CN102433095A - 新型白乳胶及其生产方法 - Google Patents
新型白乳胶及其生产方法 Download PDFInfo
- Publication number
- CN102433095A CN102433095A CN2011102521283A CN201110252128A CN102433095A CN 102433095 A CN102433095 A CN 102433095A CN 2011102521283 A CN2011102521283 A CN 2011102521283A CN 201110252128 A CN201110252128 A CN 201110252128A CN 102433095 A CN102433095 A CN 102433095A
- Authority
- CN
- China
- Prior art keywords
- temperature
- white latex
- functional filler
- gum
- sodium hydroxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种新型白乳胶,包括聚乙烯醇、醋酸乙烯酯、丙烯酸、改性剂、邻苯二甲酸二丁酯、玉米淀粉、功能性填料、复合乳化剂、防腐剂、过硫酸铵和氢氧化钠;生产方法如下:在瓶中加入量好的水;边搅拌加入聚乙烯醇;升温至90℃保持30分钟;然后降至75℃,加入复合乳化剂,1/3的引发剂开始滴加共聚单体,温度控制在75℃~85℃之间,单体在四小时内滴加完,中间补加过硫酸铵;滴完单体保温一段时间,降温加入玉米淀粉,控制糊化温度;保温半小时后加入功能性填料、邻苯二甲酸二丁酯;降温并加入NaOH调节pH值4~4.5,加入防腐剂搅拌即可。本发明的白乳胶不仅粘合性高、粘接强度好、低温稳定性好,而且成本低。
Description
技术领域
本发明涉及一种粘合剂,尤其是一种新型白乳胶,还涉及该种白乳胶的生产方法。
背景技术
聚醋酸乙烯PVAC作为常用的环保、安全的胶粘剂之一,由于它具有粘接强度高,固化速度快,生产工艺简单和使用方便等优点,故应用范围广。但随着原料价格的不断升高,生产此类胶粘剂的企业成本压力不断加大。玉米淀粉价格相对便宜,广泛易得,但加入聚醋酸乙烯乳液中量大就会影响产品的低温稳定性和胶膜的强度。因此在保证白乳胶性能的情况下,提高玉米淀粉的用量,减少PVA的用量,即可明显降低成本。
发明内容
本发明的前一目的是提供一种不仅粘合性高、粘接强度好、低温稳定性好,而且成本低的新型白乳胶。
本发明的后一目的是提供制备前一目的白乳胶的加工方法。
为实现前一目的,本发明所采用的技术方案是:一种新型白乳胶,包括聚乙烯醇PVA、醋酸乙烯酯VAC、丙烯酸AA、改性剂、邻苯二甲酸二丁酯DBP、玉米淀粉、功能性填料、复合乳化剂、防腐剂、过硫酸铵和氢氧化钠NaOH,各组分的配比为(按重量百分比):
聚乙烯醇PVA 1.8%-2.5%
醋酸乙烯酯VAC 23%-27%
丙烯酸AA 0.3%-0.8%
改性剂DF-608 0.8%-1.5%
邻苯二甲酸二丁酯DBP 2.5%-4%
玉米淀粉 5%-7%
功能性填料 3%-6%
复合乳化剂 0.15%-0.3%
防腐剂 0.2%-0.3%
过硫酸铵 0.1%-0.15%
水 56%-58%
氢氧化钠NaOH 0.1%-0.2%。
所述复合乳化剂由壬基酚聚氧乙烯醚琥珀黄酸盐DNS-1035和壬基酚聚氧乙烯醚OP-10组成,它们的配比为 1:2~2:1之间的任意值。
本发明的白乳胶以丙烯酸AA以及功能性改型剂对醋酸乙烯酯VAC进行共聚改性,减少聚乙烯醇PVA的用量,加入玉米淀粉及功能性填充料,制成的胶粘剂不仅初粘力和粘接强度有不同程度的提高,并且产品具有良好的低温稳定性。产品在性价比上有较高优势,具有广阔的市场前景。本发明改善了普通白胶的低温稳定性,提高了产品的内聚强度和附着力,明显降低了成本。
为了实现后一目的,本发明还提供了一种上述白乳胶的生产方法,该方法包括如下步骤:
(1)在装有回流冷凝器、温度计和滴液漏斗的四口瓶中加入量好的水;
(2)边搅拌边加入聚乙烯醇PVA;慢慢升温至90℃保持30分钟;
(3)然后等温度降至75℃,加入复合乳化剂,1/3的引发剂并开始滴加共聚单体,反应温度控制在75℃~85℃之间,单体在四小时内滴加完,中间补加引发剂过硫酸铵;
(4)滴完单体保温一段时间,开始降温加入玉米淀粉,控制糊化温度;
(5)保温半小时后加入功能性填料、邻苯二甲酸二丁酯;
(6)继续降温并加入10%的NaOH调节PH值4~4.5,加入防腐剂搅拌即可。
采用上述生产方法,科学合理地安排原料加入次序,采用合理的温度时间,利用共聚反应即可得到本发明的白乳胶。
具体实施方式
下面结合具体实施例对本发明的白乳胶极其生产方法作具体说明,以助于理解本发明的内容。
实施例1
所用原料配方为:
聚乙烯醇PVA 2kg、醋酸乙烯酯VAC 25 kg、丙烯酸AA 0.5 kg、改性剂DF-608 1 kg、邻苯二甲酸二丁酯DBP 3 kg、玉米淀粉 6 kg、功能性填料 5 kg、DNS-1035 0.1 kg、OP-10 0.1kg、防腐剂 0.2 kg、过硫酸铵0.1 kg、水56.85 kg、氢氧化钠NaOH 0.15 kg。
其生产方法为:
(1)在装有回流冷凝器、温度计和滴液漏斗的四口瓶中加入量好的水;(2)边搅拌边加入聚乙烯醇PVA;慢慢升温至90℃保持30分钟;(3)然后等温度降至75℃,加入DNS-1035和OP-10复合乳化剂,1/3的引发剂并开始滴加共聚单体,反应温度控制在75℃~85℃之间,单体在四小时内滴加完,中间补加引发剂过硫酸铵,(4)滴完单体保温一段时间,开始降温加入玉米淀粉,控制糊化温度;(5)保温半小时后加入功能性填料、邻苯二甲酸二丁酯DBP;(6)继续降温并加入NaOH调节PH值4~4.5,加入防腐剂搅拌即可出成品。
实施例2
所用原料配方为:
聚乙烯醇PVA1.8kg 、醋酸乙烯酯VAC27 kg、丙烯酸AA 0.3 kg、改性剂DF-608 0.8 kg、邻苯二甲酸二丁酯DBP 2.5 kg、 玉米淀粉5 kg、功能性填料 4.05 kg、DNS-1035 0.05 kg、OP-10乳化剂0.1 kg、 防腐剂 0.2 kg、过硫酸铵 0.1 kg、水 58kg、氢氧化钠NaOH 0.1 kg。
其生产方法同实施例1。
实施例3
所用原料配方为:
聚乙烯醇PVA 2.5kg 、醋酸乙烯酯VAC 23 kg、丙烯酸AA 0.8 kg、改性剂DF-608 1.5 kg、 邻苯二甲酸二丁酯DBP 4 kg、 玉米淀粉7 kg、 功能性填料 4.25 kg、DNS-1035 0.2 kg、OP-10乳化剂0.1 kg、 防腐剂 0.3 kg、过硫酸铵0.15 kg、水 56 kg、 氢氧化钠NaOH 0.2 kg。
其生产方法同实施例1。
实施例4
所用原料配方为:
聚乙烯醇PVA 2kg、醋酸乙烯酯VAC 26 kg、丙烯酸AA 0.4 kg、改性剂DF-608 1 .4 kg、邻苯二甲酸二丁酯DBP 3.5 kg、 玉米淀粉5 kg、 功能性填料 3 kg、DNS-1035 0.1kg和OP-10乳化剂0.1 kg、防腐剂 KGS 0.25 kg、过硫酸铵0.1 kg、 水 58 kg、 氢氧化钠NaOH 0.15 kg。
其生产方法同实施例1。
实施例5
所用原料配方为:
聚乙烯醇PVA 1.8kg、 醋酸乙烯酯VAC 24 kg、丙烯酸AA 0.6 kg、改性剂DF-608 0.8 kg、邻苯二甲酸二丁酯DBP 3 kg、 玉米淀粉6 kg、 功能性填料 6 kg、DNS-1035 0.1 kg、OP-10乳化剂0.2 kg、防腐剂 0.3 kg、过硫酸铵0.1 kg、 水57 kg、 氢氧化钠NaOH 0.1 kg。 其生产方法同实施例1。
上述的DF-608为功能***联剂的一种。
以上所述是本发明的优选实施方式而已,当然不能以此来限定本发明之权利范围,应当指出,对于本技术领域的普通技术人员来说,对本发明的技术方案进行修改或者等同替换,都不脱离本发明技术方案的保护范围。
Claims (3)
1.一种新型白乳胶,其特征是包括聚乙烯醇PVA、醋酸乙烯酯VAC、丙烯酸AA、改性剂、邻苯二甲酸二丁酯DBP、玉米淀粉、功能性填料、复合乳化剂、防腐剂、过硫酸铵和氢氧化钠NaOH,各组分的配比为(按重量百分比):
聚乙烯醇PVA 1.8%-2.5%
醋酸乙烯酯VAC 23%-27%
丙烯酸AA 0.3%-0.8%
改性剂DF-608 0.8%-1.5%
邻苯二甲酸二丁酯DBP 2.5%-4%
玉米淀粉 5%-7%
功能性填料 3%-6%
复合乳化剂 0.15%-0.3%
防腐剂 0.2%-0.3%
过硫酸铵 0.1%-0.15%
水 56%-58%
氢氧化钠NaOH 0.1%-0.2% 。
2.根据权利要求1所述的新型白乳胶,其特征是:所述复合乳化剂由壬基酚聚氧乙烯醚琥珀黄酸盐DNS-1035和壬基酚聚氧乙烯醚OP-10组成,它们的配比为 1:2~2:1之间的任意值。
3.一种权利要求1所述的新型白乳胶生产方法,该方法包括如下步骤:
(1)在装有回流冷凝器、温度计和滴液漏斗的四口瓶中加入量好的水;
(2)边搅拌边加入聚乙烯醇PVA;慢慢升温至90℃保持30分钟;
(3)然后等温度降至75℃,加入复合乳化剂,1/3的引发剂并开始滴加共聚单体,反应温度控制在75℃~85℃之间,单体在四小时内滴加完,中间补加引发剂过硫酸铵;
(4)滴完单体保温一段时间,开始降温加入玉米淀粉,控制糊化温度;
(5)保温半小时后加入功能性填料、邻苯二甲酸二丁酯;
(6)继续降温并加入NaOH调节PH值4~4.5,加入防腐剂搅拌即可。