CN114349456A - 一种环保轻质抹灰石膏的制备方法 - Google Patents

一种环保轻质抹灰石膏的制备方法 Download PDF

Info

Publication number
CN114349456A
CN114349456A CN202210074000.0A CN202210074000A CN114349456A CN 114349456 A CN114349456 A CN 114349456A CN 202210074000 A CN202210074000 A CN 202210074000A CN 114349456 A CN114349456 A CN 114349456A
Authority
CN
China
Prior art keywords
environment
plastering gypsum
light plastering
gypsum
friendly light
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202210074000.0A
Other languages
English (en)
Inventor
李双贵
袁丽丹
单兴宇
徐启勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Yuanfeng New Building Materials Technology Co ltd
Original Assignee
Jiangsu Yuanfeng New Building Materials Technology Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Yuanfeng New Building Materials Technology Co ltd filed Critical Jiangsu Yuanfeng New Building Materials Technology Co ltd
Priority to CN202210074000.0A priority Critical patent/CN114349456A/zh
Publication of CN114349456A publication Critical patent/CN114349456A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种环保轻质抹灰石膏的制备方法，该环保轻质抹灰石膏由如下重量份的原料制成：脱硫石膏750‑800kg、煤渣20‑30kg、煤灰20‑80kg，重钙粉45‑55kg，膨胀珍珠岩80‑100kg，胶凝材料3‑5kg，膨化蛭石1‑2kg。本发明所述的环保轻质抹灰石膏以废弃的脱硫石膏、煤渣、煤灰粉作为主料，并添加胶凝材料以及膨化蛭石混合制成，不仅实现废弃物料的循环利用，使得该轻质抹灰石膏更加的经济环保，而且使得生产出的轻质抹灰石膏在使用时能够产生大量的负离子，有益于人体健康，提高了轻质抹灰石膏的使用效果。

Description

一种环保轻质抹灰石膏的制备方法
技术领域
本发明属于建筑材料技术领域，尤其是涉及一种环保轻质抹灰石膏的制备方法。
背景技术
在建筑装饰过程中，为了确保室内墙面的整洁美观，常需要在室内墙面上涂抹一层轻质抹灰石膏。
然而目前的轻质抹灰石膏主要采用天然矿石粉磨后与缓凝剂、减水剂等辅助添加剂混合制备而成，一方面使得轻质抹灰石膏的制备成本较高，另一方面轻质抹灰石膏在使用后会散发异味，不利于人体健康，降低了轻质抹灰石膏的使用效果。
发明内容
有鉴于此，本发明旨在提出一种环保轻质抹灰石膏的制备方法，该环保轻质抹灰石膏以废弃的脱硫石膏、煤渣、煤灰粉作为主料，并添加胶凝材料以及膨化蛭石混合制成，不仅实现废弃物料的循环利用，使得该轻质抹灰石膏更加的经济环保，而且使得生产出的轻质抹灰石膏在使用时能够产生大量的负离子，有益于人体健康，提高了轻质抹灰石膏的使用效果。
为达到上述目的，本发明的技术方案是这样实现的：
一种环保轻质抹灰石膏的制备方法，该环保轻质抹灰石膏由如下重量份的原料制成：脱硫石膏750-800kg、煤渣20-30kg、煤灰20-80kg，重钙粉45-55kg，膨胀珍珠岩80-100kg，胶凝材料3-5kg，膨化蛭石1-2kg。
进一步的，该环保轻质抹灰石膏的最优配比为：脱硫石膏780kg，煤渣20kg，煤灰50kg，重钙粉50kg，膨胀珍珠岩95kg，胶凝材料5kg,膨化蛭石1kg。
进一步的，所述胶凝材料由羟丙甲基纤维素HPMC、触变剂以及缓凝剂按照1:1:3的比列混合制得，所述触变剂为钠基膨润土，所述缓凝剂为无机酸类缓凝剂。
进一步的，所述膨化蛭石以及所述膨胀珍珠岩均为粉末状产品，所述膨化蛭石是高绝缘的层状云母片组成的电容器结构，能够大量吸附空气中的电荷，逐渐堆积的电荷碰到水分子以后，能在层状云母片边缘产生放电电离效应，能将空气中的水电离产生空气负离子，采用膨化蛭石制备的涂料在遇水后能够产生大量的负离子，低能量激发的负离子是以OH-(H2O)n为主的小粒径纳米负离子，小粒径负离子又良好的生物活性，易于透过人体血脑屏障，进入人体细胞发挥生物效应。
所述的环保轻质抹灰石膏的制备方法，包括如下步骤：
步骤(1)：按照最优配比将脱硫石膏、煤渣、煤灰粉与重钙粉以及膨胀珍珠岩按照比例进行混合搅拌，得到混合物料A，备用；
步骤(2)：将步骤(1)中所得到的混合物料A与混合好的胶凝材料进行混合搅拌，得到混合物料B，备用；
步骤(3)：向步骤(2)中混合好的物料中加入相应的膨化蛭石进行搅拌，待膨化蛭石与混合物料均匀混合后，便可制得该环保轻质抹灰石膏。
进一步的，该环保轻质抹灰石膏的使用方法如下：使用时首先按照水料比为1:3的比例将环保轻质抹灰石膏粉末搅拌至泥浆状，然后只需通过抹平板将环保轻质抹灰石膏涂抹到室内墙面上，即可使得该环保轻质抹灰石膏投入使用。
相对于现有技术，本发明所述的环保轻质抹灰石膏具有以下优势：
本发明所述的环保轻质抹灰石膏以废弃的脱硫石膏、煤渣、煤灰粉作为主料，并添加胶凝材料以及膨化蛭石混合制成，不仅实现废弃物料的循环利用，使得该轻质抹灰石膏更加的经济环保，而且使得生产出的轻质抹灰石膏在使用时能够产生大量的负离子，有益于人体健康，提高了轻质抹灰石膏的使用效果。
具体实施方式
除有定义外，以下实施例中所用的技术术语具有与本发明所属领域技术人员普遍理解的相同含义。
下面来详细说明本发明。
一种环保轻质抹灰石膏的制备方法，脱硫石膏750-800kg、煤渣20-30kg、煤灰20-80kg，重钙粉45-55kg，膨胀珍珠岩80-100kg，胶凝材料3-5kg，膨化蛭石1-2kg。
本实施例中，该环保轻质抹灰石膏的最优配比为：脱硫石膏780kg，煤渣20kg，煤灰50kg，重钙粉50kg，膨胀珍珠岩95kg，胶凝材料5kg,膨化蛭石1kg。
本实施例中，所述胶凝材料由羟丙甲基纤维素HPMC、触变剂以及缓凝剂按照1:1:3的比列混合制得，所述触变剂为钠基膨润土，所述缓凝剂为无机酸类缓凝剂。
本实施例中，所述膨化蛭石以及所述膨胀珍珠岩均为粉末状产品，所述膨化蛭石是高绝缘的层状云母片组成的电容器结构，能够大量吸附空气中的电荷，逐渐堆积的电荷碰到水分子以后，能在层状云母片边缘产生放电电离效应，能将空气中的水电离产生空气负离子，采用膨化蛭石制备的涂料在遇水后能够产生大量的负离子，低能量激发的负离子是以OH-(H2O)n为主的小粒径纳米负离子，小粒径负离子又良好的生物活性，易于透过人体血脑屏障，进入人体细胞发挥生物效应。
所述的环保轻质抹灰石膏的制备方法，包括如下步骤：
步骤(1)：按照最优配比将脱硫石膏、煤渣、煤灰粉与重钙粉以及膨胀珍珠岩按照比例进行混合搅拌，得到混合物料A，备用；
步骤(2)：将步骤(1)中所得到的混合物料A与混合好的胶凝材料进行混合搅拌，得到混合物料B，备用；
步骤(3)：向步骤(2)中混合好的物料中加入相应的膨化蛭石进行搅拌，待膨化蛭石与混合物料均匀混合后，便可制得该环保轻质抹灰石膏。
本实施例中，该环保轻质抹灰石膏的使用方法如下：使用时首先按照水料比为1:3的比例将环保轻质抹灰石膏粉末搅拌至泥浆状，然后只需通过抹平板将环保轻质抹灰石膏涂抹到室内墙面上，即可使得该环保轻质抹灰石膏投入使用。
以上所述仅为本发明的较佳实施例而已，并不用以限制本发明，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (6)

1.一种环保轻质抹灰石膏的制备方法，其特征在于：该环保轻质抹灰石膏由如下重量份的原料制成：脱硫石膏750-800kg、煤渣20-30kg、煤灰20-80kg，重钙粉45-55kg，膨胀珍珠岩80-100kg，胶凝材料3-5kg，膨化蛭石1-2kg。
2.根据权利要求1所述的环保轻质抹灰石膏的制备方法，其特征在于：该环保轻质抹灰石膏的最优配比为：脱硫石膏780kg，煤渣20kg，煤灰50kg，重钙粉50kg，膨胀珍珠岩95kg，胶凝材料5kg,膨化蛭石1kg。
3.根据权利要求1所述的环保轻质抹灰石膏的制备方法，其特征在于：所述胶凝材料由羟丙甲基纤维素HPMC、触变剂以及缓凝剂按照1:1:3的比列混合制得。
4.根据权利要求1所述的环保轻质抹灰石膏的制备方法，其特征在于：所述膨化蛭石以及所述膨胀珍珠岩均为粉末状产品。
5.权利要求1-4中任一项所述的环保轻质抹灰石膏的制备方法，其特征在于：包括如下步骤：
步骤(1)：按照最优配比将脱硫石膏、煤渣、煤灰粉、与重钙粉以及膨胀珍珠岩按照比例进行混合搅拌，得到混合物料A，备用；
步骤(2)：将步骤(1)中所得到的混合物料A与混合好的胶凝材料进行混合搅拌，得到混合物料B，备用；
步骤(3)：向步骤(2)中混合好的物料中加入相应的膨化蛭石进行搅拌，待膨化蛭石与混合物料均匀混合后，便可制得该环保轻质抹灰石膏。
6.根据权利要求5所述的环保轻质抹灰石膏的制备方法，其特征在于：该环保轻质抹灰石膏的使用方法如下：使用时首先按照水料比为1:3的比例将环保轻质抹灰石粉末搅拌至泥浆状，然后只需通过抹平板将环保轻质抹灰石膏涂抹到室内墙面上，即可使得该环保轻质抹灰石膏投入使用。
CN202210074000.0A 2022-01-21 2022-01-21 一种环保轻质抹灰石膏的制备方法 Pending CN114349456A (zh)