CN112850786A - 一种Na2CO3浸出硫化砷泥膏制备砷酸镁方法 - Google Patents
一种Na2CO3浸出硫化砷泥膏制备砷酸镁方法 Download PDFInfo
- Publication number
- CN112850786A CN112850786A CN202011610933.4A CN202011610933A CN112850786A CN 112850786 A CN112850786 A CN 112850786A CN 202011610933 A CN202011610933 A CN 202011610933A CN 112850786 A CN112850786 A CN 112850786A
- Authority
- CN
- China
- Prior art keywords
- magnesium
- arsenate
- arsenic sulfide
- leaching
- solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种Na2CO3浸出硫化砷泥膏制备砷酸镁方法,涉及一种制备砷酸镁方法,本发明采用废弃资源利用,用Na2CO3浸出硫化砷渣,用MgCl2作为沉淀药剂,首先将硫化砷渣按液固比5‑8,按碳酸钠过量20%比例与硫化砷渣混合,温度28‑90℃,通入空气或氧化剂,搅拌速度150‑500rpm对硫化砷渣浸出,浸出时间0.5‑2小时,得到砷酸钠溶液。将砷酸钠溶液与氯化镁溶液混合,生成砷酸镁沉淀,过滤分离得到砷酸镁结晶。本发明具有浸出效率高,残渣率低的特点,浸出反应和镁转化反应速度都可在很短时间内完成,转化后的沉淀主要是5价砷砷酸镁(Mg(AsO3)2̦·xH2O),性质十分稳定。本发明操作简单、反应温度低、反应时间快速、成本低、是个获得砷酸镁的理想方法。
Description
技术领域
本发明涉及一种制备砷酸镁方法,特别是涉及一种Na2CO3浸出硫化砷泥膏制备砷酸镁方法。
背景技术
砷酸镁(Mg(AsO3)2̦·xH2O)因其具有很强的毒性,最初被用于制作农药,2018年所有砷类农药都被农业部列入禁用和限用目录。Mg(AsO3)2̦·xH2O因其分子中的原子中的电子吸收太阳光中光子的能量,之后电子跃迁到更高的能级,电子处于高能级后是非稳态,在电子跃迁到低一些的能级后释放一定的能量,可以发出发射光谱为630~ 680 nm红光波段的荧光。近年来它被用于生产以Mn离子为激活剂的荧光粉涂层材料,唐明道,赵成久,丛国刚等公开了由MgO或MgCl2与As2O5合成大红色荧光灯用荧光粉制备方法(唐明道,赵成久,丛国刚,等.大红色荧光灯用荧光粉及其制备[Z]. CN87104810.8),葛大勇提出了由MgO或MgCl2与As2O5合成荧光砷酸镁材料改进的方法[葛大勇.Mg6As2O11:Mn发光材料制备方法的改进[J].河北大学学报(自然科学版),2001,21(3):251-253.]。杨琮介绍了由MgCl2与As2O5合成荧光砷酸镁材料的方法[杨琮.萤光物质砷酸镁的制法[J].化学世界, 1957, (11):499.]。近几年林建忠、林子柯提出了由铜冶炼含砷废酸液制备砷酸镁的方法(林子柯.一种含砷废液生产砷酸镁的方法[Z]. CN201610939859.8.林建忠. 一种冶铜过程中产生的含砷废液综合利用的方法[Z]. CN201110315629.1.)。本文提出了一种由铜冶炼废渣硫化砷泥膏为原料,经Na2CO3浸出制成NaH2AsO3,然后与MgCl2反应制成Mg(AsO3)2̦·xH2O。该方法所用原料来源广泛,纯度较高,制作工艺简单。硫化砷泥膏和MgCl2均为有色金属冶炼过程的排放的固体废弃物。利用硫化砷和氯化镁为原料制备砷酸镁,即可利用冶炼行业产生的固体废弃物料,也可生产科用于农业、电子工业、军事工业的有用原料,促进了绿色生产和循环经济的发展。
硫化法由制酸废水产生的硫化砷多为无定型硫化砷,具有多种成分组成和矿物结构,由纳米颗粒结构聚集而成的凝胶或者絮凝体,比表面积大,孔隙率高,在溶液中或者空气中非常不稳定,极易吸潮和氧化分解,遇碱易被分解转化为砷酸盐。
发明内容
本发明的目的在于提供一种Na2CO3浸出硫化砷泥膏制备砷酸镁方法,通过用Na2CO3对硫化砷渣进行浸出,用空气或氧化剂氧化,然后将浸出得到的砷酸钠与氯化镁反应,生成砷酸镁沉淀。该方法操作简单、反应温度低、反应时间快速、成本低,是个获得砷酸镁的理想方法。
本发明的目的是通过以下技术方案实现的:
一种Na2CO3浸出硫化砷泥膏制备砷酸镁方法,所述方法按照以下步骤进行:
(1)将硫化砷渣按液固比5-8,按碳酸钠过量20%比例与碳酸钠溶液混合,通入空气或氧化剂,对硫化砷渣浸出,过滤,得到浸出渣和砷酸钠溶液;
(2)将砷酸钠溶液与氯化镁溶液混合,得到砷酸镁沉淀;
(3)过滤分离砷酸镁沉淀和氯化钠溶液,溶液返回浸出***;
(4)经过干燥得到砷酸镁结晶。
所述的一种Na2CO3浸出硫化砷泥膏制备砷酸镁方法,所述步骤(1)碳酸钠为质量分数为99.8%的无水碳酸钠,按硫化砷渣过量称取碳酸钠,按水与硫化砷液固比5-8量取水,将碳酸钠溶于水中,然后向碳酸钠溶液加入硫化砷渣。
所述的一种Na2CO3浸出硫化砷泥膏制备砷酸镁方法,所述步骤(1)浸出温度常温~90℃,通入空气或氧化剂,搅拌速度150-500rpm,浸出时间0.5-2小时。
所述的一种Na2CO3浸出硫化砷泥膏制备砷酸镁方法,所述步骤(1)所述氧化剂为10-30%双氧水或工业氧气。
所述的一种Na2CO3浸出硫化砷泥膏制备砷酸镁方法,所述步骤(2)氯化镁为质量分数为≥98%的六水氯化镁,按氯化镁与水质量比例20:100配制氯化镁溶液,将氯化镁溶液与砷酸钠溶液混合,搅拌1-3分钟,得到砷酸镁沉淀。
所述的一种Na2CO3浸出硫化砷泥膏制备砷酸镁方法,所述步骤(4)过滤的砷酸镁沉淀在80-120℃温度下烘干。
本发明的优点与效果是:
本发明采用废弃资源利用,用Na2CO3浸出硫化砷渣,用MgCl2作为沉淀药剂,具有浸出效率高,残渣率低的特点,浸出反应和镁转化反应速度都可在很短时间内完成,转化后的沉淀主要是5价砷砷酸镁(Mg(AsO3)2̦·xH2O),性质十分稳定。
附图说明
图1为本发明工艺流程图;
图2为本发明实施例原料硫化砷渣样外观照片;
图3为本发明实施例原料硫化砷渣样SEM图;
图4为本发明实施例原料硫化砷渣样XRD图;
图5为本发明实施例镁转化反应后的渣样外观照片;
图6为本发明实施例镁转化反应后的渣样XRD图。
具体实施方式
以下结合附图所示实施例对本发明做进一步说明。
本发明实施例中采用的硫化砷成分如表1所示。
实施例1
取碳酸钠27.5g,溶于150mL蒸馏水中,取硫化砷渣50g(含水率53.6%), 加入碳酸钠溶液中,浸出温度为 29℃,搅拌0.5小时,搅拌速度150 rpm,过滤,得到砷酸钠溶液。
取6水氯化镁80g,溶于100mL蒸馏水中,将砷酸钠溶液与氯化钙溶液混合,反应在瞬间完成,过滤,得到钙砷酸镁沉淀29.4g。
实施例2
取碳酸钠27.5g,溶于150mL蒸馏水中,取硫化砷渣50g(含水率53.6%), 加入碳酸钠溶液中,浸出温度为 90℃,搅拌0.5小时,搅拌速度150 rpm,过滤,得到砷酸钠溶液。
取6水氯化镁80g,溶于100mL蒸馏水中,将砷酸钠溶液与氯化钙溶液混合,反应在瞬间完成,过滤,得到砷酸镁沉淀31.4g。
实施例3
取碳酸钠27.5g,溶于150mL蒸馏水中,取硫化砷渣50g(含水率53.6%), 加入碳酸钠溶液中,浸出温度为 29℃,搅拌2小时,搅拌速度150 rpm,过滤,得到砷酸钠溶液。
取6水氯化镁80g,溶于100mL蒸馏水中,将砷酸钠溶液与氯化钙溶液混合,反应在瞬间完成,过滤,得到砷酸镁沉淀27.2g。
实施例4
取碳酸钠27.5g,溶于150mL蒸馏水中,取硫化砷渣50g(含水率53.6%), 加入碳酸钠溶液中,浸出温度为 90℃,搅拌2小时,搅拌速度150 rpm,过滤,得到砷酸钠溶液。
取6水氯化钙80g,溶于100mL蒸馏水中,将砷酸钠溶液与氯化钙溶液混合,反应在瞬间完成,过滤,得到砷酸镁沉淀31.4g。
Claims (6)
1.一种Na2CO3浸出硫化砷泥膏制备砷酸镁方法,其特征在于,所述方法按照以下步骤进行:
(1)将硫化砷渣按液固比5-8,按碳酸钠过量20%比例与碳酸钠溶液混合,通入空气或氧化剂,对硫化砷渣浸出,过滤,得到浸出渣和砷酸钠溶液;
(2)将砷酸钠溶液与氯化镁溶液混合,得到砷酸镁沉淀;
(3)过滤分离砷酸镁沉淀和氯化钠溶液,溶液返回浸出***;
(4)经过干燥得到砷酸镁结晶。
2.根据权利要求1所述的一种Na2CO3浸出硫化砷泥膏制备砷酸镁方法,其特征在于,所述步骤(1)碳酸钠为质量分数为99.8%的无水碳酸钠,按硫化砷渣过量称取碳酸钠,按水与硫化砷液固比5-8量取水,将碳酸钠溶于水中,然后向碳酸钠溶液加入硫化砷渣。
3.根据权利要求1所述的一种Na2CO3浸出硫化砷泥膏制备砷酸镁方法,其特征在于,所述步骤(1)浸出温度常温~90℃,通入空气或氧化剂,搅拌速度150-500rpm,浸出时间0.5-2小时。
4.根据权利要求1所述的一种Na2CO3浸出硫化砷泥膏制备砷酸镁方法,其特征在于,所述步骤(1)所述氧化剂为10-30%双氧水或工业氧气。
5.根据权利要求1所述的一种Na2CO3浸出硫化砷泥膏制备砷酸镁方法,其特征在于,所述步骤(2)氯化镁为质量分数为≥98%的六水氯化镁,按氯化镁与水质量比例20:100配制氯化镁溶液,将氯化镁溶液与砷酸钠溶液混合,搅拌1-3分钟,得到砷酸镁沉淀。
6.根据权利要求1所述的一种Na2CO3浸出硫化砷泥膏制备砷酸镁方法,其特征在于,所述步骤(4)过滤的砷酸镁沉淀在80-120℃温度下烘干。