CN110627080A - 一种用于消解甲醛的分子筛及其制备方法 - Google Patents
一种用于消解甲醛的分子筛及其制备方法 Download PDFInfo
- Publication number
- CN110627080A CN110627080A CN201911008130.9A CN201911008130A CN110627080A CN 110627080 A CN110627080 A CN 110627080A CN 201911008130 A CN201911008130 A CN 201911008130A CN 110627080 A CN110627080 A CN 110627080A
- Authority
- CN
- China
- Prior art keywords
- parts
- carrier
- digesting
- molecular sieve
- deionized water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及甲醛消解技术领域，具体是公开了一种用于消解甲醛的分子筛，包括载体和附着剂；所述载体包括以下重量份的原料：铝土50‑70份、粉煤灰10‑25份、草木灰8‑20份、高岭土3‑9份、羰甲基纤维素2‑6份、硅溶胶1.2‑2.6份和去离子水20‑35份；所述附着剂包括以下重量份的原料：氢氧化钠12‑18份、高锰酸钾3‑15份、乙酸锰6‑30份、硫酸锌5‑10份、氨基酸3‑7份、苯酚0.2‑0.6份、蜂胶4‑8份和去离子水1‑5份。本发明克服了现有技术的不足，降低分子筛的生产成本，提高分子筛消解甲醛的稳定性。
Description
技术领域
本发明涉及甲醛消解技术技术领域，具体属于一种用于消解甲醛的分子筛。
背景技术
甲醛是一种透明无色，有刺激性气体，装修后室内的涂料、家具等都含有甲醛。人长时间的吸入甲醛气体的话，会出现恶心、呕吐、咳嗽、胸闷、哮喘或者是肺气肿，也会引起慢性呼吸道疾病、女性***、妊娠综合症、引起新生儿体质降低或染色体异常，引起少年儿童智力下降，被世界卫生组织确认为一类致癌和致畸性物质，是公认的***反应源，也是潜在的强致突变物之一。其在室内空气中的危害尤为突出，因此，国家安全标准规定室内空气甲醛含量≤0.1mg/m。
目前常用的消解甲醛的手段是在已有无机氧化物载体负载贵金属催化剂，而这种方式成本高昂，贵金属催化剂存在抗湿性差且稳定性差等问题，消解甲醛的效果不稳定，难以满足市场需求。
发明内容
本发明的目的是提供了一种用于消解甲醛的分子筛，克服了现有技术的不足，降低分子筛的生产成本，提高分子筛消解甲醛的稳定性。
为解决上述问题，本发明所采取的技术方案如下：
一种用于消解甲醛的分子筛，包括载体和附着剂；所述载体包括以下重量份的原料：铝土50-70份、粉煤灰10-25份、草木灰8-20份、高岭土3-9份、羰甲基纤维素2-6份、硅溶胶1.2-2.6份和去离子水20-35份；所述附着剂包括以下重量份的原料：氢氧化钠12-18份、高锰酸钾3-15份、乙酸锰6-30份、硫酸锌5-10份、氨基酸3-7份、苯酚0.2-0.6份、蜂胶4-8份和去离子水1-5份。
进一步，所述载体包括以下重量份的原料：铝土55-65份、粉煤灰15-20份、草木灰10-18份、高岭土4-8份、羰甲基纤维素3-5份、硅溶胶1.4-2.4份和去离子水25-30份；所述附着剂包括以下重量份的原料：氢氧化钠13-17份、高锰酸钾4-14份、乙酸锰8-28份、硫酸锌6-9份、氨基酸4-6份、苯酚0.3-0.5份、蜂胶5-7份和去离子水2-4份。
进一步，所述载体包括以下重量份的原料：铝土60份、粉煤灰17.5份、草木灰14份、高岭土6份、羰甲基纤维素4份、硅溶胶1.9份和去离子水27.5份；所述附着剂包括以下重量份的原料：氢氧化钠15份、高锰酸钾9份、乙酸锰18份、硫酸锌7.5份、氨基酸5份、苯酚0.4份、蜂胶6份和去离子水3份。
进一步，所述铝土为天然铝土经过去杂、球磨、焙烧处理得到。
进一步，所述高锰酸钾与乙酸锰的重量份数比为1:2。
一种生产如上述的用于消解甲醛的分子筛的方法，其特征在于：包括以下步骤：
步骤一，按照上述载体的配方称取原料，将铝土、粉煤灰、草木灰和高岭土放置到反应釜中进行搅拌，搅拌过程中依次加入羰甲基纤维素、硅溶胶和去离子水，混合后得到膏状物；
步骤二，将步骤一中得到的膏状物装入水热反应釜中晶化，晶化反应结束后冷却，分离固体结晶产物与上清液，并将固体结晶产物用去离子水洗涤至中性，干燥，在空气中焙烧，得到载体；
步骤三，按照上述附着剂的配方称取原料，将氢氧化钠在磁力搅拌下溶解在去离子水中，然后在加入高锰酸钾和乙酸锰，继续搅拌至完全反应后再依次加入硫酸锌、氨基酸、苯酚和蜂胶，得到凝胶；
步骤四，将步骤三中得到的凝胶放置到反应釜中，搅拌升温，然后将载体加入到反应釜中，充分搅拌混合；
步骤五，将反应釜中的载体取出，用去离子水洗涤至中性，干燥，在空气中焙烧，得到用于消解甲醛的分子筛。
进一步，所述步骤四中反应釜升温至80-100℃，搅拌时间为1-3小时。
进一步，所述步骤五中干燥温度为120℃，干燥时间为6小时；焙烧温度为550℃，焙烧时间为4小时。
本发明与现有技术相比较，本发明的实施效果如下：
1、本发明采用天然铝土、粉煤灰和草木灰作为载体的主要原料，降低了载体的生产成本，使粉煤灰、草木灰得到的二次利用，绿色环保。
2、本发明在载体表面包裹消解甲醛的附着剂，提高消解甲醛的能力，更加稳定、快速的消解甲醛，满足使用者的需求。
具体实施方式
下面结合实施例对本发明作进一步的描述，但本发明不仅限于这些实例，在为脱离本发明宗旨的前提下，所为任何改进均落在本发明的保护范围之内。
实施例1
本实施例的用于消解甲醛的分子筛的生产方法，包括以下步骤：
步骤一，按照上述载体的配方称取原料，将铝土50份、粉煤灰10份、草木灰8份和高岭土3份放置到反应釜中进行搅拌，搅拌过程中依次加入羰甲基纤维素2份、硅溶胶1.2份和去离子水20份，混合后得到膏状物；
步骤二，将步骤一中得到的膏状物装入水热反应釜中晶化，晶化反应结束后冷却，分离固体结晶产物与上清液，并将固体结晶产物用去离子水洗涤至中性，干燥，在空气中焙烧，得到载体；
步骤三，按照上述附着剂的配方称取原料，将氢氧化钠12份在磁力搅拌下溶解在去离子水1份中，然后在加入高锰酸钾3份和乙酸锰6份，继续搅拌至完全反应后再依次加入硫酸锌5份、氨基酸3份、苯酚0.2份和蜂胶4份，得到凝胶；
步骤四，将步骤三中得到的凝胶放置到反应釜中，搅拌升温至80-100℃，然后将载体加入到反应釜中，充分搅拌混合1-3小时；
步骤五，将反应釜中的载体取出，用去离子水洗涤至中性，干燥，干燥温度为120℃，干燥时间为6小时；在空气中焙烧，焙烧温度为550℃，焙烧时间为4小时；得到用于消解甲醛的分子筛。
实施例2
本实施例的用于消解甲醛的分子筛的生产方法，包括以下步骤：
步骤一，按照上述载体的配方称取原料，将铝土60份、粉煤灰17.5份、草木灰14份和高岭土6份放置到反应釜中进行搅拌，搅拌过程中依次加入羰甲基纤维素4份、硅溶胶1.9份和去离子水27.5份，混合后得到膏状物；
步骤二，将步骤一中得到的膏状物装入水热反应釜中晶化，晶化反应结束后冷却，分离固体结晶产物与上清液，并将固体结晶产物用去离子水洗涤至中性，干燥，在空气中焙烧，得到载体；
步骤三，按照上述附着剂的配方称取原料，将氢氧化钠15份在磁力搅拌下溶解在去离子水3份中，然后在加入高锰酸钾9份和乙酸锰18份，继续搅拌至完全反应后再依次加入硫酸锌7.5份、氨基酸5份、苯酚0.4份和蜂胶6份，得到凝胶；
步骤四，将步骤三中得到的凝胶放置到反应釜中，搅拌升温至80-100℃，然后将载体加入到反应釜中，充分搅拌混合1-3小时；
步骤五，将反应釜中的载体取出，用去离子水洗涤至中性，干燥，干燥温度为120℃，干燥时间为6小时；在空气中焙烧，焙烧温度为550℃，焙烧时间为4小时；得到用于消解甲醛的分子筛。
实施例3
本实施例的用于消解甲醛的分子筛的生产方法，包括以下步骤：
步骤一，按照上述载体的配方称取原料，将铝土70份、粉煤灰25份、草木灰20份和高岭土9份放置到反应釜中进行搅拌，搅拌过程中依次加入羰甲基纤维素6份、硅溶胶2.6份和去离子水35份，混合后得到膏状物；
步骤二，将步骤一中得到的膏状物装入水热反应釜中晶化，晶化反应结束后冷却，分离固体结晶产物与上清液，并将固体结晶产物用去离子水洗涤至中性，干燥，在空气中焙烧，得到载体；
步骤三，按照上述附着剂的配方称取原料，将氢氧化钠18份在磁力搅拌下溶解在去离子水5份中，然后在加入高锰酸钾15份和乙酸锰30份，继续搅拌至完全反应后再依次加入硫酸锌10份、氨基酸7份、苯酚0.6份和蜂胶8份，得到凝胶；
步骤四，将步骤三中得到的凝胶放置到反应釜中，搅拌升温至80-100℃，然后将载体加入到反应釜中，充分搅拌混合1-3小时；
步骤五，将反应釜中的载体取出，用去离子水洗涤至中性，干燥，干燥温度为120℃，干燥时间为6小时；在空气中焙烧，焙烧温度为550℃，焙烧时间为4小时；得到用于消解甲醛的分子筛。
对比例1
与实施例3的材料及制备工艺基本相同，唯有不同的是没有使用附着剂。
对比例2
与实施例3的材料及制备工艺基本相同，唯有不同的是附着剂改为贵金属盐溶液。
对比例3
市售的上海某公司生产的甲醛消解分子筛。
使用上述实施例1-3和对比例1-3生产的产品进行甲醛消解试验，表1为室温条件下产品的甲醛降解率。
分析表1的结果可知，本发明提高了分子筛消解甲醛的分解率，同时还降低了生产成本，更加绿色环保。
以上内容仅仅是对本发明构思所作的举例和说明，所属本技术领域的技术人员对所描述的具体实施例做各种各样的修改或补充或采用类似的方式替代，只要不偏离发明的构思或者超越本权利要求书所定义的范围，均应属于本发明的保护范围。
Claims (8)
1.一种用于消解甲醛的分子筛，其特征在于：包括载体和附着剂；所述载体包括以下重量份的原料：铝土50-70份、粉煤灰10-25份、草木灰8-20份、高岭土3-9份、羰甲基纤维素2-6份、硅溶胶1.2-2.6份和去离子水20-35份；所述附着剂包括以下重量份的原料：氢氧化钠12-18份、高锰酸钾3-15份、乙酸锰6-30份、硫酸锌5-10份、氨基酸3-7份、苯酚0.2-0.6份、蜂胶4-8份和去离子水1-5份。
2.根据权利要求1所述的一种用于消解甲醛的分子筛，其特征在于：所述载体包括以下重量份的原料：铝土55-65份、粉煤灰15-20份、草木灰10-18份、高岭土4-8份、羰甲基纤维素3-5份、硅溶胶1.4-2.4份和去离子水25-30份；所述附着剂包括以下重量份的原料：氢氧化钠13-17份、高锰酸钾4-14份、乙酸锰8-28份、硫酸锌6-9份、氨基酸4-6份、苯酚0.3-0.5份、蜂胶5-7份和去离子水2-4份。
3.根据权利要求1所述的一种用于消解甲醛的分子筛，其特征在于：所述载体包括以下重量份的原料：铝土60份、粉煤灰17.5份、草木灰14份、高岭土6份、羰甲基纤维素4份、硅溶胶1.9份和去离子水27.5份；所述附着剂包括以下重量份的原料：氢氧化钠15份、高锰酸钾9份、乙酸锰18份、硫酸锌7.5份、氨基酸5份、苯酚0.4份、蜂胶6份和去离子水3份。
4.根据权利要求1所述的一种用于消解甲醛的分子筛，其特征在于：所述铝土为天然铝土经过去杂、球磨、焙烧处理得到。
5.根据权利要求1所述的一种用于消解甲醛的分子筛，其特征在于：所述高锰酸钾与乙酸锰的重量份数比为1:2。
6.一种生产如权利要求1-5任一项所述的用于消解甲醛的分子筛的方法，其特征在于：包括以下步骤：
步骤一，按照上述载体的配方称取原料，将铝土、粉煤灰、草木灰和高岭土放置到反应釜中进行搅拌，搅拌过程中依次加入羰甲基纤维素、硅溶胶和去离子水，混合后得到膏状物；
步骤二，将步骤一中得到的膏状物装入水热反应釜中晶化，晶化反应结束后冷却，分离固体结晶产物与上清液，并将固体结晶产物用去离子水洗涤至中性，干燥，在空气中焙烧，得到载体；
步骤三，按照上述附着剂的配方称取原料，将氢氧化钠在磁力搅拌下溶解在去离子水中，然后在加入高锰酸钾和乙酸锰，继续搅拌至完全反应后再依次加入硫酸锌、氨基酸、苯酚和蜂胶，得到凝胶；
步骤四，将步骤三中得到的凝胶放置到反应釜中，搅拌升温，然后将载体加入到反应釜中，充分搅拌混合；
步骤五，将反应釜中的载体取出，用去离子水洗涤至中性，干燥，在空气中焙烧，得到用于消解甲醛的分子筛。
7.根据权利要求6所述的一种用于消解甲醛的分子筛，其特征在于：所述步骤四中反应釜升温至80-100℃，搅拌时间为1-3小时。
8.根据权利要求6所述的一种用于消解甲醛的分子筛，其特征在于：所述步骤五中干燥温度为120℃，干燥时间为6小时；焙烧温度为550℃，焙烧时间为4小时。