CN114854339A - 一种粘接pet、bopp基材的水性封口胶及其制备方法 - Google Patents
一种粘接pet、bopp基材的水性封口胶及其制备方法 Download PDFInfo
- Publication number
- CN114854339A CN114854339A CN202210689723.1A CN202210689723A CN114854339A CN 114854339 A CN114854339 A CN 114854339A CN 202210689723 A CN202210689723 A CN 202210689723A CN 114854339 A CN114854339 A CN 114854339A
- Authority
- CN
- China
- Prior art keywords
- water
- temperature
- based sealing
- initiator
- pet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提出了一种粘接PET、BOPP基材的水性封口胶的制备方法，其特征在于，包括如下步骤：S1、于升温搅拌条件下，依次向釜体内加入A‑9乳化剂、丙烯酸、氢氧化钠以及208交联单体并进行搅拌；S2、向釜体内加入种子引发剂并升温至90℃保温20min；S3、釜体降温至85℃并向釜体内滴加单体及滴加引发剂完成后续反应过程，反应温度为81.5‑82.5℃；S4、于反应完成后向釜体内滴加保温引发剂保温1.5h；S5、依次滴加叔丁基、亚硫酸氢钠以及二酰肼，以150目滤布出料即得水性封口胶。本发明通过利用水做为介质，经济环保，于制作粘接PET、BOPP基材的水性封口胶过程中零VOC排放。
Description
技术领域
本发明涉及水性封口胶领域，尤其涉及一种粘接PET、BOPP基材的水性封口胶及其制备方法。
背景技术
现有粘接PET、BOPP基材的水性封口胶所用原料为甲苯、SBS、SIS、固体松香、120号溶剂油、萜烯树脂、C9石油树脂、C5石油树脂，所做出来的产品，含有甲苯溶剂，味道大，不环保，产品主要用于食品包装行业，对食品安全产生隐患。
发明内容
本发明要解决的技术问题是克服现有技术存在的缺陷，本发明提出了一种粘接PET、BOPP基材的水性封口胶及其制备方法，以解决上述技术问题。
为解决上述技术问题，本发明采用的技术方案是：一种粘接PET、BOPP基材的水性封口胶的制备方法，包括如下步骤：
S1、于升温搅拌条件下，依次向釜体内加入A-9乳化剂、丙烯酸、氢氧化钠以及208交联单体并进行搅拌，所述搅拌转速为25r/min；
S2、将釜底温度升至80℃并稳定5min，降低搅拌转速为17r/min并向釜体内加入种子引发剂并升温至90℃保温20min；
S3、釜体降温至85℃并向釜体内滴加单体及滴加引发剂完成后续反应过程，于所述反应过程中，反应温度为81.5-82.5℃；
S4、于反应完成后向釜体内滴加保温引发剂保温1.5h，保温温度为87-89℃；
S5、依次滴加叔丁基、亚硫酸氢钠以及二酰肼，持续降温至50℃并调节pH至5-5.5，以150目滤布出料即得所述粘接PET、BOPP基材的水性封口胶；
所述粘接PET、BOPP基材的水性封口胶以质量份数计包括230份丙烯酸丁酯，286份醋酸乙烯，316份丙烯酸异辛酯，100份甲基丙烯酸甲酯，470份vv10,7.8份双丙酮，0.65份硫醇，1027份水，26份A-6乳化剂，60份丙烯酸，9.1份氢氧化钠，45份208交联单体。
进一步地，于S5中，滴加保温引发剂，保温1.5小时，保温温度在87℃-89℃；保温完毕，开始降温，降至75℃时关闭降温水阀门，开始滴加叔丁基10分钟滴完，保温15分钟，此时温度在72℃，开始滴加亚硫酸氢钠，10分钟滴完，保温10分钟，此时温度于63℃-65℃，继续降温至50℃，加入二酰肼。
进一步地，于S1中，加入所述氢氧化钠之前，氢氧化钠以水化开，氢氧化钠与水的质量比为9.1：26。
进一步地，于S2中，所述种子引发剂加入前，种子引发剂以水化开，种子引发剂与水的质量比为3.9:13。
进一步地，于S3中，加入所述滴加引发剂之前以水化开，所述滴加引发剂与水的质量比为7.8:91。
进一步地，于S4中，滴加所述保温引发剂之前以水化开，所述保温引发剂与水的质量比为2.6:26。
进一步地，于S5中，滴加叔丁基、亚硫酸氢钠以及二酰肼前以水化开，所述叔丁基与水的质量比为0.8:26；所述亚硫酸氢钠与水的质量比为0.8:26；，所述二酰肼与水的质量比为3.9：26。
进一步地，一种粘接PET、BOPP基材的水性封口胶，依照权利要求1-7任一所述的粘接PET、BOPP基材的水性封口胶的制备方法制得。
与现有技术相比，本发明的有益效果包括：通过利用水做为介质，经济环保，而且同样可以达到溶剂型胶粘剂的要求，于制作粘接PET、BOPP基材的水性封口胶过程中零VOC排放。
具体实施方式
容易理解，根据本发明的技术方案，在不变更本发明实质精神下，本领域的一般技术人员可以提出可相互替换的多种结构方式以及实现方式。因此，以下具体实施方式仅是对本发明的技术方案的示例性说明，而不应当视为本发明的全部或者视为对本发明技术方案的限定或限制。
一种粘接PET、BOPP基材的水性封口胶，其组成如下表所示：
加入氢氧化钠之前，氢氧化钠以水化开，氢氧化钠与水的质量比为9.1：26。
种子引发剂加入前，种子引发剂以水化开，种子引发剂与水的质量比为3.9:13。
加入滴加引发剂之前以水化开，滴加引发剂与水的质量比为7.8:91。
滴加保温引发剂之前以水化开，保温引发剂与水的质量比为2.6:26。
滴加叔丁基、亚硫酸氢钠以及二酰肼前以水化开，叔丁基与水的质量比为0.8:26；亚硫酸氢钠与水的质量比为0.8:26；，二酰肼与水的质量比为3.9：26。
水性封口胶作工艺如下所示：
1、釡底加入水，开动搅拌机转速调为25转/分钟，通蒸汽开始升温；然后加入A-9乳化剂，搅拌10分钟。
2、加入丙烯酸，搅拌10分钟；加入氢氧化钠(用水化开)，搅拌10分钟。
3、加入208后搅拌，升温
4、当釡底温度升到80℃时，并稳定5分钟，釡底转速降到17转/分钟(釡底转速按实际情况调整，只要稍微有漩涡即可)，釡底加入种子引发剂，釡底开始反应，大概10分钟左右釡底温度会升到90度左右，然后釡底在90℃左右保温20分钟，降温至85℃，开始滴加单体和滴加引发剂，设计好滴加速度，按照4.5-5小时滴加完毕。前半个小时比正常速度慢，中间时间快，最后半个小时慢，全程反应温度控制在81.5℃---82.5℃，全程反应温度不要超过83℃，否则回流很大，在反应过程中主要观察回流、转速和温度，其一：如果回流越来越大，哪怕是变大一点，就开冷却水，一直开到回流消失或变小为止，如果温度降大了就排夹层水；其二：如果温度升高，哪怕是升高0.1℃，就开冷却水，一直开到温度降低为止，如果温度降大了就排夹层水；其三：在滴加单体过程中，当单体滴加到20分钟时，就要调转速至25转/分钟，同时每20分钟左右就要调转速，转速在2.5小时内就要调到35转/分钟；之后根据实际情况将转速调整至合适即可；其四：在单体还剩100公斤左右时，釡底温度控制在81℃--82℃，此时就要全开冷却水，否则，单体滴加完后回流会很大，全开冷却水将温度始终控制在85℃以下，如果温度和回流控制不住，就在引发剂槽处快速补加50公斤水，观察回流，当回流没有了，将夹层水全放空，滴加保温引发剂，保温1.5小时，保温温度在87℃-89℃。保温完毕，开始降温，降至75℃时关闭降温水阀门，开始滴加叔丁基10分钟滴完，保温15分钟，此时温度在72℃左右，开始滴加亚硫酸氢钠，10分钟滴完，保温10分钟，此时温度大概在63℃-65℃左右，继续降温至50℃左右，加入二酰肼(用水化开)，调PH至5，用150目滤布出料。
于上述调整pH过程中，可以氨水进行调整，且氨水可以用AMP-95或者片碱代替，乳液pH值可以调整到5-7之间。
基于上述水性封口胶制作工艺所制得的粘接PET、BOPP基材的水性封口胶，于其使用过程中，粘度控制在15000到20000cps作为机封胶使用，粘度控制在20000到30000cps作为手封胶使用，粘度控制在6000到8000cps作为喷胶使用。
本发明的技术范围不仅仅局限于上述说明中的内容，本领域技术人员可以在不脱离本发明技术思想的前提下，对上述实施例进行多种变形和修改，而这些变形和修改均应当属于本发明的保护范围内。
Claims (8)
1.一种粘接PET、BOPP基材的水性封口胶的制备方法，其特征在于，包括如下步骤：
S1、于升温搅拌条件下，依次向釜体内加入A-9乳化剂、丙烯酸、氢氧化钠以及208交联单体并进行搅拌，所述搅拌转速为25r/min；
S2、将釜底温度升至80℃并稳定5min，降低搅拌转速为17r/min并向釜体内加入种子引发剂并升温至90℃保温20min；
S3、釜体降温至85℃并向釜体内滴加单体及滴加引发剂完成后续反应过程，于所述反应过程中，反应温度为81.5-82.5℃；
S4、于反应完成后向釜体内滴加保温引发剂保温1.5h，保温温度为87-89℃；
S5、依次滴加叔丁基、亚硫酸氢钠以及二酰肼，持续降温至50℃并调节pH至5-5.5，以150目滤布出料即得所述粘接PET、BOPP基材的水性封口胶；
所述粘接PET、BOPP基材的水性封口胶以质量份数计包括230份丙烯酸丁酯，286份醋酸乙烯，316份丙烯酸异辛酯，100份甲基丙烯酸甲酯，470份vv10,7.8份双丙酮，0.65份硫醇，1027份水，26份A-6乳化剂，60份丙烯酸，9.1份氢氧化钠，45份208交联单体。
2.根据权利要求1所述的粘接PET、BOPP基材的水性封口胶的制备方法，其特征在于，于S5中，滴加保温引发剂，保温1.5小时，保温温度在87℃-89℃；保温完毕，开始降温，降至75℃时关闭降温水阀门，开始滴加叔丁基10分钟滴完，保温15分钟，此时温度在72℃，开始滴加亚硫酸氢钠，10分钟滴完，保温10分钟，此时温度于63℃-65℃，继续降温至50℃，加入二酰肼。
3.根据权利要求1所述的粘接PET、BOPP基材的水性封口胶的制备方法，其特征在于，于S1中，加入所述氢氧化钠之前，氢氧化钠以水化开，氢氧化钠与水的质量比为9.1：26。
4.根据权利要求1所述的粘接PET、BOPP基材的水性封口胶的制备方法，其特征在于，于S2中，所述种子引发剂加入前，种子引发剂以水化开，种子引发剂与水的质量比为3.9:13。
5.根据权利要求1所述的粘接PET、BOPP基材的水性封口胶的制备方法，其特征在于，于S3中，加入所述滴加引发剂之前以水化开，所述滴加引发剂与水的质量比为7.8:91。
6.根据权利要求1所述的粘接PET、BOPP基材的水性封口胶的制备方法，其特征在于，于S4中，滴加所述保温引发剂之前以水化开，所述保温引发剂与水的质量比为2.6:26。
7.根据权利要求1所述的粘接PET、BOPP基材的水性封口胶的制备方法，其特征在于，于S5中，滴加叔丁基、亚硫酸氢钠以及二酰肼前以水化开，所述叔丁基与水的质量比为0.8:26；所述亚硫酸氢钠与水的质量比为0.8:26；，所述二酰肼与水的质量比为3.9：26。
8.一种粘接PET、BOPP基材的水性封口胶，其特征在于，依照权利要求1-7任一所述的粘接PET、BOPP基材的水性封口胶的制备方法制得。