CN113582621A - 一种保温隔热填充材料 - Google Patents
一种保温隔热填充材料 Download PDFInfo
- Publication number
- CN113582621A CN113582621A CN202110933261.9A CN202110933261A CN113582621A CN 113582621 A CN113582621 A CN 113582621A CN 202110933261 A CN202110933261 A CN 202110933261A CN 113582621 A CN113582621 A CN 113582621A
- Authority
- CN
- China
- Prior art keywords
- parts
- heat
- filling material
- water
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种保温隔热填充材料,所述保温隔热填充材料包括粉料、试剂和水;所述粉料包括以下重量份的原料:水泥50~150份、粉煤灰150~250份、钢渣微粉200~400份、干粉砂浆200~400份;所述试剂包括以下重量份的原料:减水剂1~2份、发泡剂1~3份;所述水与干粉料的质量比为0.3~0.5:1;本发明提供的保温隔热填充材料用于墙体填充、制作建筑板材,施工简单,成本低,能够大大减轻主体的承载重量,并且本身具备高强度、耐冲击性能;另外,具备优异的耐火完整性和隔热性,能够有效地防火阻燃,提高建筑安全,避免二次火灾危害,保障人身、财产安全,同时具备优异的保温和隔音性能。
Description
技术领域
本发明涉及建筑材料技术领域,具体为一种保温隔热填充材料。
背景技术
随着生活水平的提高,人们对自身生活环境的要求也与日剧增,房屋的修建过程中,采取了保温、隔热和静音措施,在主体工程表面增加了一层隔热层。
现有技术中,为达到墙体隔音的效果,大多采用砌筑体涂布砂浆配合隔热板材作为填充,以求达到保温、隔热和静音的效果。但是此种方式隔热、保温效果不佳,不仅结构承重较大,而且施工复杂,成本高;另外,其中的隔热板材的耐高温效果极差,防火效果不理想,容易造成更具危害的火灾二次助燃。因此,为解决上述问题,现提出一种保温隔热填充材料。
发明内容
本发明目的是提供一种保温隔热填充材料,以解决背景技术中提出的现有的保温隔热填充材料耐高温隔热效果极差,防火效果不理想的问题。
为实现上述目的,本发明提供如下技术方案:一种保温隔热填充材料,所述保温隔热填充材料包括粉料、试剂和水;
所述粉料包括以下重量份的原料:水泥50~150份、粉煤灰150~250份、钢渣微粉200~400份、干粉砂浆200~400份;
所述试剂包括以下重量份的原料:减水剂1~2份、发泡剂1~3份;
所述水与干粉料的质量比为0.3~0.5:1;
所述保温隔热填充材料按照以下方法制备得到:
步骤1,以重量份计,将发泡剂和超过一半的水加入搅拌机中,以20~60rpm的转速搅拌均匀,共计搅拌时间为1~2分钟;
步骤2,以重量份计,将水泥、干粉砂浆、粉煤灰、钢渣微粉依次投入搅拌机中,并将余下的水在粉料的投料间隔中向搅拌机中添加补水,以20~60rpm的转速搅拌均匀,搅拌时间为4~8分钟;
步骤3,以重量份计,将减水剂加入搅拌机中,以10~60rpm的转速搅拌均匀,搅拌1~2分钟后出料,得到保温隔热填充材料。
优选的,所述保温隔热填充材料包括以下重量份的原料:水泥100份、粉煤灰200份、钢渣微粉300份、干粉砂浆300份、水400份、减水剂1份、发泡剂2份。
优选的,所述水泥为普通硅酸盐水泥、复合硅酸盐水泥和铝酸盐水泥中的一种。
优选的,钢渣微粉的比表面积为400~600m2/kg。
优选的,所述干粉砂浆采用DM普通砌筑砂浆、DP普通抹灰砂浆、DAA加气混凝土专用粘结砂浆中的一种。
优选的,步骤2中所述水泥、干粉砂浆、粉煤灰、钢渣微粉的投料时间为1~2分钟,单次投料完成后,将余下的水的一部分加入搅拌机中,直至水按重量份添加结束。
本发明至少具备以下有益效果:
本发明提供的保温隔热填充材料用于墙体填充、制作建筑板材,施工简单,成本低,能够大大减轻主体的承载重量,并且本身具备高强度、耐冲击性能;另外,具备优异的耐火完整性和隔热性,能够有效地防火阻燃,提高建筑安全,避免二次火灾危害,保障人身、财产安全,同时具备优异的保温和隔音性能。
具体实施方式
下面对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其它实施例,都属于本发明保护的范围。
本发明提供了一种保温隔热填充材料,所述保温隔热填充材料包括粉料、试剂和水;
所述粉料包括以下重量份的原料:水泥50~150份、粉煤灰150~250份、钢渣微粉200~400份、干粉砂浆200~400份;
所述试剂包括以下重量份的原料:减水剂1~2份、发泡剂1~3份;
实施例1
一种保温隔热填充材料,包括以下重量份的原料:水泥50kg、粉煤灰150kg、钢渣微粉300kg、干粉砂浆400kg、减水剂2kg、发泡剂1kg、水270kg;
所述保温隔热填充材料按照以下方法制备得到:
步骤1,以重量份计,将发泡剂1kg和200kg的水加入搅拌机中,以20rpm的转速搅拌均匀,共计搅拌时间为2分钟;
步骤2,以重量份计,将干粉料中的代号为P.O的32.5级普通硅酸盐水泥50kg、型号为M10的DM中保水普通砌筑砂浆400kg、粉煤灰150kg、比表面积为400m2/kg的钢渣微粉300kg依次投入搅拌机中,以20rpm的转速搅拌均匀,搅拌时间为8分钟;并在水泥、干粉砂浆、粉煤灰、钢渣微粉的依次投料间,将余下的70kg水分为多次加入搅拌机中,直至水按重量比添加结束;
步骤3,以重量份计,将减水剂1kg加入搅拌机中,以10rpm的转速搅拌均匀,搅拌2分钟后出料,得到保温隔热填充材料。
实施例2
一种保温隔热填充材料,包括以下重量份的原料:水泥100kg、粉煤灰200kg、钢渣微粉300kg、干粉砂浆300kg、减水剂1kg、发泡剂2kg、水360kg;
所述保温隔热填充材料按照以下方法制备得到:
步骤1,以重量份计,将发泡剂2kg和300kg的水加入搅拌机中,以35rpm的转速搅拌均匀,共计搅拌时间为2分钟;
步骤2,以重量份计,将干粉料中的代号为P.O的42.5级普通硅酸盐水泥100kg、型号为M15的DM低保水普通砌筑砂浆300kg、粉煤灰200kg、比表面积为450m2/kg的钢渣微粉300kg依次投入搅拌机中,以35rpm的转速搅拌均匀,搅拌时间为6分钟,并在水泥、干粉砂浆、粉煤灰、钢渣微粉的依次投料间,将余下的60kg水分为多次加入搅拌机中,直至水按重量比添加结束;
步骤3,以重量份计,将减水剂1kg加入搅拌机中,以20rpm的转速搅拌均匀,搅拌2分钟后出料,得到保温隔热填充材料。
实施例3
一种保温隔热填充材料,包括以下重量份的原料:水泥150kg、粉煤灰150kg、钢渣微粉250kg、干粉砂浆350kg、减水剂2kg、发泡剂3kg、水450kg;
所述保温隔热填充材料按照以下方法制备得到:
步骤1,以重量份计,将发泡剂3kg和300kg的水加入搅拌机中,以60rpm的转速搅拌均匀,共计搅拌时间为1分钟;
步骤2,以重量份计,将干粉料中的代号为P.O的42.5级普通硅酸盐水泥150kg、型号为M15的DM低保水普通砌筑砂浆350kg、粉煤灰150kg、比表面积为600m2/kg的钢渣微粉250kg依次投入搅拌机中,以60rpm的转速搅拌均匀,搅拌时间为4分钟,并在水泥、干粉砂浆、粉煤灰、钢渣微粉的依次投料间,将余下的150kg水分为多次加入搅拌机中,直至水按重量比添加结束;
步骤3,以重量份计,将减水剂2kg加入搅拌机中,以60rpm的转速搅拌均匀,搅拌1分钟后出料,得到保温隔热填充材料。
对以上实施例制备保温隔热填充材料充入宽600mm、高3000mm、厚100mm模具中,自然晾干28天后的成品进行测试,结果如下:
表1:基本性能
表2:耐火隔热检测
以上显示和描述了本发明的基本原理和主要特征和本发明的优点,对于本领域技术人员而言,显然本发明不限于上述示范性实施例的细节,而且在不背离本发明的精神或基本特征的情况下,能够以其他的具体形式实现本发明。因此,无论从哪一点来看,均应将实施例看作是示范性的,而且是非限制性的,本发明的范围由所附权利要求而不是上述说明限定,因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。
尽管已经示出和描述了本发明的实施例,对于本领域的普通技术人员而言,可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型,本发明的范围由所附权利要求及其等同物限定。
Claims (6)
1.一种保温隔热填充材料,其特征在于,所述保温隔热填充材料包括粉料、试剂和水;
所述粉料包括以下重量份的原料:水泥50~150份、粉煤灰150~250份、钢渣微粉200~400份、干粉砂浆200~400份;
所述试剂包括以下重量份的原料:减水剂1~2份、发泡剂1~3份;
所述水与干粉料的质量比为0.3~0.5:1;
所述保温隔热填充材料按照以下方法制备得到:
步骤1,以重量份计,将发泡剂和超过一半的水加入搅拌机中,以20~60rpm的转速搅拌均匀,共计搅拌时间为1~2分钟;
步骤2,以重量份计,将水泥、干粉砂浆、粉煤灰、钢渣微粉依次投入搅拌机中,并将余下的水在粉料的投料间隔中向搅拌机中添加补水,以20~60rpm的转速搅拌均匀,搅拌时间为4~8分钟;
步骤3,以重量份计,将减水剂加入搅拌机中,以10~60rpm的转速搅拌均匀,搅拌1~2分钟后出料,得到保温隔热填充材料。
2.根据权利要求1所述的一种保温隔热填充材料,其特征在于:所述保温隔热填充材料包括以下重量份的原料:水泥100份、粉煤灰200份、钢渣微粉300份、干粉砂浆300份、水400份、减水剂1份、发泡剂2份。
3.根据权利要求1所述的一种保温隔热填充材料,其特征在于:所述水泥为普通硅酸盐水泥、复合硅酸盐水泥和铝酸盐水泥中的一种。
4.根据权利要求1所述的一种保温隔热填充材料,其特征在于:钢渣微粉的比表面积为400~600m2/kg。
5.根据权利要求1所述的一种保温隔热填充材料,其特征在于:所述干粉砂浆采用DM普通砌筑砂浆、DP普通抹灰砂浆、DAA加气混凝土专用粘结砂浆中的一种。
6.根据权利要求1所述的一种保温隔热填充材料,其特征在于:步骤2中所述水泥、干粉砂浆、粉煤灰、钢渣微粉的投料时间为1~2分钟,单次投料完成后,将余下的水的一部分加入搅拌机中,直至水按重量份添加结束。