CN116178215A - 一种1,3-位二烷基脲类化合物的制备方法 - Google Patents
一种1,3-位二烷基脲类化合物的制备方法 Download PDFInfo
- Publication number
- CN116178215A CN116178215A CN202211593407.0A CN202211593407A CN116178215A CN 116178215 A CN116178215 A CN 116178215A CN 202211593407 A CN202211593407 A CN 202211593407A CN 116178215 A CN116178215 A CN 116178215A
- Authority
- CN
- China
- Prior art keywords
- reaction
- dicyclohexylurea
- compound
- room temperature
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种1,3‑二环己基脲化合物的制备方法,涉及一种化合物的制备方法,所述方法包括如下步骤:先通入二氧化碳换气,再将正丙胺化合物、金属氧化物、无机盐加入有机溶剂中,在二氧化碳(5 MPa)氛围下,将温度控制在130℃~170℃,在磁力搅拌条件下反应12~48 h;反应结束后,反应结束后将温度恢复室温,过滤收集催化剂,然后向滤液中加入100 mL去离子水,室温搅拌30 min后过滤,得到白色固体的目标产品1,3‑二环己基脲化合物;反应底物为有机胺化合物,其结构如式(Ⅰ)所示。其中R为C3‑C6烷基或环烷基;(Ⅰ)。本发明分离方法简单,原料廉价易得,副产物为水,提高了反应的清洁性,降低了对环境的污染。
Description
技术领域
本发明涉及一种化合物合成方法,特别是涉及一种1,3-位二烷基脲类化合物的制备方法。
背景技术
CO2是一种丰富、无毒、不易燃且价格低廉的 C1 源,近些年得到了世界的广泛关注。将CO2直接转化为高附加值的化学品极具发展潜力。CO2具有很强的双键,化学性质稳定,将其直接进行化学转化通常比较困难,具有很大挑战。与 CO2还原转化为甲醇和甲酸等化学品相比,从能量输入的角度来看,非还原转化为碳酸盐、氨基甲酸酯和尿素等化学品更可取, 其中尿素衍生物是一类重要的羰基化合物,可用作合成药物或农用化学品的中间体及燃料添加剂。
尿素衍生物传统合成方法是采用光气或其衍生物制备。然而,光气法具有相当大的缺点,例如光气的毒性和在转化过程中会产生大量的副产物。除此之外合成脲衍生物的方法还包括胺与CO 的氧化羰基化、胺与 CO 的还原羰基化、脲与胺的转酰胺基化、碳酸盐与胺的反应以及 CO2 与胺的反应。在这些方法中,CO2 与胺直接反应生成尿素衍生物具有非常广阔的前景,其转化过程中的副产物为水,符合绿色化学的发展理念。从工业、环境和经济的角度来看,采用多相催化或非均相催化体系更理想。
发明内容
本发明的目的在于提供一种二烷基脲类化合物的制备方法,本发明方法以二氧化碳为反应原料合成二烷基脲类化合物,为温室气体的化工利用减排提供了方向,本发明经过滤即可分离出催化剂,分离方法简单。避免了现有合成方法中使用高毒光气的弊端,原料廉价易得,副产物为水,提高了反应的清洁性,降低了对环境的污染。
本发明采用的技术方案是:
一种1,3-二环己基脲化合物的制备方法,所述方法包括如下步骤:先通入二氧化碳换气,再将正丙胺化合物、金属氧化物、无机盐加入有机溶剂中,在二氧化碳(5 MPa)氛围下,将温度控制在130℃~170℃,在磁力搅拌条件下反应12~48 h;反应结束后,反应结束后将温度恢复室温,过滤收集催化剂,然后向滤液中加入100 mL去离子水,室温搅拌30 min后过滤,得到白色固体的目标产品1,3-二环己基脲化合物;反应底物为有机胺化合物,其结构如式(Ⅰ)所示。其中R为C3-C6烷基或环烷基;
所述的一种1,3-二环己基脲类化合物的制备方法,有机溶剂为乙腈(MeCN)、四氢呋喃(THF)、N-甲基吡咯烷酮(NMP)和二甲基亚砜(DMSO)极性溶剂。
所述的一种1,3-二环己基脲化合物的制备方法,所述的金属氧化物为CeO2、ZnO2、ZrO2和MnO2中的一种。
所述的一种1,3-二环己基脲化合物的制备方法,所述的无机盐为NaOH、KOH、K3PO4和K2HPO3中的一种。
所述的一种1,3-二环己基脲化合物的制备方法,金属氧化物的用量为反应底物有机胺的0.1~1.0 equiv.。
所述的一种1,3-二环己基脲化合物的制备方法,无机盐的用量为反应底物有机胺的0.5 mol%~10 mol%。
本发明的有益效果是:
本发明以二氧化碳为反应原料合成二烷基脲类化合物,为温室气体的化工利用减排提
供了方向。过滤即可分离出催化剂,分离方法简单。避免了传统合成方法中使用高毒光气的弊端,原料廉价易得,副产物为水,提高了反应的清洁性,降低了对环境的污染。本发明的合成方法具有简单高效的特点。
本发明以节能高效为目标,以“绿色化学”为宗旨,兼顾“原子经济性”,以CO2和有机胺化合物为原料,在金属氧化物与无机盐的复合非均相催化剂的作用下进行插羰反应,将CO2高效转化为二烷基脲产品,具有重要的研究意义。
附图说明
图1为本发明1,3-二环己基脲核磁共振氢谱。
具体实施方式
本发明以有机胺类化合物(Ⅰ)为原料,先通入二氧化碳换气,再依次加入复合非均相催化剂及溶剂,反应在二氧化碳气体氛围(5 MPa),一定温度条件下进行反应,得到式(Ⅱ)所示的二烷基脲类化合物,反应路线如下:
其中,式(Ⅱ)中R为C3-C6烷基或环烷基。
催化剂为金属氧化物(MO2)与无机盐的复合非均相催化剂,其中M为Ce2+、Zn2+、Zr2+、Mn2+等;无机盐为NaOH、KOH、K3PO4、K2HPO3等。
金属氧化物为氧化铈、氧化锌、氧化锆、氧化锰的一种,优选的金属氧化物为氧化铈。
金属氧化物用量为0.1~1.0 equiv.,优选的金属氧化物用量为0.3~0.5equiv.。
无机盐为氢氧化钠、氢氧化钾、磷酸钾、亚磷酸钾的一种,优选的无机盐为磷酸钾。
无机盐用量为0.5 mol%~10 mol%,优选的无机盐用量为1 mol%~1.2 mol%。
有机溶剂为乙腈、四氢呋喃、N-甲基吡咯烷酮和二甲基亚砜中的一种,优选的有机溶剂为N-甲基吡咯烷酮。
反应温度为130至170℃,优选的反应温度为130℃。
反应时间为12至48 h,优选的反应时间为24 h。
下面以合成1,3-二环己基脲为例以及具体实施例对本发明作进一步的详细说明,但所举实施例并不是对本发明的限定。
下面各实施例中未注明具体条件的试验方法,均按照本领域的常规方法和条件进行,所用的材料若无特殊说明均为市售。
实施例1
一种1,3-二环己基脲的合成方法,包括以下步骤:
在二氧化碳环境下,向体积为50 mL 的反应釜中依次加入氧化铈(861 mg,0.1equiv.),磷酸钾(106 mg,1 mol%),环己胺(50 mmol)和干燥过的N-甲基吡咯烷酮(20 mL),在通CO2(5 MPa),在130 ℃条件下,搅拌反应12 h。反应结束后将温度恢复室温,过滤收集催化剂,然后向反滤液中加入100 mL去离子水,室温搅拌30 min后过滤,得到白色固体的目标产品1,3-二环己脲,其产率为42 %。
实施例2
一种1,3-二环己基脲的合成方法,包括以下步骤:
在二氧化碳环境下,向体积为50 mL 的反应釜中依次加入氧化铈(4.30 g,0.5equiv.),磷酸钾(106 mg,1 mol%),环己胺(50 mmol)和干燥过的N-甲基吡咯烷酮(20 mL),在通CO2(5 MPa),在130 ℃条件下,搅拌反应12 h。反应结束后将温度恢复室温,过滤收集催化剂,然后向反滤液中加入100 mL去离子水,室温搅拌30 min后过滤,得到白色固体的目标产品1,3-二环己基脲,其产率为89 %。
实施例3
一种1,3-二环己基脲的合成方法,包括以下步骤:
在二氧化碳环境下,向体积为50 mL 的反应釜中依次加入氧化铈(8.61 g,1.0equiv.),磷酸钾(106 mg,1 mol%),环己胺(50 mmol)和干燥过的N-甲基吡咯烷酮(20 mL),在通CO2(5 MPa),在130 ℃条件下,搅拌反应12 h。反应结束后将温度恢复室温,过滤收集催化剂,然后向反滤液中加入100 mL去离子水,室温搅拌30 min后过滤,得到白色固体的目标产品1,3-二环己基脲,其产率为89 %。
实施例4
一种1,3-二环己基脲的合成方法,包括以下步骤:
在二氧化碳环境下,向体积为50 mL 的反应釜中依次加入氧化铈(4.30 g,0.5equiv.),磷酸钾(53 mg,0.5 mol%),环己胺(50 mmol)和干燥过的N-甲基吡咯烷酮(20mL),在通CO2(5 MPa),在130 ℃条件下,搅拌反应12 h。反应结束后将温度恢复室温,过滤收集催化剂,然后向反滤液中加入100 mL去离子水,室温搅拌30 min后过滤,得到白色固体的目标产品1,3-二环己基脲,其产率为71 %。
实施例5
一种1,3-二环己基脲的合成方法,包括以下步骤:
在二氧化碳环境下,向体积为50 mL 的反应釜中依次加入氧化铈(4.30 g,0.5equiv.),磷酸钾(159 mg,1.5 mol%),环己胺(50 mmol)和干燥过的N-甲基吡咯烷酮(20mL),在通CO2(5 MPa),在130 ℃条件下,搅拌反应12 h。反应结束后将温度恢复室温,过滤收集催化剂,然后向反滤液中加入100 mL去离子水,室温搅拌30 min后过滤,得到白色固体的目标产品1,3-二环己基脲,其产率为85 %。
实施例6
一种1,3-二环己基脲的合成方法,包括以下步骤:
在二氧化碳环境下,向体积为50 mL 的反应釜中依次加入氧化铈(4.30 g,0.5equiv.),磷酸钾(531 mg,5 mol%),环己胺(50 mmol)和干燥过的N-甲基吡咯烷酮(20 mL),在通CO2(5 MPa),在130 ℃条件下,搅拌反应12 h。反应结束后将温度恢复室温,过滤收集催化剂,然后向反滤液中加入100 mL去离子水,室温搅拌30 min后过滤,得到白色固体的目标产品1,3-二环己基脲,其产率为84 %。
实施例7
一种1,3-二环己基脲的合成方法,包括以下步骤:
在二氧化碳环境下,向体积为50 mL 的反应釜中依次加入氧化铈(4.30 g,0.5equiv.),磷酸钾(106 mg,1 mol%),环己胺(50 mmol)和干燥过的乙腈(20 mL),在通CO2(5MPa),在130 ℃条件下,搅拌反应12 h。反应结束后将温度恢复室温,过滤收集催化剂,然后向反滤液中加入100 mL去离子水,室温搅拌30 min后过滤,得到白色固体的目标产品1,3-二环己基脲,其产率为68 %。
实施例8
一种1,3-二环己基脲的合成方法,包括以下步骤:
在二氧化碳环境下,向体积为50 mL 的反应釜中依次加入氧化铈(4.30 g,0.5equiv.),磷酸钾(106 mg,1 mol%),环己胺(50 mmol)和干燥过的四氢呋喃(20 mL),在通CO2(5 MPa),在130 ℃条件下,搅拌反应12 h。反应结束后将温度恢复室温,过滤收集催化剂,然后向反滤液中加入100 mL去离子水,室温搅拌30 min后过滤,得到白色固体的目标产品1,3-二环己基脲,其产率为74 %。
实施例9
一种1,3-二环己基脲的合成方法,包括以下步骤:
在二氧化碳环境下,向体积为50 mL 的反应釜中依次加入氧化铈(4.30 g,0.5equiv.),磷酸钾(106 mg,1 mol%),环己胺(50 mmol)和干燥过的二甲基亚砜(20 mL),在通CO2(5 MPa),在130 ℃条件下,搅拌反应12 h。反应结束后将温度恢复室温,过滤收集催化剂,然后向反滤液中加入100 mL去离子水,室温搅拌30 min后过滤,得到白色固体的目标产品1,3-二环己基脲,其产率为65 %。
对比实施例
一种1,3-二环己基脲的合成方法,包括以下步骤:
在二氧化碳环境下,向体积为50 mL 的反应釜中依次加入环己胺(50 mmol)和干燥过的N-甲基吡咯烷酮(20 mL),在通CO2(5 MPa),在130 ℃条件下,搅拌反应12 h。反应结束后将温度恢复室温,向反应液中加入100 mL去离子水,室温搅拌30 min,未能得到目标产品1,3-二环己基脲。
上述实施例表明,采用本发明一种二烷基脲类化合物的制备方法,以二氧化碳和有机胺化物为原料,在金属氧化物和无机盐的复合作用下制备1,3-二环己基脲,将CO2转化高附加值化学品,该反应过程简单易操作,为二氧化碳高值化利用提供了一条新的工艺路线。
Claims (6)
2.根据权利要求1所述的一种1,3-二环己基脲类化合物的制备方法,其特征在于,有机溶剂为乙腈(MeCN)、四氢呋喃(THF)、N-甲基吡咯烷酮(NMP)和二甲基亚砜(DMSO)极性溶剂。
3.根据权利要求1所述的一种1,3-二环己基脲化合物的制备方法,其特征在于,所述的金属氧化物为CeO2、ZnO2、ZrO2和MnO2中的一种。
4.根据权利要求1所述的一种1,3-二环己基脲化合物的制备方法,其特征在于,所述的无机盐为NaOH、KOH、K3PO4和K2HPO3中的一种。
5.根据权利要求1所述的一种1,3-二环己基脲化合物的制备方法,其特征在于,金属氧化物的用量为反应底物有机胺的0.1~1.0 equiv.。
6.根据权利要求1所述的一种1,3-二环己基脲化合物的制备方法,其特征在于,无机盐的用量为反应底物有机胺的0.5 mol%~10 mol%。