长丝。