CN1101025A - Glazed porcelain - Google Patents
Glazed porcelain Download PDFInfo
- Publication number
- CN1101025A CN1101025A CN 93102363 CN93102363A CN1101025A CN 1101025 A CN1101025 A CN 1101025A CN 93102363 CN93102363 CN 93102363 CN 93102363 A CN93102363 A CN 93102363A CN 1101025 A CN1101025 A CN 1101025A
- Authority
- CN
- China
- Prior art keywords
- glaze
- porcelain
- dioxide
- kaolin
- glazed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a ceramic process technology.
The invention provides a glazed porcelain: the porcelain body has bright color under the glaze, the glaze surface is transparent and crystal-clear, and the effect of the flowing glaze causes the artistic charm like 'honey transformation', has both metallic luster and glass luster, and can be in the shape of an archaizing model and a modern model. Can be used as modern decoration and can beautify the artistic valuables in hotels and homes. And is fired at one time. The energy-saving effect is obvious. The invention is widely applied to daily-use porcelain, furnishing porcelain, craft gift porcelain and building garden porcelain. The invention is realized as follows: the formula and the process flow of the underglaze color running glaze, the formula and the process flow of the glaze color running glaze; a one-time sintering system and a product process flow.
Description
The present invention relates to the ceramic technology field, particularly relate to a kind of novel glazed porcelain technology.
Glazed porcelain is the product that new technology and process of decorating combine.Glazed porcelain is a kind of soft-paste, and blank utilizes local raw material, and glaze adopts unique formula.Decoration is selected secondary color decoration technology under a kind of glaze for use, utilizes sagging to make ground-coat enamel, carries out technology processing colored drawing, uses mechanical aerograph cover-coat enamel then.Product once-firing, but save energy 30%, it is extensive to can be made into product scope: household china, display china, process gift porcelain, garden architecture porcelain etc.
The objective of the invention is to formulate under the glaze bright in luster, deep or light clearly demarcated, glaze is transparent sparkling and crystal-clear, gorgeous, and once-firing, the glazed porcelain of obvious energy conservation and novel process thereof.
The present invention is achieved in that
1, utilize various different materials, press following prescription:
Opaque glaze: tri-lead tetroxide 58%, silicon-dioxide 24%, zinc oxide 3%, titanium dioxide 3%, tindioxide 5%, kaolin 7%.
Green glaze: tri-lead tetroxide 58%, silicon-dioxide 25%, cupric oxide 5%, kaolin 7%, oxygenant 5%.
Yellow glaze: tri-lead tetroxide 58%, silicon-dioxide 24%, ferric oxide 10%, kaolin 7%.
Black glaze: tri-lead tetroxide 60.5%, silicon-dioxide 25.8%, cupric oxide 3.6%, Manganse Dioxide 2.1%, kaolin 7%.
And technical process:
Carry out a series of technology processing, products therefrom as ground-coat enamel, manually carries out under glazed and paints with sagging as sagging.
2, utilize various mineral substance, press following prescription:
Feldspar 53%, quartz 21%, marble 12%, kaolin 7% burns talcum 4%, zinc oxide 3%.
Carry out ball milling with ball mill, products therefrom adopts mechanical aerograph to carry out the glaze colored drawing as cover-coat enamel.
3, through the porcelain base of under glazed and glaze aerograph,, determine different calcining systems according to different composition of raw materials, Chemical Composition, furnace construction.The present invention confirms: adopt oxidizing atmosphere, once-firing, firing temperature are for 1080 ℃-1120 ℃ to guarantee the best best calcining system of glazed porcelain product effect.
The characteristic effect that the present invention reaches: glazed porcelain adopts the once-firing system, and energy-saving effect is remarkable, and product gets final product type modelled after an antique, again can modern type.Be Modern Decorative, beautify the gem of art of hotel, household.
The present invention is further illustrated below in conjunction with accompanying drawing:
Accompanying drawing is the process implementing axonometric drawing of glazed porcelain of the present invention-drum chair, and its manufacturing processed now is described:
1, design drum chair model
2, base mud prescription is made
3, injection forming: base substrate requires dry, and promptly " free water " got rid of clean.
4, glazing technology step: (1) earlier is coated with (representing with A) earlier with the black ground-coat enamel of the writing brush libation at an ancient wedding ceremony as figure, decides layout and carries out colored drawing by giving, and milky white ground-coat enamel is modified at last comprehensively on " A " blank space in addition then, finishes the work of ground-coat enamel colored drawing.(2) spray plane glaze utilizes the pressure of air compressor to load onto varnish spray gun and carries out the spray plane glaze.
5, burn till: burn till with 1080 ℃~1120 ℃ with oxydizing flame.Calcining system, temperature and the effect and the color-painting method of joining glaze must carry out in strict accordance with pre-provisioning request, could guarantee the goods glaze is fluidized to natural beautiful pattern.
Claims (3)
1, a kind of glazed porcelain: bright in luster under the porcelain body glaze, glaze is transparent sparkling and crystal-clear.Its feature is at the prescription of glazed porcelain under glazed:
Opaque glaze: tri-lead tetroxide 58%, silicon-dioxide 24%, zinc oxide 3%,
Titanium dioxide 3%, tindioxide 5%, kaolin 7%.
Green glaze: tri-lead tetroxide 58%, silicon-dioxide 25%, cupric oxide 5%, kaolin 7%, oxygenant 5%.
Yellow glaze: tri-lead tetroxide 58%, silicon-dioxide 24%, ferric oxide 10%, kaolin 8%.
Black glaze: tri-lead tetroxide 60.5%, silicon-dioxide 25.8%,
Cupric oxide 3.6%, Manganse Dioxide 2.1%, kaolin 7%.
2, by the described glazed porcelain of claim 1: the prescription that it is characterized in that the glazed porcelain overglaze decoration:
The quartzy marble kaolin of raw material feldspar burns the talcum oxygenant
Composition %:53 21 12 743
3, by the described glazed porcelain of claim 1: it is characterized in that the once-firing system: firing atmosphere system uses oxidizing atmosphere, temperature to be controlled at 1080 ℃~1120 ℃.