CN114230592A - 一种饱和碳链类电解质及其制备和应用 - Google Patents
一种饱和碳链类电解质及其制备和应用 Download PDFInfo
- Publication number
- CN114230592A CN114230592A CN202010941839.0A CN202010941839A CN114230592A CN 114230592 A CN114230592 A CN 114230592A CN 202010941839 A CN202010941839 A CN 202010941839A CN 114230592 A CN114230592 A CN 114230592A
- Authority
- CN
- China
- Prior art keywords
- electrolyte
- chain
- substituent
- battery
- independently
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
技术领域
本发明涉及电池技术领域,具体涉及一种饱和碳链类电解质及其制备和应用。
背景技术
电解质是二次电池的重要及必要组成,锂/钠电池具有高能量密度、高电压、循环次数多、储存时间长等优点,自从商业化以来,被广泛应用于电动汽车、储能电站、无人机、便携式设备等各个方面,无论哪种应用方向,均迫切需要在保证电池安全性的前提下提高电池的能量密度和循环性能。
锂/钠电池主要包括正极、负极、电解质和隔膜,提高电池的能量密度就是要提高电池的工作电压和放电容量,即使用高电压高容量正极材料和低电压高容量负极材料;提高电池的循环性能主要是提高电解质与正负极之间形成的界面层的稳定性。
以锂电池为例,目前锂电池中,常用的正极材料包括高电压钴酸锂(LCO)、高镍三元 (NCM811、NCM622、NCM532和NCA)、镍锰酸锂(LNMO)、富锂(Li-rich)等;常用的负极材料包括金属锂、石墨、硅碳、硅氧碳等;常用的隔膜主要为聚乙烯、聚丙烯多孔膜。电解质包括液态电解质和固态电解质,液态电解质为锂盐和非水溶剂的混合物,按照溶剂类型分为碳酸酯类电解质和醚类电解质;固态电解质主要包括聚合物电解质、无机氧化物电解质、硫化物电解质。其中,硫化物电解质对空气极其敏感、电化学窗口较窄、对正极不稳定;氧化物电解质硬度太大、脆性大;聚合物电解质电化学窗口不宽、电导率低、离子迁移数低。因此目前常用的电解质以液态电解液居多,少数使用聚合物电解质。此外,当高电压正极、低电压负极匹配常规液态电解液时,在首周会消耗部分从正极脱出的锂离子,而在正负极颗粒表面形成只导离子、不导电子的钝化层,若形成的钝化层不稳定,随着循环次数的增加,钝化层不断破坏、形成,因此不断消耗电池中的活性锂离子,导致电池首周放电容量较低、容量衰减严重,电池很快失效。钠离子电池也存在类似问题。
常常在电解液中加入一些添加剂来提高电池性能,如氟代碳酸乙烯酯、碳酸亚乙烯酯等,但常规电解液添加剂中常常不含可以解离的离子,只能通过消耗正极的离子来形成表面钝化层,因此首效和放电比容均比较低。若添加的盐/添加剂能在电极表面形成一层传导离子、且稳定性好的钝化层,那么可以将电化学窗口窄的液态电解质、聚合物电解质应用于高电压电池体系中。此外,目前商用的锂/钠盐价格均非常高,造成整个电池的成本也比较高,若有一类新的锂/钠盐或代替现有技术锂/钠盐的其它盐类能够兼顾高性能和低成本,那么电池的价格必将大大降低。
本申请人的其中一个研究团队一直在对含有通过一个羟基-OH取代后得到的-OBF3M基团的化合物进行研究。由于-OBF3是一个强极性的基团,其能够与阳离子形成盐结构,因此, -OBF3M在一个分子结构中,具有很强的存在感,其可能会改变整个分子结构的性质。而在现有技术中,也仅有极个别研究者对含有BF3基团的化合物进行零星的研究,且都是仅对含有一个BF3基团进行研究,目前,并没有太大成果,更没有发现工业应用的成果;现有技术中鲜有针对-O-BF3M基团进行研究,更没有针对含有两个-OBF3M基团的研究发表。这还是因为-OBF3M的存在感强,若在分子中增加-OBF3M数量,可能会对整个分子结构的整体性质产生不可预料的改变,因此,研究团队如果进行含有两个或多个-OBF3M的研究,阻力会大大增加,可能耗费的时间成本和经济成本极大,且结果也不好预测,因此,本研究团队一直仅对含有一个-OBF3M进行研究。即使对含有一个-OBF3M进行研究,由于现有技术极少,借鉴价值也很小,而对于两个该基团的研究更没有任何的借鉴源了。本研究团队也是在偶然的研究中意外的发现含有双羟基取代的-OBF3M有机物在液态电解质和固态电解质中,应用于锂/钠电池,制备的电池经测试,性能优异效果很惊喜,因此,专门成立团队进行专门研究双取代的-OBF3M,并取得了较好的研究成果。
更重要的是,本申请针对-OBF3M连接于饱和链状的结构上进行独立研究,即两个-OBF3M均连接于饱和碳链上。这是因为,其本身的电性等化学性质也是比较特殊自成一体的,而两个强极性的-OBF3M连接于饱和碳链上时,也会影响整个链的化学和物理性质,其与环和其它类型的链结构等等都有实质性不同的地方,故彼此之间的关联性或可推断性不确定。因此,在饱和碳链上连接-OBF3M时,可能会产生不同于其他结构的效果,尤其连接两个-OBF3M时,其可能具有更意想不到的优异效果。故本申请将研究对象确定为在饱和链上连接两个-O-BF3M,以此来更加有针对性更明确的确定-O-BF3M连接饱和链的具体情况。
发明内容
本发明针对现有技术的缺陷提供了一种饱和碳链类电解质及其制备和应用,旨在克服现有技术中的不足。
本发明的目的是通过以下技术方案来实现:
本发明的一个发明点为提供一种饱和碳链类电解质,所述电解质包括以下通式I所表示的饱和碳链类三氟化硼盐:
在以上通式Ⅰ中,R、R1独立地为无或含有至少一个碳原子的第一链;且R和R1不同时为无;R2或R3独立地为无或含有至少一个碳原子的第二链;与-OBF3M连接的原子为碳原子C;M为金属阳离子;第一链和第二链均为饱和碳链;所述第一链和第二链中的任意一个C 上的H均可独立地被取代基取代。
优选地,在通式Ⅰ中,R或R1独立地为1-30个原子的饱和碳链;R2、R3独立地为0-5个原子的饱和碳链。
优选地,所述取代基包括H、饱和烷基或环状取代基。进一步优选地,该环状取代基包括三元环、四元环、五元环、六元环、七元环、八元环和同时含有两个或两个以上环结构的多环取代基;该环状取代基上能够选择连接第一取代基。
优选地,结构通式Ⅰ中的主链为1-20个碳原子长的链;所述第二链为0-3个原子的饱和碳链。
优选地,在通式Ⅰ中,包括:(1)R2与R3均为无,R与R1独立地为含有至少一个碳原子的第一链,记为两个-OBF3M分别连接于R和R1中的任意一个C原子上;(2)R1、 R2与R3均为无,R为含有至少一个碳原子的第一链,两个-OBF3M连接于同一个C上,记为(3)R和R1独立地为含有至少一个碳原子的第一链,R2与R3独立地为无或1-4个碳原子的第二链,且二者不同时为无,记为所述R、R1、R2或R3上能够连接所述取代基。
优选地,对于所述的通式Ⅰ,其结构可为以下任意一个结构:
优选地,所述取代基选自H、甲基、乙基、丙基、异丙基、丁基、异丁基、环丙基、环丁基、环戊基、环己基和多环,这些环状取代基中的任意一个H均可独立地被所述第一取代基取代;优选地,第一取代基选自H、甲基、乙基、卤素、硝基、氰基、醛基、酯基、氨基、烷氧基、烷硫基、=O、=S、=CH2。且连接于末尾碳原子上的取代基Z(指上述的Z0~Z24)优选为H或甲基。
优选地,所述通式Ⅰ为锂盐、钾盐、钠盐、钙盐或镁盐,即通式Ⅰ中的M包括Na+、K+、 Li+、Mg2+或Ca2+,优选锂盐、钾盐或钠盐。
本发明的另一个发明点为提供一种根据以上任意一段所述的电解质的制备方法,该方法为:含有两个-OH的饱和碳链二元结构、三氟化硼类化合物和M源(如M盐、M碱或其它能够为本申请的通式Ⅰ提供金属M的物质等)反应得到产物,即含有两个-OBF3M的饱和碳链类三氟化硼结构。
本发明还有一个发明点为提供一种以上任意一段所述的饱和碳链类的电解质在二次电池中的应用,所述应用为:所述电解质既能够作为盐应用也能够作为添加剂应用。
本发明还有一个发明点为提供一种应用于锂/钠电池中的添加剂,该添加剂包括以上任意一项通式所述的饱和碳链类三氟化硼盐。
本发明还有一个发明点为提供一种应用于锂/钠电池中的锂/钠盐,该锂/钠盐包括以上任意一项通式所述的饱和碳链类三氟化硼盐。
本发明还有一个发明点为提供一种电解质,该电解质包括液态电解液、固态电解质、电解质复合膜或凝胶电解质,这些电解质包括以上任意一段所述的饱和碳链类的电解质。
本发明还有一个发明点为提供一种电池,所述电池包括液态电池、固态电池、固液混合电池或凝胶电池;该电池包括以上任意一段所述的饱和碳链类的电解质以及正极、负极、隔膜和封装外壳。
本发明最后一个发明点为提供一种电池组,所述电池组包括所述电池。
本发明提供了一种饱和碳链类电解质及其制备和应用,其主要具有的有益效果为:
本申请中的电解质创造性的将两个-OBF3M复合于一个化合物中,且优选-OBF3M与碳原子C连接。该硼有机化合物可作为液态或固态电解质中的添加剂,其能够在锂/钠电池的电极表面形成稳定、致密的钝化膜,阻碍电解液与电极直接接触,抑制电解液分解,可显著提高锂/钠电池的循环性能、放电比容量和充放电效率;此外,该硼有机化合物添加剂本身是一种锂/钠离子导体,作为添加剂,其在电极表面形成的钝化层在成膜时极少消耗正极脱出的锂/钠离子,能够对电池的首次库伦效率、首周放电比容量有明显的提升。且含有该硼有机化合物的电解液和现有的高电压高比容的正极材料及低电压高比容负极材料复配成锂/钠电池时,电池的电化学性能均有改善。此外,本申请结构还能与常规添加剂混合使用,即双添加剂,使用双添加剂的电池显示出更优异的电化学性能。
更重要的是,本申请含有2个-OBF3M的硼有机化合物可作为电解液中的盐,更惊喜的是,其还可作为全固态电池中的盐,其更安全,本申请的含硼锂/钠盐在非水溶剂中,锂/钠离子容易被溶剂化,为电池提供较高的离子电导率,可以克服传统电解液中锂/钠盐的缺点,即含有硼有机化合物盐的固态电解质具有不腐蚀集流体、可耐高电压的优点,并且其可将窄电化学窗口的PEO与高电压(>3.9V)正极匹配,显著提高锂/钠电池的电化学性能。而且,本申请中的盐可以与传统中的锂/钠盐作为双盐联合应用,效果也很好。此外,在电解质中使用本申请中的结构,其自身作为添加剂属性和作为盐属性也能够协同作用,使其具有极佳的、优于传统添加剂或锂/钠盐的效果,如,其作为锂盐时,不仅有较好的离子传输性,在电池循环过程中,在电极表面可以形成一层稳定的钝化层,阻止PEO或其他组分等被进一步分解,因此电池展现出更加优异的长循环稳定性。
此外,本申请中的硼有机化合物的原料来源丰富,原料选择性广,成本低,制备过程非常简单,仅需要将含有两个-OH的化合物与三氟化硼类有机物和M源(M为金属阳离子)进行反应便可,反应简单条件温和,具有极佳的工业应用前景。
另外,本申请还能采用钠、钾等除了传统锂以外的金属来形成盐,这为本申请后期的应用、成本控制或原料选择等提供了更多可能性,意义较大。
附图说明
图1~图12分别为本发明实施例1-12所示产物的核磁氢谱图;
图13~图16为本申请作为电解液添加剂的循环效果图;
图17~图18为本申请作为电解液锂盐的循环效果图;
图19为本申请作为固态电解质中锂盐的循环效果图;
图20为本申请结构M14的红外图。
具体实施方式
为使本发明实施例的目的、技术方案和优点更加清楚,下面将结合本发明具体实施例对本发明的技术方案进行清楚、完整地描述,显然,所描述的实施例是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。
所述的“xx个原子长的链”或类似表达,指的是最长链为xx个原子,如若为3个原子长的链,则构成该链的原子数为3个,其上的H或取代基不计算在内,如CH3-CH(CH3)-CH3为3个原子长度的链,CH3-O-CH3也为3个原子长度的链。
在本发明的所有权项和说明书中,-OBF3M中的M可以为一价、二价、三价或多价的金属阳离子,若为非一价离子,则-OBF3的数量对应的增加以使其与M的价数恰好配合便可。
所述“三氟化硼类化合物”指三氟化硼、含有三氟化硼的化合物或三氟化硼络合物等等。
在本发明中,若链上的某一个原子上连接有一个取代基Z0,则代表与Z0连接的原子上的任意一个H都可以独立地被取代基Z0取代,若有多个H,则Z0可取代一个H也可以取代两个或多个H,取代基可相同也可不同;例如,结构为其中Z0选自=O、甲基、F 等取代基,则其可为等。
本发明的发明点为提供了一种可同时作为电解质添加剂和电解质锂/钠盐的二元有机三氟化硼盐,即在该有机物中含有两个-OBF3M基团,其中,M为Li+或Na+等。该二元的三氟化硼盐不仅可应用于液态电池,还能够极好的应用于凝胶电池和固态电池中。该化合物的制备方法简单、巧妙,得率高。即将原料、三氟化硼类化合物和M源进行反应所得,具体为原料中的-OH参与反应,其他结构不参与反应。具体的制备方法主要包括两种:
一、氮气/氩气气氛下,M源与原料加入到溶剂中,混合,在5℃~45℃反应1-12小时,所得混合溶液于0℃-50℃、真空度约-0.1MPa的条件下减压干燥除去溶剂,得到中间体;加三氟化硼类化合物,5-50℃搅拌反应6-24小时,将所得混合液于30-80℃、真空度约-0.1MPa 的条件下减压干燥,得到的粗产物,将粗产物洗涤、过滤、干燥,得终产物二元有机三氟化硼盐,得率为74~95%。
二、氮气/氩气气氛下,原料与三氟化硼类化合物加入到溶剂中,混合均匀,在5-40℃下反应12小时,所得混合溶液于0-40℃、真空度约-0.1MPa的条件下减压干燥除去溶剂,反应得中间体;将M源加入至溶剂中,然后将含有M源的溶剂加入到中间体中,5-50℃搅拌反应6-8小时,即得粗产物,将粗产物直接洗涤或减压干燥后洗涤,然后过滤、干燥,得终产物二元有机三氟化硼盐,得率为74~95%。
以上两种具体的制备方法中,三氟化硼类化合物可包括三氟化硼***络合物、三氟化硼四氢呋喃络合物、三氟化硼丁醚络合物、三氟化硼乙酸络合物、三氟化硼单乙胺络合物、三氟化硼磷酸络合物等等。M源包括金属锂/钠片、甲醇锂/钠、氢氧化锂/钠、乙醇锂/钠、丁基锂/钠、乙酸锂/钠等。每一处所述的溶剂独立地为醇类(有些液体类的原料也可同时为溶剂)、乙酸乙酯、DMF、丙酮、己烷、二氯、四氢呋喃、乙二醇二甲醚等。洗涤可用***、正丁醚、环己烷、二苯醚等。
制备方法:氮气气氛下,将原料3-乙基-2,4-戊二醇(1.32g,0.01mol)和三氟化硼四氢呋喃络合物(2.8g,0.02mol)在15ml乙二醇二甲醚中混合均匀,室温反应12小时。所得混合溶液于40℃、真空度约-0.1MPa的条件下减压干燥除去溶剂,得到中间体。将乙醇锂(1.04g, 0.02mol)溶解在10ml的乙醇中缓慢加入到中间体中,45℃搅拌反应8小时,将所得混合液于 45℃、真空度约-0.1MPa的条件下减压干燥,得到的固体用正丁醚洗涤三次,经过滤、干燥,得到产物M1。产率为77%,核磁如图1所示。
制备方法:氩气气氛下,将金属锂片(0.7g,0.1mol)缓慢加到原料1,13-十三烷二醇(2.16g, 0.05mol)中,在室温下反应1小时,随后升温到50℃直到锂片反应完全得到中间体。将三氟化硼丁醚络合物(3.96g,0.02mol)加入到中间体中,50℃搅拌反应6小时,将所得混合液于 50℃、真空度约-0.1MPa的条件下减压干燥,得到的固体用异丙醚洗涤三次,经过滤、干燥,得到产物M2。产率为85%,核磁如图2所示。
制备方法:氩气气氛下,将原料1,6-己二醇(1.19g,0.01mol)和三氟化硼***络合物(2.98g, 0.021mol)在15ml乙二醇二甲醚中混合均匀,室温反应12小时。所得混合溶液于30℃、真空度约-0.1MPa的条件下减压干燥除去溶剂,得到中间体。将14ml丁基锂的己烷溶液 (c=1.6mol/L)加入到中间体中,室温搅拌反应10小时,将所得混合液于40℃、真空度约-0.1MPa 的条件下减压干燥,得到的粗产物用环己烷洗涤3次,过滤、干燥,得到产物M3。产率为 86%,核磁如图3所示。
制备方法:氮气气氛下,取原料3-(叔丁基)戊烷-2,4-二醇(1.6g,0.01mol)和甲醇锂(0.76g, 0.02mol),用20ml甲醇混合均匀,室温反应12小时。所得混合溶液于30℃、真空度约-0.1MPa 的条件下减压干燥除去溶剂,得到中间体。将三氟化硼四氢呋喃络合物(3.07g,0.022mol)加入到中间体中,室温搅拌反应14小时,将所得混合液于40℃、真空度约-0.1MPa的条件下减压干燥,得到的固体用异丙醚洗涤三次、经过滤、干燥,得到产物M4。产率78%,核磁如图4所示。
制备方法:氩气气氛下,将原料2,4-二甲基-2,4-戊二醇(1.32g,0.01mol)和三氟化硼乙酸络合物(3.83g,0.0204mol)在15ml THF中混合均匀,30℃反应12小时,所得混合溶液于35℃、真空度约-0.1MPa的条件下减压干燥除去溶剂,得到中间体。将乙酸锂(1.35g,0.0204mol)溶解在10ml DMF中并加入到中间体中,50℃搅拌反应8小时,将所得混合液于80℃、真空度约-0.1MPa的条件下减压干燥,得到的固体用二苯醚洗涤三次、经过滤、干燥,得到产物M5。产率为78%,核磁如图5所示。
制备方法:氮气气氛下,将原料2,5-二甲基-2,5-己二醇(1.46,0.01mol)和氢氧化钠(0.80g, 0.02mol)用10ml甲醇溶液混合均匀,15℃反应8小时。所得混合溶液于40℃、真空度约-0.1MPa 的条件下减压干燥除去溶剂,得到中间体。将三氟化硼***络合物(2.98g,0.021mol)加入到中间体中,加入10ml的乙二醇二甲醚溶剂,室温搅拌24小时,将所得混合液于20℃、真空度约-0.1MPa的条件下减压干燥,得到的固体用二氯甲烷洗涤三次、经过滤、干燥,得到产物M6。产率为72%,核磁如图6所示。
制备:由原料通过实施例4的方法制备得到产物M7。产率85%,核磁如图7所示。
制备:由原料通过实施例1的方法制备得到产物M8。产率80%,核磁如图8所示。
制备:由原料通过实施例5的方法制备得到产物M9。产率80%,核磁如图9所示。
制备:由原料通过实施例1的方法制备得到产物M10。产率86%,核磁如图10所示。
制备:由原料通过实施例4的方法制备得到产物M11。产率80%,核磁如图11所示。
制备:由原料通过实施例1的方法制备得到产物M12。产率79%,核磁如图12所示。
实施例13
本发明所保护的饱和碳链类三氟化硼有机盐电解质(包括液态和固态)中主要用作添加剂,主要起到生成钝化层的作用,且自身携带可被解离的离子,所以对于电池的首周效率、首周放电比容量、长循环稳定性、倍率性能均有很大提升。而且,这些饱和碳链类三氟化硼有机盐还可作为电解质(包括液态和固态)中的锂盐应用。下面以试验的方式来说明本申请的性能。
一、作为电解液添加剂
(1)正极极片
将正极主材活性物质、电子导电添加剂、粘结剂按照质量比95:2:3加入到溶剂中,溶剂占总浆料的65%,混合搅拌均匀得到具有一定流动性的正极浆料;将正极浆料涂布在铝箔上,烘干、压实后,得到可用的正极极片。这里活性物质选择使用钴酸锂(LiCoO2,简写LCO)、镍钴锰酸锂(选用NCM811)、镍钴铝酸锂(LiNi0.8Co0.15Al0.05O2,简写NCA)、镍锰酸锂(LiNi0.5Mn1.5O4,简写LNMO)、Na0.9[Cu0.22Fe0.3Mn0.48]O2(简写NCFMO),电子导电添加剂均选择使用碳纳米管(CNT)和Super P,粘结剂使用聚偏氟乙烯(PVDF),溶剂使用N- 甲基吡咯烷酮(NMP)。
(2)负极极片
将负极主材活性物质(金属Li除外)、电子导电添加剂、粘结剂按照95:2.5:2.5加入到溶剂去离子水中,溶剂占总浆料的42%,混合搅拌均匀得到具有一定流动性的负极浆料;将负极浆料涂布在铜箔上,烘干、压实后得到可用的负极极片。这里活性物质选择使用石墨(C)、硅碳(SiOC450)、金属锂(Li)、软碳(SC),导电剂为CNT和Super P,粘结剂为羧甲基纤维素(CMC)和丁苯橡胶(SBR)。
本发明选用的正负极体系如表1所示:
表1正负极体系
电池正负极体系 | 正极主材 | 负极主材 |
A1 | LCO | SiOC450 |
A2 | NCM811 | SiOC450 |
A3 | NCM811 | Li |
A4 | NCA | C |
A5 | LNMO | C |
A6 | LCO | Li |
A7 | NCFMO | SC |
(3)配制电解液
M1~M12、有机溶剂、常规锂/钠盐、常规添加剂混合均匀得到系列电解液E1~E12,这里所用到的溶剂为碳酸甲乙酯(EMC)、碳酸二甲酯(DMC)、碳酸二乙酯(DEC)、碳酸乙烯酯(EC)、碳酸丙烯酯(PC)。常规添加剂为氟代碳酸乙烯酯(FEC)、碳酸亚乙烯酯(VC)、磷酸三甲酯(TMP)、乙氧基五氟环三磷腈(PFPN)、硫酸乙烯酯(DTD);常规锂盐为双草酸硼酸锂(LiBOB)、二氟草酸硼酸锂(LiODFB)、双氟磺酰亚胺锂(LiFSI)、六氟磷酸锂(LiPF6)、双(三氟甲基)磺酰亚胺锂(LiTFSI)、六氟磷酸钠(NaPF6)。具体成分、配比等如表2所示。
表2 M1~M12作为添加剂配制的电解液E1~E12
注:1M指1mol/L。
对比样:按照E1~E12的比例,将M1~M12换成空白(即不添加M1~M12),即可得到对应的常规电解液对比样L1~L12。
(4)扣式电池装配
含有本申请实施例中结构作为添加剂的电解液系列E1~E12和常规电解液L1~L12对比样组装成扣式电池,具体如下:负极壳、负极极片、PE/Al2O3隔膜、电解质、正极极片、不锈钢片、弹簧片、正极壳装配成扣式电池,室温进行长循环测试,其中循环方式0.1C/0.1C1 周、0.2C/0.2C 5周、1C/1C 44周(C代表倍率),所述正极极片是直径为12mm的圆片,所述负极极片是直径为14mm的圆片,所述隔膜是直径为16.2mm的圆片,为商用Al2O3/PE多孔隔膜。
由E1~E12配制的电池体系分别为电池1~12,由L1~L12配制的电池体系分别为对比电池1~12。电池具体配置和电压范围如表3所示。电池1~12和对比电池1~12室温下的首周放电比容量、首周效率、循环50周容量保持率结果如表4所示。
表3实施例电池1~12和对比电池1~12的配置和测试方式
表4实施例电池1~12和对比电池1~12测试结果对比
实施例电池和对比例电池 | 首周放电比容(mAh/g) | 首周效率(%) | 循环50周容量保持率(%) |
电池1 | 161.7 | 77.8 | 83.4 |
对比电池1 | 132.1 | 67.6 | 73.5 |
电池2 | 160.5 | 78.2 | 82.9 |
对比电池2 | 131.9 | 68.3 | 73.8 |
电池3 | 166.2 | 82.1 | 87.7 |
对比电池3 | 158.9 | 80.2 | 82.3 |
电池4 | 160.7 | 79.3 | 83.8 |
对比电池4 | 131.6 | 68.0 | 73.6 |
电池5 | 174.1 | 80.9 | 90.5 |
对比电池5 | 160.4 | 79.5 | 87.3 |
电池6 | 110.6 | 80.5 | 90.3 |
对比电池6 | 95.2 | 70.6 | 87.2 |
电池7 | 173.9 | 80.7 | 90.2 |
对比电池7 | 162.7 | 79.4 | 87.9 |
电池8 | 172.5 | 80.8 | 90.6 |
对比电池8 | 142.2 | 75.3 | 83.0 |
电池9 | 202.3 | 91.9 | 89.9 |
对比电池9 | 195.1 | 90.2 | 86.3 |
电池10 | 200.7 | 91.4 | 87.4 |
对比电池10 | 191.5 | 83.7 | 80.5 |
电池11 | 170.2 | 83.2 | 88.9 |
对比电池11 | 159.3 | 79.7 | 85.6 |
电池12 | 142.7 | 87.6 | 88.7 |
对比电池12 | 128.3 | 80.4 | 75.8 |
从上述实施例电池和对比例电池测试结果来看,在扣式电池中,正负极体系相同时,使用该发明的结构M1~M12作为电解液添加剂的锂/钠电池首周效率、放电比容量、容量保持率均比不添加的效果要好很多,且性能优于目前的常规添加剂。此外,在有常规添加剂存在的情况下,使用含硼锂盐添加剂的电池显示出更优异的电化学性能。
二、作为电解液中的锂盐
(1)配制电解液
M1、M2、M5、M10、M11、M12,有机溶剂、常规添加剂、常规锂盐混合均匀得到系列电解液R1、R2、R5、R10、R11、R12,常规锂盐、有机溶剂、常规添加剂混合均匀得到系列常规电解液Q1、Q2、Q5、Q10、Q11、Q12,使用的溶剂和常规添加剂均包含在本实施例“一”中所述的溶剂和常规添加剂。电解液具体成分、配比等如表5所示。
表5电解液锂盐配制的电解质
(2)电池装配
获得的系列电解液R(表5所示)和常规电解液Q(表5所示)组装成扣式电池,正负极、隔膜大小、装配方法、电池的循环方式同本实施例“一”中所示的扣式电池,分别为电池1、2、 5、10、11、12以及对应的对比电池。电池具体配置、循环方式和电压范围如表6所示,电池和对比电池室温下的首周放电比容量、首周效率、循环50周容量保持率结果如表7所示。
表6实施例电池和对比电池的配置和测试方式
表7表6所示的电池和对比电池测试结果对比
综上,本发明所提供的含硼有机盐单独作为锂盐或与常规锂盐形成双盐在非水溶剂中,锂离子容易被溶剂化,为电池提供较高的离子电导率,在LCO、NCM811为正极,SiOC450、 Li为负极的液态锂电池体系中,均显示出非常优异的电化学性能,首效、首周放电容量、容量保持率均比较高且性能与传统锂盐对应的电池相当或优于传统锂盐对应的电池。
三、作为固态电解质中的锂盐
(1)制备聚合物电解质膜
将M5、M8、M9、M12、聚合物、无机填料和溶剂混合均匀得到系列聚合物电解质浆料,将浆料刮涂在玻璃板上,烘干除去溶剂后得到聚合物电解质膜G5、G8、G9、G12和聚合物对比电解质G’1~G’2,具体成分、配比等如表8所示。聚合物为聚环氧乙烷(PEO)。
表8聚合物电解质的具体成分和配比
聚合物电解质膜 | 聚合物 | 锂/钠盐 | 无机填料 | 前者质量比 | 溶剂 |
G5 | PEO100万 | M5 | 200nmLLZO | 4.2:1:0.8 | DMF |
G8 | PEO100万 | M8 | / | 4.2:1 | DMF |
G9 | PEO100万 | M9 | 200nmLLZO | 4.2:1:0.8 | DMF |
G12 | PEO100万 | M12 | / | 4.2:1 | DMF |
G’1 | PEO100万 | LiTFSI | 200nmLLZO | 4.2:1:0.8 | DMF |
G’2 | PEO100万 | LiTFSI | / | 4.2:1 | DMF |
(2)正极极片的制备
在水分低于100ppm的环境中,将正极主材活性物质、聚合物+锂盐、电子导电添加剂、粘结剂按照质量比80:10:5:5加入到NMP中,混合搅拌均匀,将正极浆料涂布在铝箔上,烘干,得到全固态正极极片。这里活性物质选择使用钴酸锂(LiCoO2,简写LCO)、镍钴锰酸锂(选用NCM811),电子导电添加剂使用Super P,粘结剂使用聚偏氟乙烯(PVDF)
(3)电池装配及测试
将聚合物电解质膜和正负极极片组装成全固态扣式电池,具体如下:负极壳、Li片、聚合物电解质膜、正极极片、不锈钢片、弹簧片、正极壳装配成扣式电池,得到锂二次电池,电池进行50℃长循环测试,循环方式为0.1C/0.1C 2周,0.5/0.5C 48周。所述正极极片是直径为12mm的圆片,所述Li片是直径为14mm的圆片,聚合物电解质膜是直径为16.2mm的圆片,电池具体的装配体系和测试方法如表9所示,测试结果如表10所示。
表9电池和对比例电池的配置和测试方式
表10表9中电池和对比电池的测试结果对比
通过表9和表10的数据,可以看出M5、M8、M9、M12制备而成的电池具有优异的长循环稳定性且性能均优于LiTFSI对应电池的循环性能。这是因为PEO电化学窗口为3.9V,在4.2V容易被正极催化分解;此外,LiTFSI对集流体腐蚀严重,因此对比电池表现出较差的循环性能。而本专利合成的锂盐不仅有较好的离子传输性,且具有很好的成膜性,在电池充放电过程中形成致密的钝化层,阻止PEO进一步被分解,因此长循环性能好。
此外,以锂电池为例,图13~图16分别为实施例2/5/10/12作为电解液添加剂所制成的电池2/5/10/12与对应的不含有本发明实施例的对比电池2/5/10/12的效果对比图。图17~18 分别为实施例2/11作为电解液锂盐所制成的电池2/11与对应的不含有本发明实施例的对比电池2/11的效果对比图。图19为实施例12作为固态电解质锂盐的电池12和以LiTFSI作为锂盐的对比电池2的效果对比图。由图也可知本申请结构具有极佳的效果。此外,在循环图中,上面有小方块的线条代表实施例电池,有小圆圈的线条代表对比例电池,由图可知,代表实施例电池的线条均在代表对比例电池的线条上方,实施例电池效果更优。
首周效率、放电比容量、容量保持率等性能对于电池的整体性能具有直接且显著的影响,其直接决定着电池能否应用。因此,提高这些性能是众多本领域研究者的目标或方向,但在本领域中,这些性能的提高是非常不易的,一般能提高3-5%左右便是较大的进展。本申请在前期试验数据中,很惊喜的发现,这些数据与常规的数据相比,具有很大的提高,尤其是作为电解液添加剂时,性能提高了5-30%左右,且本申请中的添加剂与常规添加剂联合应用也表现出了较佳的效果。更惊喜的是,该组分还可作为电解质中的盐,且效果非常好,试验中显示,其优于现有使用比较成熟的组分。此外,本申请还能够应用于固态电池中,且效果极优,具有极好的应用前景。更重要的是,本申请的结构类型也与常规的结构具有巨大的区别,这为本领域的研发提供了一种新的方向和思路,也为进一步的研究带来了很大的空间,且本申请中的一个结构有多种用途,意义极大。
实施例14:
为了进一步研究和了解本申请中的结构性能,本申请人将其与以下3个结构分别作为电解液添加剂评测其对电池在室温下的长循环性能的影响。本申请的结构选择M13(如下所示),以下3个对比例结构分别为结构W1、结构W2和W3。
(1)电解液配置
表11 W1~W3、M13作为电解液配置的电解液S1~S4
其中,S0为对照组。
(2)扣式电池装配
获得的电解液S0~S4组装成扣式电池,正负极、隔膜大小、装配方法、电池的循环方式同本实施例13“一”中所示的扣式电池,分别为电池Y0~Y4。电池具体配置、循环方式和电压范围如表12所示,测试结果如表13所示。
表12电池的装配和测试方式
表13电池的测试结果
从对比例Y0~Y4测试结果可以看出,W1~W3、M2作为电解液添加剂,均能提升电池的首效、1~50周放电比容量和容量保持率。但与W1~W3相比,M13对电池的首周放电比容量的提升更明显,可能是由于含两个-OBF3M的M13本身含锂源,在形成良好钝化层的过程中同时较少消耗正极脱出的锂离子,从而提升电池的首效,首周放电比容量和50周的容量保持率。而W1含1个-OBF3M,W2中的-OLi作用力较强,Li+不容易解离,因此形成的钝化层主要消耗正极中的锂源,W2中不含锂源,因此其首效、首周放电比容量和50周容量保持率相对较低。即本申请中的三氟化硼有机盐,其在电解质中时,既可作为添加剂又可作为锂盐/钠盐,如M13,其本身在电解质中可协同作用,故效果比其他组分好。更清晰明确的机理,本申请人还在进一步研究中。但无论如何,可以肯定的是,OBF3M的存在以及数量对于电池性能是有实质性影响的。
在本发明中,实施例中只选择了部分结构作为代表来说明本申请的制备方法和效果等,其他没有列举的结构均具有相似的效果。例如: 等效果均比较优异,而且与这些结构较为相似的其他结构也有相似效果,由于篇幅原因,现只以实施例 1-12为例来说明本发明所保护的结构的效果。此外,结构等效果也均比较好。且实施例7-12以及以上所列结构的制备方法均为由原料、M源和三氟化硼类化合物反应得到产物三氟化硼有机物盐,即原料中的-OH变为-OBF3M,M可为Li+、Na+等,其它结构不变,参见实施例1-6。在实施例中没有列举出来的结构,其制备方法均是这样。
在本发明中,还需要注意的是,①-OBF3M中的-BF3须与氧原子O连接,且氧原子再以一个单键与碳原子C连接,因此,O不可以是位于环上的氧。O如果与N、S或其它原子连接后,结构均与本申请区别较大,这种结构是否可以应用在本申请的电解质中、会有什么效果、应用场景等均无法预测,因此,对于这些结构本发明人会进行单独研究,这里不会进行过多探讨;②结构中不含有巯基。③本申请中的饱和碳链类三氟化硼盐电解质优选为非聚合态的有机物,聚合态有其独特的特性和特点,本申请人以后可能会专门对聚合态进行研究,本申请为非聚合态。
对于本申请而言,以上三种情况均需要满足,因为,若不满足,则与本申请的性质会有较大区别,故改变以后的应用场景或效果不好预测,可能会有较大改变,若有价值,以后本发明人会另行进行专门研究。
还需要说明的是,本申请人对该系列结构做了极大量的试验,在第一个结构效果出来以后,后续的试验探索以及数据补充加起来跨度为两年左右,有时候为了更好的与现有体系进行对比,存在同一个结构和体系,做了不止一次试验的情况,因此,不同次的试验可能会存在一定的误差。
最后应说明的是:以上所述的各实施例仅用于说明本发明的技术方案,而非对其限制;尽管参照前述实施例对本发明进行了详细的说明,本领域的普通技术人员应当理解:其依然可以对前述实施例所记载的技术方案进行修改,或者对其中部分或全部技术特征进行等同替换;而这些修改或替换,并不使相应技术方案的本质脱离本发明各实施例技术方案的范围。
Claims (10)
2.根据权利要求1所述的电解质,其特征在于:在通式Ⅰ中,
R或R1独立地为1-30个原子的饱和碳链;R2、R3独立地为0-5个原子的饱和碳链;
优选地,结构通式Ⅰ中的主链为1-20个碳原子长的链;所述第二链为0-3个原子的饱和碳链。
3.根据权利要求2所述的电解质,其特征在于:所述取代基包括H、饱和烷基或环状取代基;
优选地,该环状取代基包括三元环、四元环、五元环、六元环、七元环、八元环和同时含有两个或两个以上环结构的多环取代基;
该环状取代基上能够选择连接第一取代基,优选地,该第一取代基与所述取代基所限定的种类一致。
6.根据权利要求5所述的电解质,其特征在于:所述取代基选自H、甲基、乙基、丙基、异丙基、丁基、环丙基、环丁基、环戊基、环己基和多环,这些环状取代基中的任意一个H均可独立地被所述第一取代基取代;优选地,第一取代基选自H、甲基、乙基、卤素、硝基、氰基、醛基、酯基、氨基、烷氧基、烷硫基、=O、=S、=CH2。
8.根据权利要求1所述的饱和碳链类的电解质,其特征在于:所述通式Ⅰ为锂盐、钾盐、钠盐、钙盐或镁盐,优选锂盐、钾盐或钠盐。
9.一种根据权利要求1-8中任意一项所述的电解质的制备方法,其特征在于:该方法为:含有两个-OH的饱和碳链二元结构、三氟化硼类化合物和M源反应得到产物,即含有两个-OBF3M的饱和碳链类三氟化硼结构。
10.一种权利要求1-8中任意一项所述的饱和碳链类的电解质在二次电池中的应用,其特征在于:所述应用为:所述电解质既能够作为盐应用也能够作为添加剂应用;
优选地,所述应用包括在液态电解液、固态电解质、电解质复合膜或凝胶电解质中的应用,所述液态电解液、固态电解质、电解质复合膜或凝胶电解质均独立地包括权利要求1-8中任意一项所述的饱和碳链类的电解质;
优选地,所述应用还包括作为电池或电池组的应用,所述电池包括权利要求1-8中任意一项所述的饱和碳链类的电解质以及正极、负极、隔膜和封装外壳;所述电池组包括所述电池。