CN115648844A - Technology for carving Buddha golden tripod by cinnabar die-pressing technology - Google Patents
Technology for carving Buddha golden tripod by cinnabar die-pressing technology Download PDFInfo
- Publication number
- CN115648844A CN115648844A CN202211123590.8A CN202211123590A CN115648844A CN 115648844 A CN115648844 A CN 115648844A CN 202211123590 A CN202211123590 A CN 202211123590A CN 115648844 A CN115648844 A CN 115648844A
- Authority
- CN
- China
- Prior art keywords
- cinnabar
- raw ore
- crystal
- die
- buddha
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of industrial arts, in particular to a cinnabar die-pressing process for carving Buddha gold tripod, which comprises the following steps: preparing raw materials; (2) relief model processing; (3) carrying out compression molding treatment; (4) drying; (5) demolding; and (6) carrying out fine engraving process treatment to obtain a final finished product. The raw ore cinnabar crystal powder and the crystal raw ore are adopted to ensure the glossiness of the raw ore cinnabar crystal powder, and particularly, the raw ore is proportioned and designed, and process parameters are properly regulated and controlled, so that the Zhu Shahua is bright and uniform in color, rich in luster, obvious in layering, and has oriental classical charm, the hardness of the raw ore cinnabar crystal powder is greatly improved, and the raw ore cinnabar crystal powder and the crystal raw ore are not easy to damage.
Description
Technical Field
The invention relates to the technical field of industrial arts, in particular to a technology for carving Buddha golden tripod by a cinnabar die-pressing technology.
Background
Cinnabar, named cinnabar as cinnabar, is a main raw material for refining mercury and is also called mercury sand. Also known as Dansha, red Dan, zhu Shadan, etc. because of their bright red, vermilion, light red, dark red or red color. The chemical component is mercuric sulfide, which is a trigonal system, the crystal is in a plate shape or a soil shape, and the crystal cluster is usually in a rhombohedral twin crystal, large-particle single crystal, semitransparent or opaque. The light-sensitive floor tile is crisp in nature, sensitive to light, high in refractive index, 2-2.5 in hardness, 8.09-8.2 in specific gravity, light in weight and crisp in texture, flaky in shape and glittering, and tasteless in powder shape.
Cinnabar has the name of 'soft ruby', and Zhu Shahua is a traditional handicraft in China. However, zhu Shahua on the market at present is mainly made of cinnabar ink or cinnabar color drawing or simply cinnabar powder. The pattern is simple, and the pattern is of a plane structure, and has no strong relief stereoscopic impression.
Disclosure of Invention
In order to overcome the defects, the invention provides a cinnabar die pressing process for carving a Buddha golden tripod.
The technical implementation scheme of the invention is as follows:
the cinnabar die-pressing process for carving Buddha gold tripod comprises the following steps:
(1) Preparing raw materials: mixing raw ore cinnabar crystal powder and crystal raw ore, putting the mixture into a crusher to be crushed for 20 to 30min, sieving the mixture by a sieve of 300 to 400 meshes, putting the mixture into a high-speed stirrer to be stirred for 5 to 10min, controlling the temperature to be 40 to 50 ℃ and the humidity to be 65 to 75 percent during stirring, and adding colloid accounting for 20 to 35 percent of the weight of the colloid;
(2) And (3) processing the relief model: cleaning and soaking for 20-30 min by using purified water, wherein the soaking temperature is 30-40 ℃, taking out the model after soaking is finished, cleaning for 3-5 min by using ultrasonic waves, and drying the water on the surface;
(3) And (3) die pressing treatment: placing the die in a die pressing machine, pressing the die for 3-10 min under the pressure of 50-80 MPa, and performing die pressing treatment for 2-3 times;
(4) And (3) drying: drying the mold filled with the material in a sealed environment at the temperature of 40-45 ℃ for 2-3 h, and cooling at normal temperature;
(5) Demolding: removing the press-molded rough product from the mold through a demolding process;
(6) And (5) carrying out fine engraving process treatment to obtain a final finished product.
Preferably, the raw ore cinnabar crystal powder and the crystal raw ore are uniformly mixed according to the weight ratio of 2.5-3:1-2.
Preferably, the colloid is prepared from gelatin, white latex, glue and clear water.
Preferably, the colloid is prepared from the following raw materials in parts by weight: 200-300 parts of gelatin, 200-300 parts of white latex, 200-300 parts of glue and 100-200 parts of clear water.
Preferably, 5 to 10 weight percent of agilawood and 0.5 to 2 weight percent of fly ash are also added into the colloid.
The invention has the following advantages:
the raw ore cinnabar crystal powder and the crystal raw ore are adopted to ensure the glossiness of the raw ore cinnabar crystal powder, and particularly, the raw ore is proportioned and designed, and process parameters are properly regulated and controlled, so that the Zhu Shahua is bright and uniform in color, rich in luster, obvious in layering, and has oriental classical charm, the hardness of the raw ore cinnabar crystal powder is greatly improved, and the raw ore cinnabar crystal powder and the crystal raw ore are not easy to damage.
Detailed Description
Reference herein to an embodiment means that a particular feature, structure, or characteristic described in connection with the embodiment can be included in at least one embodiment of the invention. The appearances of the phrase in various places in the specification are not necessarily all referring to the same embodiment, nor are separate or alternative embodiments mutually exclusive of other embodiments. It is explicitly and implicitly understood by one skilled in the art that the embodiments described herein can be combined with other embodiments.
Example 1
The cinnabar die-pressing process for carving Buddha gold tripod comprises the following steps:
(1) Preparing raw materials: mixing raw ore cinnabar crystal powder and crystal raw ore, putting into a grinder for grinding for 20min, sieving with a 300-mesh sieve, putting into a high-speed stirrer for stirring for 5min, controlling the temperature at 40 ℃ and the humidity at 65% in the stirring process, and adding 20% colloid of the weight of the raw ore cinnabar crystal powder and the crystal raw ore;
(2) And (3) processing the relief model: cleaning with purified water, soaking at 30 deg.C for 20min, taking out the mold, cleaning with ultrasonic wave for 3min, and drying surface water;
(3) And (3) die pressing treatment: placing the mould in a mould pressing machine, pressing for 10min under 50 MPa pressure, and performing mould pressing treatment for 3 times;
(4) And (3) drying: drying the mold filled with the material in a sealed environment at the temperature of 40 ℃ for 2 hours, and cooling at normal temperature;
(5) Demolding: removing the press-molded rough product from the mold through a demolding process;
(6) And (5) carrying out fine engraving process treatment to obtain a final finished product.
In order to further optimize the scheme, the raw ore cinnabar crystal powder and the crystal raw ore are uniformly mixed according to the weight ratio of 2.5.
In order to further optimize the scheme, the colloid is prepared from gelatin, white latex, glue and clear water.
In order to further optimize the scheme, the colloid is prepared from the following raw materials in parts by weight: 200 parts of gelatin, 200 parts of white latex, 200 parts of glue and 100 parts of clear water.
In order to further optimize the scheme, 5% of agilawood and 2% of fly ash by weight are added into the colloid.
The raw ore cinnabar crystal powder and the crystal raw ore are adopted to ensure the glossiness, and particularly, the raw material proportioning design is combined with the proper regulation and control of process parameters, so that the Zhu Shahua has the advantages of bright and uniform color, luster and obvious layering, has oriental classical charm, greatly improves the hardness and is not easy to damage.
Example 2
The cinnabar die-pressing process for carving Buddha gold tripod comprises the following steps:
(1) Preparing raw materials: mixing raw ore cinnabar crystal powder and crystal raw ore, putting into a grinder for grinding for 25min, sieving with a 350-mesh sieve, putting into a high-speed stirrer for stirring for 6min, controlling the temperature at 45 ℃ and the humidity at 70% in the stirring process, and adding colloid accounting for 25% of the weight of the raw ore cinnabar crystal powder and the crystal raw ore;
(2) And (3) processing the relief model: cleaning with purified water, soaking at 35 deg.C for 25min, taking out the mold, cleaning with ultrasonic wave for 4min, and drying surface water;
(3) And (3) compression molding treatment: placing the mould in a mould pressing machine, pressing for 6min under 65 MPa, and performing mould pressing treatment for 2 times;
(4) And (3) drying: drying the mold filled with the material in a sealed environment at the temperature of 45 ℃ for 3h, and cooling at normal temperature;
(5) Demolding: removing the press-molded rough product from the mold through a demolding process;
(6) And (5) carrying out fine engraving process treatment to obtain a final finished product.
In order to further optimize the scheme, the raw ore cinnabar crystal powder and the crystal raw ore are uniformly mixed according to the weight ratio of 3:2.
In order to further optimize the scheme, the colloid is prepared from gelatin, white latex, glue and clear water.
In order to further optimize the scheme, the colloid is prepared from the following raw materials in parts by weight: 250 parts of gelatin, 300 parts of white latex, 300 parts of glue and 200 parts of clear water.
In order to further optimize the scheme, 10 weight percent of agilawood and 0.5 weight percent of fly ash are also added into the colloid.
The raw ore cinnabar crystal powder and the crystal raw ore are adopted to ensure the glossiness of the raw ore cinnabar crystal powder, and particularly, the raw ore is proportioned and designed, and process parameters are properly regulated and controlled, so that the Zhu Shahua is bright and uniform in color, rich in luster, obvious in layering, and has oriental classical charm, the hardness of the raw ore cinnabar crystal powder is greatly improved, and the raw ore cinnabar crystal powder and the crystal raw ore are not easy to damage.
Example 3
The cinnabar die-pressing process for carving Buddha gold tripod comprises the following steps:
(1) Preparing raw materials: mixing raw ore cinnabar crystal powder and crystal raw ore, putting the mixture into a crusher to be crushed for 20 to 30min, sieving the mixture by a sieve of 300 to 400 meshes, putting the mixture into a high-speed stirrer to be stirred for 5 to 10min, controlling the temperature to be 40 to 50 ℃ and the humidity to be 65 to 75 percent during stirring, and adding colloid accounting for 20 to 35 percent of the weight of the colloid;
(2) And (3) processing the relief model: cleaning and soaking for 20-30 min by using purified water, wherein the soaking temperature is 30-40 ℃, taking out the model after soaking is finished, cleaning for 3-5 min by using ultrasonic waves, and drying the water on the surface;
(3) And (3) die pressing treatment: placing the die in a die pressing machine, pressing the die for 3-10 min under the pressure of 50-80 MPa, and performing die pressing treatment for 2-3 times;
(4) And (3) drying: drying the mold filled with the material in a sealed environment at the temperature of 40-45 ℃ for 2-3 h, and cooling at normal temperature;
(5) Demolding: removing the press-molded rough product from the mold through a demolding process;
(6) And (5) carrying out fine engraving process treatment to obtain a final finished product.
In order to further optimize the scheme, the raw ore cinnabar crystal powder and the crystal raw ore are uniformly mixed according to the weight ratio of 2.5-3:1-2.
In order to further optimize the scheme, the colloid is prepared from gelatin, white latex, glue and clear water.
In order to further optimize the scheme, the colloid is prepared from the following raw materials in parts by weight: 200-300 parts of gelatin, 200-300 parts of white latex, 200-300 parts of glue and 100-200 parts of clear water.
In order to further optimize the scheme, 5-10% of agilawood and 0.5-2% of fly ash by weight are also added into the colloid.
The raw ore cinnabar crystal powder and the crystal raw ore are adopted to ensure the glossiness of the raw ore cinnabar crystal powder, and particularly, the raw ore is proportioned and designed, and process parameters are properly regulated and controlled, so that the Zhu Shahua is bright and uniform in color, rich in luster, obvious in layering, and has oriental classical charm, the hardness of the raw ore cinnabar crystal powder is greatly improved, and the raw ore cinnabar crystal powder and the crystal raw ore are not easy to damage.
The above description is only for the specific embodiments of the present invention, but the scope of the present invention is not limited thereto, and any person skilled in the art can easily conceive of the changes or substitutions within the technical scope of the present invention, and all the changes or substitutions should be covered within the scope of the present invention. Therefore, the protection scope of the present invention shall be subject to the protection scope of the claims.
Claims (5)
1. The technology for carving the Buddha gold tripod by the cinnabar die-pressing technology is characterized by comprising the following steps of:
(1) Preparing raw materials: mixing raw ore cinnabar crystal powder and crystal raw ore, putting the mixture into a crusher to be crushed for 20 to 30min, sieving the mixture by a sieve of 300 to 400 meshes, putting the mixture into a high-speed stirrer to be stirred for 5 to 10min, controlling the temperature to be 40 to 50 ℃ and the humidity to be 65 to 75 percent during stirring, and adding colloid accounting for 20 to 35 percent of the weight of the colloid;
(2) And (3) processing the relief model: cleaning and soaking for 20-30 min by using purified water, wherein the soaking temperature is 30-40 ℃, taking out the model after soaking is finished, cleaning for 3-5 min by using ultrasonic waves, and drying the water on the surface;
(3) And (3) die pressing treatment: placing the die in a die pressing machine, pressing the die for 3-10 min under the pressure of 50-80 MPa, and performing die pressing treatment for 2-3 times;
(4) And (3) drying: drying the mold filled with the material in a sealed environment at the temperature of 40-45 ℃ for 2-3 h, and cooling at normal temperature;
(5) Demolding: removing the press-molded rough product from the mold through a demolding process;
(6) And (5) carrying out fine engraving process treatment to obtain a final finished product.
2. The cinnabar compression molding process carving Buddha gold tripod process according to claim 1, wherein the weight ratio of the raw ore cinnabar crystal powder to the crystal raw ore is 2.5-3:1-2 and the raw ore is mixed evenly.
3. The cinnabar compression molding process carving Buddha gold tripod process according to claim 1, wherein the colloid is prepared from gelatin, white latex, glue and clear water.
4. The cinnabar compression molding process carving Buddha gold tripod process according to claim 3, wherein the colloid is prepared from the following raw materials in parts by weight: 200 to 300 portions of gelatin, 200 to 300 portions of white latex, 200 to 300 portions of glue and 100 to 200 portions of clear water.
5. The cinnabar compression molding process engraving Buddha gold tripod process according to claim 4, wherein 5-10% by weight of agilawood and 0.5-2% by weight of fly ash are also added into the colloid.