CN110284238A - A kind of regenerated polyester fiber fabric and its production technology - Google Patents
A kind of regenerated polyester fiber fabric and its production technology Download PDFInfo
- Publication number
- CN110284238A CN110284238A CN201910479506.8A CN201910479506A CN110284238A CN 110284238 A CN110284238 A CN 110284238A CN 201910479506 A CN201910479506 A CN 201910479506A CN 110284238 A CN110284238 A CN 110284238A
- Authority
- CN
- China
- Prior art keywords
- polyester fiber
- yarn
- regenerated polyester
- fiber fabric
- production technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of regenerated polyester fiber fabric and its production technologies, wherein, regenerated polyester fiber fabric, including warp thread and weft yarn, it is uniformly worn in the warp thread and weft yarn and is woven with oblique yarn, the oblique yarn is relatively 45 degree with the tilt angle of warp thread and weft yarn, the warp thread, weft yarn and oblique yarn use identical complex yarn, complex yarn is by regenerated polyester fiber, non-renewable polyester fiber, ramee, cotton fiber and viscose rayon are mixed, a kind of regenerated polyester fiber fabric production technology successively includes warping, sizing, weaving, dyeing, softening, setting and calendering step.Regenerated polyester fiber fabric in the present invention is a kind of energy conservation and environmental protection, securely durable, comfortable and easy to wear regenerated polyester fiber fabric.
Description
Technical field
The present invention relates to regeneration fabric technical field, specially a kind of regenerated polyester fiber fabric and its production technology.
Background technique
Currently, the polyester fiber in waste and old clothing still has a value of recycling, however few utilizations at present
The practical application of regenerated polyester fiber production fabric.It can be recycled using regenerated polyester fiber and effectively reduce carbon dioxide
Discharge amount, reduces the advantages that air pollution at the usage amount for reducing petroleum.Be conducive to protect environment, save petroleum resources, enhancing produces
The sustainable development of industry.However, a small amount of regenerated polyester fiber production fabric existing at present exists mostly, fabric intensity is low, no
Enough consolidations, fiber drawback easy to aging.It solves the above problems so needing the novel regenerated polyester fiber fabric of one kind.
Summary of the invention
The purpose of the present invention is to provide a kind of regenerated polyester fiber fabric and its production technologies, to solve above-mentioned background skill
The problem of being proposed in art.
To achieve the above object, the invention provides the following technical scheme:
A kind of regenerated polyester fiber fabric, including warp thread and weft yarn are uniformly worn in the warp thread and weft yarn and are woven with oblique yarn, institute
Stating oblique yarn is relatively 45 degree with the tilt angle of warp thread and weft yarn, and the warp thread, weft yarn and oblique yarn use identical complex yarn,
Complex yarn is mixed by regenerated polyester fiber, non-renewable polyester fiber, ramee, cotton fiber and viscose rayon.
A kind of regenerated polyester fiber fabric production technology, successively include warping, sizing, weaving, dyeing, softening, setting with
And calendering step, the warping technology are, by regenerated polyester fiber, non-renewable polyester fiber, ramee, cotton fiber and
Viscose rayon is spun into the complex yarn of compact form, warping speed 200-300m/min, thread density 200-250g/dm3。
As a further solution of the present invention: the slashing technique is to be wound complex yarn on sizing machine,
Slurry accounts for 10%-20% using polyvinyl alcohol weight percentage, and phosphate ester starch weight percent accounts for 40%-50%, solid third
Olefin(e) acid weight percent accounts for 20%-25%, and antistatic agent weight percent accounts for 2%-3%.
As a further solution of the present invention: the weaving process is to be sprayed water using the complex yarn after sizing with pound
Loom is weaved, main jet time 55-60 degree, speed 250n/min, the temperature of weaving rooms: 18-27 DEG C, relative humidity 50-
60%.
As a further solution of the present invention: the dyeing is to select the polyester fiber fabric weaved and overflow
Stream cylinder is dyed, and the weight ratio for controlling cloth and water is 1:10-15, and dyeing liquor is that acetic acid 0.4-0.6g/L, even is added in water
Stain 0.5-0.8g/L, and with detergent 2-3g/L, HAC auxiliary agent 1-2g/L, color fixing agent 1-1.5g/L.
As a further solution of the present invention: the softening technique is that the fabric after first being dyed with degreaser carries out clearly
It washes, after cleaning, the weight ratio for controlling cloth and water is 1:15-20, and softening liquid is that acetic acid 0.2-0.3g/L is added in water, silicone oil cream
Liquid 3-4g/L.
As a further solution of the present invention: the setting process is to be carried out by forming machine to the fabric after softening
Processing is carried out shaping, speed is controlled in 45 yards/minute, and setting temperature is between 135 DEG C -145 DEG C.
As a further solution of the present invention: the calen-dering process is the calendering in calender by fabric cloth, control
The pressure of the upper lower compression roller of calender is 15-18Mpa, speed 14-17m/min.
Compared with prior art, the beneficial effects of the present invention are: yarn used in regenerated polyester fiber fabric in the present invention
For the complex yarn that regenerated polyester fiber, non-renewable polyester fiber, ramee, cotton fiber and viscose rayon are mixed,
So that regenerated polyester fiber fabric has good snugness of fit, avoids single regenerated polyester fiber and weave brought face
Expect problem easy to aging, while the present invention increases oblique yarn on the basis of original warp thread and weft yarn, improve fabric intensity and
The degree of packing.Regenerated polyester fiber fabric in the present invention is a kind of energy conservation and environmental protection, securely durable, comfortable and easy to wear regenerated terylene
Fabric lining.
Detailed description of the invention
Fig. 1 is a kind of structural schematic diagram of regenerated polyester fiber fabric；
Fig. 2 is a kind of structural schematic diagram of complex yarn in regenerated polyester fiber fabric.
In figure: 1- warp thread, 2- weft yarn, the oblique yarn of 3-, 4- regenerated polyester fiber, the non-renewable polyester fiber of 5-, 6- ramee,
7- cotton fiber, 8- viscose rayon.
Specific embodiment
The following is a clear and complete description of the technical scheme in the embodiments of the invention, it is clear that described embodiment
Only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, the common skill in this field
Art personnel every other embodiment obtained without making creative work belongs to the model that the present invention protects
It encloses.
Embodiment 1:
A kind of regenerated polyester fiber fabric, including warp thread 1 and weft yarn 2 are uniformly worn in the warp thread 1 and weft yarn 2 and are woven with tiltedly
Yarn 3, the oblique yarn 3 is relatively 45 degree with the tilt angle of warp thread 1 and weft yarn 2, and the warp thread 1, weft yarn 2 and oblique yarn 3 use phase
Same complex yarn, complex yarn is by regenerated polyester fiber 4, non-renewable polyester fiber 5, ramee 6, cotton fiber 7 and glues
Glue fiber 8 is mixed.
A kind of regenerated polyester fiber fabric production technology, successively include warping, sizing, weaving, dyeing, softening, setting with
And calendering step, the warping technology are, by regenerated polyester fiber 4, non-renewable polyester fiber 5, ramee 6, cotton fiber 7
And viscose rayon 8 is spun into the complex yarn of compact form, warping speed 200m/min, thread density 200g/dm3。
The slashing technique is to be wound complex yarn on sizing machine, and slurry uses polyvinyl alcohol weight hundred
Ratio is divided to account for 10%, phosphate ester starch weight percent accounts for 40%, and solid propenoic acid weight percent accounts for 20%, antistatic agent weight
Percentage accounts for 2%.
The weaving process is to be weaved using the complex yarn after sizing with scale water jet loom, the main jet time 55
Degree, speed 250n/min, the temperature of weaving rooms: 18 DEG C, relative humidity 50%.
The dyeing is, the polyester fiber fabric weaved selection overflow cylinder is dyed, control cloth with
The weight ratio of water is 1:10, and dyeing liquor is acetic acid 0.4g/L, levelling agent 0.5g/L to be added in water, and helped with detergent 2g/L, HAC
Agent 1g/L, color fixing agent 1g/L.
The softening technique is that the fabric after first being dyed with degreaser is cleaned, and after cleaning, controls cloth and water
Weight ratio is 1:15, and softening liquid is that acetic acid 0.2g/L, silicone oil emulsion 3g/L are added in water.
The setting process is to carry out carrying out shaping the fabric after softening processing by forming machine, and speed control exists
45 yards/minute, setting temperature is at 135 DEG C.
The calen-dering process is that the calendering in calender by fabric cloth controls the pressure of the upper lower compression roller of calender
For 15Mpa, speed 14m/min.
Embodiment 2:
A kind of regenerated polyester fiber fabric, including warp thread 1 and weft yarn 2 are uniformly worn in the warp thread 1 and weft yarn 2 and are woven with tiltedly
Yarn 3, the oblique yarn 3 is relatively 45 degree with the tilt angle of warp thread 1 and weft yarn 2, and the warp thread 1, weft yarn 2 and oblique yarn 3 use phase
Same complex yarn, complex yarn is by regenerated polyester fiber 4, non-renewable polyester fiber 5, ramee 6, cotton fiber 7 and glues
Glue fiber 8 is mixed.
A kind of regenerated polyester fiber fabric production technology, successively include warping, sizing, weaving, dyeing, softening, setting with
And calendering step, the warping technology are, by regenerated polyester fiber 4, non-renewable polyester fiber 5, ramee 6, cotton fiber 7
And viscose rayon 8 is spun into the complex yarn of compact form, warping speed 300m/min, thread density 250g/dm3。
The slashing technique is to be wound complex yarn on sizing machine, and slurry uses polyvinyl alcohol weight hundred
Ratio is divided to account for 20%, phosphate ester starch weight percent accounts for 50%, and solid propenoic acid weight percent accounts for 25%, antistatic agent weight
Percentage accounts for 3%.
The weaving process is to be weaved using the complex yarn after sizing with scale water jet loom, the main jet time 60
Degree, speed 250n/min, the temperature of weaving rooms: 27 DEG C, relative humidity 60%.
The dyeing is, the polyester fiber fabric weaved selection overflow cylinder is dyed, control cloth with
The weight ratio of water is 1:15, and dyeing liquor is that acetic acid 0.6g/L, levelling agent 0.8g/L are added in water, and with detergent 2-3g/L, HAC
Auxiliary agent 2g/L, color fixing agent 1.5g/L.
The softening technique is that the fabric after first being dyed with degreaser is cleaned, and after cleaning, controls cloth and water
Weight ratio is 1:20, and softening liquid is that acetic acid 0.3g/L, silicone oil emulsion 4g/L are added in water.
The setting process is to carry out carrying out shaping the fabric after softening processing by forming machine, and speed control exists
45 yards/minute, setting temperature is at 145 DEG C.
The calen-dering process is that the calendering in calender by fabric cloth controls the pressure of the upper lower compression roller of calender
For 18Mpa, speed 17m/min.
Embodiment 3:
A kind of regenerated polyester fiber fabric, including warp thread 1 and weft yarn 2 are uniformly worn in the warp thread 1 and weft yarn 2 and are woven with tiltedly
Yarn 3, the oblique yarn 3 is relatively 45 degree with the tilt angle of warp thread 1 and weft yarn 2, and the warp thread 1, weft yarn 2 and oblique yarn 3 use phase
Same complex yarn, complex yarn is by regenerated polyester fiber 4, non-renewable polyester fiber 5, ramee 6, cotton fiber 7 and glues
Glue fiber 8 is mixed.
A kind of regenerated polyester fiber fabric production technology, successively include warping, sizing, weaving, dyeing, softening, setting with
And calendering step, the warping technology are, by regenerated polyester fiber 4, non-renewable polyester fiber 5, ramee 6, cotton fiber 7
And viscose rayon 8 is spun into the complex yarn of compact form, warping speed 250m/min, thread density 225g/dm3。
The slashing technique is to be wound complex yarn on sizing machine, and slurry uses polyvinyl alcohol weight hundred
Ratio is divided to account for 15%, phosphate ester starch weight percent accounts for 45%, and solid propenoic acid weight percent accounts for 23%, antistatic agent weight
Percentage accounts for 2.5%.
The weaving process is to be weaved using the complex yarn after sizing with scale water jet loom, the main jet time 57
Degree, speed 250n/min, the temperature of weaving rooms: 19 DEG C, relative humidity 57%.
The dyeing is, the polyester fiber fabric weaved selection overflow cylinder is dyed, control cloth with
The weight ratio of water is 1:12, and dyeing liquor is that acetic acid 0.5g/L, levelling agent 0.6g/L are added in water, and with detergent 2.5g/L, HAC
Auxiliary agent 1.5g/L, color fixing agent 1.3g/L.
The softening technique is that the fabric after first being dyed with degreaser is cleaned, and after cleaning, controls cloth and water
Weight ratio is 1:17, and softening liquid is that acetic acid 0.25g/L, silicone oil emulsion 3.5g/L are added in water.
The setting process is to carry out carrying out shaping the fabric after softening processing by forming machine, and speed control exists
45 yards/minute, setting temperature is between 139 DEG C.
The calen-dering process is that the calendering in calender by fabric cloth controls the pressure of the upper lower compression roller of calender
For 17Mpa, speed 16m/min.
It is obvious to a person skilled in the art that invention is not limited to the details of the above exemplary embodiments, Er Qie
In the case where without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power
Benefit requires rather than above description limits, it is intended that all by what is fallen within the meaning and scope of the equivalent elements of the claims
Variation is included within the present invention.Any reference signs in the claims should not be construed as limiting the involved claims.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiments being understood that.
Claims (8)
1. a kind of regenerated polyester fiber fabric, including warp thread (1) and weft yarn (2), it is characterised in that: the warp thread (1) and weft yarn
(2) it uniformly wears and is woven with oblique yarn (3) in, the oblique yarn (3) is relatively 45 degree with the tilt angle of warp thread (1) and weft yarn (2), described
Warp thread (1), weft yarn (2) and oblique yarn (3) use identical complex yarn, complex yarn by regenerated polyester fiber (4), non-renewable wash
Synthetic fibre fiber (5), ramee (6), cotton fiber (7) and viscose rayon (8) are mixed.
2. a kind of regenerated polyester fiber fabric production technology, which is characterized in that successively include warping, sizing, weaving, dyeing, soft
Change, setting and calendering step, the warping technology are, by regenerated polyester fiber (4), non-renewable polyester fiber (5), ramie
Fiber (6), cotton fiber (7) and viscose rayon (8) are spun into the complex yarn of compact form, warping speed 200-300m/min, yarn
Density 200-250g/dm3。
3. a kind of regenerated polyester fiber fabric production technology according to claim 2, which is characterized in that the sizing work
Skill is to be wound complex yarn on sizing machine, and slurry accounts for 10%-20%, phosphoric acid using polyvinyl alcohol weight percentage
Ester starch weight percentage accounts for 40%-50%, and solid propenoic acid weight percent accounts for 20%-25%, antistatic agent weight percent
Than accounting for 2%-3%.
4. a kind of regenerated polyester fiber fabric production technology according to claim 3, which is characterized in that the weaving work
Skill is to be weaved using the complex yarn after sizing with scale water jet loom, and main jet time 55-60 degree, speed 250n/min is knitted
Make the temperature in workshop: 18-27 DEG C, relative humidity 50-60%.
5. a kind of regenerated polyester fiber fabric production technology according to claim 4, which is characterized in that the dyer
Skill is to dye the polyester fiber fabric weaved selection overflow cylinder, and the weight ratio for controlling cloth and water is 1:10-15,
Dyeing liquor is that acetic acid 0.4-0.6g/L, levelling agent 0.5-0.8g/L are added in water, and with detergent 2-3g/L, HAC auxiliary agent 1-2g/
L, color fixing agent 1-1.5g/L.
6. a kind of regenerated polyester fiber fabric production technology according to claim 5, which is characterized in that the softening work
Skill is that the fabric after first being dyed with degreaser is cleaned, and after cleaning, the weight ratio for controlling cloth and water is 1:15-20, softening
Liquid is that acetic acid 0.2-0.3g/L, silicone oil emulsion 3-4g/L are added in water.
7. a kind of regenerated polyester fiber fabric production technology according to claim 6, which is characterized in that the setting work
Skill is to carry out carrying out shaping the fabric after softening processing by forming machine, and speed is controlled in 45 yards/minute, and setting temperature exists
Between 135 DEG C -145 DEG C.
8. a kind of regenerated polyester fiber fabric production technology according to claim 7, which is characterized in that the calendering work
Skill is the calendering in calender by fabric cloth, and the pressure for controlling the upper lower compression roller of calender is 15-18Mpa, speed 14-
17m/min。