CN109849546B - 一种烫印图文抗氧化型电化铝烫印箔 - Google Patents
一种烫印图文抗氧化型电化铝烫印箔 Download PDFInfo
- Publication number
- CN109849546B CN109849546B CN201711440194.7A CN201711440194A CN109849546B CN 109849546 B CN109849546 B CN 109849546B CN 201711440194 A CN201711440194 A CN 201711440194A CN 109849546 B CN109849546 B CN 109849546B
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- coating
- hot stamping
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种烫印图文抗氧化型电化铝烫印箔，其可解决现有电化铝烫印箔在薄纸表面烫印后，烫印图文容易出现氧化性腐蚀现象这一问题。其技术方案要点是：以水性热塑性马来松香树脂、蒙丹蜡、热固性丙烯酸树脂、苯酚、乙醇、水为原料复配成剥离料；以酚醛改性丙烯酸酯、聚酰胺树脂、改性乙烯树脂、乙基羟乙基纤维素、染料、环烷酸锌皂、混合溶剂为原料复配成色料；以苯乙烯‑马来酸酐共聚物、改性PU、异氰酸酯、混合溶剂为原料复配成阻隔层涂料；以聚丙烯酸酯、松香改性烷基酚醛树脂、硝酸纤维素、邻苯二酚、成膜助剂、混合溶剂复配成胶料；依次经过涂布剥离料、涂布色料、真空镀铝、涂布阻隔层涂料、涂布胶料生产制得。产品具有：烫印图文精美、烫印图文抗氧化耐腐蚀的特点。
Description
技术领域
本发明涉及的是一种烫印图文抗氧化型电化铝烫印箔，属于涂布印刷技术领域。
背景技术
电化铝烫印箔作为一种新型的包装印刷材料，以其使用简便、图文精美、具备金属质感等诸多优点，使用范围不断扩大，然而由于生产工艺和技术的限制，常规电化铝烫印箔烫印在一些纸类基材表面后，烫印图文受环境以及纸类表面油墨等因素作用，容易出现不同程度氧化腐蚀现象，影响外观效果。
发明内容
本发明的目的在于克服现有技术存在的不足，而提供一种烫印图文精美、烫印图文抗氧化耐腐蚀的一种烫印图文抗氧化型电化铝烫印箔。
为了实现上述目的，本发明采用的技术方案是：一种烫印图文抗氧化型电化铝烫印箔，其特征在于：它至少包括一层BOPET薄膜基材，BOPET薄膜基材上依次涂布剥离料、色料；经真空镀铝后，再在铝层上涂布阻隔层涂料和胶料生产制得。
所述的剥离料是有5-15重量份水性热塑性马来松香树脂、1-10重量份蒙丹蜡、2-8重量份水性热固性丙烯酸树脂、0.2-1重量份苯酚、35-60重量份乙醇、30-50重量份水复配而成。
所述的色料是有5-20重量份酚醛改性丙烯酸酯、5-15重量份聚酰胺树脂、3-10重量份改性乙烯树脂、2-10重量份乙基羟乙基纤维素、2-10重量份染料、0.3-2重量份环烷酸锌皂、80-160重量份混合溶剂复配而成。
所述的阻隔层涂料是有5-30重量份苯乙烯-马来酸酐共聚物、5-10重量份改性PU、1-10重量份异氰酸酯、50-150重量份混合溶剂复配而成。
所述的胶料是有5-30重量份聚丙烯酸酯、2-20重量份松香改性烷基酚醛树脂、3-15重量份硝酸纤维素、0.5-2重量份邻苯二酚、0.2-2重量份成膜助剂、50-200重量份混合溶剂复配而成。
本发明与现有技术相比，具有烫印图文精美、烫印图文抗氧化耐腐蚀的特点。
具体实施方式
下面将结合具体实施例对本发明作详细的介绍：本发明所述的一种烫印图文抗氧化型电化铝烫印箔，其特征在于：它至少包括一层BOPET薄膜基材，BOPET薄膜基材上依次涂布剥离料、色料；经真空镀铝后，再在铝层上涂布阻隔层涂料和胶料生产制得。
实施例1
原料复配：将15重量份水性热塑性马来松香树脂、1重量份蒙丹蜡、2重量份水性热固性丙烯酸树脂、0.5重量份苯酚、60重量份乙醇、50重量份水复配成剥离料；将20重量份酚醛改性丙烯酸酯、5重量份聚酰胺树脂、3重量份改性乙烯树脂、5重量份乙基羟乙基纤维素、10重量份染料、2重量份环烷酸锌皂、150重量份混合溶剂复配成色料；将30重量份苯乙烯-马来酸酐共聚物、5重量份改性PU、2重量份异氰酸酯、150重量份混合溶剂复配成阻隔层涂料；将30重量份聚丙烯酸酯、5重量份松香改性烷基酚醛树脂、5重量份硝酸纤维素、0.5重量份邻苯二酚、0.5重量份成膜助剂、160重量份混合溶剂复配成胶料。
涂布、镀铝工序：
(1)、剥离料涂布：使用涂布机，采用180目网辊将剥离料涂布在BOPET薄膜基材表面，设定烘道温度90、130、165、165、135℃，车速110m/min，不使用均平辊；
(2)、色料涂布：使用涂布机，采用220目网辊将色料涂布到剥离料层表面，设定烘道温度85、135、175、165、135℃，车速130m/min，不使用均平辊，色料干涂量控制1.15～1.5g/m2；
(3)、真空镀铝：使用真空镀铝机，选用高纯铝丝为原料，将铝蒸汽均匀蒸镀到色料层表面，控制镀铝层在550～650埃之间；
(4)、阻隔层涂布：使用涂布机，采用260目网辊将阻隔层涂料涂布到真空镀铝层表面，设定烘道温度85、135、175、175、150℃，车速110m/min，不使用均平辊，控制干涂量0.7～0.85g/m2；
(5)、胶料涂布：使用涂布机，采用180目网辊将胶料涂布到阻隔层表面，设定烘道温度80、115、150、150、125℃，车速100m/min，使用均平辊，设定均平辊转速30～50转/分钟，控制干涂量1.1～1.25g/m2。
实施例2
原料复配：将5重量份水性热塑性马来松香树脂、10重量份蒙丹蜡、8重量份水性热固性丙烯酸树脂、0.8重量份苯酚、35重量份乙醇、30重量份水复配成剥离料；将5重量份酚醛改性丙烯酸酯、10重量份聚酰胺树脂、5重量份改性乙烯树脂、10重量份乙基羟乙基纤维素、2重量份染料、0.5重量份环烷酸锌皂、100重量份混合溶剂复配成色料；将5重量份苯乙烯-马来酸酐共聚物、10重量份改性PU、6重量份异氰酸酯、100重量份混合溶剂复配成阻隔层涂料；将10重量份聚丙烯酸酯、20重量份松香改性烷基酚醛树脂、10重量份硝酸纤维素、2重量份邻苯二酚、1重量份成膜助剂、200重量份混合溶剂复配成胶料。
涂布、镀铝工序：
(1)、剥离料涂布：使用涂布机，采用180目网辊将剥离料涂布在BOPET薄膜基材表面，设定烘道温度80、130、160、155、130℃，车速90m/min，不使用均平辊；
(2)、色料涂布：使用涂布机，采用220目网辊将色料涂布到剥离料层表面，设定烘道温度80、130、165、160、135℃，车速100m/min，不使用均平辊，色料干涂量控制1.15～1.5g/m2；
(3)、真空镀铝：使用真空镀铝机，选用高纯铝丝为原料，将铝蒸汽均匀蒸镀到色料层表面，控制镀铝层在550～650埃之间；
(4)、阻隔层涂布：使用涂布机，采用260目网辊将阻隔层涂料涂布到真空镀铝层表面，设定烘道温度85、135、175、175、150℃，车速110m/min，不使用均平辊，控制干涂量0.7～0.85g/m2；
(5)、胶料涂布：使用涂布机，采用180目网辊将胶料涂布到阻隔层表面，设定烘道温度80、115、155、150、125℃，车速110m/min，使用均平辊，设定均平辊转速30～50转/分钟，控制干涂量1.0～1.2g/m2。
Claims (4)
1.一种烫印图文抗氧化型电化铝烫印箔，其特征在于：它至少包括一层BOPET薄膜基材，BOPET薄膜基材上依次涂布剥离料、色料；经真空镀铝后，再在铝层上涂布阻隔层涂料和胶料生产制得，所述的阻隔层涂料是由5-30重量份苯乙烯-马来酸酐共聚物、5-10重量份改性PU、1-10重量份异氰酸酯、50-150重量份混合溶剂复配而成，所述阻隔层由涂布机涂布在铝层上，且涂布机的烘道温度85、135、175、175、150℃。
2.根据权利要求1所述的一种烫印图文抗氧化型电化铝烫印箔，其特征是所述的剥离料是由5-15重量份水性热塑性马来松香树脂、1-10重量份蒙丹蜡、2-8重量份水性热固性丙烯酸树脂、0.2-1重量份苯酚、35-60重量份乙醇、30-50重量份水复配而成。
3.根据权利要求1所述的一种烫印图文抗氧化型电化铝烫印箔，其特征是所述的色料是由5-20重量份酚醛改性丙烯酸酯、5-15重量份聚酰胺树脂、3-10重量份改性乙烯树脂、2-10重量份乙基羟乙基纤维素、2-10重量份染料、0.3-2重量份环烷酸锌皂、80-160重量份混合溶剂复配而成。
4.根据权利要求1所述的一种烫印图文抗氧化型电化铝烫印箔，其特征是所述的胶料是由5-30重量份聚丙烯酸酯、2-20重量份松香改性烷基酚醛树脂、3-15重量份硝酸纤维素、0.5-2重量份邻苯二酚、0.2-2重量份成膜助剂、50-200重量份混合溶剂复配而成。