CN108729008A - A kind of production method of digit printing Rachael blanket - Google Patents
A kind of production method of digit printing Rachael blanket Download PDFInfo
- Publication number
- CN108729008A CN108729008A CN201810548517.2A CN201810548517A CN108729008A CN 108729008 A CN108729008 A CN 108729008A CN 201810548517 A CN201810548517 A CN 201810548517A CN 108729008 A CN108729008 A CN 108729008A
- Authority
- CN
- China
- Prior art keywords
- hot light
- production method
- fabric
- temperature
- digit printing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of production methods of digit printing Rachael blanket.The production method of the digit printing Rachael blanket of the present invention, includes the following steps：1) it weaves：By suede yarn and filling respectively by being woven on volume machine after warping on warping machine, fabric is obtained after cuing open width, perching, filling and suede yarn all use FDY polyester filaments；2) prefinishing：Fabric is carried out shaping, a hot light, bristle, secondary hot light, pretreatment, drying and processing；3) it prints and dyes：Fabric through prefinishing is subjected to digit printing, decatize, washing, dewatered drying processing；4) it post-processes：By the figured cloth after printing and dyeing carry out hot light scald cut, the processing of a bristle, secondary hot light, secondary bristle, it is clipped, be packaged to be digit printing Rachael blanket.The production method of the digit printing Rachael blanket of the present invention, process is simple, and obtained woollen blanket color fastness greatly improves, and can be improved half grade or more, simpler compared with screen printing process flexible.
Description
Technical field
The invention belongs to home textile product technical fields, are related to a kind of production method of digit printing Rachael blanket.
Background technology
With the raising of people's living standard and spiritual culture, more and more people pursue personalized unique.Common
Screen printing is made a plate before stamp, the problems such as so as to cause factory's flower pattern transformation is slow, exploitation is new flower-shaped of high cost.And
With the development of digital printing technology, digit printing is widely used on textile of being in.
The production process of digit printing makes original process route greatly shorten, and order speed is fast, and cost of drawing a design drops significantly
It is low.The principle of digital printing technology makes its product break the chromatography of traditional mode of production and spend back the limitation of length, can make spinning
Knitted fabric realizes the printing effect of high-grade printing.Digit printing production is truly realized small lot, the production process of fast response, raw
Production batch is unrestricted, meanwhile, environmental protection is also helped, almost without the discarded and wave of dyestuff and auxiliary agent in digit printing production
Take, without sewage discharge, and low noise.
Traditional polyester raschel blanket is produced using screen printing technology, still, the stamp period of silk-screen printing
Long, flower pattern cycle is restricted, there is also to version not just, the single unfavorable condition of flower pattern.Therefore, using digit printing come solve with
Upper problem improves the competitiveness of woollen blanket.
CN104831569A discloses a kind of polyester carpet digit printing processing method, the stamp of the polyester carpet of the invention
Processing method includes the following steps：Step 1: the selected base blanket for needing to carry out stamp；Step 2: the base blanket is filled through work feed
Horizontalization is layered on to be printed on ink-jet decorating machine conduction band, selected pattern and typesetting, digital ink-jet printed to base blanket progress；Step
Three, the base blanket after stamp is sent into color development machine color development；Step 4: handling the roads Pi Tanzuohou after color development, it is made
Finished product.The polyester carpet digit printing processing method of the invention compared with Conventional decal technique, be omitted printing before starching and
The processes such as fixation, washing after color development reduce energy consumption and three waste discharge, and optimize digit printing on polyester carpet
Using making its volume production ability and quality obtain practical raising, still, the colorfastness to rubbing of woollen blanket needs to be further increased.
Invention content
In view of the deficiencies of the prior art, the purpose of the present invention is to provide a kind of producers of digit printing Rachael blanket
Method, process simple and flexible, woollen blanket color fastness improve half grade or more.
For this purpose, the present invention uses following technical scheme：
A kind of production method of digit printing Rachael blanket, includes the following steps：
1) it weaves：By suede yarn and filling respectively by being woven on volume machine after warping on warping machine, obtained after cuing open width, perching
Fabric, the filling and suede yarn all use FDY polyester filaments；
2) prefinishing：The fabric that step 1) obtains is carried out shaping, a hot light, bristle, secondary hot light, pretreatment, baking
Dry-cure；
3) it prints and dyes：Digit printing, decatize, washing, dewatered drying processing will be carried out through the fabric of step 2) prefinishing；
4) it post-processes：By through step 3) printing and dyeing after figured cloth carry out hot light scald cut, a bristle, secondary hot light, secondary brush
Hair processing, it is clipped, be packaged to be the digit printing Rachael blanket.
In step 1), the warping technology is specially：By suede yarn and filling respectively by warping on warping machine, warping radical is
400~500, for example, warping radical be 400,410,420,430,440,450,460,470,480
Root, 490,500；Warping coiled hair number is 5~10, such as warping coiled hair number is 5,6,7,8,9,10；Speed of beaming be 600~
700m/min, for example, speed of beaming be 600m/min, 610m/min, 620m/min, 630m/min, 640m/min, 650m/min,
660m/min、670、680m/min、690m/min、700m/min。
Preferably, in step 1), the weaving is specially：It is knitted using double-needle bed raschel tricot machine TJ5-190E18
Make, the gauge of two-needle bar is 40~60mm, such as the gauge of two-needle bar is 40mm, 42mm, 44mm, 46mm, 48mm, 50mm,
52mm,55mm,56mm,58mm,60mm；Fabric 200~230cm of breadth, for example, fabric breadth be 200cm, 205cm, 210cm,
215cm、220cm、225cm、230cm。
In step 2), the color fastness of Woollen blanket printing can be improved after pretreatment process.The pretreated process is specific
For：The grey cloth after secondary hot light is pre-processed using 2.2~3.6% polyethylene glycol oxide, such as polyethylene glycol oxide
A concentration of 2.2%, 2.3%, 2.4%, 2.5%, 2.6%, 2.7%, 2.8%, 2.9%, 3%, 3.1%, 3.2%, 3.3%,
3.4%, 3.5%, 3.6%.
In step 2), the temperature of the sizing is 100~120 DEG C, for example, the temperature of sizing is 100 DEG C, 102 DEG C, 105
℃,106℃,108℃,110℃,112℃,115℃,118℃,120℃；The cloth speed of the sizing is 6~8m/min, such as institute
The cloth speed for stating sizing is 6m/min, 6.5m/min, 7m/min, 7.5m/min, 8m/min.
Preferably, in step 2), the temperature of a hot light and the secondary hot light is 180~190 DEG C, such as described
The temperature of hot light and the secondary hot light be 180 DEG C, 181 DEG C, 182 DEG C, 183 DEG C, 184 DEG C, 185 DEG C, 186 DEG C, 187
℃,188℃,189℃,190℃；The cloth speed of hot light and the secondary hot light is 25~26m/min, such as described one
The cloth speed of secondary hot light and the secondary hot light be 25m/min, 25.1m/min, 25.2m/min, 25.3m/min, 25.4m/min,
25.5m/min、25.6m/min、25.7m/min、25.8m/min、25.9m/min、26m/min。
Preferably, in step 2), the cloth speed of the bristle is 3~5m/min, for example, bristle cloth speed be 3m/min,
3.5m/min、4m/min、4.5m/min、5m/min。
Preferably, in step 2), the temperature of the drying is 110~130 DEG C, for example, the temperature of drying is 100 DEG C, 105
℃,110℃,115℃,120℃,125℃,130℃；The cloth speed of the drying is 8~12m/min, such as the cloth of the drying
Speed is 8m/min, 9m/min, 10m/min, 11m/min, 12m/min.
In step 3), the digit printing process is specially：Using the good flower pattern of Computer Design, corresponding color is chosen to warp
Fabric after drying and processing carries out digit printing, wherein optional 8~16 chromatography, precision are 16dpi × 16dpi, the digital print
Colored cloth speed be 0.4~1.2m/min, such as the digit printing cloth speed be 0.4m/min, 0.5m/min, 0.6m/min,
0.7m/min、0.8m/min、0.9m/min、1m/min、1.1m/min、1.2m/min。
In step 3), the temperature of the decatize is 100~124 DEG C, for example, the temperature of decatize is 100 DEG C, 105 DEG C, 110
℃,115℃,120℃,124℃；The time of the decatize be 10~16min, such as decatize time be 10min, 11min,
12min、13min、14min、15min、16min。
In step 3), the washing step is specially：Fabric after decatize is washed, wherein the cloth of the washing
Speed is 16~20m/min, such as the cloth speed of washing is 16m/min, 17m/min, 18m/min, 19m/min, 20m/min；It is described
The temperature of washing is 80~100 DEG C, such as the temperature of washing is 80 DEG C, 85 DEG C, 90 DEG C, 95 DEG C, 100 DEG C.
Preferably, the washing is washed through eight slots, wherein first and second, six, seven, eight slot cold water are washed；Third and fourth slot hot water
It washes；5th slot is soaped, and is soaped using soaping agent in the soap washing, a concentration of 2~3g/L of the soaping agent, such as
A concentration of 2g/L, 2.1g/L of lotion, 2.2g/L, 2.3g/L, 2.4g/L, 2.5g/L, 2.6g/L, 2.7g/L, 2.8g/L,
2.9g/L,3g/L；The temperature soaped is 85~95 DEG C, for example, the temperature soaped is 85 DEG C, 86 DEG C, 87 DEG C, 88 DEG C, 89
℃、90℃、91℃、92℃、93℃、94℃、95℃。
In step 3), the temperature of the dewatered drying is 130~150 DEG C, for example, the temperature of dewatered drying is 130 DEG C, 135
℃,140℃,145℃,150℃；The cloth speed of the dewatered drying is 10~15m/min, such as the cloth speed of dewatered drying is 10m/
min、11m/min、12m/min、13m/min、14m/min、15m/min。
In step 4), it is 170~190 DEG C that the hot light, which scalds the temperature cut, for example, hot light scald the temperature cut be 170 DEG C, 175
℃,180℃,185℃,190℃；It is 20~30m/min that the hot light, which scalds the cloth speed cut, such as it is 20m/ that hot light, which scalds the cloth speed cut,
min、21m/min、22m/min、23m/min、24m/min、25m/min、26m/min、27m/min、28m/min、29m/min、
30m/min。
In step 4), the cloth speed of a bristle and the secondary bristle is 10~20m/min, such as the primary brush
The cloth speed of hair and the secondary bristle is 10m/min, 11m/min, 12m/min, 13m/min, 14m/min, 15m/min, 16m/
min、17m/min、18m/min、19m/min、20m/min。
Compared with prior art, beneficial effects of the present invention are：
The production method of the digit printing Rachael blanket of the present invention, process is simple, using polyethylene glycol oxide to terylene hair
Blanket is pre-processed, and using specific hot pressing temperature and steaming time and temperature, the woollen blanket color obtained by such method
Fastness greatly improves, and can be improved half grade or more, and the digit printing process of the present invention is compared with the simpler spirit of screen printing process
It is living.
Specific implementation mode
The technical solution further illustrated the present invention below by specific implementation mode.
Unless specific instructions, various raw materials of the invention are commercially available buys, or is prepared according to the conventional method of this field
It obtains.
Embodiment 1
Warping：Wool yarn raw material uses polyester FDY 200D/96f, and base fabric raw material uses polyester FDY 100D/36f, using warping
Machine carries out warping, and coiled hair number is 8, and head number is 420, speed of beaming 650m/min；
Weaving：It is weaved using double-needle bed raschel tricot machine TJ5-190E18, two-needle bar gauge 48mm, fabric breadth
210cm；
Openpore is shaped：The openpore weaved is carried out shaping on forming machine, the control of cloth speed is in 7.5m/min, temperature control
At 110 DEG C；
Hot light：Hot light is carried out to the fabric after sizing, cloth speed is 25.5m/min, and temperature is 182 DEG C；
Bristle：Bristle is carried out to the fabric after hot light, cloth speed is controlled in 4m/min；
Secondary hot light：Hot light is carried out again to the fabric after bristle, cloth speed is 25.5m/min, and temperature is 182 DEG C；
Pretreatment：The grey cloth after secondary hot light is pre-processed using 2.2% polyethylene glycol oxide；
Preliminary drying：Pretreated fabric is dried, temperature is 120 DEG C, speed 10m/min；
Digit printing：8 chromatographys, precision 16dpi × 16dpi, speed 1.2m/min；
Decatize：104 DEG C of steam temperature, steaming time 12min；
Washing：Fabric after evaporating is washed, cloth speed is 18m/min, and the first and second slot cold water is washed, third and fourth slot heat
Washing, the 5th slot are soaped, and soaping agent 2g/L, 95 DEG C, the six, the seven, eight slot cold water are washed；
Dewatered drying：By the fabric dewatered drying after washing, temperature is 140 DEG C, speed 12m/min；
Figured cloth hot light, which is scalded, cuts：Hot light is carried out to the front of fabric and scalds to cut, wherein the control of the temperature of ironing roller is at 180 DEG C, cloth
Speed is 25m/min；
Bristle：Cloth speed is controlled in 18m/min；
It cuts：Figured cloth is cut into the size of 200 × 240cm；
Sewing：Both sides figured cloth is not had into fitting together on one side for lint, edge-covering cloth is sewed on around.
Embodiment 2
Warping：Wool yarn raw material uses polyester FDY 200D/96f, and base fabric raw material uses polyester FDY 100D/36f, using warping
Machine carries out warping, and coiled hair number is 8, and head number is 440, speed of beaming 650m/min；
Weaving：It is weaved using double-needle bed raschel tricot machine TJ5-190E18, two-needle bar gauge 48mm, fabric breadth
230cm；
Openpore is shaped：The openpore weaved is carried out shaping on forming machine, the control of cloth speed is in 7.5m/min, temperature control
At 110 DEG C；
Hot light：Hot light is carried out to the fabric after sizing, cloth speed is 25.5m/min, and temperature is 182 DEG C；
Bristle：Bristle is carried out to the fabric after hot light, cloth speed is controlled in 5m/min；
Secondary hot light：Hot light is carried out again to the fabric after bristle, cloth speed is 25.5m/min, and temperature is 182 DEG C；
Pretreatment：The grey cloth after secondary hot light is pre-processed using 3.2% polyethylene glycol oxide；
Preliminary drying：Pretreated fabric is dried, temperature is 120 DEG C, speed 10m/min；
Digit printing：12 chromatographys, precision 16dpi × 16dpi, speed 1m/min；
Decatize：114 DEG C of steam temperature, steaming time 16min；
Washing：Fabric after evaporating is washed, cloth speed is 18m/min, and the first and second slot cold water is washed, third and fourth slot heat
Washing, the 5th slot are soaped, and soaping agent 2.1g/L, 90 DEG C, the six, the seven, eight slot cold water are washed；
Dewatered drying：By the fabric dewatered drying after washing, temperature is 140 DEG C, speed 12m/min；
Figured cloth hot light, which is scalded, cuts：Hot light is carried out to the front of fabric and scalds to cut, wherein the control of the temperature of ironing roller is at 180 DEG C, cloth
Speed is 25m/min；
Bristle：Cloth speed 15m/min；
It cuts：Figured cloth is cut into the size of 220 × 240cm；
Sewing：By two panels figured cloth backwards to suture.
Embodiment 3
Warping：Wool yarn raw material uses polyester FDY 200D/96f, and base fabric raw material uses polyester FDY 100D/36f, using warping
Machine carries out warping, and coiled hair number is 10, and head number is 480, speed of beaming 670m/min；
Weaving：It is weaved using double-needle bed raschel tricot machine TJ5-190E18, two-needle bar gauge 58mm, fabric breadth
220cm；
Openpore is shaped：The openpore weaved is carried out shaping on forming machine, the control of cloth speed is in 7.8m/min, temperature control
At 120 DEG C；
Hot light：Hot light is carried out to the fabric after sizing, cloth speed is 25.8m/min, and temperature is 188 DEG C；
Bristle：Bristle is carried out to the fabric after hot light, cloth speed is controlled in 5m/min；
Secondary hot light：Hot light is carried out again to the fabric after bristle, cloth speed is 25.8m/min, and temperature is 188 DEG C；
Pretreatment：The grey cloth after secondary hot light is pre-processed using 3.6% polyethylene glycol oxide；
Preliminary drying：Pretreated fabric is dried, temperature is 130 DEG C, speed 12m/min；
Digit printing：12 chromatographys, precision 16dpi × 16dpi, speed 1.2m/min；
Decatize：120 DEG C of steam temperature, steaming time 15min；
Washing：Fabric after evaporating is washed, cloth speed is 18m/min, and the first and second slot cold water is washed, third and fourth slot heat
Washing, the 5th slot are soaped, and soaping agent 2.8g/L, 95 DEG C, the six, the seven, eight slot cold water are washed；
Dewatered drying：By the fabric dewatered drying after washing, temperature is 145 DEG C, speed 15m/min；
Figured cloth hot light, which is scalded, cuts：Hot light is carried out to the front of fabric and scalds to cut, wherein the control of the temperature of ironing roller is at 188 DEG C, cloth
Speed is 27m/min；
Bristle：Cloth speed 15m/min；
It cuts：Figured cloth is cut into the size of 220 × 240cm；
Sewing：By two panels figured cloth backwards to suture.
The production method of the digit printing Rachael blanket of the present invention, process is simple, using polyethylene glycol oxide to terylene hair
Blanket is pre-processed, and using specific hot pressing temperature and steaming time and temperature, the woollen blanket color obtained by such method
Fastness greatly improves, and can be improved half grade or more, and the digit printing process of the present invention is compared with the simpler spirit of screen printing process
It is living.
The present invention illustrates detailed process equipment and the technological process of the present invention by above-described embodiment, but the present invention is not
It is confined to above-mentioned detailed process equipment and technological process, that is, does not mean that the present invention has to rely on above-mentioned detailed process equipment and work
Skill flow could be implemented.Person of ordinary skill in the field is it will be clearly understood that any improvement in the present invention, to product of the present invention
The equivalence replacement of each raw material and the addition of auxiliary element, the selection of concrete mode etc., all fall within protection scope of the present invention and public affairs
Within the scope of opening.
Claims (10)
1. a kind of production method of digit printing Rachael blanket, which is characterized in that include the following steps：
1) it weaves：By suede yarn and filling respectively by being woven on volume machine after warping on warping machine, base is obtained after cuing open width, perching
Cloth, the filling and suede yarn all use FDY polyester filaments；
2) prefinishing：The fabric that step 1) obtains is carried out shaping, a hot light, bristle, secondary hot light, pretreatment, at drying
Reason；
3) it prints and dyes：Digit printing, decatize, washing, dewatered drying processing will be carried out through the fabric of step 2) prefinishing；
4) it post-processes：Figured cloth progress hot light after step 3) printing and dyeing is scalded and is cut, at a bristle, secondary hot light, secondary bristle
Reason, it is clipped, be packaged to be the digit printing Rachael blanket.
2. production method according to claim 1, which is characterized in that in step 1), the warping technology is specially：By suede
Yarn and filling are respectively by warping on warping machine, and warping radical is 400~500, and warping coiled hair number is 5~10, and speed of beaming is
600~700m/min；
Preferably, in step 1), the weaving is specially：It is weaved using double-needle bed raschel tricot machine TJ5-190E18,
The gauge of two-needle bar is 40~60mm, 200~230cm of fabric breadth.
3. production method according to claim 1 or 2, which is characterized in that in step 2), the pretreated process is specific
For：The grey cloth after secondary hot light is pre-processed using 2.2~3.6% polyethylene glycol oxide.
4. according to the production method described in one of claim 1-3, which is characterized in that in step 2), the temperature of the sizing is
100~120 DEG C, the cloth speed of the sizing is 6~8m/min；
Preferably, in step 2), the temperature of a hot light and the secondary hot light is 180~190 DEG C, a hot light
Cloth speed with the secondary hot light is 25~26m/min；
Preferably, in step 2), the cloth speed of the bristle is 3~5m/min；
Preferably, in step 2), the temperature of the drying is 110~130 DEG C, and the cloth speed of the drying is 8~12m/min.
5. according to the production method described in one of claim 1-4, which is characterized in that in step 3), the digit printing process
Specially：Using the good flower pattern of Computer Design, choosing corresponding color, treated that fabric carries out digit printing to drying,
In, optional 8~16 chromatography, precision is 16dpi × 16dpi, and the cloth speed of the digit printing is 0.4~1.2m/min.
6. according to the production method described in one of claim 1-5, which is characterized in that in step 3), the temperature of the decatize is
100~124 DEG C, the time of the decatize is 10~16min.
7. according to the production method described in one of claim 1-6, which is characterized in that in step 3), the washing step is specific
For：Fabric after decatize is washed, wherein the cloth speed of the washing is 16~20m/min, and the temperature of the washing is 80
~100 DEG C；
Preferably, the washing is washed through eight slots, wherein first and second, six, seven, eight slot cold water are washed；Third and fourth slot hot water wash；The
Five slots are soaped, and are soaped using soaping agent in the soap washing, a concentration of 2~3g/L of the soaping agent, described to soap
Temperature be 85~95 DEG C.
8. according to the production method described in one of claim 1-7, which is characterized in that in step 3), the temperature of the dewatered drying
Degree is 130~150 DEG C, and the cloth speed of the dewatered drying is 10~15m/min.
9. according to the production method described in one of claim 1-8, which is characterized in that in step 4), the hot light scalds the temperature cut
Degree is 170~190 DEG C, and it is 20~30m/min that the hot light, which scalds the cloth speed cut,.
10. according to the production method described in one of claim 1-9, which is characterized in that in step 4), a bristle and institute
The cloth speed for stating secondary bristle is 10~20m/min.