CN111018527A - Preparation method of nano gadolinium oxide for dielectric ceramic capacitor - Google Patents

Preparation method of nano gadolinium oxide for dielectric ceramic capacitor Download PDF

Info

Publication number
CN111018527A
CN111018527A CN201911364451.2A CN201911364451A CN111018527A CN 111018527 A CN111018527 A CN 111018527A CN 201911364451 A CN201911364451 A CN 201911364451A CN 111018527 A CN111018527 A CN 111018527A
Authority
CN
China
Prior art keywords
solution
gadolinium
salt solution
concentration
dielectric ceramic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201911364451.2A
Other languages
Chinese (zh)
Inventor
戴连欣
秦庆新
刘卫华
黄雍
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangxi Xintai Functional Materials Technology Co Ltd
Original Assignee
Jiangxi Xintai Functional Materials Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangxi Xintai Functional Materials Technology Co Ltd filed Critical Jiangxi Xintai Functional Materials Technology Co Ltd
Priority to CN201911364451.2A priority Critical patent/CN111018527A/en
Publication of CN111018527A publication Critical patent/CN111018527A/en
Pending legal-status Critical Current

Abstract

The invention discloses a preparation method of nano gadolinium oxide for a dielectric ceramic capacitor, aiming at solving the problems of large particle size and poor dispersion performance of the existing rare earth oxide. The method comprises the following specific steps: preparing a gadolinium salt solution and an alkaline precipitator solution; stirring and heating the gadolinium salt solution to 30-100 ℃, slowly dripping alkaline precipitator solution into the gadolinium salt solution, and controlling the final pH value of the solution after precipitation to be 4.5-9.0; thirdly, aging the precipitate precursor; filtering and washing the aged precipitate precursor; and step five, drying, roasting, crushing and screening the washed precipitate precursor to obtain a finished product. The nano rare earth oxide finished product obtained by the invention can reach the nano size, is easy to disperse, and is particularly suitable for producing miniaturized or miniaturized dielectric ceramic capacitors.

Description

Preparation method of nano gadolinium oxide for dielectric ceramic capacitor
Technical Field
The invention relates to the field of dielectric ceramic capacitors, in particular to a preparation method of nano gadolinium oxide for a miniaturized or miniaturized dielectric ceramic capacitor.
Background
The ceramic material is an indispensable material in human life and modern construction, the excellent performance of the ceramic material is unique in the material field and is highly valued by people, and the dielectric ceramic as one of electronic ceramics plays a vital role in miniaturization and the production of portable electronic products.
The dielectric ceramic is also called dielectric ceramic, and is functional ceramic which has polarization capability under the action of an electric field and can establish the electric field in a body for a long time. And may be classified into electrical insulation, capacitors, piezoelectric, pyroelectric, and ferroelectric ceramics according to the use and properties. The insulating material has the characteristics of high insulating resistivity, small dielectric constant, small dielectric loss, good heat conducting property, small expansion coefficient, good thermal stability and chemical stability and the like. In order to meet the requirements of miniaturization and miniaturization of various electronic products, the volume of the dielectric ceramic multilayer capacitor is smaller and smaller, and the thickness of the dielectric layer is only about 1 micron. In order to prepare the dielectric layer material, the particle size of barium-titanium powder is controlled, and more strict requirements are provided for the particle size and the dispersion property of additives, such as rare earth oxide, uniformly covered on the surfaces of the barium-titanium powder particles. The particle size of the existing rare earth oxide is generally 3-5 microns, and the existing rare earth oxide is difficult to grind to be within 100 nanometers by physical means, which brings a bottleneck for the miniaturization and microminiaturization production of dielectric ceramics.
Disclosure of Invention
An object of an embodiment of the present invention is to provide a method for preparing nano gadolinium oxide for a dielectric ceramic capacitor, so as to solve the problems in the background art.
In order to achieve the above purpose, the embodiments of the present invention provide the following technical solutions:
a preparation method of nano gadolinium oxide for a dielectric ceramic capacitor comprises the following specific steps:
preparing a gadolinium salt solution and an alkaline precipitator solution, wherein the concentration of gadolinium oxide in the gadolinium salt solution is 30-400g-REO/L, the concentration of free acid in the gadolinium salt solution is 0.05-2.0mol/L, the concentration of hydroxyl in the alkaline precipitator solution is 0.1-10mol/L, and g-REO/L is the weight (g, g) of oxide (REO) in unit volume (liter, L);
step two, stirring and heating the gadolinium salt solution to 30-100 ℃, preferably 40-90 ℃, more preferably 45-80 ℃, slowly dripping alkaline precipitator solution into the gadolinium salt solution, and controlling the final pH value of the solution after precipitation to be 4.5-9.0;
step three, carrying out aging treatment on the precipitate precursor, wherein the temperature of the aging treatment is 45-150 ℃, preferably 50-120 ℃, more preferably 60-100 ℃, and the time of the aging treatment is 0.25-15h, preferably 0.5-10h, more preferably 1-7 h;
filtering and washing the aged precipitate precursor at the washing temperature of 40-80 ℃, wherein the conductivity of the filtered filtrate is less than 1 mu s/cm;
and step five, drying, roasting, crushing and screening the washed precipitate precursor to obtain a finished product. The invention can also adopt the method that gadolinium salt solution is slowly dropped into alkaline precipitator solution or gadolinium salt solution and alkaline precipitator solution are simultaneously added into primer solution to generate precipitate precursor, wherein the primer solution can be pure water or aqueous solution containing gadolinium salt solution.
As a further scheme of the embodiment of the invention: the gadolinium salt solution in the first step comprises at least one of gadolinium chloride solution, gadolinium sulfate solution and gadolinium nitrate solution.
As a further scheme of the embodiment of the invention: the alkaline precipitant solution in the first step comprises one or more of sodium hydroxide solution, potassium hydroxide solution, ammonia water solution, sodium carbonate solution, sodium bicarbonate solution, ammonium carbonate solution and ammonium bicarbonate solution.
As a further scheme of the embodiment of the invention: in the second step, the time for dripping the alkaline precipitator solution into the gadolinium salt solution is 0.25-8 h.
As a further scheme of the embodiment of the invention: in the fifth step, the roasting temperature is 500-950 ℃, preferably 550-850 ℃, and the roasting time is 2-20h, preferably 5-15 h.
As a further scheme of the embodiment of the invention: the concentration of gadolinium oxide in the gadolinium salt solution is 40-300 g-REO/L.
As a further scheme of the embodiment of the invention: the concentration of the gadolinium oxide in the gadolinium salt solution is 50-200 g-REO/L.
As a further scheme of the embodiment of the invention: the concentration of hydroxide radical in the alkaline precipitant solution is 0.3-5 mol/L.
As a further scheme of the embodiment of the invention: the concentration of hydroxide radical in the alkaline precipitant solution is 0.5-3 mol/L.
Compared with the prior art, the embodiment of the invention has the beneficial effects that:
the invention has reasonable design, the obtained finished product can reach the nanometer size, is easy to disperse, is particularly suitable for the production of dielectric ceramic capacitors, and has wide application prospect.
Drawings
FIG. 1 is a flow chart of a method for preparing nano gadolinium oxide for dielectric ceramic capacitors.
FIG. 2 is a scanning electron microscope image of a finished product in a preparation method of nano gadolinium oxide for a dielectric ceramic capacitor.
Detailed Description
The technical solution of the present patent will be described in further detail with reference to the following embodiments.
Example 1
In a 2L three-necked flask, 0.5L of gadolinium chloride (GdCl) was added3) Solution of gadolinium oxide (Gd)2O3) The conversion concentration is 50g/L, the concentration of free acid is 0.1mol/L, and the mixture is stirred and heated to 50 ℃;
precipitant sodium carbonate (Na) at room temperature2CO3) Slowly dripping the solution into the gadolinium chloride solution with the concentration of 0.5mol/L for 1h, and controlling the final pH value of the solution after precipitation to be between 6.0 and 6.5;
aging treatment is carried out after precipitation, the aging temperature is 50 ℃, and the aging time is 1 h;
filtering the aged slurry, and washing with warm water at 50-60 deg.C until the conductivity of the filtrate is less than 1 μ s/cm;
drying the washed filter cake at 110 ℃ overnight, and then roasting at 700 ℃ for 5 h;
and crushing and screening the roasted oxide product to obtain the gadolinium oxide powder.
Example 2
The procedure is as described in example 1, except that gadolinium oxide (Gd)2O3) Gadolinium sulfate (Gd) at a reduced concentration of 50g/L2(SO4)3) The solution is used as a starting material for carrying out precipitation reaction.
Example 3
The procedure is as described in example 1, except that gadolinium oxide (Gd)2O3) Gadolinium nitrate (Gd (NO) at a reduced concentration of 50g/L3)3) The solution is used as a starting material for carrying out precipitation reaction.
Example 4
The procedure is as described in example 1, except that gadolinium oxide (Gd)2O3) Gadolinium chloride (GdCl) at a reduced concentration of 100g/L3) The solution is used as a starting material for carrying out precipitation reaction.
Example 5
The preparation was carried out as described in example 1, except that the precipitation reaction and aging treatment were carried out at 70 ℃.
Example 6
The preparation was carried out as described in example 1, except that ammonium carbonate ((NH) was used in a concentration of 1.0mol/L4)2CO3) The solution is used as a precipitant to carry out precipitation reaction.
Example 7
The procedure was as described in example 1, except that ammonium hydrogencarbonate (NH) was used in a concentration of 1.0mol/L4HCO3) The solution is used as a precipitant to carry out precipitation reaction.
Example 8
The procedure was carried out as described in example 1, except that a mixed solution of an ammonium carbonate solution having a concentration of 1.0mol/L and a sodium hydroxide (NaOH) solution having a concentration of 0.5mol/L was used as a precipitant to carry out the precipitation reaction.
Example 9
The preparation as described in example 1 was followedThe process was carried out with the exception that an ammonium carbonate solution having a concentration of 1.0mol/L and an aqueous ammonia solution (NH) having a concentration of 0.5mol/L were used4OH) as a precipitant to perform precipitation reaction.
Example 10
The procedure was carried out as described in example 1, except that the precipitation reaction was carried out using a mixed solution of an ammonium hydrogencarbonate solution at a concentration of 1.0mol/L and an aqueous ammonia solution at a concentration of 0.5mol/L as a precipitant.
The finished products of examples 1-10 were tested for performance and the results are shown in Table 1.
TABLE 1
Figure BDA0002338040490000041
Figure BDA0002338040490000051
As can be seen from Table 1, the finished products of examples 1-10 have small particle sizes and good dispersibility.
The above description is only for the purpose of illustrating the preferred embodiments of the present invention and is not to be construed as limiting the invention, and any modifications, equivalents, improvements and the like that fall within the spirit and principle of the present invention are intended to be included therein. Any reference sign in a claim should not be construed as limiting the claim concerned.
Furthermore, it should be understood that although the present description refers to embodiments, not every embodiment may contain only a single embodiment, and such description is for clarity only, and those skilled in the art should integrate the description, and the embodiments may be combined as appropriate to form other embodiments understood by those skilled in the art.

Claims (7)

1. A preparation method of nano gadolinium oxide for a dielectric ceramic capacitor is characterized by comprising the following specific steps:
preparing a gadolinium salt solution and an alkaline precipitator solution, wherein the concentration of gadolinium oxide in the gadolinium salt solution is 30-400g-REO/L, the concentration of free acid in the gadolinium salt solution is 0.05-2.0mol/L, and the concentration of hydroxyl in the alkaline precipitator solution is 0.1-10 mol/L;
stirring and heating the gadolinium salt solution to 30-100 ℃, slowly dripping alkaline precipitator solution into the gadolinium salt solution, and controlling the final pH value of the solution after precipitation to be 4.5-9.0;
thirdly, aging the precipitate precursor at 45-150 ℃ for 0.25-15 h;
filtering and washing the aged precipitate precursor, wherein the conductivity of the filtered filtrate is less than 1 mu s/cm, and the washing temperature is 40-80 ℃;
and step five, drying, roasting, crushing and screening the washed precipitate precursor to obtain a finished product.
2. The method as claimed in claim 1, wherein the gadolinium salt solution in the first step includes at least one of gadolinium chloride solution, gadolinium sulfate solution and gadolinium nitrate solution.
3. The method for preparing nano-sized gadolinium oxide for dielectric ceramic capacitor as claimed in claim 1 or 2, wherein the alkaline precipitant solution in the first step includes one or more of sodium hydroxide solution, potassium hydroxide solution, ammonia water solution, sodium carbonate solution, sodium bicarbonate solution, ammonium carbonate solution and ammonium bicarbonate solution.
4. The method for preparing nano gadolinium oxide for dielectric ceramic capacitor as claimed in claim 1, wherein the time for dropping alkaline precipitant solution into gadolinium salt solution in said second step is 0.25-8 h.
5. The method as claimed in claim 1 or 4, wherein the temperature of the step five is 500-950 ℃ and the time of the step five is 2-20 h.
6. The method of claim 1, wherein the gadolinium oxide salt solution has a gadolinium oxide concentration of 40 to 300 g-REO/L.
7. The method of claim 1, wherein the concentration of hydroxyl group in the alkaline precipitant solution is 0.3 to 5 mol/L.
CN201911364451.2A 2019-12-26 2019-12-26 Preparation method of nano gadolinium oxide for dielectric ceramic capacitor Pending CN111018527A (en)