CN1125283A - 轻质多孔隔墙板及其生产工艺 - Google Patents

轻质多孔隔墙板及其生产工艺 Download PDF

Info

Publication number
CN1125283A
CN1125283A CN 95118330 CN95118330A CN1125283A CN 1125283 A CN1125283 A CN 1125283A CN 95118330 CN95118330 CN 95118330 CN 95118330 A CN95118330 A CN 95118330A CN 1125283 A CN1125283 A CN 1125283A
Authority
CN
China
Prior art keywords
percent
water
partition board
lightweight concrete
blowing agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 95118330
Other languages
English (en)
Inventor
陈鹤云
徐亚萍
刘光华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
China Building Materials Academy CBMA
Original Assignee
China Building Materials Academy CBMA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by China Building Materials Academy CBMA filed Critical China Building Materials Academy CBMA
Priority to CN 95118330 priority Critical patent/CN1125283A/zh
Publication of CN1125283A publication Critical patent/CN1125283A/zh
Pending legal-status Critical Current

Abstract

本发明属于一种轻质墙体材料，由轻质砼及无机增强纤维制成，其轻质砼配方为：特种低碱水泥65-90％、粉状发泡剂0.1-0.5％、膨化矿物轻集料10-20％、水溶性乙烯类聚合物1-10％，其中，所述的特种低碱水泥的化学成分为：SiO26-9％、Al2O311-21％、Fe2O31-2％、CaO40-45％、SO313-25％、烧失量7-11％。该板的生产工艺采用成组立模法。本发明所述的板重量轻、强度高、耐潮湿、耐水性、耐久性好、外观平整。

Description

轻质多孔隔墙板及其生产工艺
本发明涉及一种隔墙板，主要是以特种低碱水泥和粉状发泡剂，用成组立模浇注成型工艺生产的无机纤维增强轻质多孔隔墙板。
传统的建筑中多以砖作为隔墙材料，但用在高层建筑由于砖的自重大，无疑使建筑物地基承重增加，因此迫切需要轻质的隔墙材料，目前国内应用的轻质隔墙材料有：轻钢龙骨复合纸面石膏板，石膏珍珠岩空心条板，水泥珍珠岩夹心板，超轻混凝土夹心板，泰柏板，天荣板，硅镁加气板等。但石膏板和硅镁加气板耐湿，耐水性差。水泥珍珠岩夹心板和超轻混凝土夹心板重量不如人意，泰柏板和天荣板的价格又太贵，使轻质隔墙材料的使用受到限制。
本发明的目的在于研制出一种隔墙板。使其不仅强度高、耐潮湿、耐水、防火、耐久性能好，而且成本较低。
本发明首先对隔墙板的配方进行研究，采用水化液相(固/液＝1/10)PH值1小时＜10.5的特种低碱水泥，降低了水泥对增强纤维的腐蚀，提高了隔墙板的耐久性：另外加入粉状发泡剂，在成型过程中产生大量封闭气泡，降低了隔墙板的重量，相对也降低了成本；采用成组立模浇注成型的工艺生产，降低了生产成本，提高了生产效率，生产出的制品强度高，外观平整，更便于装修施工。
本发明所述隔墙板是由轻质砼与无机增强纤维采用成组立模工艺生产的。
本发明所述轻质砼的配方为：
特种低碱水泥          65～90％
粉状发泡剂            0.1～0.5％
膨化矿物轻集料        10～20％
水溶性乙烯类聚合物    1～10％
本发明所述特种低碱水泥的化学成分为：
SiO2                 6～9％
Al2O3               11～21％
Fe2O3               1～2％
CaO                   0～45％
SO3                  13～25％
烧失量                7～11％
本发明所述粉状发泡剂的化学成分为：
萘系扩散剂             5～15％
木质素系减水剂         35～50％
含SiO2的废渣微粉      45～60％
本发明所述的隔墙板生产工艺为：将特种低碱水泥、膨化矿物轻集料、粉状发泡剂按配比称好，放入搅拌机中搅拌均匀后加入水溶性乙烯类聚合物及水搅拌均匀，制成轻质砼的拌合物，在立模中将无机增强纤维排布好，再将配好的轻质砼拌合物注入组装好的立模中，待初凝后，放入温度为35～50℃的环境中养护6小时拆模，制品再湿养三天，就可作为成品。
采用特种低碱水泥∶膨化矿物轻集料∶粉状发泡剂∶水溶性乙烯类聚合物＝80∶20∶0.4∶5配制本发明(1#样)，则与普通低碱水泥与珍珠岩配制的隔墙板(2#样)，它们的物理力学性能比较如表1：
                                                            表1
样品编号 不平度 单位面积重量 抗折力 饱水抗折力
    1# ＜1mm    35～45kg/m2 2000N     1800N
    2# 2～3mm    55～65kg/m2 1600N     1200N
采用本发明不仅生产过程中机械化程度高，可大大提高生产效率，而且制成的隔墙板具有重量轻，强度高，耐潮湿、耐水性、耐久性好，外观平整，成本低等优点。

Claims (2)

1.一种轻质多孔隔墙板，由轻质砼及无机增强纤维制成，其特征在于：所述轻质砼的配方为：
    特种低碱水泥          65-90％
    粉状发泡剂            0.1-0.5％
    膨化矿物轻集料        10-20％
    水溶性乙烯类聚合物    1-10％
其中，所述特种低碱水泥的化学成分为：
    SiO2             6-9％
    Al2O3           11-21％
    Fe2O3           1-2％
    CaO               40-45％
    SO3              13-25％
    烧失量            7-11％
上述粉状发泡剂的化学成分为：
    萘系扩散剂        5-15％
    木质素系减水剂    35-50％
    含SiO2的废渣细粉 45-60％
2.一种生产权利要求1所述隔墙板的生产工艺，其特征在于：将特种低碱水泥、粉状发泡剂、膨化矿物轻集料按配比放入搅拌机中搅拌均匀后，加入水溶性乙烯类聚合物及水搅拌均匀，制成轻质砼拌和物，在立模中将无机增强纤维网格布排布好，再将配好的轻质砼拌和物注入组装好的立模中，待初凝后，放入温度为35-50℃的环境中养护6小时拆模，制品再湿养三天即成。
CN 95118330 1995-11-16 1995-11-16 轻质多孔隔墙板及其生产工艺 Pending CN1125283A (zh)