CN111763949A - 一种不锈钢除锈防锈膏 - Google Patents
一种不锈钢除锈防锈膏 Download PDFInfo
- Publication number
- CN111763949A CN111763949A CN201910258522.4A CN201910258522A CN111763949A CN 111763949 A CN111763949 A CN 111763949A CN 201910258522 A CN201910258522 A CN 201910258522A CN 111763949 A CN111763949 A CN 111763949A
- Authority
- CN
- China
- Prior art keywords
- rust
- stainless steel
- paste
- parts
- hydroxyethylidene diphosphonic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种不锈钢除锈防锈膏,其特征在于包括螯合剂20‑30份、聚合物0‑10份、缓蚀剂10‑30份、摩擦剂5‑15份、非离子表面活性剂1‑10份、黄原胶1‑3份、水10‑67份;所述缓蚀剂为改性羟基乙叉二膦酸;所述改性羟基乙叉二膦酸的制备方法如下:取质量浓度为40%的羟基乙叉二膦酸溶液,按溶液质量的25‑35wt%添加相应量的硅烷偶联剂KH560,60‑80℃下搅拌回流反应1‑3h,最后加入三乙醇胺,调节pH值为8‑10,即得到所述改性羟基乙叉二膦酸。与现有技术相比,本发明所提供的不锈钢防锈除锈膏呈弱碱性,不需要浸泡,可直接擦拭,立即除锈,除锈容易,除锈效果好,且能够有效防止返锈。
Description
技术领域
本发明涉及到精细化工领域,尤其涉及一种用于不锈钢的除锈防锈膏。
背景技术
不锈钢因不易生锈在生活和工业中的应用广泛,但是当其置于室外或者防护方法不当时也会生锈,较多为锈斑,如不能及时去除会产生点蚀,影响外观甚至使用。当家用器具或设备上生锈时,直接用抹布擦难以清除,若用钢丝球擦,一方面除锈效果不好,另一方面会造成表面划伤,影响外观,且划伤处容易产生进一步的腐蚀。
现有除锈剂大多呈酸性,需要浸泡一段时间才能起到较好的除锈效果。但是酸性除锈剂容易进一步腐蚀金属,且除锈慢,效果不理想,使用体验差。另外,酸性除锈剂容易引起返锈。
发明内容
本发明所要解决的技术问题是针对现有技术的现状提供一种不需要浸泡、能立即除锈且具有高效除锈和防止返锈作用的不锈钢除锈防锈膏。
本发明解决上述技术问题所采用的技术方案为:一种不锈钢的除锈防锈膏,其特征在于包括下述重量组成:
所述螯合剂选自葡萄糖酸钠、柠檬酸钠、乙二胺四乙酸钠盐、酒石酸钠、聚天冬氨酸钠、甲基甘氨酸二乙酸三钠、二乙基二胺基五磷酸钠、羟基乙叉二膦酸、氨基三亚甲基磷酸盐和植酸盐中的至少一种;
所述聚合物选自分子量为3000~4000的聚丙烯酸均聚物和聚丙烯酸共聚物中的至少一种;
所述非离子表面活性剂选自聚乙二醇非离子表面活性剂、聚氧乙烯脂肪酸酯、烷基苷型非离子表面活性剂、脂肪酸烷基醇酰胺和氧化胺中的至少一种;
所述缓蚀剂为改性羟基乙叉二膦酸;所述改性羟基乙叉二膦酸的制备方法如下:
取质量浓度为40%的羟基乙叉二膦酸溶液,加入溶液质量的25-35wt%添加硅烷偶联剂KH560,60-80℃下搅拌回流反应1-3h,最后用加入三乙醇胺,调节pH值为8-10,即得到所述改性羟基乙叉二膦酸。
较好的,所述聚丙烯酸的共聚物为丙烯酸-苯乙烯共聚物或丙烯酸-马来酸酐共聚物。
较好的,所述摩擦剂为氧化铝和/或二氧化硅;所述摩擦剂的粒径为200-500目。
优选不锈钢除锈膏包括下述重量组成:
所述丙烯酸-苯乙烯共聚物的平均分子量为3000。
上述各不锈钢的除锈防锈膏的制备方法,其特征性在于包括下述步骤:
将所述螯合剂、相应质量的葡萄糖酸钠、聚合物、缓蚀剂混合均匀后,加入水,溶解完全后,加入所述的非离子表面活性剂,搅拌均匀后,在200-700rpm搅拌条件下加入所述黄原胶,继续按原有转速搅拌至得到膏状物;
向所述膏状物中加入所述的摩擦剂,在研磨机中研磨混合均匀,记得到不锈钢除锈防锈膏。
与现有技术相比,本发明所提供的不锈钢防锈除锈膏呈弱碱性,不需要浸泡,可直接擦拭,立即除锈,除锈容易,除锈效果好,且能够有效防止返锈。
具体实施方式
以下结合实施例对本发明作进一步详细描述。
制备改性羟基乙叉二磷酸:
取质量浓度为40%的羟基乙叉二膦酸溶液,按溶液质量的32.5wt%加入γ-缩水甘油醚氧丙基三甲氧基硅烷(即为硅烷偶联剂KH560,后用KH560代指),80℃条件下搅拌回流反应1h,最后用加入三乙醇胺,调节pH值为8.5,即得到所述改性羟基乙叉二膦酸。
实施例1
按下述重量组成称取各物质:
实施例2
实施例3
实施例4
实施例1至实施例4中的除锈防锈膏的制备方法如下:
将所述螯合剂、相应质量的葡萄糖酸钠、聚合物、缓蚀剂剂混合均匀后,加入水,溶解完全后,加入所述的非离子表面活性剂,搅拌均匀后,加热至50℃,并在400rpm搅拌条件下加入所述黄原胶,继续按原有转速搅拌至得到膏状物;
向所述膏状物中加入所述的摩擦剂,在研磨机中研磨混合均匀,即得到pH值为8的弱碱性不锈钢除锈防锈膏。
对实施例1至实施例4制备的除锈防锈膏进行测试。
制备生锈不锈钢板:
取多块相同形状的覆膜430拉丝不锈钢板,除去表面覆膜,酒精擦拭,待表面干后放入中性盐雾箱中试验,寻得4块生锈程度接近的430不锈钢,生锈等级为C级(GB8923-88),即表面均呈现出点蚀和锈斑。
除锈效果测试:
取各实施例制备的等量防锈除锈膏,均匀涂覆在生锈处,用湿的棉布包裹质量为1kg,直径为5cm的圆柱形铁块,以均匀的速度和幅度在生锈处来回滑动擦拭,记录擦除铁锈所需滑动次数;除去铁锈后,过2min后再用水冲去生锈处残余的防锈除锈膏。
测试结果如表1所示。
防锈效果测试:
将上述4块除锈后的不锈钢放入盐雾箱中进行试验,比较出现锈点需要的时间。
测试结果如表1所示。
表1
由表1可以看出,实施例2的配方除锈更易,且不易返锈,防锈效果好。
Claims (5)
1.一种不锈钢除锈防锈膏,其特征在于包括下述重量组成:
所述螯合剂选自葡萄糖酸钠、柠檬酸钠、乙二胺四乙酸钠盐、酒石酸钠、聚天冬氨酸钠、甲基甘氨酸二乙酸三钠、二乙基二胺基五磷酸钠、羟基乙叉二膦酸、氨基三亚甲基磷酸盐和植酸盐中的至少一种;
所述聚合物选自分子量为3000~4000的聚丙烯酸均聚物和聚丙烯酸共聚物中的至少一种;
所述非离子表面活性剂选自聚乙二醇非离子表面活性剂、聚氧乙烯脂肪酸酯、烷基苷型非离子表面活性剂、脂肪酸烷基醇酰胺和氧化胺中的至少一种;
所述缓蚀剂为改性羟基乙叉二膦酸;所述改性羟基乙叉二膦酸的制备方法如下:
取质量浓度为40%的羟基乙叉二膦酸溶液,按溶液质量的25-35wt%添加相应量的硅烷偶联剂KH560,60-80℃下搅拌回流反应1-3h,最后加入三乙醇胺,调节pH值为8-10,即得到所述改性羟基乙叉二膦酸。
2.根据权利要求1所述的不锈钢除锈防锈膏,其特征性在于所述聚丙烯酸的共聚物为丙烯酸-苯乙烯共聚物或丙烯酸-马来酸酐共聚物。
3.根据权利要求1或2所述的不锈钢除锈防锈膏,其特征性在于所述摩擦剂为氧化铝和/或二氧化硅;所述摩擦剂的粒径为200-500目。
5.如权利要求1至4任一项所述的不锈钢除锈防锈膏的制备方法,其特征性在于包括下述步骤:
将所述螯合剂、相应质量的葡萄糖酸钠、聚合物、缓蚀剂剂混合均匀后,加入水,溶解完全后,加入所述的非离子表面活性剂,搅拌均匀后,加热至50℃,并在200-700rpm搅拌条件下加入所述黄原胶,继续按原有转速搅拌至得到膏状物;
向所述膏状物中加入所述的摩擦剂,在研磨机中研磨混合均匀,记得到不锈钢除锈防锈膏。