CN110435250A - A kind of woolen knitting sheep shearing fur imitation and its production technology - Google Patents
A kind of woolen knitting sheep shearing fur imitation and its production technology Download PDFInfo
- Publication number
- CN110435250A CN110435250A CN201910736443.XA CN201910736443A CN110435250A CN 110435250 A CN110435250 A CN 110435250A CN 201910736443 A CN201910736443 A CN 201910736443A CN 110435250 A CN110435250 A CN 110435250A
- Authority
- CN
- China
- Prior art keywords
- cut pile
- woolen knitting
- production technology
- fabric
- pile fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of production technologies of woolen knitting sheep shearing fur imitation, include the following steps: S1: wool yarn and polyester filaments being woven into woolen knitting cut pile fabric, then carry out final finishing;Wherein, wool yarn content is 50%-70%, and the content of polyester filaments is 30%-50%;S2: the woolen knitting cut pile fabric by step S1 Jing Guo final finishing is compound by adhesive and leather.It is compound to realize stablizing for woolen knitting cut pile fabric and leather, forms the rock-steady structure of double-face leather;The phenomenon that hair of woolen knitting cut pile fabric has firmly been sticked on leather, avoids later period hair loss reduces the difficulty that the later period arranges.
Description
Technical field
The present invention relates to weaving manufacture and fabric complex technique fields, and in particular to a kind of woolen knitting sheep shearing imitated furs
Fabric and its production technology.
Background technique
Booming with each industry with advances in technology, traditional textile manufacturing industry has been unable to meet the need of existing market
It asks, people have no longer been to wear warm so simple to the needs of dress ornament or household items, and people are to new institutional framework, new work
The fabric of skill, new function etc. is more pursued and is had deep love for, it is desirable to enjoy more pleasing clothes and household items, can enjoy
To more added with the life of quality, or perhaps wish that textile can also bring the vision being pleasantly surprised and completely new body to people's lives
It tests.
Woolen knitting sheep shearing imitation leather wool fabric be compound resulting fabric, can partially meet people to hair wool fabric,
The needs of the subdivided products such as blanket class, tippet.There are compound difficulties with leather for woolen knitting sheep shearing in process of production for the based article
Larger problem is spent, keeps woolen knitting sheep shearing low with leather combined strength bination, the phenomenon for causing later period hair loss serious occurs, after giving
The use of phase arranges process and causes very big trouble and inconvenience.Therefore a kind of woolen knitting sheep shearing imitation leather hair of not hair loss is researched and developed
Fabric is a problem to be solved by those skilled in the art.
Summary of the invention
In view of the above shortcomings of the prior art, the object of the present invention is to provide a kind of woolen knitting sheep shearing fur imitations
And its production technology.
To achieve the above object, the present invention adopts the following technical scheme:
The first aspect of the present invention provides a kind of production technology of woolen knitting sheep shearing fur imitation, including as follows
Step:
S1: wool yarn and polyester filaments are woven into woolen knitting cut pile fabric, then carry out final finishing;Wherein,
Wool yarn content is 50%-70%, and the content of polyester filaments is 30%-50%;
S2: the woolen knitting cut pile fabric by step S1 Jing Guo final finishing is compound by adhesive and leather.
Preferably, wool yarn is veil, and polyester filaments are filling.Wool yarn and polyester filaments are woven into
Woolen knitting cut pile fabric, wherein wool yarn is fabric veil, and polyester filaments are filling, and wool yarn content is
50%-70%, the content of polyester filaments are 30%-50%;Manufactured fabric lint sense is strong under the conditions of the ratio, not bottom drain
Silk, and it is soft, it is close with atural fur feel.
Preferably, wool yarn is formed by weaving by mercerized wool in step S1;Wherein, mercerized wool yarn count is 20s/2-
40s/2, mercerized wool fiber hair Chang≤30mm, fineness 60s-90s.
Preferably, the weaving of woolen knitting cut pile fabric is to carry out warp knit cut pile or weft knitting by cut pile loom in step S1
Cut pile;Wherein, wool yarn yarn count used is 16s/2-40s/2.
Preferably, the weaving of woolen knitting cut pile fabric further includes dyeing course in step S1, and dyeing course is in silk
Before light wool textile is at wool yarn, or woolen knitting cut pile fabric weaving complete after carry out.Dyeing processing is 80
At a temperature of DEG C -90 DEG C, heat preservation 40min dyeing is heated up at a slow speed, is heated up with the speed of 1 DEG C/min;Sheep is woven into mercerized wool
It is dyed before wool yarn line, can be convenient postorder colour mixture demand, it can be according to product demand, selective staining mode.
Preferably, the final finishing successively includes soft treatment, dehydration, stentering forming, fluffing, hot light, cropping.
Preferably, soft treatment is processing in the softening agent for be placed in woolen knitting cut pile fabric 30 DEG C -50 DEG C
20min—60min;The softening agent is made of one or more of softening agent, the brightener that adds lustre to, antistatic agent.By soft
After supple-settlement, soft fabric and the smooth not clot of hair.Softening agent is the cashmere softening agent FK- of Beijing Zhong Fang Chemical Co., Ltd.
220B2, the brightener that adds lustre to are the LY-101 of Shandong Long Yuan Chemical Co., Ltd., and antistatic agent is that Dongguan Fiat electrostatic science and technology has
The antistatic agent E-3118 of limit company.
Preferably, dehydration is that be dehydrated through dewaterer to moisture content of fabric be 40% -70%, then through framing shaping machine tentering
Sizing, stentering forming temperature are 100 DEG C -140 DEG C, time 5-10min.Keep hair more suitable by stentering forming before fluffing
Directly, hair retraction clot is avoided, the uniformity for guaranteeing postorder fluffing is facilitated, avoids fluffing uneven.
Preferably, fluffing be by raising machine bristle 3-6 times, by scald cut combination machine carry out scald cut, hot light temperature is
180-220 DEG C, hot light, cropping 3-6 times.Every fluffing is primary, and hot light, cropping carry out once, keeping hair more straight by bristle,
Guarantee that fluffing uniformly, facilitates the compound working procedure of later period woolen knitting cut pile fabric and leather.
Preferably, compound in step S2 makes to press by fur pressing machine, pressing pressure 350-450Mpa, fabric fortune
Scanning frequency degree is 18-22m/min, and the additional amount of adhesive is the 15%-20% of fabric weight, and the solid content of adhesive is 30%.
Described adhesive is environment-friendly water-based polyurethane adhesive.Woolen knitting cut pile fabric is set firmly to be combined with each other with leather,
Avoid later period hair loss phenomenon.
The second aspect of the present invention provides a kind of woolen knitting sheep shearing fur imitation, by above-mentioned production technology system
It is standby to form.
Beneficial effects of the present invention:
1, the combined strength bination of woolen knitting cut pile fabric of the present invention and leather is good, and adhesive strength, tearing resistance realizes
Stablizing for woolen knitting cut pile fabric and leather is compound, forms the rock-steady structure of double-face leather;The hair of woolen knitting cut pile fabric
The phenomenon that being firmly sticked on leather, having avoided later period hair loss reduces the difficulty that the later period arranges;
2, the woolen knitting cut pile fabric that raw material and fabric postprocessing working procedures through the invention is produced, can be very
Good realizes that it is compound with leather, solves the problems, such as that the compound difficulty of the two is larger, completely solves woolen knitting sheep shearing
Imitation leather woolens Tetramune hair loss phenomenon;
3, stablized by woolen knitting cut pile fabric and leather compound, on the one hand solve woolen knitting cut pile fabric hair loss
Phenomenon, another aspect woolen knitting cut pile fabric are located at leather skin, can have color abundant, avoid and contaminate leather
Color reduces technology difficulty;
4, present invention process is simple and easy, is convenient for practical operation and production.
Specific embodiment
It is noted that following detailed description is all illustrative, it is intended to provide further instruction to the application.Unless another
It indicates, all technical and scientific terms used herein has usual with the application person of an ordinary skill in the technical field
The identical meanings of understanding.
In order to enable those skilled in the art can clearly understand the technical solution of the application, below with reference to tool
The technical solution of the application is described in detail in the embodiment of body.
Embodiment 1
A kind of woolen knitting sheep shearing fur imitation and its production technology, include the following steps:
S1: mercerized wool is woven into wool yarn, wherein mercerized wool yarn count is 20s/2, mercerized wool fiber staple length
≤ 30mm, fineness 60s;
The polyester filaments that content is 50% wool yarn and content is 50% are carried out warp knit by cut pile loom to cut
Suede or weft-knitted cut pile, are woven into woolen knitting cut pile fabric, wherein wool yarn yarn count used is 16s/2, and wool yarn is face
Yarn, polyester filaments are filling;
Woolen knitting cut pile fabric weaving after the completion of is dyed, dyeing processing be 80 DEG C at a temperature of, keep the temperature 40min
Dyeing, heats up at a slow speed, is heated up with the speed of 1 DEG C/min.
After the completion of dyeing, carry out final finishing, final finishing successively includes soft treatment, dehydration, stentering forming, fluffing, hot light,
Cropping;
Soft treatment is to handle 60min in the softening agent for be placed in woolen knitting cut pile fabric 30 DEG C;The softening agent by
One or more of softening agent, the brightener that adds lustre to, antistatic agent composition.
Dehydration is that be dehydrated through dewaterer to moisture content of fabric be 40%, then through framing shaping machine stentering forming, stentering forming
Temperature is 100 DEG C, time 10min.
Fluffing be by raising machine bristle 3 times, by scald cut combination machine carry out scald cut, hot light temperature be 220 DEG C, hot light,
Cropping 3 times.Every fluffing is primary, and hot light, cropping carry out primary.
S2: the woolen knitting cut pile fabric by step S1 Jing Guo final finishing is answered by aqueous polyurethane adhesive and leather
It closes, compound pressed by fur pressing machine, pressing pressure 350Mpa, and the fabric speed of service is 18m/min;Adhesive adds
Enter 15% that amount is fabric weight.
Embodiment 2
A kind of production technology of woolen knitting sheep shearing fur imitation, includes the following steps:
S1: mercerized wool is woven into wool yarn, wherein mercerized wool yarn count is 40s/2, mercerized wool fiber staple length
≤ 30mm, fineness 90s;
The polyester filaments that content is 70% wool yarn and content is 30% are carried out warp knit by cut pile loom to cut
Suede or weft-knitted cut pile, are woven into woolen knitting cut pile fabric, wherein wool yarn yarn count used is 40s/2, and wool yarn is face
Yarn, polyester filaments are filling;
Woolen knitting cut pile fabric weaving after the completion of is dyed, dyeing processing be 90 DEG C at a temperature of, keep the temperature 40min
Dyeing, heats up at a slow speed, is heated up with the speed of 1 DEG C/min.
After the completion of dyeing, carry out final finishing, final finishing successively includes soft treatment, dehydration, stentering forming, fluffing, hot light,
Cropping;
Soft treatment is to handle 20min in the softening agent for be placed in woolen knitting cut pile fabric 50 DEG C;The softening agent by
One or more of softening agent, the brightener that adds lustre to, antistatic agent composition.
Dehydration is that be dehydrated through dewaterer to moisture content of fabric be 70%, then through framing shaping machine stentering forming, stentering forming
Temperature is 140 DEG C, time 5min.
Fluffing be by raising machine bristle 6 times, by scald cut combination machine carry out scald cut, hot light temperature be 180 DEG C, hot light,
Cropping 6 times.Every fluffing is primary, and hot light, cropping carry out primary.
S2: the woolen knitting cut pile fabric by step S1 Jing Guo final finishing is answered by aqueous polyurethane adhesive and leather
It closes, compound pressed by fur pressing machine, pressing pressure 450Mpa, and the fabric speed of service is 22m/min;Adhesive adds
Enter 20% that amount is fabric weight.
Embodiment 3
A kind of production technology of woolen knitting sheep shearing fur imitation, includes the following steps:
S1: mercerized wool is woven into wool yarn, wherein mercerized wool yarn count is 30s/2, mercerized wool fiber staple length
≤ 30mm, fineness 80s;
The polyester filaments that content is 60% wool yarn and content is 40% are carried out warp knit by cut pile loom to cut
Suede or weft-knitted cut pile, are woven into woolen knitting cut pile fabric, wherein wool yarn yarn count used is 30s/2, and wool yarn is face
Yarn, polyester filaments are filling;
Woolen knitting cut pile fabric weaving after the completion of is dyed, dyeing processing be 85 DEG C at a temperature of, keep the temperature 40min
Dyeing, heats up at a slow speed, is heated up with the speed of 1 DEG C/min.
After the completion of dyeing, carry out final finishing, final finishing successively includes soft treatment, dehydration, stentering forming, fluffing, hot light,
Cropping;
Soft treatment is to handle 40min in the softening agent for be placed in woolen knitting cut pile fabric 40 DEG C;The softening agent by
One or more of softening agent, the brightener that adds lustre to, antistatic agent composition.
Dehydration is that be dehydrated through dewaterer to moisture content of fabric be 60%, then through framing shaping machine stentering forming, stentering forming
Temperature is 120 DEG C, time 8min.
Fluffing be by raising machine bristle 4 times, by scald cut combination machine carry out scald cut, hot light temperature be 200 DEG C, hot light,
Cropping 4 times.Every fluffing is primary, and hot light, cropping carry out primary.
S2: the woolen knitting cut pile fabric by step S1 Jing Guo final finishing is answered by aqueous polyurethane adhesive and leather
It closes, compound pressed by fur pressing machine, pressing pressure 400Mpa, and the fabric speed of service is 20m/min, and adhesive adds
Enter 18% that amount is fabric weight.
Embodiment 4
A kind of production technology of woolen knitting sheep shearing fur imitation, includes the following steps:
S1: mercerized wool is dyed, dyeing processing be 85 DEG C at a temperature of, heat preservation 40min dyeing, rise at a slow speed
Temperature is heated up with the speed of 1 DEG C/min;
Mercerized wool after dyeing is woven into wool yarn, wherein mercerized wool yarn count is 30s/2, mercerized wool fiber
Mao Chang≤30mm, fineness 80s;
By content is 50%-70% wool yarn and content is 40% polyester filaments by cut pile loom carry out through
Cut pile or weft-knitted cut pile are compiled, woolen knitting cut pile fabric is woven into, wherein wool yarn yarn count used is 30s/2, wool yarn
For veil, polyester filaments are filling;
Final finishing is carried out after the completion of woolen knitting cut pile fabric weaving, final finishing successively includes soft treatment-dehydration, drawing
Width sizing-fluffing, hot light, cropping;
Soft treatment is to handle 40min in the softening agent for be placed in woolen knitting cut pile fabric 40 DEG C;The softening agent by
One or more of softening agent, the brightener that adds lustre to, antistatic agent composition.
Dehydration is that be dehydrated through dewaterer to moisture content of fabric be 60%, then through framing shaping machine stentering forming, stentering forming
Temperature is 120 DEG C, time 8min.
Fluffing be by raising machine bristle 4 times, by scald cut combination machine carry out scald cut, hot light temperature be 200 DEG C, hot light,
Cropping 4 times.Every fluffing is primary, and hot light, cropping carry out primary.
S2: the woolen knitting cut pile fabric by step S1 Jing Guo final finishing is answered by aqueous polyurethane adhesive and leather
It closes, compound pressed by fur pressing machine, pressing pressure 400Mpa, and the fabric speed of service is 20m/min, and adhesive adds
Enter 18% that amount is fabric weight.
Physical index detection
Woolen knitting sheep shearing fur imitation made from above-described embodiment 1-4 is subjected to physical index detection, physics refers to
Mark includes adhesive strength and tearing resistance, and bond strength test method is measured with ASTM D2724, adhesive strength unit
The intensity of breadth indicates;Fabric tear strength national standard GB/T3917.1-199 Indexs measure.Testing result is as shown in the table:
The foregoing is merely preferred embodiment of the present application, are not intended to limit this application, for the skill of this field
For art personnel, various changes and changes are possible in this application.Within the spirit and principles of this application, made any to repair
Change, equivalent replacement, improvement etc., should be included within the scope of protection of this application.
Claims (10)
1. a kind of production technology of woolen knitting sheep shearing fur imitation, which comprises the steps of:
S1: wool yarn and polyester filaments are woven into woolen knitting cut pile fabric, then carry out final finishing;Wherein, wool
Yarn content is 50%-70%, and the content of polyester filaments is 30%-50%;
S2: the woolen knitting cut pile fabric by step S1 Jing Guo final finishing is compound by adhesive and leather.
2. production technology according to claim 1, which is characterized in that in step S1 wool yarn by mercerized wool weave and
At wherein mercerized wool yarn count is 20s/2-40s/2, mercerized wool fiber hair Chang≤30mm, fineness 60s-90s;
The weaving of woolen knitting cut pile fabric is that warp knit cut pile or weft-knitted cut pile are carried out by cut pile loom, wherein wool yarns used
Yarns branch is 16s/2-40s/2.
3. production technology according to claim 1, which is characterized in that the weaving of woolen knitting cut pile fabric is also in step S1
Including dyeing course, dyeing course is spun before mercerized wool is woven into wool yarn, or in woolen knitting cut pile fabric
It casts off into and carries out later.
4. production technology according to claim 1, which is characterized in that the final finishing includes soft treatment, dehydration, tentering
Sizing, fluffing, hot light, cropping.
5. production technology according to claim 4, which is characterized in that soft treatment is to be placed in woolen knitting cut pile fabric
In 30 DEG C -50 DEG C of softening agent, 20min -60min is handled;The softening agent is by softening agent, the brightener that adds lustre to, antistatic agent
One or more of composition.
6. production technology according to claim 4, which is characterized in that dehydration is to be dehydrated through dewaterer to moisture content of fabric to be
40% -70%.
7. production technology according to claim 4, which is characterized in that stentering forming is by framing shaping machine stentering forming
5-10min, stentering forming temperature are 100 DEG C -140 DEG C.
8. production technology according to claim 4, which is characterized in that fluffing be by raising machine bristle 3-6 times, by
Scald cut combination machine carry out scald cut, hot light temperature be 180-220 DEG C, hot light, cropping 3-6 times.
9. production technology according to claim 1, which is characterized in that compound in step S2 is by fur pressing machine pressure
It closes, pressing pressure 350-450Mpa, the fabric speed of service is 18-22m/min;The additional amount of adhesive is fabric weight
15%-20%.
10. a kind of woolen knitting sheep shearing fur imitation, which is characterized in that by the described in any item productions of claim 1-9
Technique is prepared.