CN115139604B - 一种高强低膨胀塑胶地板及其制备方法 - Google Patents

一种高强低膨胀塑胶地板及其制备方法 Download PDF

Info

Publication number
CN115139604B
CN115139604B CN202110985842.7A CN202110985842A CN115139604B CN 115139604 B CN115139604 B CN 115139604B CN 202110985842 A CN202110985842 A CN 202110985842A CN 115139604 B CN115139604 B CN 115139604B
Authority
CN
China
Prior art keywords
layer
parts
weight
precipitation
wear
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN202110985842.7A
Other languages
English (en)
Other versions
CN115139604A (zh
Inventor
王周林
徐杭波
全军
陆成杰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang Haixiang New Materials Co ltd
Original Assignee
Zhejiang Haixiang New Materials Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhejiang Haixiang New Materials Co ltd filed Critical Zhejiang Haixiang New Materials Co ltd
Priority to CN202110985842.7A priority Critical patent/CN115139604B/zh
Publication of CN115139604A publication Critical patent/CN115139604A/zh
Application granted granted Critical
Publication of CN115139604B publication Critical patent/CN115139604B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及E04F技术领域，更具体地，本发明涉及一种高强低膨胀塑胶地板及其制备方法。高强低膨胀塑胶地板，依次包括耐磨层、印刷层、中料层、底料层、防析出层。本申请所述高强低膨胀塑胶地板能够有效阻止增塑剂的析出问题，同时具有优异的力学性能。

Description

一种高强低膨胀塑胶地板及其制备方法
技术领域
本发明涉及E04F技术领域，更具体地，本发明涉及一种高强低膨胀塑胶地板及其制备方法。
背景技术
塑胶地板又称PVC地板，在欧美及亚洲广受欢迎。CN201821984682通过使用PVC耐磨层、PVC装饰层、PVC片材、PVC发泡层等得到一种新型复合地板，具有较好的隔音效果，然而该复合地板存在小分子增塑剂易于析出，膨胀率高、直线度差的问题。CN201110182685提供了一种PVC塑木贴面企口地板，通过使用PVC材料、润滑剂等材料得到木质地板层，得到的地板涨缩均匀，然而其存在尺寸稳定性的问题，膨胀收缩率无法满足生产的要求。此外，现有的塑胶地板还存在刚性差，容易受到外力变形，受热胀冷缩影响发生尺寸变化，导致拼接处产生缝隙或变形，粘结强度降低等问题。
发明内容
针对现有技术中存在的一些问题，本发明第一个方面提供了一种高强低膨胀塑胶地板，包括依次连接的耐磨层、印刷层、中料层、底料层、防析出层。
在一种实施方式中，按重量份计，所述耐磨层的制备原料包括60-70份PVC树脂粉、20-30份增塑剂、0.5-1份稳定剂、5-10份硅酸盐矿物质。
在一种优选的实施方式中，按重量份计，所述耐磨层的制备原料还包括0.5-1份抗氧化剂、0.5-1份抗紫外线剂。
在一种更优选的实施方式中，按重量份计，所述耐磨层的制备原料包括65份PVC树脂粉、25份增塑剂、0.8份稳定剂、8份硅酸盐矿物质、0.7份抗氧化剂、0.6份抗紫外线剂。
优选的，所述PVC树脂粉的聚合度为800-1000，优选为845-980。
优选的，所述PVC树脂粉根据ASTM D-I243-58T得到的特性粘度为0.8-1dL/g，更优选为0.89-0.95dL/g。
更优选的，所述PVC树脂粉的型号为SG-5。
申请人意外的发现，当PVC树脂粉的聚合度为800-1000时，得到的塑胶地板的硬度较高，申请人认为可能的原因是该特定聚合度的PVC树脂粉具有合适长度的分子链，增大了塑胶地板的分子之间的作用力。此外，申请人意外的发现，当PVC树脂粉的特性粘度为0.8-1dL/g时，在制备过程中流动性好。
本申请所述增塑剂不作特别限定，本领域技术人员可作常规选择。
在一种实施方式中，所述增塑剂为对苯二甲酸二辛酯。
本申请所述稳定剂不作特别限定，本领域技术人员可作常规选择。
在一种实施方式中，所述稳定剂为钙锌稳定剂。
本申请所述抗氧化剂、抗紫外线剂不作特别限定，本领域技术人员可作常规选择。
优选的，所述硅酸盐矿物质在25℃的密度为2.5-3g/cm3，更优选为2.65g/cm3。
进一步优选的，所述硅酸盐矿物质包括(a)粒径为40-60目的硅酸盐矿物质和(b)粒径为90-120目的硅酸盐矿物质；更优选的，所述硅酸盐矿物质包括(a)粒径为50目的硅酸盐矿物质和(b)粒径为100目的硅酸盐矿物质。
优选的，所述硅酸盐矿物质为石英砂。
在一种实施方式中，所述(a)粒径为40-60目的硅酸盐矿物质和(b)粒径为90-120目的硅酸盐矿物质的重量比为(0.6-1.5)：1，优选为1：1。
申请人在实验中发现，当采用本申请中特定的PVC树脂粉在得到一定硬度的塑胶地板时，使用常规的无机填料来提高防滑性时，防滑等级比较低，此外，本申请在实验中意外的发现，当使用特定含量的硅酸盐矿物质，尤其是硅酸盐矿物质包括(a)粒径为40-60目的硅酸盐矿物质和(b)粒径为90-120目的硅酸盐矿物质时，此时防滑等级较高，同时与印刷层之间复合的强度增大，申请人认为可能的原因是该特定粒径的硅酸盐矿物质，特别是密度为2.5-3g/cm3，在耐磨层各个原料混合搅拌时能够与分子链较长的PVC分子相互协调，在耐磨层的制备过程中，不同粒径的硅酸盐矿物质被较长分子链的PVC分子包裹缠结，使得该2种特定粒径的硅酸盐矿物质呈现一定的分布结构，不仅提高了防滑等级，同时增大了该塑胶地板的耐环境稳定性。
本申请所述印刷层不作特别限定，本领域技术人员可作常规选择。
优选的，所述印刷层的厚度为0.07mm。
在一种实施方式中，按重量份计，所述中料层的制备原料包括17-20份PVC树脂粉、5-7份增塑剂、0.1-1份稳定剂、72-75份无机粉体、1-3份纤维增强材料。
在一种优选的实施方式中，按重量份计，所述中料层的制备原料包括17.5-19份PVC树脂粉、5-6.5份增塑剂、0.5份稳定剂、73-74.5份无机粉体、1-2.5份纤维增强材料。
本申请所述无机粉体不作特别限定，本领域技术人员可作常规选择。
在一种实施方式中，所述纤维增强材料的长度为6-15mm。
优选的，所述纤维增强材料为短切玻璃纤维。
申请人在实验中意外的发现，在本申请中料层特定的原料中加入特定含量的短切玻璃纤维，在一定程度上降低了在23-50℃的膨胀率和80℃的收缩率。
在一种实施方式中，按重量份计，所述底料层的制备原料包括40-45份PVC树脂粉、8-10份增塑剂、0.5-2份稳定剂、40-60份填料。
在一种实施方式中，按重量份计，所述底料层的制备原料包括40-41份PVC树脂粉、8.5-9份增塑剂、1份稳定剂、50份填料。
申请人在实验中意外的发现，当底料层的制备原料包括40-41份PVC树脂粉、8.5-9份增塑剂、1份稳定剂、50份填料时，各个原料之间互相促进，具有较好的直线度，同时抵抗外力变形性较好。
在一种实施方式中，所述防析出层的材质选自TPU薄膜、NBR薄膜、PVC膜中任一种。
优选的，所述防析出层厚度为0.02-0.05mm。
优选的，所述防析出层中不含有增塑剂。
本申请中碳酸钙均为重质碳酸钙。
在一种实施方式中，所述碳酸钙的粒径为180目。
本发明第二个方面提供了一种所述高强低膨胀塑胶地板的制备方法，包括：分别将耐磨层、中料层的各个制备原料混合，经过密炼、开炼、四辊压延、冷却裁切、拉制出片，得到耐磨层、中料层；将底料层的各个制备原料混合，经过密炼、开炼、四辊压延，压延的同时与防析出层复合，之后冷却裁切、拉制出片，得到底料层和防析出层双层产品；将耐磨层、印刷层、中料层、底料层和防析出层双层产品依次叠放热压和冷压贴合，然后对耐磨层表面进行UV处理和回火处理，获得半产品；半成品经过自动削边机削边，即得。
优选的，在长度为36m的回火炉于120-145℃进行回火处理，处理速率为10-12m/min。
在一种实施方式中，所述高强低膨胀塑胶地板的制备方法，包括下面步骤：
(1)将PVC树脂粉、增塑剂、稳定剂共混，搅拌2-3min后加入无机粉体和纤维增强材料，高速搅拌2-3min后，投入密炼机中，物料在密炼机中温度达到120℃后密炼2-6min，之后在开炼机中于150-160℃开炼，然后经过四辊压延、冷却裁切，以30m/min的速度拉制出片完成，获得中料层；
(2)将PVC树脂粉、增塑剂、稳定剂、抗氧化剂、抗紫外线剂共混，搅拌2-3min后加入碳酸钙和石英砂，高速搅拌2-3min后，投入密炼机中密炼2-6min，之后经过开炼、四辊压延、冷却裁切，以30m/min的速度拉制出片完成，获得耐磨层；
(3)将PVC树脂粉、增塑剂、稳定剂共混，搅拌2-3min后加入无机粉体，高速搅拌2-3min后，投入密炼机中密炼2-6min，之后经过开炼、四辊压延，压延的同时与防析出层复合，冷却裁切，以30m/min的速度拉制出片完成，获得底料层和防析出层双层产品；
(4)将耐磨层、印刷层、中料层、底料层和防析出层双层产品依次叠放，在140-150℃于3-8MPa热压贴合30-40min，再10-15MPa进行冷压贴合20-30min，冷压贴合的冷却水温度为28-30℃，然后对耐磨层表面进行UV处理和回火处理，获得半产品，其中在长度为36m的回火炉于130℃进行回火处理，处理速率为11m/min；
(5)将半成品的长度和宽度在尺寸上均预留至少2mm，再用自动削边机削边，获得成品。
本申请高强低膨胀塑胶地板的制备方法中未公开的部分，本领域技术人员可作常规选择。
本发明与现有技术相比具有以下有益效果：
(1)采用本申请特定的PVC树脂粉，得到的塑胶地板的硬度较高，同时制备过程中流动性好；
(2)粒径为40-60目的硅酸盐矿物质和(b)粒径为90-120目的硅酸盐矿物质的复合使用，避免了本申请特定PVC树脂粉带来的防滑等级比较低的问题，同时与印刷层之间复合的强度增大；
(3)中料层特定的原料中加入特定含量的短切玻璃纤维，在一定程度上降低了在23-50℃的膨胀率和80℃的收缩率；
(4)本申请中底料层各个原料之间互相促进，具有较好的直线度，同时抵抗外力变形性较好，软硬度从原先的55D提高到65D，大大提高了产品强度；
(5)使用本申请中特定的防析出层，实现了基材的防DOTP析出功能，同时该防析出层不含增塑剂，其本身不会出现析出的问题，不会影响地板和地面的粘结力，此外具有更优异的止滑耐磨性能；
(6)通过本申请制备方法，短切玻璃纤维能均匀分布在中料层中，有效降低产品膨胀率，克服现有技术地板加工过程中短切玻璃纤维量受限的问题，因为随着短切玻璃纤维量的增加，存在压延时的脱辊，油压时的气泡以及冲切削边时的崩边等技术难题；
(7)本申请中采用热压后冷压的贴合工艺，避免了产生气泡和溢料；
(8)采用特殊的冲切削边工艺避免了崩边现象，要求冲切时尺寸上至少预留2mm，再用自动削边机削边，保证产品不崩边，四边光滑，拼接无缝隙。
具体实施方式
以下通过具体实施方式说明本发明，但不局限于以下给出的具体实施例。
实施例
实施例1
本发明的实施例1提供了一种高强低膨胀塑胶地板，由耐磨层、印刷层、中料层、底料层、防析出层构成。
按重量份计，所述耐磨层的制备原料如下：65份PVC树脂粉、25份对苯二甲酸二辛酯、0.8份钙锌稳定剂、0.7份抗氧化剂、0.6份抗紫外线剂、4份粒径为50目的石英砂、4份粒径为100目的石英砂。
按重量份计，所述中料层的制备原料如下：17.5份PVC树脂粉、6.5份对苯二甲酸二辛酯、0.5份钙锌稳定剂、74.5份碳酸钙、1份短切玻璃纤维。
按重量份计，所述底料层的制备原料如下：40份PVC树脂粉、9份对苯二甲酸二辛酯、1份钙锌稳定剂、50份碳酸钙。
所述防析出层为TPU薄膜，聚酯型95A，厚度为0.05mm。
所述PVC树脂粉型号为SG-5；所述钙锌稳定剂购自济南万得丰环保科技有限公司；所述碳酸钙为重质碳酸钙，粒径为180目；所述短切玻璃纤维的长度为6-15mm，购自桐乡巨石集团。
所述抗氧化剂为抗氧化剂168，所述抗紫外线为紫外线吸收剂UV-531；所述印刷层的厚度为0.07mm，购自大桔。
所述高强低膨胀塑胶地板的制备方法如下：
(1)将PVC树脂粉、增塑剂、稳定剂共混，搅拌2.5min后加入无机粉体和纤维增强材料，高速搅拌2.5min后，投入密炼机中，物料在密炼机中温度达到120℃后密炼5min，之后在开炼机中于155℃开炼，然后经过四辊压延、冷却裁切，以30m/min的速度拉制出片完成，获得中料层；
(2)将PVC树脂粉、增塑剂、稳定剂、抗氧化剂、抗紫外线剂共混，搅拌2.5min后加入碳酸钙和石英砂，高速搅拌2.5min后，投入密炼机中密炼5min，之后经过开炼、四辊压延、冷却裁切，以30m/min的速度拉制出片完成，获得耐磨层；
(3)将PVC树脂粉、增塑剂、稳定剂共混，搅拌2.5min后加入无机粉体，高速搅拌2.5min后，投入密炼机中密炼5min，之后经过开炼、四辊压延，压延的同时与防析出层复合，冷却裁切，以30m/min的速度拉制出片完成，获得底料层和防析出层双层产品；
(4)将耐磨层、印刷层、中料层、底料层和防析出层双层产品依次叠放，在145℃于5MPa热压贴合35min，再12MPa进行冷压贴合25min，冷压贴合的冷却水温度为30℃，然后对耐磨层表面进行UV处理和回火处理，获得半产品，其中在长度为36m的回火炉于130℃进行回火处理，处理速率为11m/min；
(5)将半成品的长度和宽度在尺寸上均预留2mm，再用自动削边机削边，获得成品。
获得的成品在使用过程中未出现增塑剂析出的问题，根据测试标准DIN51130，该塑胶地板的防滑等级为R10。
实施例2
本发明的实施例2提供了一种高强低膨胀塑胶地板，其具体实施方式同实施例1，不同之处在于，按重量份计，所述底料层的成分如下：40.5份PVC树脂粉、8.5份对苯二甲酸二辛酯、1份钙锌稳定剂、50份碳酸钙。所述印刷层的厚度为0.07mm，购自恒昌。
所述高强低膨胀塑胶地板的制备方法其具体实施方式同实施例1。
实施例3
本发明的实施例3提供了一种高强低膨胀塑胶地板，其具体实施方式同实施例1，不同之处在于，按重量份计，所述底料层的成分如下：42份PVC树脂粉、7份对苯二甲酸二辛酯、1份钙锌稳定剂、50份碳酸钙。所述印刷层的厚度为0.07mm，购自华丽。
所述高强低膨胀塑胶地板的制备方法其具体实施方式同实施例1。
实施例4
本发明的实施例4提供了一种高强低膨胀塑胶地板，其具体实施方式同实施例1，不同之处在于，按重量份计，所述中料层的成分如下：17.5份PVC树脂粉、6.5份对苯二甲酸二辛酯、0.5份钙锌稳定剂、73份碳酸钙、2.5份短切玻璃纤维。
所述高强低膨胀塑胶地板的制备方法其具体实施方式同实施例1。
实施例5
本发明的实施例5提供了一种高强低膨胀塑胶地板，其具体实施方式同实施例1，不同之处在于，按重量份计，所述中料层的成分如下：17.5份PVC树脂粉、6.5份对苯二甲酸二辛酯、0.5份钙锌稳定剂、71.5份碳酸钙、4份短切玻璃纤维。
所述高强低膨胀塑胶地板的制备方法其具体实施方式同实施例1。
实施例6
本发明的实施例6提供了一种高强低膨胀塑胶地板，其具体实施方式同实施例1，不同之处在于，按重量份计，所述中料层的成分如下：19份PVC树脂粉、5份对苯二甲酸二辛酯、0.5份钙锌稳定剂、73份碳酸钙、2.5份短切玻璃纤维。
所述高强低膨胀塑胶地板的制备方法其具体实施方式同实施例1。
实施例7
本发明的实施例7提供了一种塑胶地板，其具体实施方式同实施例1，不同之处在于，按重量份计，所述中料层的成分如下：17.5份PVC树脂粉、6.5份对苯二甲酸二辛酯、0.5份钙锌稳定剂、75.5份碳酸钙、0份短切玻璃纤维。按重量份计，所述底料层的成分如下：39份PVC树脂粉、10份对苯二甲酸二辛酯、1份钙锌稳定剂、50份碳酸钙。
实施例8
本发明的实施例8提供了一种市售的PVC塑胶地板，该PVC塑胶地板不含防析出层。
该PVC塑胶地板在使用的过程中出现增塑剂析出的问题，塑胶地板与地面的粘结力变差。
实施例9
本发明的实施例9提供了一种塑胶地板，其具体实施方式同实施例1，不同之处在于，按重量份计，所述耐磨层的制备原料如下：65份PVC树脂粉、25份对苯二甲酸二辛酯、0.8份钙锌稳定剂、0.7份抗氧化剂、0.6份抗紫外线剂。
根据测试标准DIN51130，该塑胶地板的防滑等级为R9。
性能评估
1.膨胀率：分别对实施例1、4-7的塑胶地板在23-50℃的膨胀率进行测试，测试方法如下：将产品放入23℃烘箱中放置6h后，测试得尺寸A，将烘箱温度提高到50℃，6h后测试得到尺寸B，得膨胀率C＝(B-A)/A。
2.收缩率：分别对实施例1、4、6、7的塑胶地板在80℃处理6h的收缩率进行测试，测试标准为ISO 23999。
3.硬度：分别对实施例1-3、7的底料层的硬度使用邵氏D硬度计进行测试。
4.直线度：分别对实施例1、2、7的塑胶地板的直线度进行测试，测试标准为ISO24342。
表1
表2
5.翘曲测试：对实施例1的塑胶地板进行翘曲测试，测试标准为ISO 24342。
表3
实施例1 实施例7
翘曲 0.23mm 0.5mm

Claims (3)

1.一种高强低膨胀塑胶地板，其特征在于，包括依次连接的耐磨层、印刷层、中料层、底料层、防析出层；所述耐磨层的制备原料包括60-70份PVC树脂粉、20-30份增塑剂、0.5-1份稳定剂、5-10份硅酸盐矿物质；
所述PVC树脂粉的聚合度为845-980，根据ASTM D-I243-58T得到的特性粘度0 .89-0.95dL/g；
所述硅酸盐矿物质包括（a）粒径为50目的硅酸盐矿物质和（b）粒径为100目的硅酸盐矿物质，所述（a）粒径为50目的硅酸盐矿物质和（b）粒径为100目的硅酸盐矿物质的重量比为1：1；所述硅酸盐矿物质为石英砂；
所述防析出层的材质选自TPU薄膜、NBR薄膜、PVC膜中任一种，所述防析出层厚度为0.02-0.05mm；
按重量份计，所述中料层的制备原料包括17-20份PVC树脂粉、5-7份增塑剂、0.1-1份稳定剂、72-75份无机粉体、1-3份纤维增强材料；
所述纤维增强材料为短切玻璃纤维，所述纤维增强材料的长度为6-15mm。
2.根据权利要求1所述高强低膨胀塑胶地板，其特征在于，按重量份计，所述底料层的制备原料包括40-45份PVC树脂粉、8-10份增塑剂、0.5-2份稳定剂、40-60份填料。
3.一种根据权利要求1-2任一项所述高强低膨胀塑胶地板的制备方法，其特征在于，包括：分别将耐磨层、中料层的各个制备原料混合，经过密炼、开炼、四辊压延、冷却裁切、拉制出片，得到耐磨层、中料层；将底料层的各个制备原料混合，经过密炼、开炼、四辊压延，压延的同时与防析出层复合，之后冷却裁切、拉制出片，得到底料层和防析出层双层产品；将耐磨层、印刷层、中料层、底料层和防析出层双层产品依次叠放热压和冷压贴合，然后对耐磨层表面进行UV处理和回火处理，获得半产品；半成品经过自动削边机削边，即得。
CN202110985842.7A 2021-08-26 2021-08-26 一种高强低膨胀塑胶地板及其制备方法 Active CN115139604B (zh)