CN111003942A - Frost crystal glaze and preparation method thereof - Google Patents
Frost crystal glaze and preparation method thereof Download PDFInfo
- Publication number
- CN111003942A CN111003942A CN202010016129.7A CN202010016129A CN111003942A CN 111003942 A CN111003942 A CN 111003942A CN 202010016129 A CN202010016129 A CN 202010016129A CN 111003942 A CN111003942 A CN 111003942A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- crystal
- blank
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a frost crystal glaze and a preparation method thereof, wherein the glaze used by the invention comprises the following components in parts by mass: quartz: 20 parts of (1); calcite: 7 parts; zinc oxide: 15 parts of (1); spodumene: 10 parts of (A); titanium dioxide: 10 parts of (A); boundary plate mud: 10 parts of (A); bone charcoal: 18 parts of a mixture; high boron frit: 10 parts of (A); cobalt oxide: 2 parts of (1); copper oxide: and 2 parts. The crystal of the invention has the effect of forming stripe-shaped scattered radiation from the center crystal nucleus to the outside, and the decorative effect of the existing glaze is enhanced greatly.
Description
Technical Field
The invention relates to a frost crystal glaze and a preparation method thereof.
Background
At present, the crystalline glaze in the prior art mainly comprises annular crystals radiating outwards from the center, and has a single decorative effect.
Disclosure of Invention
The technical problem to be solved by the invention is to overcome the defects of the prior art and provide a frost crystal glaze, the crystal of which has the effect of forming stripe-shaped scattered radiation from a central crystal nucleus to the outside and greatly improves the decorative effect of the prior glaze.
The technical scheme for solving the technical problem of the invention is as follows: a glaze used for the crystal glaze of frost comprises the following components in parts by mass:
quartz: 20 parts of (1); calcite: 7 parts; zinc oxide: 15 parts of (1); spodumene: 10 parts of (A); titanium dioxide: 10 parts of (A); boundary plate mud: 10 parts of (A); bone charcoal: 18 parts of a mixture; high boron frit: 10 parts of (A); cobalt oxide: 2 parts of (1); copper oxide: and 2 parts.
The invention also provides a preparation method of the frost crystal glaze, which is characterized by comprising the following steps:
preparing the components according to the mass parts of the components;
ball milling is carried out after material preparation;
sieving the ball-milled material;
sieving the materials to prepare glaze slurry;
taking a clean blank, and glazing the blank by adopting glaze slip;
the glazed blank is fired in a kiln at 1230 ℃, and the heat preservation time is required to be more than 45 minutes in the firing process.
After the technical scheme is adopted, the invention adopts a basic saturated flux mechanism of silicon zinc crystallization, and spodumene is added in the middle to form a low-viscosity solution, so that the growth and precipitation of crystals are more facilitated, meanwhile, the addition of the crystallization nucleus formed by titanium dioxide and zinc oxide can ensure that the stability of crystallization is kept without additional manual addition of the crystallization nucleus, and the mode that the crystallization nucleus is independently formed and grows in a single-layer glaze layer is adopted, so that the process operation of manual decoration is reduced, and the large-scale production is more facilitated.
Detailed Description
The invention provides a frost crystal glaze and a preparation method thereof, and a person skilled in the art can realize the frost crystal glaze by properly improving process parameters by referring to the content. It is expressly intended that all such similar substitutes and modifications apparent to those skilled in the art are deemed to be within the scope of the invention. While the methods and applications of this invention have been described in terms of preferred embodiments, it will be apparent to those of ordinary skill in the art that variations and modifications in the methods and applications described herein, as well as other suitable variations and combinations, may be made to implement and use the techniques of this invention without departing from the spirit and scope of the invention.
A glaze used for the crystal glaze of frost comprises the following components in parts by mass:
quartz: 20 parts of (1); calcite: 7 parts; zinc oxide: 15 parts of (1); spodumene: 10 parts of (A); titanium dioxide: 10 parts of (A); boundary plate mud: 10 parts of (A); bone charcoal: 18 parts of a mixture; high boron frit: 10 parts of (A); cobalt oxide: 2 parts of (1); copper oxide: and 2 parts.
In the present embodiment, the quartz is Anhui quartz; the calcite is Guangxi calcite; the zinc oxide is Shanghai zinc oxide; spodumene is spodumene australia; the titanium dioxide is the titanium dioxide of the strain; the boundary mud is hengyang boundary mud; the bone charcoal is inner Mongolia bone charcoal.
The high-boron frit is commercially available, and the manufacturer is the high-boron frit produced by Kexin ceramic materials of Glene.
The preparation method of the frost crystal glaze comprises the following steps:
preparing the components according to the mass parts of the components;
ball milling is carried out after material preparation;
sieving the ball-milled material;
sieving the materials to prepare glaze slurry;
taking a clean blank, and glazing the blank by adopting glaze slip;
the glazed blank is fired in a kiln at 1230 ℃, and the heat preservation time is required to be more than 45 minutes in the firing process.
The frosted crystal glaze prepared by the above embodiment is observed, and the crystal of the glaze surface has the effect of forming stripe-shaped scattered radiation from the center crystal nucleus to the outside, and meets the design requirement.
The above-mentioned embodiments are intended to illustrate the objects, technical solutions and advantages of the present invention in further detail, and it should be understood that the above-mentioned embodiments are only exemplary embodiments of the present invention, and are not intended to limit the present invention, and any modifications, equivalents, improvements and the like made within the spirit and principle of the present invention should be included in the protection scope of the present invention.
Claims (2)
1. The frosted crystal glaze is characterized in that the glaze used by the frosted crystal glaze comprises the following components in parts by mass:
quartz: 20 parts of (1); calcite: 7 parts; zinc oxide: 15 parts of (1); spodumene: 10 parts of (A); titanium dioxide: 10 parts of (A); boundary plate mud: 10 parts of (A); bone charcoal: 18 parts of a mixture; high boron frit: 10 parts of (A); cobalt oxide: 2 parts of (1); copper oxide: and 2 parts.
2. A method for preparing a frosted crystalline glaze according to claim 1, characterized in that the method comprises the steps of:
preparing the components according to the mass parts of the components;
ball milling is carried out after material preparation;
sieving the ball-milled material;
sieving the materials to prepare glaze slurry;
taking a clean blank, and glazing the blank by adopting glaze slip;
the glazed blank is fired in a kiln at 1230 ℃, and the heat preservation time is required to be more than 45 minutes in the firing process.