CN111003942A - 冰霜结晶釉及其制备方法 - Google Patents
冰霜结晶釉及其制备方法 Download PDFInfo
- Publication number
- CN111003942A CN111003942A CN202010016129.7A CN202010016129A CN111003942A CN 111003942 A CN111003942 A CN 111003942A CN 202010016129 A CN202010016129 A CN 202010016129A CN 111003942 A CN111003942 A CN 111003942A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- crystal
- blank
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种冰霜结晶釉及其制备方法,它所使用的釉料含有的组分及各组分质量份如下:石英:20份;方解石:7份;氧化锌:15份;锂辉石:10份;二氧化钛:10份;界牌泥:10份;骨炭:18份;高硼熔块:10份;氧化钴:2份;氧化铜:2份。本发明的结晶呈现一种从中心结晶核开始结晶向外形成条纹状散射辐射的效果,较强地增加了现有釉料的装饰效果。
Description
技术领域
本发明涉及一种冰霜结晶釉及其制备方法。
背景技术
目前,现有技术的结晶釉均是以中心向外放射的圆环状结晶为主,装饰效果单一。
发明内容
本发明所要解决的技术问题是克服现有技术的缺陷,提供一种冰霜结晶釉,它的结晶呈现一种从中心结晶核开始结晶向外形成条纹状散射辐射的效果,较强地增加了现有釉料的装饰效果。
解决本发明的技术问题的技术方案是:一种冰霜结晶釉,它所使用的釉料含有的组分及各组分质量份如下:
石英:20份;方解石:7份;氧化锌:15份;锂辉石:10份;二氧化钛:10份;界牌泥:10份;骨炭:18份;高硼熔块:10份;氧化钴:2份;氧化铜:2份。
本发明还提供了一种冰霜结晶釉的制备方法,其特征在于方法的步骤中含有:
按照各组分及各组分质量份备料;
备料后进行球磨;
球磨后的球磨料过筛;
过筛料调成釉浆;
取干净的坯件,采用釉浆在坯件上施釉;
施釉的坯件在1230℃的窑炉中烧成,烧制过程中,保温时间要求在45分钟以上。
采用了上述技术方案后,本发明采用硅锌结晶的基本饱和熔剂机理,在中间加入锂辉石形成低粘度溶液,从而更加有利于结晶体的生长析出,而同时加入了二氧化钛和氧化锌形成的结晶核能够保障不需要额外手工加入结晶核来保持结晶的稳定性,采用单层釉料在有层内自主的形成结晶核并长大的方式,减少了人工装饰的工序操作,更加利于大规模生产。
具体实施方式
本发明提供了一种冰霜结晶釉及其制备方法,本领域技术人员可以借鉴本文内容,适当改进工艺参数实现。特别需要指出的是,所有类似的替换和改动对本领域技术人员来说是显而易见的,它们都属于本发明保护的范围。本发明的方法及应用已经通过较佳实施例进行了描述,相关人员明显能在不脱离本发明内容、精神和范围内对本文的方法和应用进行改动或适当变更与组合,来实现和应用本发明技术。
一种冰霜结晶釉,它所使用的釉料含有的组分及各组分质量份如下:
石英:20份;方解石:7份;氧化锌:15份;锂辉石:10份;二氧化钛:10份;界牌泥:10份;骨炭:18份;高硼熔块:10份;氧化钴:2份;氧化铜:2份。
在本实施例中,石英为安徽石英;方解石为广西方解石;氧化锌为上海氧化锌;锂辉石为澳洲锂辉石;二氧化钛为株洲二氧化钛;界牌泥为衡阳界牌泥;骨炭为内蒙骨炭。
高硼熔块为市售,生产厂家为醴陵市科信陶瓷材料有限公司生产的高硼熔块。
冰霜结晶釉的制备方法,方法的步骤中含有:
按照各组分及各组分质量份备料;
备料后进行球磨;
球磨后的球磨料过筛;
过筛料调成釉浆;
取干净的坯件,采用釉浆在坯件上施釉;
施釉的坯件在1230℃的窑炉中烧成,烧制过程中,保温时间要求在45分钟以上。
以上实施例制备得到的冰霜结晶釉,经过观察发现,其釉面的结晶呈现从中心结晶核开始结晶向外形成条纹状散射辐射的效果,符合设计要求。
以上所述的具体实施例,对本发明的目的、技术方案和有益效果进行了进一步详细说明,所应理解的是,以上所述仅为本发明的具体实施例而已,并不用于限制本发明,凡在本发明的精神和原则之内,所做的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (2)
1.一种冰霜结晶釉,其特征在于它所使用的釉料含有的组分及各组分质量份如下:
石英:20份;方解石:7份;氧化锌:15份;锂辉石:10份;二氧化钛:10份;界牌泥:10份;骨炭:18份;高硼熔块:10份;氧化钴:2份;氧化铜:2份。
2.一种如权利要求1所述的冰霜结晶釉的制备方法,其特征在于方法的步骤中含有:
按照各组分及各组分质量份备料;
备料后进行球磨;
球磨后的球磨料过筛;
过筛料调成釉浆;
取干净的坯件,采用釉浆在坯件上施釉;
施釉的坯件在1230℃的窑炉中烧成,烧制过程中,保温时间要求在45分钟以上。