CN111347748A - 一种具有储热功能的光学膜材料 - Google Patents

一种具有储热功能的光学膜材料 Download PDF

Info

Publication number
CN111347748A
CN111347748A CN202010205744.2A CN202010205744A CN111347748A CN 111347748 A CN111347748 A CN 111347748A CN 202010205744 A CN202010205744 A CN 202010205744A CN 111347748 A CN111347748 A CN 111347748A
Authority
CN
China
Prior art keywords
interlayer
solution
heat storage
storage function
optical film
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202010205744.2A
Other languages
English (en)
Inventor
许忠明
许宗扬
陈国立
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Aoluodan New Material Co ltd
Original Assignee
Suzhou Aoluodan New Material Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Aoluodan New Material Co ltd filed Critical Suzhou Aoluodan New Material Co ltd
Priority to CN202010205744.2A priority Critical patent/CN111347748A/zh
Publication of CN111347748A publication Critical patent/CN111347748A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种具有储热功能的光学膜材料，涉及PVB中间膜技术领域。一种具有储热功能的光学膜材料，包括两个夹层和一个中间层，所述夹层为PVB中间膜，所述中间层为玻璃棉，所述夹层的组分包括7.5‑8.8wt％醇类、4.6‑4.8wt％醛类、0.01‑0.03wt％抗氧剂、0.01‑0.02wt％氧化物、0.01wt％无机盐，所述醇类为聚乙烯醇，所述醛类为正丁醛，所述无机盐为乙酸钾、甲酸钾、乙酸镁、乙酸钙和乙酸钠中的一种或多种的混合物。本发明明显增强了PVB中间膜的储热能力，运用于建筑物的外壁幕墙上，能有效地提高建筑幕墙的保温能力，降低建筑室内温度随外界温度的变化速率，使得PVB中间膜的延展性增强，降低温差过大造成PVB中间膜开裂的风险。

Description

一种具有储热功能的光学膜材料
技术领域
本发明涉及PVB中间膜技术领域，具体为一种具有储热功能的光学膜材料。
背景技术
PVB中间膜是半透明的薄膜，PVB中间膜主要用于夹层玻璃，是在两块玻璃之间夹进一层PVB薄膜，经高压复合、加温而成的特殊玻璃。PVB夹层玻璃由于具有安全、控制噪音和隔离紫外线等多项功能，广泛应用于建筑、汽车、光伏等行业。采用特殊配方生产的PVB中间膜在航天、军事和高新技术工业等领域也有着广泛的应用，如用于飞机、航天品、军事仪器、太阳能电池和太阳能接收器等。
应用于建筑幕墙上的一些带有PVB中间膜的玻璃幕墙保温性能较差，尤其对于一些层数较高的楼层，使用这些保温性能较差的玻璃幕墙会致使建筑内温差变化大，这一问题有待进一步改进，因此本发明提出一种具有储热功能的光学膜材料。
发明内容
本发明的目的在于提供一种具有储热功能的光学膜材料，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：一种具有储热功能的光学膜材料，包括两个夹层和一个中间层，所述夹层为PVB中间膜，所述中间层为玻璃棉，所述夹层的组分包括7.5-8.8wt％醇类、4.6-4.8wt％醛类、0.01-0.03wt％抗氧剂、0.01-0.02wt％氧化物和0.01wt％无机盐。
更进一步地，所述醇类为聚乙烯醇，所述醛类为正丁醛。
更进一步地，所述抗氧剂为2-亚甲基双(4-甲基-6-叔丁基苯酚)、四(3,5-二叔丁基-4-羟基)苯丙酸季戊四醇酯、三(2,4-二叔丁基)亚磷酸苯酯、双十八烷基醇季戊二亚磷酸酯、双(3，5-二叔丁基苯基)季戊四醇二亚磷酸酯中的一种或多种的混合物。
更进一步地，所述氧化物为纳米ATO、纳米GTO和纳米钨青铜中的一种或多种的混合物。
更进一步地，所述无机盐为乙酸钾、甲酸钾、乙酸镁、乙酸钙和乙酸钠中的一种或多种的混合物。
更进一步地，所述夹层的制备过程如下：
S1:用适量的醇类配成浓度小于10％的溶液A；
S2:将溶液A降温到50°C以下，加入醛类、抗氧剂、氧化物和无机盐，并搅拌2.5小时,得到溶液B；
S3:保温3-5小时，得到溶液C；
S4:将溶液C放于反应釜中并升温至40-50°C，并保温3-5小时，保温后冷却至室温，得到溶液D；
S5：将溶液D水洗后在升温至50°C，调节pH值至9-10，再保温2-3小时，得到溶液E；
S6：将溶液E脱水干燥制成半成品F；
S7：将半成品F投入到双螺杆挤出机中，按尺寸卷取，得到夹层。
更进一步地，所述PVB中间膜制备工艺如下：
S1:在其中一个夹层外壁粘接中间层；
S2:再从中间层一侧粘接另一个夹层并静置1-2小时。
与现有技术相比，本发明的有益效果是：
（1）、一种具有储热功能的光学膜材料，通过中间层的设置，明显增强了PVB中间膜的储热能力，运用于建筑物的外壁幕墙上，能有效地提高建筑幕墙的保温能力，降低建筑室内温度随外界温度的变化速率。
（2）、一种具有储热功能的光学膜材料，中间层为纵横交错的玻璃棉，有助于提高玻璃幕墙的稳定性，保障玻璃幕墙的安全，另外，夹层中还添加有无机盐成分能起到增强夹层延展性的作用，中间层为网状玻璃棉结构本身的延展性也较高，使得PVB中间膜的延展性增强，降低温差过大造成PVB中间膜开裂的风险。
附图说明
图1为本发明的结构示意图；
图2为本发明的四个实施例与普通PVB中间膜在同样时常阳光照射后外部温度变化曲线图。
图中：1夹层、2中间层。
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例一：
本发明提供一种技术方案：一种具有储热功能的光学膜材料，包括两个夹层1和一个中间层2，夹层1为PVB中间膜，中间层2为玻璃棉，夹层1的组分包括8wt％醇类、4.6wt％醛类、0.02wt％抗氧剂、0.02wt％氧化物、0.01wt％无机盐。
醇类为聚乙烯醇，醛类为正丁醛。
抗氧剂为20%的2-亚甲基双(4-甲基-6-叔丁基苯酚)、25%的四(3,5-二叔丁基-4-羟基)苯丙酸季戊四醇酯和45%双(3，5-二叔丁基苯基)季戊四醇二亚磷酸酯的混合物。
氧化物为纳米ATO。
无机盐为50%乙酸钾和50%甲酸钾。
夹层1的制备过程如下：
S1:用适量的醇类配成浓度小于10％的溶液A；
S2:将溶液A降温到50°C以下，加入醛类、抗氧剂、氧化物和无机盐，并搅拌2.5小时,得到溶液B；
S3:保温4小时，得到溶液C；
S4:将溶液C放于反应釜中并升温至50°C，并保温4小时，保温后冷却至室温，得到溶液D；
S5：将溶液D水洗后在升温至50°C，调节pH值至9，再保温3小时，得到溶液E；
S6：将溶液E脱水干燥制成半成品F；
S7：将半成品F投入到双螺杆挤出机中，按尺寸卷取，得到夹层1。
PVB中间膜制备工艺如下：
S1:在其中一个夹层1外壁粘接中间层2；
S2:再从中间层2一侧粘接另一个夹层1并静置2小时。
将本实施例的保温PVB中间膜用于制备夹层玻璃时，首先将保温PVB中间膜的两个夹层1分别与两层玻璃贴合，然后抽真空，并将周边进行封边，保证PVB中间膜主体与玻璃间的真空状态，夹层玻璃完成。
实施例二：
本发明提供一种技术方案：一种具有储热功能的光学膜材料，包括两个夹层1和一个中间层2，夹层1为PVB中间膜，中间层2为玻璃棉，夹层1的组分包括8.3wt％醇类、4.7wt％醛类、0.01wt％抗氧剂、0.02wt％氧化物、0.01wt％无机盐。
醇类为聚乙烯醇，醛类为正丁醛。
抗氧剂为50%的三(2,4-二叔丁基)亚磷酸苯酯和50%的双十八烷基醇季戊二亚磷酸酯的混合物。
氧化物为纳米GTO。
无机盐为50%的乙酸钾和50%的乙酸钠中的一种或多种的混合物。
夹层1的制备过程如下：
S1:用适量的醇类配成浓度小于10％的溶液A；
S2:将溶液A降温到50°C以下，加入醛类、抗氧剂、氧化物和无机盐，并搅拌2.5小时,得到溶液B；
S3:保温5小时，得到溶液C；
S4:将溶液C放于反应釜中并升温至45°C，并保温4小时，保温后冷却至室温，得到溶液D；
S5：将溶液D水洗后在升温至50°C，调节pH值至9，再保温3小时，得到溶液E；
S6：将溶液E脱水干燥制成半成品F；
S7：将半成品F投入到双螺杆挤出机中，按尺寸卷取，得到夹层1。
PVB中间膜制备工艺如下：
S1:在其中一个夹层1外壁粘接中间层2；
S2:再从中间层2一侧粘接另一个夹层1并静置2小时。
将本实施例的保温PVB中间膜用于制备夹层玻璃时，首先将保温PVB中间膜的两个夹层1分别与两层玻璃贴合，然后抽真空，并将周边进行封边，保证PVB中间膜主体与玻璃间的真空状态，夹层玻璃完成。
实施例三：
本发明提供一种技术方案：一种具有储热功能的光学膜材料，包括两个夹层1和一个中间层2，夹层1为PVB中间膜，中间层2为玻璃棉，夹层1的组分包括7.8wt％醇类、4.8wt％醛类、0.03wt％抗氧剂、0.01wt％氧化物、0.01wt％无机盐。
醇类为聚乙烯醇，醛类为正丁醛。
抗氧剂为为30%的2-亚甲基双(4-甲基-6-叔丁基苯酚)、20%的四(3,5-二叔丁基-4-羟基)苯丙酸季戊四醇酯和50%的双(3，5-二叔丁基苯基)季戊四醇二亚磷酸酯的混合物。
氧化物为纳米ATO。
无机盐为50%的甲酸钾和50%的乙酸钙的混合物。
夹层1的制备过程如下：
S1:用适量的醇类配成浓度小于10％的溶液A；
S2:将溶液A降温到50°C以下，加入醛类、抗氧剂、氧化物和无机盐，并搅拌2.5小时,得到溶液B；
S3:保温3-5小时，得到溶液C；
S4:将溶液C放于反应釜中并升温至40-50°C，并保温4小时，保温后冷却至室温，得到溶液D；
S5：将溶液D水洗后在升温至50°C，调节pH值至10，再保温2.5小时，得到溶液E；
S6：将溶液E脱水干燥制成半成品F；
S7：将半成品F投入到双螺杆挤出机中，按尺寸卷取，得到夹层1。
PVB中间膜制备工艺如下：
S1:在其中一个夹层1外壁粘接中间层2；
S2:再从中间层2一侧粘接另一个夹层1并静置2小时。
将本实施例的保温PVB中间膜用于制备夹层玻璃时，首先将保温PVB中间膜的两个夹层1分别与两层玻璃贴合，然后抽真空，并将周边进行封边，保证PVB中间膜主体与玻璃间的真空状态，夹层玻璃完成。
实施例四：
本发明提供一种技术方案：一种具有储热功能的光学膜材料，包括两个夹层1和一个中间层2，夹层1为PVB中间膜，中间层2为玻璃棉，夹层1的组分包括8.1wt％醇类、4.6wt％醛类、0.02wt％抗氧剂、0.01wt％氧化物、0.01wt％无机盐。
醇类为聚乙烯醇，醛类为正丁醛。
抗氧剂为为30%的2-亚甲基双(4-甲基-6-叔丁基苯酚)、20%的四(3,5-二叔丁基-4-羟基)苯丙酸季戊四醇酯和50%的双(3，5-二叔丁基苯基)季戊四醇二亚磷酸酯的混合物。
氧化物为纳米GTO。
无机盐为50%的甲酸钾和50%的乙酸钙的混合物。
夹层1的制备过程如下：
S1:用适量的醇类配成浓度小于10％的溶液A；
S2:将溶液A降温到50°C以下，加入醛类、抗氧剂、氧化物和无机盐，并搅拌2.5小时,得到溶液B；
S3:保温3小时，得到溶液C；
S4:将溶液C放于反应釜中并升温至45°C，并保温4小时，保温后冷却至室温，得到溶液D；
S5：将溶液D水洗后在升温至50°C，调节pH值至10，再保温2.5小时，得到溶液E；
S6：将溶液E脱水干燥制成半成品F；
S7：将半成品F投入到双螺杆挤出机中，按尺寸卷取，得到夹层1。
PVB中间膜制备工艺如下：
S1:在其中一个夹层1外壁粘接中间层2；
S2:再从中间层2一侧粘接另一个夹层1并静置2小时。
将本实施例的保温PVB中间膜用于制备夹层玻璃时，首先将保温PVB中间膜的两个夹层1分别与两层玻璃贴合，然后抽真空，并将周边进行封边，保证PVB中间膜主体与玻璃间的真空状态，夹层玻璃完成。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。

Claims (7)

1.一种具有储热功能的光学膜材料，包括两个夹层（1）和一个中间层（2），其特征在于：所述夹层（1）为PVB中间膜，所述中间层（2）为玻璃棉，所述夹层（1）的组分包括7.5-8.8wt％醇类、4.6-4.8wt％醛类、0.01-0.03wt％抗氧剂、0.01-0.02wt％氧化物和0.01wt％无机盐。
2.根据权利要求1所述的一种具有储热功能的光学膜材料，其特征在于：所述醇类为聚乙烯醇，所述醛类为正丁醛。
3.根据权利要求1所述的一种具有储热功能的光学膜材料，其特征在于：所述抗氧剂为2-亚甲基双(4-甲基-6-叔丁基苯酚)、四(3,5-二叔丁基-4-羟基)苯丙酸季戊四醇酯、三(2,4-二叔丁基)亚磷酸苯酯、双十八烷基醇季戊二亚磷酸酯、双(3，5-二叔丁基苯基)季戊四醇二亚磷酸酯中的一种或多种的混合物。
4.根据权利要求1所述的一种具有储热功能的光学膜材料，其特征在于：所述氧化物为纳米ATO、纳米GTO和纳米钨青铜中的一种或多种的混合物。
5.根据权利要求1所述的一种具有储热功能的光学膜材料，其特征在于：所述无机盐为乙酸钾、甲酸钾、乙酸镁、乙酸钙和乙酸钠中的一种或多种的混合物。
6.根据权利要求1所述的一种具有储热功能的光学膜材料，其特征在于：所述夹层（1）的制备过程如下：
S1:用适量的醇类配成浓度小于10％的溶液A；
S2:将溶液A降温到50°C以下，加入醛类、抗氧剂、氧化物和无机盐，并搅拌2.5小时,得到溶液B；
S3:保温3-5小时，得到溶液C；
S4:将溶液C放于反应釜中并升温至40-50°C，并保温3-5小时，保温后冷却至室温，得到溶液D；
S5：将溶液D水洗后在升温至50°C，调节pH值至9-10，再保温2-3小时，得到溶液E；
S6：将溶液E脱水干燥制成半成品F；
S7：将半成品F投入到双螺杆挤出机中，按尺寸卷取，得到夹层（1）。
7.根据权利要求1所述的一种具有储热功能的光学膜材料，其特征在于：所述PVB中间膜制备工艺如下：
S1:在其中一个夹层（1）外壁粘接中间层（2）；
S2:再从中间层（2）一侧粘接另一个夹层（1）并静置1-2小时。
CN202010205744.2A 2020-03-23 2020-03-23 一种具有储热功能的光学膜材料 Pending CN111347748A (zh)