CN114892091A - 一种抗co2腐蚀油套管热轧圆管坯及其生产工艺 - Google Patents
一种抗co2腐蚀油套管热轧圆管坯及其生产工艺 Download PDFInfo
- Publication number
- CN114892091A CN114892091A CN202210588480.2A CN202210588480A CN114892091A CN 114892091 A CN114892091 A CN 114892091A CN 202210588480 A CN202210588480 A CN 202210588480A CN 114892091 A CN114892091 A CN 114892091A
- Authority
- CN
- China
- Prior art keywords
- equal
- round pipe
- pipe blank
- less
- hot
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种抗CO2腐蚀油套管热轧圆管坯及其生产工艺,热轧圆管坯的组成成分按质量百分数计为:C:0.18~0.24%、Si:0.25~0.35%、Mn:0.45~0.55%、P:≤0.015%、S:0~0.005%、Cr:2.80~3.20%、Mo:0.38~0.44%、Cu:0.20~0.30%、Ti:0.015~0.030%、Al:0.020~0.030%、V:≤0.020%、H:≤1.5ppm、O:≤40ppm、N:≤100ppm,余量为Fe和不可避免的杂质,屈服强度为758‑956Mpa,最小抗拉强度≥862MPa,伸长率≥0.6%,‑20℃冲击功≥40J,生产工艺包括依次的优化电炉炼钢、LF精炼、VD真空处理、连铸、加热、轧制和坑冷工序,A、B、C、D类夹杂在1.5级以内,DS类夹杂≤1.0级,中心疏松、一般疏松、中心偏析在1.5级以内,满足成品管的致密度和各项性能需求,适用于海洋油气钻探油套管的复杂工况,能够满足环境考验。
Description
技术领域
本发明属于合金钢技术领域,具体涉及一种海洋油气钻探用抗CO2腐蚀油套管热轧圆管 坯及其生产工艺。
背景技术
海洋油气钻探具有其特殊性,油套管的工作环境复杂,要求其性能要能够满足环境的考 验。现有油套管钢种的关键成分控制为C:0.26~0.28%、Si:0.19~0.25%、Mn:0.67~0.77%、 P≤0.012%、S:0~0.003%、Cr:0.96~1.03%、Mo:0.33~0.38%、Cu:≤0.10%、Ti:0.010~ 0.020%、Al:0.020~0.030%、Nb:0.016~0.020%、H:≤1.5ppm、O:≤40ppm、N:≤100ppm, 余量为Fe和不可避免的杂质,其屈服强度为655-758Mpa,最小抗拉强度≥724MPa,冲击功 (-20℃)≥35J,强度、韧性的力学性能和耐蚀性难以满足应用需求。同时为了满足海洋钻探 的性能需求,对钢水纯净度要求苛刻,现有生产工艺的热轧圆管坯非金属夹杂物较多,圆管 坯低倍质量、中心疏松、一般疏松、中心偏析难以满足海洋油气钻探用成品管的致密度和质 量要求。
发明内容
本发明旨在至少在一定程度上解决上述技术问题之一,本发明提供一种抗CO2腐蚀油套 管热轧圆管坯及其生产工艺,满足海洋油气钻探应用需求。
本发明解决其技术问题所采用的技术方案是:
一种抗CO2腐蚀油套管热轧圆管坯,其组成成分按质量百分数计为:C:0.18~0.24%、 Si:0.25~0.35%、Mn:0.45~0.55%、P:≤0.015%、S:0~0.005%、Cr:2.80~3.20%、Mo: 0.38~0.44%、Cu:0.20~0.30%、Ti:0.015~0.030%、Al:0.020~0.030%、V:≤0.020%、H: ≤1.5ppm、O:≤40ppm、N:≤100ppm,余量为Fe和不可避免的杂质。
上述抗CO2腐蚀油套管热轧圆管坯,优选地,所述热轧圆管坯的屈服强度为758-956Mpa, 最小抗拉强度≥862MPa,伸长率≥0.6%,-20℃冲击功≥40J。
上述抗CO2腐蚀油套管热轧圆管坯的化学成分设计原因为:
(1)C:降低C含量有利于提高塑性和热性,改善含有CO2等腐蚀环境下不锈钢的耐腐 蚀性,但C含量再低会影响热轧圆管坯强度,故C含量设计为0.18~0.24%。
(2)Si:Si能溶于铁素体和奥氏体中提高钢的硬度、屈服强度和屈服比,但Si过高会 降低钢的塑性和韧性,因此Si含量设计为0.25~0.35%。
(3)Mn:Mn能与Fe无限固溶,在提高钢材强度的同时,对塑性的影响相对较小,但Mn过高会降低钢的塑性,因此Mn含量设计为0.45~0.55%。
(4)Cr:Cr可提高碳钢的硬度和耐磨性而不使钢变脆,能提高碳素钢轧制状态的强度 和硬度,使组织细化和均匀分布,使钢有良好的抗CO2腐蚀等耐氧化性腐蚀的作用和热强性, 但Cr过高会影响热轧强度和钢的塑性,降低伸长率和断面收缩率,不利于受力,因此Cr含 量设计为2.80~3.20%。
(5)Mo:Mo能提高淬透性和热强性,进一步提高耐腐蚀性,但Mo过高会出现铁素体或其他脆性相时韧性降低,因此Mo含量设计为0.38~0.44%。
(6)Cu:增加Cu含量能与P联合改善钢的抗CO2腐蚀性能、提高强度和韧性,但Cu 过高会在热加工时产生热脆、影响塑性,因此Cu含量设计为0.20~0.30%。
(7)Ti:Ti是脱氧去气剂和固定氮和碳的有效元素,有细化晶粒,阻止晶粒长大、提高 钢的塑性和冲击韧性的、增大屈服强度、抗拉强度和屈服比的作用,但Ti过高会降低伸长率、 引起脆化效应,因此Ti含量设计为0.015~0.030%。
(8)Al:Al能细化钢的晶粒组织,阻抑低碳钢的时效,提高钢在低温下的韧性,还能与钼、铜、硅、铬等元素配合使用提高钢的抗氧化性,提高钢的耐磨性和疲劳强度,但Al 过高会影响钢的热加工性能,恶化钢水的可浇性,同时会造成B类(氧化铝)夹杂物增多, 因此Al含量设计为0.020~0.030%。
(9)V:V可以提高钢材强度、提高强度、韧性和抗氢腐蚀能力,降低钢的过热敏感性, 但V过高会阻碍钢的脱碳,V含量设计为≤0.020%。
(10)P、S:磷易引起塑性、冲击韧性显著降低,硫易降低钢的延展性和韧性,在锻造和轧制时造成裂纹,磷和硫含量越低越好,因此P含量设计为≤0.015%,S含量设计为0~0.005%,
上述抗CO2腐蚀油套管热轧圆管坯的生产工艺,其生产工艺包括将炼钢原料依次经电炉 炼钢、LF精炼、VD真空处理、连铸工序得到连铸圆坯,所述VD真空处理工序按铝线、硅 钙线顺序喂线处理,控制A、B、C、D类夹杂在1.5级以内,DS类夹杂≤1.0级,将连铸圆坯依次经加热、轧制和坑冷工序得到热轧圆管坯,控制圆管坯的中心疏松、一般疏松、中心偏析在1.5级以内。
上述抗CO2腐蚀油套管热轧圆管坯的生产工艺,优选地,所述电炉炼钢工序中将炼钢原 料经电炉冶炼得到钢水,电炉出钢终点C≥0.05%,目标碳0.06%≥C≥0.12%,电炉出钢目标 P≤0.008%,目标温度T≥1620℃,出钢过程中,每100-110t的钢水中加入石灰600kg,促净剂 200kg,出钢铝110-130kg/炉。
上述抗CO2腐蚀油套管热轧圆管坯的生产工艺,优选地,所述LF精炼工序中白渣保持 时间≥20min,冶炼时间≥40min,每100-110t钢水采用碳化硅100-140kg扩散脱氧。
上述抗CO2腐蚀油套管热轧圆管坯的生产工艺,优选地,所述VD真空处理工序控制VD 高真空度≤67Pa,高真空保持时间≥10min,氮气软吹时间≥15min。
上述抗CO2腐蚀油套管热轧圆管坯的生产工艺,优选地,所述连铸工序采用二冷冷却配 合结晶器电磁搅拌、铸流搅拌和末端电磁搅拌,一冷水流量为4000L/min,二冷水一区水流 量为40L/min,二冷水二区水流量为19L/min,结晶器电磁搅拌电流250A、频率为2Hz,铸 流搅拌电流为100A、频率为8Hz,末端电磁搅拌电流为1100A、频率为8Hz,控制拉速为0.35m/min。
上述抗CO2腐蚀油套管热轧圆管坯的生产工艺,优选地,所述加热工序的加热程序为: 预热段温度预热段温度<900℃,预热段目标860℃;加热I段时间>1.05h、加热I段温度 900-1100℃,加热I段目标温度1000℃;加热II段时间≥1.0h、加热II段温度1200-1260℃, 加热II段目标温度1230℃;均热段时间≥2h、均热段温度1200-1260℃,均热段目标温度1240℃, 总加热时间≥6.0h。
上述抗CO2腐蚀油套管热轧圆管坯的生产工艺,优选地,所述轧制工序包括将连铸圆坯 经开坯机后轧制成中间坯,经液压剪切头尾,采用9机架连轧机轧制,控制开轧温度950-1020℃,出连轧温度850-890℃。
上述抗CO2腐蚀油套管热轧圆管坯的生产工艺,优选地,所述坑冷工序中冷床温度> 450℃入坑缓冷,缓冷至温度≤200℃出坑,缓冷时间大于24h。
与现有技术相比,本发明的有益效果是:
(1)本发明的低合金高强钢采用降低C含量、增加Cr含量、并添加一定Cu含量,配合其他有效的化学成分设计、增加其耐蚀性,具有优异的力学性能和抗CO2腐蚀性能,热轧圆管坯的屈服强度为758-956Mpa,最小抗拉强度≥862MPa,伸长率≥0.6%,-20℃冲击功≥40J。
(2)采用优化的全新冶炼、连铸生产工艺,电路炼钢+LF工序中合适的冶炼周期保证合 金成分精准控制,有效提高钢水纯净度,VD后期需进行钙处理使夹杂物变性,增加钢水可 浇性,A、B、C、D类夹杂稳定地控制在1.5级以内,DS类夹杂物稳定地≤1.0级,连铸工序通过二冷冷却配合结晶器电磁搅拌、铸流搅拌和末端电磁搅拌,增加柱状晶比例控制圆管 坯的中心疏松、一般疏松、中心偏析稳定地控制在1.5级以内。
(3)采用优化的全新连轧生产工艺,采用优化的两段加热及一段均热加热程序和大压缩 量、大下压量控轧控冷工艺,使低倍质量显著提高。
综上,满足成品管的致密度和各项性能需求,适用于海洋油气钻探油套管的复杂工况, 能够满足环境考验。
附图说明
本发明的上述和/或附加的方面和优点从结合下面附图对实施例的描述中将变得明显和 容易理解,其中:
图1是本发明实施例1和对比例的低倍组织对比图。
图中1(a)表示实施例1的低倍组织图;图1(b)表示对比例的低倍组织图。
具体实施方式
下面详细描述本发明的实施例,所述实施例的示例在附图中示出,其中自始至终相同或 类似的标号表示相同或类似的元件或具有相同或类似功能的元件。下面通过参考附图描述的 实施例是示例性的,旨在用于解释本发明,而不能理解为对本发明的限制。
实施例1:本发明所述一种抗CO2腐蚀油套管热轧圆管坯的一种较佳实施方式,所述抗 CO2腐蚀油套管热轧圆管坯的组成成分按质量百分数(单位,wt%)计为:C:0.18%、Si: 0.29%、Mn:0.48%、P:0.007%、S:0.005%、Cr:2.93%、Mo:0.41%、Cu:0.22%、Ti:0.018%、Al:0.03%、V:0.012%、H:1.0ppm、O:30ppm、N:50ppm,余量为Fe和不可 避免的杂质。
实施例2:本发明所述一种抗CO2腐蚀油套管热轧圆管坯的一种较佳实施方式,所述抗 CO2腐蚀油套管热轧圆管坯的组成成分按质量百分数(单位,wt%)计为:C:0.19%、Si: 0.31%、Mn:0.5%、P:0.008%、S:0.003%、Cr:3%、Mo:0.4%、Cu:0.21%、Ti:0.016%、Al:0.029%、V:0.013%、H:1.1ppm、O:35ppm、N:60ppm,余量为Fe和不可避免的杂 质。
实施例3:本发明所述一种抗CO2腐蚀油套管热轧圆管坯的一种较佳实施方式,所述抗 CO2腐蚀油套管热轧圆管坯的组成成分按质量百分数(单位,wt%)计为:C:0.185%、Si: 0.3%、Mn:0.51%、P:0.009%、S:0.005%、Cr:3.12%、Mo:0.4%、Cu:0.21%、Ti:0.017%、 Al:0.027%、V:0.013%、H:1.1ppm、O:28.5ppm、N:55ppm,余量为Fe和不可避免的杂质。
实施例1-3所述抗CO2腐蚀油套管热轧圆管坯的生产工艺,其生产工艺包括以下工序:
S1、电炉炼钢:将炼钢原料经电炉冶炼得到钢水,控制电炉出钢终点C≥0.05%,目标碳 0.06%≥C≥0.12%,防止钢水过氧化,有利于夹杂物的去除;控制电炉出钢目标P≤0.008%,目 标温度T≥1620℃,控制合适的出钢温度,有效控制钢水回P;出钢过程中,每炉100-110t的 钢水中加入石灰600kg,促净剂(CaO53.5%,SiO23.5%,Al2O334.3%,MgO8.5%)200kg, 出钢铝110-130kg/炉,出钢造碱性渣有利于脱S;
S2、LF精炼:将经步骤S1的钢水采用沉淀脱氧结合扩散脱氧精炼,钢水进站造白渣, 有效吸附钢中的夹杂物,白渣保持时间≥20min,冶炼时间≥40min,通过足够白渣时间充分脱 去钢水中的氧含量,合适的冶炼周期保证合金成分精准控制,夹杂物充分上浮去除,每 100-110t钢水采用碳化硅100-140kg,以保证还原性气氛、扩散脱氧,确保钢水纯净度;
S3、VD真空处理:将经步骤S2的钢水进VD站真空处理,控制VD高真空度≤67Pa, 高真空保持时间≥10min,氮气软吹时间≥15min,去除钢水中的H,促进夹杂物充分上浮,每炉100-110t的钢水按铝线、硅钙线顺序喂线处理,首炉硅钙线100m,连浇炉硅钙线65m,喂铝线以调整钢水中的铝含量,VD后期钙处理使夹杂物变性球化,增加钢水可浇性,控制A、B、C、D类夹杂在1.5级以内,DS类夹杂≤1.0级;
S4、连铸:将经步骤S3的钢水全程保护浇铸防止二次氧化,采用二冷冷却配合结晶器电 磁搅拌、铸流搅拌和末端电磁搅拌,一冷水流量为4000L/min,一冷水快冷增加柱状晶比例 使钢坯致密性更好,二冷水一区水流量为40L/min,二冷水二区水流量为19L/min,通过二冷 水水量控制了连铸坯温度回升,改善了硫化物的聚集现象,结晶器电磁搅拌电流250A、频率 为2Hz,铸流搅拌电流为100A、频率为8Hz,末端电磁搅拌电流为1100A、频率为8Hz,通 过电磁搅拌技术有利于钢水补缩,控制拉速为0.35m/min得到连铸圆坯;
S5、加热:将步骤S4的连铸圆坯送至加热炉加热,加热炉的加热程序为:预热 段温度预热段温度<900℃,预热段目标860℃,钢坯预热减小钢坯开裂的风险,加热I段时 间>1.05h、加热I段温度900-1100℃,加热I段目标温度1000℃,加热II段时间≥1.0h、加 热II段温度1200-1260℃,加热II段目标温度1230℃,均热段时间≥2h、均热段温度1200-1260℃, 均热段目标温度1240℃,总加热时间≥6.0h,通过两段加热及一段均热,使连铸圆坯内外温度 均匀而又符合轧制要求的最佳温度;
S6、轧制:将经步骤S5的连铸圆坯经开坯机后轧制成270mm*280mm的中间坯, 经液压剪切头尾,采用9机架连轧机轧制,开轧温度950-1020℃,出连轧温度850-890℃, 通过控制开轧温度和出连轧温度细化晶粒度、提高力学性能,采用大压缩量、大下压量轧制 为热轧圆管坯,控制圆管坯的中心疏松、一般疏松、中心偏析在1.5级以内,改善了 内部致密性;
S7、坑冷:将经步骤S6的热轧圆管入冷床空冷,在冷床温度>450℃入坑缓冷, 缓冷至温度≤200℃出坑,缓冷时间大于24h得到热轧圆管坯,热轧圆管坯依次经取样、精整、 探伤后入库,所述热轧圆管坯的屈服强度为758-956Mpa,最小抗拉强度≥862MPa,伸长率 ≥0.6%,-20℃冲击功≥40J。
对比例:通过电炉炼钢、LF精炼、VD真空处理、连铸、缓冷、加热、轧制、坑冷工艺 制得的现有油套管热轧圆管坯的组成成分按质量百分数(单位,wt%)计为:C:0.26%、Si:0.22%、Mn:0.69%、P:0.009%、S:0.0015%、Cr:1%、Mo:0.35%、Cu:0.019%、Ti:0.015%、Al:0.024%、V:0.003%、Nb:0.017%、H:1.2ppm、O:28ppm、N:33ppm,余 量为Fe和不可避免的杂质,以GB/T 223标准检测成分,按照《金属材料室温拉伸试验工艺》 GB/T228标准检测拉伸性能,按照《金属材料弯曲试验工艺》GB/T232标准检测弯曲性能, 以金属材料夏比摆锤冲击试验工艺GB T 229标准进行冲击试验,热轧圆管坯的屈服强度为 655-758Mpa,最小抗拉强度≥724MPa,伸长率≥0.5%,-20℃冲击功≥35J。
将实施例1-3与对比例按照GB/T10561-2005标准进行非金属夹杂物评级,其结果如下表 1:
种类 | Ae | A | Be | B | Ce | C | De | D | DS |
实施例1 | 0 | 0 | 0 | 0 | 0 | 0 | 0.5 | 0.5 | 0 |
实施例2 | 0 | 0 | 0.5 | 0.5 | 0 | 0 | 0.5 | 0.5 | 0 |
实施例3 | 0 | 0 | 0.5 | 0 | 0 | 0 | 0.5 | 0.5 | 0.5 |
对比例 | 0.5 | 0.5 | 1.0 | 1.0 | 0 | 0 | 0.5 | 1.0 | 1.0 |
将实施例1-4与对比例按照GBT 226标准进行低倍组织及缺陷酸蚀检验,其结果如下表 2和附图1:
种类 | 中心疏松 | 一般疏松 | 中心偏析 |
实施例1 | 1.0 | 0.5 | 0 |
实施例2 | 1.0 | 1.0 | 0 |
实施例3 | 1.0 | 0.5 | 0 |
对比钢种 | 1.5 | 1.0 | 0 |
由上表1、表2和附图1的对比结果可知,本发明化学成分、非金属夹杂物、低倍均得到较好控制,本发明的低合金高强钢采用降低C含量、增加Cr含量、并添加一定Cu含量, 配合其他有效的化学成分设计、增加其耐蚀性,具有优异的力学性能和抗CO2腐蚀性能,满 足海洋钻探的性能需求,同时采用优化的全新冶炼、连铸和连轧生产工艺,电路炼钢+LF工 序采用合适的冶炼周期保证合金成分精准控制,有效提高钢水纯净度,VD后期需进行钙处 理使夹杂物变性,增加钢水可浇性,A、B、C、D类夹杂稳定地控制在1.5级以内,DS类夹 杂物稳定地≤1.0级,连铸工序通过二冷冷却配合结晶器电磁搅拌、铸流搅拌和末端电磁搅拌, 增加柱状晶比例控制圆管坯的中心疏松、一般疏松、中心偏析稳定地控制在1.5级以内,加 热和轧制工序采用优化的两段加热及一段均热加热程序和大压缩量、大下压量控轧控冷工艺, 使低倍质量显著提高,满足成品管的致密度和各项性能需求,适用于海洋油气钻探油套管的 复杂工况,能够满足环境考验。
本文所列出的一系列的详细说明仅仅是针对本发明的可行性实施例的具体说明,它们并 非用以限制本发明的保护范围,凡未脱离本发明技艺精神所作的等效实施例或变更均应包含 在本发明的保护范围之内。
Claims (10)
1.一种抗CO2腐蚀油套管热轧圆管坯,其特征在于,其组成成分按质量百分数计为:C:0.18~0.24%、Si:0.25~0.35%、Mn:0.45~0.55%、P:≤0.015%、S:0~0.005%、Cr:2.80~3.20%、Mo:0.38~0.44%、Cu:0.20~0.30%、Ti:0.015~0.030%、Al:0.020~0.030%、V:≤0.020%、H:≤1.5ppm、O:≤40ppm、N:≤100ppm,余量为Fe和不可避免的杂质。
2.根据权利要求1所述的一种抗CO2腐蚀油套管热轧圆管坯,其特征在于,所述热轧圆管坯的屈服强度为758-956Mpa,最小抗拉强度≥862MPa,伸长率≥0.6%,-20℃冲击功≥40J。
3.根据权利要求1或2所述的一种抗CO2腐蚀油套管热轧圆管坯的生产工艺,其特征在于,其生产工艺包括将炼钢原料依次经电炉炼钢、LF精炼、VD真空处理、连铸工序得到连铸圆坯,所述VD真空处理工序按铝线、硅钙线顺序喂线处理,控制A、B、C、D类夹杂在1.5级以内,DS类夹杂≤1.0级,将连铸圆坯依次经加热、轧制和坑冷工序得到热轧圆管坯,控制圆管坯的中心疏松、一般疏松、中心偏析在1.5级以内。
4.根据权利要求3所述的一种抗CO2腐蚀油套管热轧圆管坯的生产工艺,其特征在于,所述电炉炼钢工序中将炼钢原料经电炉冶炼得到钢水,电炉出钢终点C≥0.05%,目标碳0.06%≥C≥0.12%,电炉出钢目标P≤0.008%,目标温度T≥1620℃,出钢过程中,每100-110t的钢水中加入石灰600kg,促净剂200kg,出钢铝110-130kg/炉。
5.根据权利要求3所述的一种抗CO2腐蚀油套管热轧圆管坯的生产工艺,其特征在于,所述LF精炼工序中白渣保持时间≥20min,冶炼时间≥40min,每100-110t钢水采用碳化硅100-140kg扩散脱氧。
6.根据权利要求3所述的一种抗CO2腐蚀油套管热轧圆管坯的生产工艺,其特征在于,所述VD真空处理工序控制VD高真空度≤67Pa,高真空保持时间≥10min,氮气软吹时间≥15min。
7.根据权利要求3所述的一种抗CO2腐蚀油套管热轧圆管坯的生产工艺,其特征在于,所述连铸工序采用二冷冷却配合结晶器电磁搅拌、铸流搅拌和末端电磁搅拌,一冷水流量为4000L/min,二冷水一区水流量为40L/min,二冷水二区水流量为19L/min,结晶器电磁搅拌电流250A、频率为2Hz,铸流搅拌电流为100A、频率为8Hz,末端电磁搅拌电流为1100A、频率为8Hz,控制拉速为0.35m/min。
8.根据权利要求3所述的一种抗CO2腐蚀油套管热轧圆管坯的生产工艺,其特征在于,所述加热工序的加热程序为:预热段温度预热段温度<900℃,预热段目标860℃;加热I段时间>1.05h、加热I段温度900-1100℃,加热I段目标温度1000℃;加热II段时间≥1.0h、加热II段温度1200-1260℃,加热II段目标温度1230℃;均热段时间≥2h、均热段温度1200-1260℃,均热段目标温度1240℃,总加热时间≥6.0h。
9.根据权利要求3所述的一种抗CO2腐蚀油套管热轧圆管坯的生产工艺,其特征在于,所述轧制工序包括将连铸圆坯经开坯机后轧制成中间坯,经液压剪切头尾,采用9机架连轧机轧制,控制开轧温度950-1020℃,出连轧温度850-890℃。
10.根据权利要求3所述的一种抗CO2腐蚀油套管热轧圆管坯的生产工艺,其特征在于,所述坑冷工序中冷床温度>450℃入坑缓冷,缓冷至温度≤200℃出坑,缓冷时间大于24h。