CN111511413A - 水胶体组合物和包含该水胶体组合物的生物贴片 - Google Patents
水胶体组合物和包含该水胶体组合物的生物贴片 Download PDFInfo
- Publication number
- CN111511413A CN111511413A CN201880083145.9A CN201880083145A CN111511413A CN 111511413 A CN111511413 A CN 111511413A CN 201880083145 A CN201880083145 A CN 201880083145A CN 111511413 A CN111511413 A CN 111511413A
- Authority
- CN
- China
- Prior art keywords
- particles
- aerogel
- hydrocolloid
- hydrophobic
- aerogel particles
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
提供了水胶体组合物和包含所述水胶体组合物的生物贴片。所述水胶体组合物具有疏水性弹性体基质。水胶体颗粒和气凝胶颗粒分散在所述基质中。所述气凝胶颗粒可以是二氧化硅气凝胶颗粒。所述气凝胶颗粒可包括具有在颗粒表面上形成有疏水性官能团的颗粒。所述气凝胶颗粒可以是疏水性气凝胶颗粒，在颗粒表面上同时形成疏水性官能团和亲水性官能团的杂化气凝胶颗粒，或者是所述疏水性气凝胶颗粒，所述杂化气凝胶颗粒和亲水性气凝胶颗粒的混合物。
Description
技术领域
本发明实施例涉及一种生物贴片，更具体地，涉及水胶体形式的生物贴片。
背景技术
保护和治疗伤口的方法，包括药物治疗，也称为敷料，该敷料可分为干燥环境的纱布敷料和封闭的湿敷料。在干燥环境的纱布敷料情况下，水分通过纱布被蒸发并除去，因此存在的缺点是在伤口上形成结皮以防止再生的上皮细胞沿伤口表面平滑地移动，从而留下疤痕。相反，在封闭的湿敷料的情况下，防止伤口干燥并且将伤口置于湿润状态以平滑地恢复伤口。
封闭的湿敷料可分为半透膜敷料，泡沫敷料或水胶体敷料，它们可根据伤口渗出液的量单独使用。在水胶体敷料中，亲水性分子从伤口吸收渗出液，但是渗出液吸收的程度受到限制，因此，如果发生大量渗出液，则需要频繁更换敷料。另外，由于透湿性和防水功能仍然不足，现有的水胶体敷料可能具有由于伤口愈合延迟而引起疼痛和气味的问题。
发明内容
技术问题
本发明要解决的问题是提供一种可隔热的水胶体型生物贴片。
本发明要解决的另一个问题是提供具有改善的透湿性和耐水性的水胶体型生物贴片。
本发明要解决的另一个问题是提供具有改善的渗出液吸收能力的水胶体型生物贴片。
技术方案
本发明的一个方面提供了一种水胶体组合物。所述水胶体组合物包含疏水性弹性体基质。分散在所述基质中的多个水胶体颗粒和多个气凝胶颗粒。所述水胶体组合物可包含100重量份的所述疏水性弹性体，70-150重量份的所述水胶体颗粒和1-15重量份的所述气凝胶颗粒。
所述疏水性弹性体可以是苯乙烯-异戊二烯-苯乙烯三嵌段共聚物(SIS)。所述水胶体颗粒可以是通过钙离子交联的藻酸盐。
所述气凝胶颗粒可以是二氧化硅气凝胶颗粒。所述气凝胶颗粒可具有在颗粒表面上形成疏水性官能团的颗粒。所述气凝胶颗粒可以是疏水性气凝胶颗粒，在颗粒表面上同时形成疏水性官能团和亲水性官能团的杂化气凝胶颗粒，或者是所述疏水性气凝胶颗粒，所述杂化气凝胶颗粒和亲水性气凝胶颗粒的混合物。
所述水胶体组合物可以进一步包含粘合剂和/或增塑剂。
本发明的另一方面提供了一种生物贴片。所述生物贴片包括具有疏水性弹性体基质以及分散在所述基质中的水胶体颗粒和气凝胶颗粒的水胶体片。所述生物贴片可以进一步包括粘合剂层，其是设置在水胶体片的上表面上的亲水性粘合剂层；和/或基层，其是设置在水胶体片的下表面上的透湿防水膜。所述水胶体片可包含100重量份的所述疏水性弹性体，70-150重量份的所述水胶体颗粒和1-15重量份的所述气凝胶颗粒。所述水胶体片可以进一步包含粘合剂和/或增塑剂。
有益效果
如上所述，根据本发明，可以提供一种水胶体型生物贴片，其由于包含高度多孔的气凝胶而隔热。另外，可以改善水胶体型生物贴片的透湿性和防水功能。除此之外，可以提高所述水胶体型生物贴片吸收渗出液的能力。
然而，本发明的效果不限于上述效果，并且本领域技术人员将可从以下描述清楚地理解未提及的其他效果。
附图说明
图1是示出了根据本发明实施例的生物贴片的横截面的示意图；
图2是示出了根据本发明的实施例的生物贴片应用于伤口部位的状态示意图；
图3a-图3c是说明气凝胶制备例1-3获得的粉末分别通过傅立叶变换红外光谱法(FT-IR光谱法)的测量结果的图；
图4是说明气凝胶粉末(a)和混合粉末(b)在水中的漂浮度的图像，所述气凝胶粉末(a)包括根据气凝胶制备例2的杂化气凝胶，所述混合粉末(b)为根据气凝胶制备例3的亲水性气凝胶和根据气凝胶制备例1的疏水性气凝胶的混合粉末；
图5是根据生物贴片制备例1的生物贴片的照片；
图6是示出了根据生物贴片制备例1的生物贴片的粘合强度的图；
图7是示出了根据生物贴片制备例1的生物贴片的透气度的照片。
具体实施方式
在下文中，将参考附图详细描述本发明的示例性实施例，以便更详细地描述本发明。然而，本发明不限于本文描述的实施例，也可以以其他形式实施。
在本说明书中，当描述为“Cx至Cy”时，应解释是，也描述了具有与碳数X和碳数Y之间的所有整数相对应的碳原子数的情况。在本说明书中，当描述“X至Y”时，对应于X和Y之间的所有整数的数字应当解释为一起描述。
在本说明书中，“气凝胶”可以指其中分散介质是气体特别是空气的凝胶，并且可以是包括狭义的气凝胶和干凝胶的概念。
水胶体组合物
根据本发明的一个实施例的水胶体组合物包括疏水性弹性体基质，和分散在所述基质中的水胶体颗粒和气凝胶颗粒。所述水胶体组合物可以包含100重量份的所述疏水性弹性体，70-150重量份的所述水胶体颗粒和1-15重量份的所述气凝胶颗粒，但不限于此，并且可以根据组合物的用途进行各种选择。
所述疏水性弹性体可以是天然橡胶，聚异戊二烯，聚丁二烯，丁基橡胶(例如异戊二烯和异丁烯共聚物)或卤化丁基橡胶，但不限于此。具体地，疏水性弹性体可以是苯乙烯-异戊二烯-苯乙烯三嵌段共聚物(SIS)或聚异丁烯和SIS的混合物。
所述水胶体颗粒可以是具有其中亲水性聚合物形成三维交联的网络结构的颗粒，并且可以表现出高持水能力。所述三维交联可以通过物理键合形成，例如氢键，范德华力或疏水相互作用；或化学键合，例如共价键。构成这些水胶体颗粒的所述亲水性聚合物可以是天然的亲水性聚合物，例如果胶，明胶，纤维素，特别是羧甲基纤维素(CMC)，胶原蛋白，右旋糖酐，弹性蛋白，甲壳素，壳聚糖，藻酸钠；或合成亲水性聚合物，例如聚丙烯酸(PAA)，聚乙烯醇，聚乙二醇，聚乙烯吡咯烷酮，聚氨酯，聚甲基丙烯酸羟乙酯，硅树脂；或其组合。所述水胶体颗粒可进一步包含用于将亲水性聚合物形成三维网络结构的交联剂，其中所述交联剂可以是氯化钙，硫酸钙，硝酸钙，硝酸锌，氯化锌，硫酸锌，过硫酸铵或戊二醛。所述交联剂不限于此，还可以根据亲水性聚合物的类型而变化。在一示例中，水胶体颗粒可以是通过钙离子交联的藻酸盐。
气凝胶颗粒的描述将稍后描述。
所述水胶体组合物可以进一步包含压敏粘合剂和/或增塑剂。所述压敏粘合剂可以是弹性体压敏粘合剂，例如聚异丁烯、苯酚改性的萜烯、松香酯，例如松香的甘油酯和松香的季戊四醇酯，包括合成多萜粘合剂的非弹性压敏粘合剂，或这些中的两种或更多种的组合。所述增塑剂可用于提供润湿作用和/或粘度控制。这些增塑剂是本领域公知的，并且包括油混合物，蜡或液体或软粘合剂，包括烃油，液态烃树脂，液体多萜，液体聚(异丁烯)，例如GLISSOPAL等。例如，所述增塑剂可以是石蜡。
本发明的所述水胶体组合物可以进一步包含痕量的其他成分，例如，本领域众所周知的药理学活性剂，例如伤口愈合促进剂，抗菌剂，芳香剂，除臭剂和抗氧化剂。
气凝胶颗粒
所述气凝胶颗粒可以是具有纳米尺寸孔的高孔纳米结构，其通过用空气代替凝胶结构中的液体而获得，并且可以是二氧化硅气凝胶颗粒。
所述气凝胶颗粒可以具有0.1-1000μm的尺寸，具体地，几至数十μm，例如1-40μm。BET法下的气凝胶颗粒的表面积可以为300-2000m2/g，具体地为500-1000m2/g，气凝胶颗粒的密度可以为0.03-0.5g/cc，并且气凝胶颗粒的孔隙率可以为70％-99％，气凝胶颗粒的孔径可以为5-50nm。
所述气凝胶颗粒可具有在颗粒表面上形成疏水性官能团的颗粒。所述疏水性官能团不仅可以布置在颗粒表面上，而且可以布置在颗粒内部的孔的表面上。所述疏水性官能团可以是键合至构成气凝胶颗粒的原子的官能团，例如，键合至Si原子的官能团，并且可以是氢，C1-C18直链或支链的烷基，由以下化学式1表示的甲硅烷氧基或其组合。
[化学式1]
*-OSiH(3-n)R1n
在化学式1中，R1可以是C1-C18的直链或支链烷基，n可以是0-3的整数，并且*可以表示与气凝胶颗粒中的Si连接的键。
当n为1-3的整数时，由化学式1表示的官能团可以被称为烷基硅氧基。所述C1-C18直链或支链烷基可以是C1-C6直链烷基，并且所述C1-C6直链烷基可以是饱和直链烷基，例如甲基，乙基，正丙基，正丁基，正戊基或正己基。在一个实施例中，所述C1-C6直链烷基可以是甲基或乙基。
在一个示例中，所述气凝胶颗粒可以是，基于颗粒表面的总官能团，具有80mol％-100mol％，特别是85mol％，90mol％，95mol％或甚至99mol％或更多疏水官能团的疏水性气凝胶颗粒。所述颗粒表面可以进一步包括颗粒内孔表面。
在另一个示例中，所述气凝胶颗粒可以是在颗粒表面上具有亲水性官能团和疏水性官能团的杂化气凝胶颗粒。所述颗粒表面可以进一步包括颗粒的内孔表面。
在又一个示例中，所述气凝胶颗粒可以是杂化气凝胶颗粒，疏水性气凝胶颗粒以及亲水性气凝胶颗粒的混合物。在此，亲水性气凝胶颗粒，基于颗粒表面的总官能团，可以具有80mol％-100mol％，特别是85mol％，90mol％，95mol％或甚至99mol％或更多亲水性官能团。所述颗粒表面可以进一步包括颗粒内孔表面。所述亲水性官能团可以键合至构成气凝胶颗粒的原子，例如，键合至Si原子，也可以是羟基(-OH)。所述混合物可包含约25-40wt％的杂化气凝胶颗粒，约25-40wt％的亲水性气凝胶颗粒和约25-40wt％的疏水气凝胶颗粒。在一实施例中，可以包含1:1:1的重量比的杂化气凝胶颗粒，亲水性气凝胶颗粒和疏水性气凝胶颗粒。
所述杂化气凝胶颗粒可以在其表面上具有7:3至3:7的摩尔比的所述疏水性官能团和所述亲水性官能团。
同时，可以根据对水的亲和力对杂化气凝胶颗粒，亲水性气凝胶颗粒和疏水性气凝胶颗粒进行分类。具体地，当将气凝胶颗粒放置在有水的容器中，所述亲水性气凝胶颗粒可能沉到容器的底部，所述疏水性气凝胶颗粒可能漂浮在水表面上，而所述杂化气凝胶颗粒可能一半淹没在水面下或刚好淹没在水面下。
具有杂化气凝胶颗粒的气凝胶粉末的制造方法可以如下。然而，不限于此。首先，可以制备疏水性气凝胶粉末，并且可以对疏水性气凝胶粉末进行热处理，以部分改性粉末中提供的颗粒的外表面，并进一步改性内孔的表面。具体地，可以将疏水性气凝胶粉末中提供的至少一些颗粒的疏水性表面官能团改变为亲水性表面官能团。具体地，可以通过热处理将疏水性表面官能团例如氢，烷基或硅氧基，特别是烷基硅氧基转化为羟基。同时，气凝胶粉末中的残留水分可以至少部分或完全除去。疏水性气凝胶粉末的热处理可包括逐渐升高疏水性气凝胶粉末的温度的升温步骤，以及将疏水性气凝胶粉末在加热状态下保持预定时间以进行烧结的烧结步骤。
因此，如上所述，所述气凝胶粉末的至少一些颗粒可以被转化为具有疏水性表面和亲水性表面的杂化气凝胶颗粒，并且一些其他颗粒可以被转化为具有亲水性表面的亲水性气凝胶颗粒，并且一些其他颗粒可能保留为保持疏水性表面的疏水性气凝胶颗粒。结果，可以获得包含亲水性气凝胶颗粒，疏水性气凝胶颗粒和杂化气凝胶颗粒全部的混合物的气凝胶粉末。
所述热处理可以使用电炉进行，并且可以在温度升高至300-500℃的状态下进行0.5-24小时。另外，可以在氧化气氛，特别是空气气氛中进行热处理。当调节热处理温度或时间时，疏水性气凝胶中仅一些疏水性表面官能团可以变为亲水性表面官能团，或者疏水性气凝胶中几乎所有疏水性表面官能团都可以变为亲水性表面官能团以形成亲水性气凝胶。例如，可以通过约345-355℃，特别是347-353℃的热处理，将疏水性气凝胶中仅一些疏水性表面官能团改变为亲水性表面官能团；并且可以通过进行约356-365℃，特别是357-363℃的热处理以形成亲水性气凝胶，其中疏水性气凝胶的所有疏水性表面官能团已经变成亲水性表面官能团。
生物贴片
图1是示出了根据本发明实施例的生物贴片的横截面的示意图。
参考图1，生物贴片可包括在基层10上的水胶体片20，粘合剂层30和剥离层40。然而，所述基层10，所述粘合剂层30和所述剥离层40中的至少一个可以省略。
所述基层10可以是透湿防水膜，并且可以是多孔聚乙烯或聚氨酯膜。所述基层10可以阻挡水滴和外部病原体，例如细菌，其尺寸大于该层的微孔(防水性质)，同时使水蒸气和空气通过微孔传递(透湿性质)。所述基层10可具有约10-100μm的厚度。
可以通过将上述水胶体组合物层压所述基层10上来形成所述水胶体片20。具体地，在将水胶体组合物挤压到所述基层10上之后，可以使用热压机，辊或等将其形成为具有均匀厚度的层，由此形成水胶体片20。
所述水胶体片20可以包括疏水性弹性体基质21。水胶体颗粒22和气凝胶颗粒23可以分散在所述疏水性弹性体基质21中。同时，在制备水胶体组合物的过程中，通过将疏水性弹性体，水胶体颗粒和气凝胶颗粒物理均匀混合的过程，水胶体颗粒和气凝胶颗粒可以几乎均匀地混合在疏水性弹性体基质中。因此，所述水胶体片20可以包括均匀分散在所述疏水性弹性体基质21中的水胶体颗粒22和气凝胶颗粒23。
所述粘合剂层30是可以提供粘合使得水胶体片20可以与皮肤紧密接触的层。所述粘合剂层30可以是压敏粘合剂层，具体地，可以是亲水性压敏粘合剂层。所述粘合剂层30可以是，例如松香酯层，硅酮层或其复合层。然而，本发明不限于此，并且可以使用本领域中使用的各种材料。所述粘合剂层30可以形成为非常薄的几微米厚度。
所述剥离层40是可以在将生物贴片黏附到受伤的皮肤上之前立即除去的层，并且可以使用本领域广泛使用的层形成。
图2是示出了根据本发明的实施例的生物贴片应用于伤口部位的状态示意图。
参考图2，将生物贴片施加在已经发生伤口105的皮肤100上。参照图1描述的剥离层40，可以从生物贴片上除去，并且所述粘合剂层30可黏附到含有伤口105的皮肤100上。当省去所述粘合剂层30时，所述水胶体片20可以设置成直接接触伤口。
所述基层10是表现出具有防水性和透湿性的膜，其可以从皮肤100的汗液或伤口105的渗出液中传递过量的水分(B)，并通过空气渗透去除异味，并抑制来自外界的水滴(C)和病原体(D)的渗透。
由于分散在水胶体片20中的气凝胶颗粒23具有高孔隙度结构，因此即使在水胶体片20中，它们也可以在颗粒中包含空气，因此可以表现出绝热性能。气凝胶颗粒23的所述绝热性能可以将伤口部位的温度保持在合适的温度或更高，从而提高伤口愈合的速度。
另外，可以使空气和水蒸气通过这种具有高孔隙度结构的气凝胶颗粒23进行传递，从而可以提高水胶体片20的透气性和透湿性。结果，来自皮肤100的汗水或来自伤口105的渗出液的过量水分(B)可通过水胶体片20和基层10散发到外部，从而使伤口部位105保持清洁，并且减少气味。
然而，气凝胶颗粒23的多孔结构没有大到足以穿透水滴或病原体。另外，由于水胶体片20设置有疏水性弹性体基质21，所以它可以具有防水性或不透水性。同时，当气凝胶颗粒23在其表面上具有疏水性官能团时，可以改善水胶体片20的防水性或不透水性。在这种情况下，可以考虑省略基层10。
在一个实例中，所述气凝胶颗粒23可以是在大部分颗粒表面上具有疏水性官能团的疏水性气凝胶颗粒，在另一个示例中，可以是在颗粒表面上具有亲水性官能团和疏水性官能团的杂化气凝胶颗粒。在另一个示例中，气凝胶颗粒23可以是疏水性气凝胶颗粒，杂化气凝胶颗粒和亲水性气凝胶颗粒的混合物。
当气凝胶颗粒23在表面上包括疏水性官能团时，由于表面上的疏水性官能团，这些气凝胶颗粒23可以不靠近水胶体颗粒22而设置，并且可以与表现出亲水性的水胶体颗粒22隔开一定距离而设置。该距离或间隙可以是来自皮肤100的汗液或伤口105的渗出液的多余水分(B)可以通过的通道。另外，该距离或间隙可提供水胶体颗粒溶胀的自由空间。当水胶体颗粒22吸收伤口105渗出液时，可能发生水胶体颗粒22的溶胀。在这种情况下，即使当水胶体片20中的水胶体颗粒22的含量增加时，可以提供水胶体颗粒22充分溶胀的自由空间，从而可以大大提高水胶体片20的吸收率。这可以解决以下问题：由于吸收率有限，当伤口渗出液过多时，不能使用常规的水胶体型敷料。换句话说，根据该实施例的生物贴片不仅可以用于渗出液少的轻伤，而且可以用于渗出液多的深而大的伤口。
当所述气凝胶颗粒23在表面上具有亲水性官能团时，即，气凝胶颗粒23是杂化气凝胶颗粒或疏水性气凝胶颗粒，杂化气凝胶颗粒和亲水性气凝胶颗粒的混合物时，气凝胶颗粒23的亲水性官能团可以提供键合到水蒸气上的氢，从而提高了水胶体片20的透湿性。另外，在表面上具有亲水性官能团的气凝胶颗粒23也可以表现出对渗出液的吸收性。
在下文中，提供优选的示例以帮助理解本发明。然而，以下实验例仅用于帮助理解本发明，并且本发明不受以下实验例的限制。
<气凝胶制备例1>
将2000g水与500g硅酸钠溶液(SiO2 6wt％)混合并使用电动搅拌器以300rpm的转速搅拌后，向其中加入200ml乙酸，使用电动搅拌器以600rpm的转速混合约30分钟以制备硅酸盐溶液。将硅酸盐溶液在真空中脱气约10分钟后，将其填充在由PVC制成的矩形框架中，然后进行凝胶化反应1小时以制备硅胶。依次用水蒸气和乙醇洗涤硅胶，将硅胶转化为醇凝胶，然后用己烷和三甲基氯硅烷(TMCS)的混合溶液处理醇凝胶表面，得到在表面包含三甲基甲硅烷氧基(-OSi(CH3)3)的甲硅烷基化凝胶。将获得的甲硅烷基化凝胶在常压下在约55℃的温度下干燥约15小时，并在约230℃的温度下烧结约10小时，以获得疏水性气凝胶。此后，将疏水性气凝胶粉碎成粉末以获得疏水性气凝胶粉末。
<气凝胶制备例2>
将由气凝胶制备例1获得的疏水性气凝胶粉末置于氧化气氛中的电炉中并加热至340℃，随后在保持该温度的同时烧结1小时。
<气凝胶制备例3>
将由气凝胶制备例1获得的疏水性气凝胶粉末置于氧化气氛中的电炉中并加热至350℃，然后在保持该温度的同时烧结1小时。
<气凝胶制备例4>
将由气凝胶制备例1获得的疏水性气凝胶粉末置于氧化气氛中的电炉中并加热至360℃，随后在保持该温度的同时烧结1小时。
图3a至3c是说明气凝胶制备例2-4获得的粉末分别通过傅立叶变换红外光谱法(FT-IR光谱法)的测量结果的图。
参照图3a，可以看出，根据气凝胶制备例2的气凝胶除了二氧化硅中固有的Si-O-Si基外还显示Si-CH3基，这表明所述气凝胶是具有疏水性表面的疏水性气凝胶。
参考图3b，可以看出，根据气凝胶制备例3的气凝胶除了二氧化硅中固有的Si-O-Si基之外还显示了Si-CH3基和OH基，这表明所述气凝胶是通过热处理将疏水表面部分改性为亲水性表面而形成的杂化气凝胶。
参考图3c，可以看出，根据气凝胶制备例4的气凝胶除了在二氧化硅中固有的Si-O-Si基之外还显示了OH基，并且在表面改性前，观察到对应于Si-CH3基的峰完全消失，这表明所述气凝胶是通过热处理将疏水性表面完全改性为亲水性表面而形成的亲水性气凝胶。
图4是说明气凝胶粉末和混合物在水中的漂浮度的图像，所述气凝胶粉末包括根据气凝胶制备例3的杂化气凝胶，所述混合物为根据气凝胶制备例4的亲水性气凝胶和根据气凝胶制备例2的疏水性气凝胶的混合物。
参照图4，可以看出，在根据气凝胶制备例4的亲水性气凝胶和根据气凝胶制备例2的疏水性气凝胶的混合物(b)的情况下，漂浮在水表面上的疏水性气凝胶和沉淀在烧杯底部的亲水性气凝胶可以很明显地区别。另一方面，可以看出，在包含根据气凝胶制备例3的气凝胶的气凝胶粉末(a)的情况下，气凝胶颗粒包括大约一半淹没在水表面下的杂化气凝胶颗粒，沉淀在烧杯底部的亲水性气凝胶颗粒，以及漂浮在水表面的疏水性气凝胶颗粒所有。
另外，同时参考图3b和图4，可以假定根据气凝胶制备例3的气凝胶粉末包括在其表面上同时具有Si-CH3基和OH基的杂化气凝胶，在其表面上主要具有OH基的亲水性气凝胶，以及在其表面上主要具有Si-CH3基的疏水性气凝胶。
另外，如图3b和图3c中每个OH峰强度和图4的结果共同表明，根据气凝胶制备例3的气凝胶粉末可包括25-40重量％的杂化气凝胶颗粒，25-40重量％的疏水性气凝胶颗粒和25-40重量％的亲水性气凝胶颗粒，以及进一步表明这些颗粒以1∶1∶1的重量比混合。
<生物贴片制备例1>
将2.5kg的苯乙烯-异戊二烯-苯乙烯共聚物(SIS)加热至170℃，并将温度保持20分钟以液化。将液化的苯乙烯-异戊二烯-苯乙烯共聚物冷却至120℃，并向其中加入2kg的聚异丁烯和1.2kg的液体石蜡，然后均匀混合以制备弹性体混合物。将所述弹性体混合物冷却至90℃，并将4.3kg海藻酸钠，100g氯化钙和0.4kg根据气凝胶制备例3的杂化气凝胶粉末添加至冷却的混合物中，然后均匀混合以制备水胶体-弹性体混合物。将水胶体混合物在100℃下挤压以制备纳米多孔生物贴片。
<生物贴片制备例2>
除了根据气凝胶制备例1使用50g氯化钙和40g疏水性气凝胶粉末以外，以与生物贴片制备例1中相同的方式制备纳米多孔生物贴片。
图5是根据生物贴片制备例1的生物贴片的照片。
参考图5，可以看出形成了浅黄色的生物贴片。
<生物贴片附着力试验例>
在测试评估机构使用ASTM D3330的方法测量生物贴片的附着力；并且在20N称重传感器，300mm/min的测试速度和附着的SUS 304的通用测试机条件下测量。
图6是示出了根据生物贴片制备例1的生物贴片的粘合强度的图。
参考图6，根据生物贴片制备例1的生物贴片表现出平均为2.31N/25mm的压敏粘合力。
<生物贴片透湿性和吸收试验例>
根据EN 13726-2标准测量生物贴片的透湿性，并根据EN 13726-1标准测量吸光度。
下表1是比较根据生物贴片制备例2的生物贴片和水胶体敷料产品的性能对比表。在此，水胶体敷料产品不包含气凝胶。
表1
参照表1，当与不包含气凝胶的水胶体敷料相比时，根据生物贴片制备例2的生物贴片，尽管厚度增加了，但透湿性提高了约5倍，并且渗出液吸收率提高了约6倍。
<生物贴片透气性测试例>
将生物贴片放置在测试仪中后，检查空气是否通过生物贴片渗透到生物贴片的顶部，同时在生物贴片下方以恒定压力引入空气。
图7是示出了根据生物贴片制备例1的生物贴片的透气度的照片。
参考图7，根据生物贴片制备例1的生物贴片因空气流入而溶胀，并且由于在生物贴片的顶部产生大量气泡，因此确认透气性非常优异。
以上，本发明已经参考优选实施例进行了详细描述，但是本发明不限于上述实施例，并且本领域技术人员可以在本发明的精神和范围内进行各种修改和改变。
Claims (17)
1.一种水胶体组合物，其包含：
疏水性弹性体基质；和
分散在所述基质中的水胶体颗粒和气凝胶颗粒。
2.根据权利要求1所述的水胶体组合物，其中所述水胶体组合物包含100重量份的所述疏水性弹性体，70-150重量份的所述水胶体颗粒和1-15重量份的所述气凝胶颗粒。
3.根据权利要求1所述的水胶体组合物，其中所述疏水性弹性体是苯乙烯-异戊二烯-苯乙烯三嵌段共聚物(SIS)。
4.根据权利要求1所述的水胶体组合物，其中所述水胶体颗粒是通过钙离子交联的藻酸盐。
5.根据权利要求1所述的水胶体组合物，其中所述气凝胶颗粒是二氧化硅气凝胶颗粒。
6.根据权利要求1或5所述的水胶体组合物，其中所述气凝胶颗粒具有在颗粒表面上形成疏水性官能团的颗粒。
7.根据权利要求6所述的水胶体组合物，其中所述气凝胶颗粒是疏水性气凝胶颗粒，在颗粒表面上同时形成疏水性官能团和亲水性官能团的杂化气凝胶颗粒，或者是所述疏水性气凝胶颗粒，所述杂化气凝胶颗粒和亲水性气凝胶颗粒的混合物。
8.根据权利要求1所述的水胶体组合物，进一步包含压敏粘合剂和/或增塑剂。
9.一种生物贴片，其包括具有疏水性弹性体基质以及分散在所述基质内的水胶体颗粒和气凝胶颗粒的水胶体片。
10.根据权利要求9所述的生物贴片，进一步包括：
粘合剂层，其是设置在水胶体片的上表面上的压敏粘合剂层；和/或
基层，其是设置在水胶体片的下表面上的透湿防水膜。
11.根据权利要求9所述的生物贴片，其中所述水胶体片包含100重量份的所述疏水性弹性体，70-150重量份的所述水胶体颗粒和1-15重量份的所述气凝胶颗粒。
12.根据权利要求9所述的生物贴片，其中所述疏水性弹性体是苯乙烯-异戊二烯-苯乙烯三嵌段共聚物(SIS)。
13.根据权利要求9所述的生物贴片，其中所述水胶体颗粒是通过钙离子交联的藻酸盐。
14.根据权利要求9所述的生物贴片，其中所述气凝胶颗粒是二氧化硅气凝胶颗粒。
15.根据权利要求9或14所述的生物贴片，其中所述气凝胶颗粒具有在颗粒表面上形成疏水性官能团的颗粒。
16.根据权利要求15所述的生物贴片，其中所述气凝胶颗粒是疏水性气凝胶颗粒，在颗粒表面上同时形成疏水性官能团和亲水性官能团的杂化气凝胶颗粒，或者是所述疏水性气凝胶颗粒，所述杂化气凝胶颗粒和亲水性气凝胶颗粒的混合物。
17.根据权利要求9所述的生物贴片，其中所述水胶体片进一步包含压敏粘合剂和/或增塑剂。