CN113136152A - 一种稳定性高的电子胶 - Google Patents
一种稳定性高的电子胶 Download PDFInfo
- Publication number
- CN113136152A CN113136152A CN202110322672.4A CN202110322672A CN113136152A CN 113136152 A CN113136152 A CN 113136152A CN 202110322672 A CN202110322672 A CN 202110322672A CN 113136152 A CN113136152 A CN 113136152A
- Authority
- CN
- China
- Prior art keywords
- parts
- reaction kettle
- polystyrene
- electronic adhesive
- liquid formaldehyde
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种稳定性高的电子胶，所述电子胶各组份质量份为：氯丁橡胶300‑400份、热塑性丁苯橡胶200‑350份、聚苯乙烯50‑80份、邻苯二甲酸二丁酯5‑25份、液体甲醛230‑300份、四氢呋喃5‑15份、丁基锂5‑25份。采用本方案后具有粘合力强、无毒、耐热、耐老化等特点；同时不易受潮，吸水性、耐候性以及阻燃性能好。
Description
技术领域
本发明涉及电子胶技术领域，尤其是指一种稳定性高的电子胶。
背景技术
目前，应用于电子元器件(如LED电视或高端广告灯箱背光灯条)的单组份环氧电子胶，存在的普遍问题是胶水的韧性不够，表现为粘接力和抗冲击性能不达标，破坏总是出现在PMMA透镜的三角位置。对应用于LED电视的背光灯条，需要提高单组份环氧电子胶抗跌落性，同时用于电子元器件的热溶胶、不饱和树脂及固化剂也存在着耐温性能差、脆性大、收缩大、易逆变和不具防伪性能等缺点。
发明内容
本发明的目的在于克服现有技术的不足，提供一种稳定性高的粘合力强、无毒、耐热、耐老化的电子胶。
为实现上述目的，本发明所提供的技术方案为：一种稳定性高的电子胶，所述电子胶各组份质量份为：氯丁橡胶300-400份、热塑性丁苯橡胶200-350份、聚苯乙烯50-80份、邻苯二甲酸二丁酯 5-25份、液体甲醛230-300份、四氢呋喃5-15份、丁基锂5-25份。
所述制备方法包括有以下步骤：
1）、将热塑性丁苯橡胶、氯丁橡胶加入反应釜内，加入一定量的液体甲醛一起，所述的氯丁橡胶为M-40；液体甲醛的加入量为反应釜内总质量20-30%；
2）、将反应釜加热到70℃，开动搅拌机搅拌充分后；
3）、向完成2）步骤的反应釜内徐徐加入聚苯乙烯，并升温至 90-95℃，使聚苯乙烯完全溶解；
4）、第3）步骤的溶液冷却至80-85℃，再继续搅拌的同时以细流方式加入邻苯二甲酸二丁酯，搅拌20分钟；
5）、再加入余量的液体甲醛进行缩合反应，时间控制在50-70分钟；
6）、降低反应釜温度并调节pH值后，用尿素进行氨基化处理，经抽样检验合格后，把pH值调至中性，然后降温至45-50℃出料，即成电子胶。
本发明的热塑性丁苯橡胶通过聚苯乙烯改性后，从而具有粘合力强、无毒、耐热、耐老化等特点；同时不易受潮，吸水性、耐候性以及阻燃性能好，固化后的材料无论是绝缘性，韧性，还是耐热性均大大优于市面同级产品，其具有广泛的市场前景。
具体实施方式
下面对本发明作进一步说明，本发明的较佳实施例为：本实施例所述的一种稳定性高的电子胶，所述电子胶各组份质量份为：氯丁橡胶300-400份、热塑性丁苯橡胶200-350份、聚苯乙烯50-80份、邻苯二甲酸二丁酯 5-25份、液体甲醛230-300份、四氢呋喃5-15份、丁基锂5-25份。
所述制备方法包括有以下步骤：
1）、将热塑性丁苯橡胶、氯丁橡胶加入反应釜内，加入一定量的液体甲醛一起，所述的氯丁橡胶为M-40；液体甲醛的加入量为反应釜内总质量20-30%；
2）、将反应釜加热到70℃，开动搅拌机搅拌充分后；
3）、向完成2）步骤的反应釜内徐徐加入聚苯乙烯，并升温至 90-95℃，使聚苯乙烯完全溶解；
4）、第3）步骤的溶液冷却至80-85℃，再继续搅拌的同时以细流方式加入邻苯二甲酸二丁酯，搅拌20分钟；
5）、再加入余量的液体甲醛进行缩合反应，时间控制在50-70分钟；
6）、降低反应釜温度并调节pH值后，用尿素进行氨基化处理，经抽样检验合格后，把pH值调至中性，然后降温至45-50℃出料，即成电子胶。
本发明的热塑性丁苯橡胶通过聚苯乙烯改性后，从而具有粘合力强、无毒、耐热、耐老化等特点；同时不易受潮，吸水性、耐候性以及阻燃性能好，固化后的材料无论是绝缘性，韧性，还是耐热性均大大优于市面同级产品，其具有广泛的市场前景。
以上所述之实施例只为本发明之较佳实施例，并非以此限制本发明的实施范围，故凡依本发明之原理所作的变化，均应涵盖在本发明的保护范围内。
Claims (2)
1.一种稳定性高的电子胶，其特征在于：所述电子胶各组份质量份为：氯丁橡胶300-400份、热塑性丁苯橡胶200-350份、聚苯乙烯50-80份、邻苯二甲酸二丁酯 5-25份、液体甲醛230-300份、四氢呋喃5-15份、丁基锂5-25份。
2.一种稳定性高的电子胶制备方法，其特征在于：所述制备方法包括有以下步骤：
1）、将热塑性丁苯橡胶、氯丁橡胶加入反应釜内，加入一定量的液体甲醛一起，所述的氯丁橡胶为M-40；液体甲醛的加入量为反应釜内总质量20-30%；
2）、将反应釜加热到70℃，开动搅拌机搅拌充分后；
3）、向完成2）步骤的反应釜内徐徐加入聚苯乙烯，并升温至 90-95℃，使聚苯乙烯完全溶解；
4）、第3）步骤的溶液冷却至80-85℃，再继续搅拌的同时以细流方式加入邻苯二甲酸二丁酯，搅拌20分钟；
5）、再加入余量的液体甲醛进行缩合反应，时间控制在50-70分钟；
6）、降低反应釜温度并调节pH值后，用尿素进行氨基化处理，经抽样检验合格后，把pH值调至中性，然后降温至45-50℃出料，即成电子胶。