CN1116153C - 一种利用秸杆制成的隔墙板及其制备方法 - Google Patents
一种利用秸杆制成的隔墙板及其制备方法 Download PDFInfo
- Publication number
- CN1116153C CN1116153C CN 01108764 CN01108764A CN1116153C CN 1116153 C CN1116153 C CN 1116153C CN 01108764 CN01108764 CN 01108764 CN 01108764 A CN01108764 A CN 01108764A CN 1116153 C CN1116153 C CN 1116153C
- Authority
- CN
- China
- Prior art keywords
- straw
- partition plate
- bittern
- utilizes
- make according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种利用秸杆制成的隔墙板及其制备方法。本发明的一种利用秸杆制成的隔墙板,是由下列成分制成:秸杆10%-30%(重量百分比),轻烧镁25%-36%,卤水30%-40%,改性剂1%-2.5%,玻璃纤维1-2%,增强剂5%-10%。同时还涉及制备上述隔墙板的制备方法。采用本发明得到的隔墙板,其抗压强度大于20MPa,软化系数大于0.8,干缩率小于0.6mm/M,能克服吸潮返卤、变形、不抗水等缺陷,生产成本较低,可以大量应用于高层住宅建筑中。
Description
所属领域:
本发明涉及一种利用秸杆制成的隔墙板及其制备方法。
背景技术:
现有技术中有关的秸杆与水泥复合墙体材料,如中国专利CN-91109899,CN-87103594,CN-99115722报道,一般是以秸杆为填充料,使用有机或无机粘结剂,加温、加压制成,在CN-87103594中,使用的粘结剂是脲醛树脂,有剧毒;CN99115722中使用的粘结剂是异氰酸酯类树脂,成本高,且上述两种方法均需加温加压;CN-91109899使用无机粘结剂,加工时也需要加压2MPa/cm2以上。
发明内容:
针对上述缺陷,本发明提供一种用秸杆制成的隔墙板及其制备方法,是以秸杆为填充料,轻烧镁和卤水为粘结剂,玻璃纤维为增韧剂,经改性处理,在常温常压下成型的一种环保隔墙板,其抗压强度大于20MPa,软化系数大于0.8,干缩率小于0.6mm/M,能克服吸潮返卤、变形、不抗水等缺陷,生产成本较低,可以大量应用于高层住宅建筑中。
本发明的技术内容是:利用秸杆制成的隔墙板,是由下列成分制成:秸杆10--30%(重量百分比),轻烧镁25--36%,卤水30--40%,改性剂1--2.5%,玻璃纤维1--2%,增强剂5--10%,其抗压强度大于20MPa,软化系数大于0.8,干缩率小于等于0.6mm/M。
上述隔墙板的制备方法,包括:
a、将卤片加入水中,制成比重为1.17-1.29的卤水;
b、称取卤片重量的2-4%的硫酸亚铁,1-5%的磷酸铝,0.5-2%的聚甲基丙烯酸甲酯乳液或/和油酸或/和乳化石蜡加入卤水中,搅拌均匀;
c、按秸杆10--30%(重量百分比),轻烧镁25--36%,卤水30--40%,改性剂1--2.5%,增强剂5--10%,玻璃纤维1--2%的比例,称取秸杆、轻烧镁、增强剂和步骤b所制成的溶液,倒入搅拌机内搅拌成稀料,称取玻璃纤维备用;
d、将稀料和玻璃纤维均匀分层铺于模具内,成型,硬化即成。本发明的具体内容是:
利用秸杆制成的隔墙板,是由下列成分制成:秸杆10--30%(重量百分比),轻烧镁25--36%,卤水30--40%,改性剂1-2.5%,增强剂5--10%,玻璃纤维1--2%,其抗压强度大于20MPa,软化系数大于0.8,干缩率小于等于0.6mm/M。其中,轻烧镁含氧化镁不低于80%;卤水是由卤片加水制成的比重为1.17-1.29的溶液,卤片含氯化镁不低于45%;改性剂是由(按卤片重量)2-4%硫酸亚铁、1--5%磷酸铝、0.5--2%聚甲基丙烯酸甲酯乳液或/和油酸或/和乳化石蜡组成;增强剂由下列一种或多种成分组成:粉煤灰、滑石粉、烧粘土粉、膨润土,优选的是粉煤灰或/和滑石粉;玻璃纤维是无碱至中碱的玻璃纤维。
上述隔墙板的制备方法,包括:
a、将卤片加入水中,制成比重为1.17-1.29的卤水;
b、称取卤片重量的2-4%的硫酸亚铁,1-5%的磷酸铝,0.5-2%的聚甲基丙烯酸甲酯乳液或/和油酸或/和乳化石蜡加入卤水中,搅拌均匀;
c、按秸杆10--30%(重量百分比),轻烧镁25--36%,卤水30--40%,改性剂1-2.5%,增强剂5--10%,玻璃纤维1--2%的比例,称取秸杆、轻烧镁、增强剂和步骤b所制成的溶液,倒入搅拌机内搅拌成稀料,称取玻璃纤维备用;
d、将稀料和玻璃纤维均匀分层铺于模具内,成型,硬化即成。
实施例一:
1、取含氯化镁45%的卤片50kg,加入50kg水,制成比重为1.2的卤水;
2、取1.5kg硫酸亚铁,1kg磷酸铝,聚甲基丙烯酸甲酯0.5kg,油酸0.5kg,乳化石蜡0.5kg,加入卤水中搅拌均匀;
3、取含氧化镁80%的轻烧镁90kg,步骤2中已加入改性剂的卤水104kg,秸杆45kg,滑石粉16kg,倒入搅拌机内搅拌均匀,制成稀料;
4、取中碱玻璃纤维3.5kg和上述稀料均匀分层铺于模具内,成型,养护28天,即硬化成产品。
检测结果:抗压强度MPa 21.3
软化系数 0.95,
干缩率mm/M 0.6
实施例二:
1、取含氯化镁46%的卤片50kg,加入50kg水,制成比重为1.2的卤水;
2、取2.0kg硫酸亚铁,1.5kg磷酸铝,聚甲基丙烯酸甲酯0.5kg,加入卤水中搅拌均匀;
3、取含氧化镁85%的轻烧镁95kg,步骤2中已加入改性剂的卤水104kg,秸杆32kg,膨润土和粉煤灰30kg,倒入搅拌机内搅拌均匀,制成稀料;
4、将无碱玻璃纤维3.0kg和上述稀料均匀分层铺于模具内,成型,养护28天,即硬化成产品。
检测结果:抗压强度MPa 20.5
软化系数 0.87
干缩率mm/M 0.6
实施例三:
1、取含氯化镁45%的卤片50kg,加入50kg水,制成比重为1.2的卤水;
2、取1.5kg硫酸亚铁,1kg磷酸铝,硅酸乙酯1kg,加入卤水中搅拌均匀;
3、取含氧化镁80%的轻烧镁90kg,步骤2中已加入改性剂的卤水103.5kg,秸杆35kg,滑石粉32kg,倒入搅拌机内搅拌均匀,制成稀料;
4、将低碱玻璃纤维3.0kg和上述稀料均匀分层铺于模具内,成型,养护28天,即硬化成产品。
检测结果:抗压强度MPa 20.3
软化系数 0.86
干缩率mm/M 0.6
实施例四:
1、取含氯化镁45%的卤片50kg,加入50kg水,制成比重为1.2的卤水;
2、取1.5kg硫酸亚铁,1kg磷酸铝,乳化石蜡1kg,加入卤水中搅拌均匀;
3、取含氧化镁82%的轻烧镁90kg,步骤2中已加入改性剂的卤水103.5kg,秸杆35kg,烧粘土粉30kg,倒入搅拌机内搅拌均匀,制成稀料;
4、将低碱玻璃纤维3.0kg和上述稀料均匀分层铺于模具内,成型,养护28天,即硬化成产品。
检测结果:抗压强度MPa 21.3
软化系数 0.95
干缩率mm/M 0.6
Claims (11)
1、一种利用秸杆制成的隔墙板,其特征在于它是由下列成分制成:按重量百分比,秸杆10--30%,轻烧镁25--36%,卤水30--40%,改性剂1--2.5%,玻璃纤维1--2%,增强剂5--10%。
2、根据权利要求1所述的一种利用秸杆制成的隔墙板,其特征在于:其抗压强度大于20MPa,软化系数大于0.8,干缩率小于或等于0.6mm/M。
3、根据权利要求1所述的一种利用秸杆制成的隔墙板,其特征在于:轻烧镁含氧化镁不低于80%。
4、根据权利要求1所述的一种利用秸杆制成的隔墙板,其特征在于:卤水是由卤片加水制成的比重为1.17-1.29的溶液。
5、根据权利要求4所述的一种利用秸杆制成的隔墙板,其特征在于:卤片中氯化镁含量不低于45%。
6、根据权利要求1所述的一种利用秸杆制成的隔墙板,其特征在于:改性剂是下列成分配制而成:按卤片重量,硫酸亚铁2--4%、磷酸铝1--5%、聚甲基丙烯酸甲酯乳液、油酸、乳化石蜡中的一种或多种物质的混合物0.5--2%。
7、根据权利要求6所述的一种利用秸杆制成的隔墙板,其特征在于:,油酸优选的是硅酸乙酯。
8、根据权利要求1所述的一种利用秸杆制成的隔墙板,其特征在于:玻璃纤维是无碱至中碱的玻璃纤维。、
9、根据权利要求1所述的一种利用秸杆制成的隔墙板,其特征在于:增强剂由下列一种或多种组分配制而成:粉煤灰、滑石粉、烧粘土粉、膨润土。
10、根据权利要求9所述的一种利用秸杆制成的隔墙板,其特征在于:优选的增强剂为粉煤灰或/和滑石粉
11、权利要求1所述的一种利用秸杆制成的隔墙板的制备方法,其步骤包括:
a、将卤片加入水中,制成比重为1.17-1.29的卤水;
b、称取卤片重量的2-4%的硫酸亚铁,1-5%的磷酸铝,0.5-2%
的聚甲基丙烯酸甲酯乳液、油酸、乳化石蜡中的一种或多种物
质的混合物加入卤水中,搅拌均匀;
c、按重量百分比,秸杆10--30%,轻烧镁25--36%,卤水30--40%,
改性剂1--2.5%,玻璃纤维1--2%,增强剂5--10%的比例,称
取秸杆、轻烧镁、增强剂和步骤b所制成的已加入改性剂的
卤水,倒入搅拌机内搅拌成稀料,称取玻璃纤维备用;
d、将稀料和玻璃纤维均匀分层铺于模具内,成型,硬化即成。