CN110539003B - 一种去除钯镜的钯粉生产方法 - Google Patents
一种去除钯镜的钯粉生产方法 Download PDFInfo
- Publication number
- CN110539003B CN110539003B CN201910742011.XA CN201910742011A CN110539003B CN 110539003 B CN110539003 B CN 110539003B CN 201910742011 A CN201910742011 A CN 201910742011A CN 110539003 B CN110539003 B CN 110539003B
- Authority
- CN
- China
- Prior art keywords
- palladium
- solution
- palladium powder
- reduced
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本申请公开了一种去除钯镜的钯粉生产方法,步骤如下:(1)将钯络合物加入去离子水中进行加热,混匀,得到待还原液;(2)在步骤(1)所得待还原液中加入盐,搅拌均匀;(3)在步骤(2)所得溶液中加入还原剂,搅拌直至溶液颜色变为无色;(4)对步骤(3)所得反应液进行抽滤,得到钯粉初品,采用超纯水洗涤后烘干,得到钯粉产品。其优点表现在:通过在待还原液引入盐,一方面盐可以起到与反应器皿的磨砂作用,将生成的钯镜快速剥离;另一方面盐可以对还原体系起到稳定作用,弱化钯镜现象。本申请实现了去除钯粉生产过程中的钯镜现象,大大提高了钯粉生产效率、产品合格率,同时也降低了钯粉生产过程的生产损耗。
Description
技术领域
本申请涉及金属材料技术领域,尤其是涉及一种去除钯镜的钯粉生产方法。
背景技术
铂族金属由于优良的物理化学性能,目前已经成为科技发展不可或缺的宝贵材料,由于其价格昂贵,一般用于关键的核心部位,被誉为“工业维他命”。
钯作为其中一种重要的贵金属,其具有无可替代的物理化学性质,比如超高的导电性、强吸氢性和优良的催化性能,故被大量应用在各种工业领域。目前大部分的钯原料都是从钯粉转化而来,然而钯粉生产过程中往往会有钯镜现象存在,并且随着生产过程的进行,钯镜会快速长大并形成钯片粘附在反应器皿表面,后期清理困难,大量钯片的存在也显著降低了生产效率。
因此,去除钯粉生产过程中的钯镜现象,可大大提高钯粉生产效率、产品合格率,同时降低钯粉生产过程的生产损耗。
发明内容
本申请实施例提供一种去除钯镜的钯粉生产方法,以克服钯粉生产过程中的钯镜、钯片现象。
本申请实施例采用下述技术方案:一种去除钯镜的钯粉生产方法,步骤如下:
(1)将钯络合物加入去离子水中进行加热,混匀,得到待还原液;
(2)在步骤(1)所得待还原液中加入盐,搅拌均匀;
(3)在步骤(2)所得溶液中加入还原剂,搅拌直至溶液颜色变为无色;
(4)对步骤(3)所得反应液进行抽滤,得到钯粉初品,采用超纯水洗涤后烘干,得到钯粉产品。
进一步地,步骤(1)中,钯络合物为二氯二氨钯或二氯四氨钯。
进一步地,步骤(1)中,钯络合物与去离子水质量比为1:1-10。
进一步地,步骤(1)中,待还原液的加热温度为30-100℃。
进一步地,步骤(2)中,所述盐为氯化钠或氯化铵。
进一步地,步骤(2)中,加入的盐与钯络合物的质量比为1:1-10。
进一步地,步骤(3)中,所述还原剂为硼氢化钠、柠檬酸钠或水合肼,还原剂与钯络合物的质量比为1:1-10。
进一步地,步骤(4)中,抽滤时真空度为0.05-0.1MPa,烘干温度为70-150℃。
进一步地,步骤(4)中,钯粉产品中钯片质量占比为0.01%-1%。
进一步地,所述钯粉产品的粒径为10-100μm,松装密度在3.0g/cm3以上。
本申请实施例采用的上述至少一个技术方案能够达到以下有益效果:
本申请的钯粉生产方法中,通过在待还原液引入盐,一方面盐可以起到与反应器皿的磨砂作用,将生成的钯镜快速剥离;另一方面盐可以对还原体系起到稳定作用,弱化钯镜现象。本申请实现了去除钯粉生产过程中的钯镜现象,大大提高了钯粉生产效率、产品合格率,同时也降低了钯粉生产过程的生产损耗。
具体实施方式
为使本申请的目的、技术方案和优点更加清楚,下面将结合本申请具体实施例对本申请技术方案进行清楚、完整地描述。
实施例1
(1)钯络合物溶液配置:称取1kg二氯二氨钯置于5L烧杯中,加入去离子水1L,然后置于加热台加热至40℃,并搅拌均匀,得到待还原液。
(2)盐加入:上述步骤(1)所得待还原液中加入氯化钠200g,将反应浆料搅拌均匀。
(3)还原剂加入:称取柠檬酸钠500g,缓慢加入步骤(2)所得溶液边加边搅拌,加料共约1小时。之后继续搅拌直至溶液颜色变为无色。
(4)抽滤烘干:对步骤(3)所得反应液进行抽滤,得到钯粉初品;超纯水洗涤5次;抽滤洗涤得到的钯粉置于烘箱中烘干,烘干温度为100℃,从而制备出钯粉产品,其粒径在10-100μm,松装密度为3.1g/cm3。
实施例2
(1)钯络合物溶液配置:称取10kg二氯二氨钯置于50L反应釜中,加入去离子水30L,然后将溶液加热至90℃,并搅拌均匀,得到待还原液。
(2)盐加入:上述步骤(1)所得待还原液中加入氯化铵1.5kg,将反应浆料搅拌均匀。
(3)还原剂加入:称取柠硼氢化钠6kg,缓慢加入步骤(2)所得溶液边加边搅拌,加料共约5小时。之后继续搅拌直至溶液颜色变为无色。
(4)抽滤烘干:对步骤(3)所得反应液进行抽滤,得到钯粉初品;超纯水洗涤5次;抽滤洗涤得到的钯粉置于烘箱中烘干,烘干温度为70℃,从而制备出钯粉产品,其粒径在10-100μm,松装密度为4.5g/cm3。
实施例3
(1)钯络合物溶液配置:称取5kg二氯四氨钯置于50L反应釜中,加入去离子水20L,然后将溶液加热至60℃,并搅拌均匀,得到待还原液。
(2)盐加入:上述步骤(1)所得待还原液中加入氯化铵1kg,将反应浆料搅拌均匀。
(3)还原剂加入:称取水合肼1kg,缓慢加入步骤(2)所得溶液边加边搅拌,加料共约3小时。之后继续搅拌直至溶液颜色变为无色。
(4)抽滤烘干:对步骤(3)所得反应液进行抽滤,得到钯粉初品;超纯水洗涤5次;抽滤洗涤得到的钯粉置于烘箱中烘干,烘干温度为150℃,从而制备出钯粉产品,其粒径在10-100μm,松装密度为4.0g/cm3。
以上所述仅为本申请的实施例而已,并不用于限制本申请。对于本领域技术人员来说,本申请可以有各种更改和变化。凡在本申请的精神和原理之内所作的任何修改、等同替换、改进等,均应包含在本申请的权利要求范围之内。
Claims (5)
1.一种去除钯镜的钯粉生产方法,其特征在于,步骤如下:
(1)将钯络合物加入去离子水中进行加热,混匀,得到待还原液;钯络合物为二氯二氨钯或二氯四氨钯,钯络合物与去离子水质量比为1:1-10;
(2)在步骤(1)所得待还原液中加入盐,搅拌均匀;所述盐为氯化钠或氯化铵,加入的盐与钯络合物的质量比为1:1-10;
(3)在步骤(2)所得溶液中加入还原剂,搅拌直至溶液颜色变为无色;所述还原剂为硼氢化钠、柠檬酸钠或水合肼,还原剂与钯络合物的质量比为1:1-10;
(4)对步骤(3)所得反应液进行抽滤,得到钯粉初品,采用超纯水洗涤后烘干,得到钯粉产品。
2.如权利要求1所述的钯粉生产方法,其特征在于,步骤(1)中,待还原液的加热温度为30-100℃。
3.如权利要求1所述的钯粉生产方法,其特征在于,步骤(4)中,抽滤时真空度为0.05-0.1MPa,烘干温度为70-150℃。
4.如权利要求1所述的钯粉生产方法,其特征在于,步骤(4)中,钯粉产品中钯片质量占比为0.01%-1%。
5.如权利要求1所述的钯粉生产方法,其特征在于,所述钯粉产品的粒径为10-100μm,松装密度在3.0g/cm3以上。