CN114990892A - Manufacturing method of sleep-benefiting skin-beautifying fabric - Google Patents
Manufacturing method of sleep-benefiting skin-beautifying fabric Download PDFInfo
- Publication number
- CN114990892A CN114990892A CN202210853627.6A CN202210853627A CN114990892A CN 114990892 A CN114990892 A CN 114990892A CN 202210853627 A CN202210853627 A CN 202210853627A CN 114990892 A CN114990892 A CN 114990892A
- Authority
- CN
- China
- Prior art keywords
- health
- flexible
- powder
- care
- beautifying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a manufacturing method of a sleep-benefiting skin-beautifying fabric, which comprises the following steps of (1) preparing health-care textile threads; (2) preparing a flexible soaking agent, and repeatedly soaking and cleaning the health care textile wire to obtain the flexible health care textile wire; (3) drying the flexible health textile yarns; (4) making the dried flexible health textile yarns into flexible health base cloth; (5) preparing an external adhesion liquid; (6) and coating the outer adhesive liquid on the surface of the flexible health-care base fabric, and drying to obtain the flexible health-care underwear fabric. The invention provides a manufacturing method of sleep-benefiting skin-beautifying fabric, which enables the texture of the material for preparing clothes to be softer, can be better attached to the surface of human skin, greatly improves the using effect of products, better enriches the types of health-care clothes, provides more choices for consumers, and well promotes the development of enterprises and industries.
Description
Technical Field
The invention belongs to the field of functional textiles, and particularly relates to a manufacturing method of a sleep-benefiting skin-beautifying fabric.
Background
Along with the development of society and the generalization of sub-health, the attention of people to the physical and mental health of the people is greatly strengthened. In order to better adjust the body condition, many consumers are interested in purchasing various health garments for wearing.
The existing clothes with health care effects are low in comfort level when being worn due to the lack of material types, so that enterprises mainly make health care materials into non-close-fitting clothes. However, because the clothes are not close to the skin, the health care effect of the clothes is difficult to continuously act on the human body, the embodiment of the health care effect on the human body is greatly limited, and the normal development of the industry is not facilitated.
In order to better improve the effect of the health-care clothes on the human body, the health-care clothes can be more attached to the skin of the human body, and the physical health of consumers is further improved, so that the health-care clothes are specially designed.
Disclosure of Invention
The invention aims to overcome the problems and provides a method for manufacturing sleep-benefiting skin-beautifying fabric, so that the material for manufacturing clothes is softer in texture and can be better attached to the surface of human skin, the using effect of the product is greatly improved, the types of health-care clothes are better enriched, more choices are provided for consumers, and the development of enterprises and industries is well promoted.
The purpose of the invention is realized by the following technical scheme:
a manufacturing method of a sleep-benefiting skin-beautifying fabric comprises the following process steps:
(1) preparing a health care textile thread;
(2) preparing a flexible soaking agent, and repeatedly soaking and cleaning the health care textile wire to obtain the flexible health care textile wire;
(3) drying the flexible health care textile thread;
(4) making the dried flexible health textile thread into flexible health base cloth;
(5) preparing an external adhesive liquid;
(6) and coating the outer attachment liquid on the surface of the flexible health-care base cloth, and drying to obtain the flexible health-care underwear fabric.
The specific method of the step (1) is as follows:
(11) uniformly mixing polyamide fiber powder, health-care powder and auxiliary materials to obtain a health-care mixture;
(12) mixing the health mixture to prepare health nylon master batch;
(13) spinning the health nylon master batch into a health line by a wire drawing machine;
(14) and baking the health care textile wire in a drying oven to obtain the health care textile wire.
In the step (11), the particle size of the polyamide fiber powder is not more than 200nm, and the health-care mixture comprises the following components in parts by weight:
the far infrared functional powder is far infrared ceramic powder, the particle size of the far infrared ceramic powder is smaller than 0.3mm, the anion functional powder is tourmaline powder, the particle size of the tourmaline powder is smaller than 0.3mm, the magnetic field functional powder is a mixture of stone needle powder and volcano energy stone powder, and the weight ratio of the stone needle powder to the volcano energy stone powder is 3: 1, and the particle diameters of the stone needle powder and the volcanic energy stone powder are both less than 0.3 mm.
The flexible soaking agent in the step (2) comprises the following components in parts by weight:
the specific preparation method of the flexible soaking agent comprises the following steps:
(21) mixing fatty alcohol-polyoxyethylene ether, esterquat, polyphosphate and polyvinyl alcohol, adding clear water, stirring and heating, and continuously stirring for 10min at the heating temperature of 80-85 ℃ to obtain a mixture A, wherein the weight ratio of the total weight of the fatty alcohol-polyoxyethylene ether, the esterquat, the polyphosphate and the polyvinyl alcohol to the clear water is 2: 3;
(22) mixing magnesium stearate, liquid paraffin, soda ash, glycerol and calcium hydrogen phosphate, and stirring at 95-105 deg.C for 15min to obtain mixture B;
(23) mixing and stirring the mixture A and the mixture B, standing for 3 hours after uniformly stirring, and filtering solid impurities to obtain filtrate C;
(24) sequentially adding bentonite, glacial acetic acid and coconut oil fatty acid diethanolamide into the filtrate C, continuously stirring, heating the filtrate C until the liquid temperature reaches 100 ℃, maintaining the temperature of the filtrate C at 100 ℃, continuously stirring for 15min, and finally filtering solid impurities to obtain the flexible soaking agent.
In the step (2), the time for soaking the health care textile wire in the flexible soaking agent for one time is 15-30min, the temperature of the flexible soaking agent for soaking the health care textile wire is maintained within the range of 60-70 ℃, and the health care textile wire needs to be soaked in the flexible soaking agent for at least 3 times; the health care textile wire is cleaned in a mode of rinsing by clear water after being soaked in the flexible soaking agent.
The external adhesive liquid in the step (5) consists of the following components in parts by weight:
the preparation method is that the macromolecule xerogel particles, the aqueous mucilage, the dispersant, the penetrating agent, the defoaming agent, the aqueous color paste and a proper amount of purified water are mixed and then stirred at low speed for at least 5 minutes at normal temperature and normal pressure until no bubbles and particles are layered in the mixed solution, then the thickening agent, the solid paste, the curing agent, the quick-drying agent and the emulsifier are added into the mixed solution and stirred rapidly for 10 minutes at normal temperature and normal pressure, and finally the external attachment solution is formed.
Compared with the prior art, the invention has the following advantages and beneficial effects:
the fabric disclosed by the invention has a good health-care function, is softer and more comfortable in texture, can be better attached to the skin surface of a human body, greatly improves the using effect of the product, better enriches the types of health-care clothes, provides more choices for consumers, and well promotes the development of enterprises and industries.
Detailed Description
The present invention will be described in further detail with reference to examples, but the embodiments of the present invention are not limited thereto.
Example 1
A manufacturing method of a sleep-benefiting skin-beautifying fabric comprises the following process steps:
(1) preparing a health care textile thread;
the specific method comprises the following steps:
(11) uniformly mixing polyamide fiber powder, health-care powder and auxiliary materials to obtain a health-care mixture;
(12) mixing the health mixture to prepare health nylon master batch;
(13) spinning the health nylon master batch into a health line by a wire drawing machine;
(14) and baking the health care yarn in a drying box to obtain the health care textile yarn.
In the step (11), the particle size of the polyamide fiber powder is not more than 200nm, and the health-care mixture comprises the following components in parts by weight:
the far infrared functional powder is far infrared ceramic powder, the particle size of the far infrared ceramic powder is smaller than 0.3mm, the negative ion functional powder is tourmaline powder, the particle size of the tourmaline powder is smaller than 0.3mm, the magnetic field functional powder is a mixture of stone needle powder and volcano energy stone powder, and the weight ratio of the stone needle powder to the volcano energy stone powder is 3: 1, and the particle diameters of the stone needle powder and the volcanic energy stone powder are both less than 0.3 mm.
(2) Preparing a flexible soaking agent, and repeatedly soaking and cleaning the health care textile wire to obtain the flexible health care textile wire;
the flexible soaking agent comprises the following components in parts by weight:
the specific preparation method of the flexible soaking agent comprises the following steps:
(21) mixing fatty alcohol-polyoxyethylene ether, esterquat, polyphosphate and polyvinyl alcohol, adding clear water, stirring and heating, controlling the heating temperature within the range of 80-85 ℃, and continuously stirring for 10min to obtain a mixture A, wherein the weight ratio of the total weight of the fatty alcohol-polyoxyethylene ether, the esterquat, the polyphosphate and the polyvinyl alcohol to the clear water is 2: 3;
(22) mixing magnesium stearate, liquid paraffin, soda ash, glycerol and calcium hydrogen phosphate, and stirring at 95-105 deg.C for 15min to obtain mixture B;
(23) mixing and stirring the mixture A and the mixture B, standing for 3 hours after uniformly stirring, and filtering solid impurities to obtain filtrate C;
(24) sequentially adding bentonite, glacial acetic acid and coconut oil fatty acid diethanolamide into the filtrate C, continuously stirring, heating the filtrate C until the liquid temperature reaches 100 ℃, maintaining the temperature of the filtrate C at 100 ℃, continuously stirring for 15min, and finally filtering solid impurities to obtain the flexible soaking agent.
The single soaking time of the health care textile wire in the flexible soaking agent is 15-30min, the temperature of the flexible soaking agent for soaking the health care textile wire is maintained in the range of 60-70 ℃, and the health care textile wire needs to be soaked in the flexible soaking agent for at least 3 times; the health care textile wire is cleaned in a mode of rinsing by clear water after being soaked in the flexible soaking agent.
(3) Drying the flexible health care textile thread;
drying is a conventional technical means in the field, and is not described herein in detail.
(4) Making the dried flexible health textile yarns into flexible health base cloth;
the method for manufacturing the textile yarns into the base fabric is a conventional technical means in the field, and the base fabric can be compiled through different equipment or different textile methods according to different requirements, so that a person skilled in the art can flexibly select the base fabric according to actual requirements, and the details are not repeated herein.
(5) Preparing an external adhesion liquid;
the external adhesive liquid consists of the following components in parts by weight:
the preparation method is that the macromolecule xerogel particles, the aqueous mucilage, the dispersant, the penetrating agent, the defoaming agent, the aqueous color paste and a proper amount of purified water are mixed and then stirred at low speed for at least 5 minutes at normal temperature and normal pressure until no bubbles and particles are layered in the mixed solution, then the thickening agent, the solid paste, the curing agent, the quick-drying agent and the emulsifier are added into the mixed solution and stirred rapidly for 10 minutes at normal temperature and normal pressure, and finally the external attachment solution is formed.
(6) And coating the outer attachment liquid on the surface of the flexible health-care base cloth, and drying to obtain the flexible health-care underwear fabric.
Example 2
The difference between this example and example 1 is only that the components and the parts by weight of the components in the health mixture in step (11) are:
example 3
The difference between this example and examples 1 and 2 is only that the components and the parts by weight of the components in the health mixture in step (11) are:
example 4
The difference between the embodiment and the embodiment 1 is only that the components and the parts by weight in the flexible soaking agent in the step (2) are as follows:
example 5
The difference between the embodiment and the embodiments 1 and 4 is only that the components and the parts by weight in the flexible soaking agent in the step (2) are as follows:
example 6
The difference between the present embodiment and embodiment 1 is only that in step (5), the external adhesive solution is composed of the following components in parts by weight:
example 7
The difference between this example and examples 1 and 6 is only that the external adhesive liquid in step (5) is composed of the following components in parts by weight:
as described above, the present invention can be preferably realized.
Claims (7)
1. A manufacturing method of a sleep-benefiting skin-beautifying fabric is characterized by comprising the following steps: the method comprises the following process steps:
(1) preparing a health care textile thread;
(2) preparing a flexible soaking agent, and repeatedly soaking and cleaning the health care textile wire to obtain the flexible health care textile wire;
(3) drying the flexible health care textile thread;
(4) making the dried flexible health textile thread into flexible health base cloth;
(5) preparing an external adhesive liquid;
(6) and coating the outer attachment liquid on the surface of the flexible health-care base cloth, and drying to obtain the flexible health-care underwear fabric.
2. The manufacturing method of the sleep-promoting skin-beautifying fabric according to claim 1, characterized in that: the specific method of the step (1) comprises the following steps:
(11) uniformly mixing polyamide fiber powder, health-care powder and auxiliary materials to obtain a health-care mixture;
(12) mixing the health mixture to prepare health nylon master batch;
(13) spinning the health nylon master batch into a health line by a wire drawing machine;
(14) and baking the health care yarn in a drying box to obtain the health care textile yarn.
3. The manufacturing method of the sleep-promoting skin-beautifying fabric according to claim 2, characterized in that: in the step (11), the particle size of the polyamide fiber powder is not more than 200nm, and the health-care mixture comprises the following components in parts by weight:
4. the manufacturing method of the sleep-promoting skin-beautifying fabric according to claim 3, characterized in that: the far infrared functional powder is far infrared ceramic powder, the particle size of the far infrared ceramic powder is smaller than 0.3mm, the negative ion functional powder is tourmaline powder, the particle size of the tourmaline powder is smaller than 0.3mm, the magnetic field functional powder is a mixture of stone needle powder and volcano energy stone powder, and the weight ratio of the stone needle powder to the volcano energy stone powder is 3: 1, and the particle diameters of the stone needle powder and the volcanic energy stone powder are both less than 0.3 mm.
5. The manufacturing method of the sleep-promoting skin-beautifying fabric according to claim 4, characterized in that: the flexible soaking agent in the step (2) comprises the following components in parts by weight:
the specific preparation method of the flexible soaking agent comprises the following steps:
(21) mixing fatty alcohol-polyoxyethylene ether, esterquat, polyphosphate and polyvinyl alcohol, adding clear water, stirring and heating, and continuously stirring for 10min at the heating temperature of 80-85 ℃ to obtain a mixture A, wherein the weight ratio of the total weight of the fatty alcohol-polyoxyethylene ether, the esterquat, the polyphosphate and the polyvinyl alcohol to the clear water is 2: 3;
(22) mixing magnesium stearate, liquid paraffin, soda ash, glycerol and calcium hydrogen phosphate, and stirring at 95-105 deg.C for 15min to obtain mixture B;
(23) mixing and stirring the mixture A and the mixture B, standing for 3 hours after uniformly stirring, and filtering solid impurities to obtain filtrate C;
(24) sequentially adding bentonite, glacial acetic acid and coconut oil fatty acid diethanolamide into the filtrate C, continuously stirring, heating the filtrate C until the liquid temperature reaches 100 ℃, maintaining the temperature of the filtrate C at 100 ℃, continuously stirring for 15min, and finally filtering solid impurities to obtain the flexible soaking agent.
6. The manufacturing method of the sleep-promoting and skin-beautifying fabric according to claim 5, characterized in that:
in the step (2), the time for soaking the health care textile wire in the flexible soaking agent for one time is 15-30min, the temperature of the flexible soaking agent for soaking the health care textile wire is maintained within the range of 60-70 ℃, and the health care textile wire needs to be soaked in the flexible soaking agent for at least 3 times; the health care textile wire is cleaned in a clean water washing mode after being soaked in the flexible soaking agent.
7. The manufacturing method of the sleep-promoting skin-beautifying fabric according to claim 6, characterized in that: the external adhesive liquid in the step (5) consists of the following components in parts by weight:
the preparation method is that the macromolecule xerogel particles, the aqueous mucilage, the dispersant, the penetrating agent, the defoaming agent, the aqueous color paste and a proper amount of purified water are mixed and then stirred at low speed for at least 5 minutes at normal temperature and normal pressure until no bubbles and particles are layered in the mixed solution, then the thickening agent, the solid paste, the curing agent, the quick-drying agent and the emulsifier are added into the mixed solution and stirred rapidly for 10 minutes at normal temperature and normal pressure, and finally the external attachment solution is formed.