CN113040949A - 一种混有氧化锌量子点的正畸托槽粘接剂 - Google Patents

一种混有氧化锌量子点的正畸托槽粘接剂 Download PDF

Info

Publication number
CN113040949A
CN113040949A CN202110260120.5A CN202110260120A CN113040949A CN 113040949 A CN113040949 A CN 113040949A CN 202110260120 A CN202110260120 A CN 202110260120A CN 113040949 A CN113040949 A CN 113040949A
Authority
CN
China
Prior art keywords
adhesive
zinc oxide
quantum dots
oxide quantum
orthodontic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202110260120.5A
Other languages
English (en)
Inventor
花放
顾家榕
贺红
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhan University WHU
Original Assignee
Wuhan University WHU
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhan University WHU filed Critical Wuhan University WHU
Priority to CN202110260120.5A priority Critical patent/CN113040949A/zh
Publication of CN113040949A publication Critical patent/CN113040949A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种混有氧化锌量子点的正畸托槽粘接剂，涉及医药技术领域，其特征在于将氧化锌量子点作为荧光成分与抗菌成分添加至口腔正畸治疗中使用到的托槽粘接剂中，与现有技术相比，氧化锌量子点添加到托槽粘接剂中，能够赋予粘接剂荧光性能与抗菌性能。其荧光性能可以指示正畸医师在托槽粘接过程中去除多余的粘接剂，以及指示正畸医师在拆除托槽时去除牙面上残留的粘接剂；其抗菌性能可以起到杀灭致龋菌变形链球菌的作用。

Description

一种混有氧化锌量子点的正畸托槽粘接剂
技术领域
本发明涉及医药技术的技术领域，尤其涉及一种混有氧化锌量子点的正畸托槽粘接剂。
背景技术
口腔正畸学是一门治疗错合畸形的学科，其治疗方法包括固定矫治技术与无托槽矫治技术，其中固定矫治技术因为发展成熟，固位较好，治疗效率较高，是目前最常用的矫治技术。固定矫治技术的原理是利用粘接剂将托槽固定至釉质表面，通过托槽将弓丝形变产生的力量或者其他来源的力传递至牙齿，从而实现牙齿的移动以治疗错合畸形。然而，托槽与粘接剂的存在导致牙面难以清洁，菌斑生物膜容易积聚产酸而导致釉质脱矿，表现为白垩斑甚至龋坏，从而影响患者牙齿的美观与健康。
针对这一问题，目前临床上常通过两种策略进行预防或治疗：(1)使用抗菌制剂抑制菌斑生物膜的聚集，减少其产酸以减少釉质脱矿的出现；(2)使用氟化物、CPP-ACP等再矿化制剂，使脱矿的釉质及时再矿化，从而减轻釉质脱矿的程度。各类试剂主要通过漱口水、保护漆、牙膏等形式进行釉质脱矿的预防与治疗，这些作用方式依赖患者的主观配合程度，或是会增加治疗的椅旁操作时间，往往难以取得良好的效果。此外，多项循证医学研究发现氟化物、 CPP-ACP等再矿化制剂的釉质脱矿预防效果有限，不能实现杜绝釉质脱矿的出现。因此，对于釉质脱矿这一临床问题，仍值得科研人员的关注与研究。
发明内容
基于以上现有技术的不足，本发明所解决的技术问题在于提供一种减少釉质脱矿效果好的混有氧化锌量子点的正畸托槽粘接剂，将氧化锌量子点应用于正畸托槽粘接剂中，从而赋予正畸粘接剂荧光性能与抗菌性能。本发明方案的研究得到国家自然科学基金(NO：81901044)的资助。
为了解决上述技术问题，本发明提供一种混有氧化锌量子点的正畸托槽粘接剂，所述粘接剂包含托槽粘接剂和氧化锌量子点。
作为上述技术方案的优选，本发明提供的混有氧化锌量子点的正畸托槽粘接剂进一步包括下列技术特征的部分或全部：
作为上述技术方案的改进，所述氧化锌量子点能够在紫外线的激发下发出黄色荧光，并且能够杀灭致龋菌变形链球菌。
作为上述技术方案的改进，所述氧化锌量子点的质量为托槽粘接剂质量的 10％-30％。
作为上述技术方案的改进，所述氧化锌量子点为粒径小于10nm的氧化锌颗粒。
作为上述技术方案的改进，所述托槽粘接剂为树脂类正畸粘接剂、玻璃离子类正畸粘接剂、光固化玻璃离子类正畸粘接剂或树脂改良玻璃离子类正畸粘接剂中的任意一种。
一种如上任一所述的混有氧化锌量子点的正畸托槽粘接剂的制备方法，将氧化锌量子点作为添加剂混入托槽粘接剂内。
一种如上任一所述的混有氧化锌量子点的正畸托槽粘接剂的应用，所述的混有氧化锌量子点的正畸托槽粘接剂用于正畸托槽的粘接。
本发明使用的氧化锌量子点具有荧光性能，能够在紫外线(波长350nm左右)的激发下发出黄色荧光(波长550nm左右)，还具有杀菌效应能够杀灭致龋菌变形链球菌。因此使用本发明通过将氧化锌量子点混入正畸粘接剂所合成的兼具抗菌性能与荧光性能的正畸托槽粘接剂，有利于正畸医生分辨粘接剂并准确地去除多余的粘接剂，并可在正畸治疗过程中杀灭致龋菌变形链球菌，从而减少釉质脱矿的出现。主要优点表现在以下两点：
1：赋予粘接剂荧光性能，在粘接托槽时以及去除托槽时指示剩余粘接剂的位置，引导正畸医师去除多余粘接剂。
在粘接托槽时，多余的粘接剂会溢出在托槽底板周围，由于颜色与牙齿相近往往难以被完全去除。这些残留的粘接剂会成为日后正畸治疗过程中细菌容易积聚的部位，从而导致托槽周围釉质脱矿的出现。本发明所涉及的混入氧化锌量子点的正畸托槽粘接剂能够在紫外线(波长350nm左右)的照射下，发出黄色荧光(波长550nm左右)。应用本发明所涉及的粘接剂后，可以在粘接托槽后用紫外线照射托槽，在黄色荧光的指示下快速而彻底地去除托槽底板周围多余的粘接剂，从而减少正畸治疗过程中细菌的聚集。
在去除托槽时，部分粘接剂与托槽底板脱粘接，残留在牙齿表面。这部分粘接剂厚度较薄且颜色与牙齿接近，在使用慢速手机磨除的过程中难以判断是否已完全磨除。若过量磨除，容易损伤正常的牙体组织，而磨除不足则导致仍然有部分粘接剂残留在牙面上，细菌容易聚集在粘接剂上导致正畸治疗结束后出现釉质脱矿。应用本发明所涉及的粘接剂后，可以在去除托槽后用紫外线照射牙面，在黄色荧光的指示下快速而彻底地去除残留在牙齿表面的粘接剂而不损伤牙体组织。
2：赋予粘接剂荧光性能，在正畸治疗过程中杀灭致龋菌变形链球菌，从而减少釉质脱矿的出现.
正畸治疗过程中，牙齿表面粘接的托槽容易积聚细菌，以变形链球菌为主的致龋菌在托槽周围聚集，分泌有机酸导致釉质脱矿的出现。本发明所涉及的混有氧化锌量子点的正畸粘接剂具有抗菌性能，能够实现对变形链球菌的杀灭，从而在正畸治疗过程中抑制托槽周围变形链球菌的活性，避免因致龋菌黏附聚集导致釉质脱矿。
上述说明仅是本发明技术方案的概述，为了能够更清楚了解本发明的技术手段，而可依照说明书的内容予以实施，并且为了让本发明的上述和其他目的、特征和优点能够更明显易懂，以下结合优选实施例，详细说明如下。
附图说明
为了更清楚地说明本发明实施例的技术方案，下面将对实施例的附图作简单地介绍。
图1：本发明实施例1涉及的氧化锌量子点荧光照片；
图2：本发明实施例1涉及的混入氧化锌量子点的粘接剂照片；
图3：应用本发明实施例1涉及的粘接剂粘接托槽后拆除托槽时的照片；
图4：本发明实施例1涉及的混有氧化锌量子点的粘接剂的杀菌效果；
图5：本发明实施例1涉及的混有氧化锌量子点的粘接剂的生物相容性。
具体实施方式
下面详细说明本发明的具体实施方式，其作为本说明书的一部分，通过实施例来说明本发明的原理，本发明的其他方面、特征及其优点通过该详细说明将会变得一目了然。
实例1：一种混有氧化锌量子点的正畸托槽粘接剂，其特征在于它是由氧化锌量子点混入树脂类正畸粘接剂内合成；
其所说的树脂粘接剂为Transbond XT粘接树脂，氧化锌量子点的混入量为粘接树脂质量的20％；
对氧化锌量子点粉末拍摄紫外线照射下照片，对混入氧化锌量子点的粘接树脂拍摄紫外线照射下照片，用混入氧化锌量子点的粘接树脂粘接托槽至牙面，去除托槽后拍摄紫外线照射下牙面上残留粘接树脂的照片；用MTT法评估粘接树脂的抗变形链球菌性能；用CCK-8法评估粘接树脂对牙龈成纤维细胞的生物相容性。
1、氧化锌量子点粉末在紫外线照射下的照片(图1所示)
氧化锌量子点粉末在紫外线(350nm左右)光源的照射下发出黄色荧光。
2、混入氧化锌量子点的粘接树脂在紫外线照射下的照片(图2所示)
将氧化锌量子点以20％的比例混入粘接树脂后，使用光固化灯固化粘接树脂，粘接树脂在自然光源下呈现为白色，在紫外线(350nm左右)光源照射下发出黄色荧光。
3、托槽去除后牙面上粘接树脂在紫外线照射下的照片(图3所示)
使用混入氧化锌量子点的粘接剂粘接托槽后拆除托槽，分别在自然光源与紫外线(混有少量紫色可见光)光源下观察牙齿表面残留的粘接剂，在自然光源下，牙齿表面的粘接剂与牙齿颜色相近，难以区分(图3A)，而在紫外线的照射下，牙齿表面的粘接剂发出黄色荧光，能够轻易同牙体组织区分开来(图3B)。
4、混入氧化锌量子点的粘接树脂的抗变形链球菌能力(如图4所示)
混入20％氧化锌量子点的粘接树脂(20％组)与未混入氧化锌量子点的粘接树脂(NC组)制作成直径4mm，厚度1mm的树脂片并进行光固化。紫外线灭菌后，将上述树脂片浸泡于含变形链球菌的BHIS培养液内37℃厌氧培养。培养24小时后吸去培养液，用MTT试剂盒检测树脂片表面变形链球菌的活性，将NC组的活性作为对照，计算20％组树脂片表面变形链球菌的相对存活情况。结果显示混入20％氧化锌量子点的粘接树脂具有较好的抗变形链球菌能力。
5、混入氧化锌量子点的粘接树脂的生物相容性(图5所示)
混入20％氧化锌量子点的粘接树脂(20％组)与未混入氧化锌量子点的粘接树脂(NC组)制作成直径4mm，厚度1mm的树脂片并进行光固化。紫外线灭菌后将树脂片浸泡于牙龈成纤维细胞的培养基内制作浸提液。将牙龈成纤维细胞培养于浸提液内，培养环境为37℃，5％CO2。培养24小时后吸去浸提液，用 CCK-8试剂盒检测牙龈成纤维细胞的增殖能力以评估树脂片的生物相容性。结果显示混入20％氧化锌量子点的粘接树脂与未混入氧化锌量子点的粘接树脂的生物相容性没有差别，即混入氧化锌量子点不会影响粘接树脂本身的生物相容性。
实例2：一种混有氧化锌量子点的正畸托槽粘接剂，其特征在于它是由氧化锌量子点混入玻璃离子类正畸粘接剂内合成；
其所说的玻璃离子类粘接剂为GC富士II玻璃离子水门汀，氧化锌量子点以20％的质量分数混入玻璃离子水门汀的粉剂中；
实例3：一种混有氧化锌量子点的正畸托槽粘接剂，其特征在于它是由氧化锌量子点混入光固化玻璃离子类正畸粘接剂内合成；
其所说的光固化玻璃离子类粘接剂为富士II LC光固化玻璃离子水门汀，氧化锌量子点以20％的质量分数混入富士II LC光固化玻璃离子水门汀的粉剂中；
实例4：一种混有氧化锌量子点的正畸托槽粘接剂，其特征在于它是由氧化锌量子点混入树脂改良玻璃离子类正畸粘接剂内合成；
其所说的树脂改良玻璃离子类粘接剂为GC Fuji Ortho LC光固化树脂改良型玻璃离子正畸粘结剂，氧化锌量子点以20％的质量分数混入GC Fuji Ortho LC光固化树脂改良型玻璃离子正畸粘结剂的粉剂中。
本发明所列举的各原料，以及本发明各原料的上下限、区间取值，以及工艺参数(如温度、时间等)的上下限、区间取值都能实现本发明，在此不一一列举实施例。
以上所述是本发明的优选实施方式而已，当然不能以此来限定本发明之权利范围，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以做出若干改进和变动，这些改进和变动也视为本发明的保护范围。

Claims (7)

1.一种混有氧化锌量子点的正畸托槽粘接剂，其特征在于：所述粘接剂包含托槽粘接剂和氧化锌量子点。
2.如权利要求1所述的混有氧化锌量子点的正畸托槽粘接剂，其特征在于：所述氧化锌量子点能够在紫外线的激发下发出黄色荧光，并且能够杀灭致龋菌变形链球菌。
3.如权利要求1所述的混有氧化锌量子点的正畸托槽粘接剂，其特征在于：所述氧化锌量子点的质量为托槽粘接剂质量的10％-30％。
4.如权利要求1所述的混有氧化锌量子点的正畸托槽粘接剂，其特征在于：所述氧化锌量子点为粒径小于10nm的氧化锌颗粒。
5.如权利要求1所述的混有氧化锌量子点的正畸托槽粘接剂，其特征在于：所述托槽粘接剂为树脂类正畸粘接剂、玻璃离子类正畸粘接剂、光固化玻璃离子类正畸粘接剂或树脂改良玻璃离子类正畸粘接剂中的任意一种。
6.一种如权利要求1-5任一所述的混有氧化锌量子点的正畸托槽粘接剂的制备方法，其特征在于：将氧化锌量子点作为添加剂混入托槽粘接剂内。
7.一种如权利要求1-5任一所述的混有氧化锌量子点的正畸托槽粘接剂的应用，其特征在于：所述的混有氧化锌量子点的正畸托槽粘接剂用于正畸托槽的粘接。
CN202110260120.5A 2021-03-10 2021-03-10 一种混有氧化锌量子点的正畸托槽粘接剂 Pending CN113040949A (zh)