CN109504206A - A kind of antifog glass and its processing technology - Google Patents
A kind of antifog glass and its processing technology Download PDFInfo
- Publication number
- CN109504206A CN109504206A CN201811163483.1A CN201811163483A CN109504206A CN 109504206 A CN109504206 A CN 109504206A CN 201811163483 A CN201811163483 A CN 201811163483A CN 109504206 A CN109504206 A CN 109504206A
- Authority
- CN
- China
- Prior art keywords
- parts
- glass
- agent
- antifog
- antifogging coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of antifog glass and its processing technologys, including glass body;Hydrophilic antifogging coating is coated on glass body, the hydrophilic antifogging coating is the component containing following parts by weight: 40~50 parts of modified acrylic acid emulsion, 1~5 part of nano silica, 5~10 parts of dispersing agent, 5~10 parts of defoaming agent, 10~15 parts of waterborne curing agent, 0.5~1 part of photoinitiator, 5~10 parts of cosolvent, 5~10 parts of conductive agent, 3~7 parts of surfactant, surplus is water;The present invention passes through scientific matching, optimization technique, so that the antifog persistence of the antifog glass produced, more practical and convenient.The transparency of final glassware can be suitable with original glass simultaneously, and the light transmittance at 550nm wavelength is greater than 85%, to not influence the optical property and its application range of glass itself.
Description
Technical field
The invention belongs to glass technology fields, and in particular to a kind of antifog glass and its processing technology.
Background technique
With the increasingly raising of people 's material life level, people's bath product clean to shower house etc. proposes requirements at the higher level,
People, which start this traditional life-form structure of having a bath gradually to develop into, intension, has health care, health, leisure
Etc. functions, and then improve the pursuit to actual life.
Shower house is a kind of daily necessities for bathing of taking a shower, the raising of people's quality of life and to daily necessity
Higher requirement and the requirement of environmental pollution and new material application;Glass is the transparent semisolid of one kind, semiliquid object
Matter, forms contiguous network structure in melting, and cooling procedure medium viscosity is gradually increased and hardens and non crystallized silicates are non-
Metal material.The main component of simple glass is silica, it have very high chemical stability, thermal stability and well
Transparency is therefore widely used in every field.
During people take a shower, temperature increases existing shower room glass, and when air humidity reaches certain value,
Fog will be generated on glass, reducing transparency influences sight, brings inconvenience to using.
In view of the above technical problems, it therefore needs to improve.
Summary of the invention
The present invention is to provide a kind of antifog glass and its processing work to overcome above-mentioned defect in the prior art
Skill.
To achieve the above object, the technical scheme adopted by the invention is that: a kind of antifog glass, including glass body;Glass
Hydrophilic antifogging coating is coated on glass ontology, the hydrophilic antifogging coating is the component containing following parts by weight: modified acroleic acid
40~50 parts of lotion, 1~5 part of nano silica, 5~10 parts of dispersing agent, 5~10 parts of defoaming agent, waterborne curing agent 10~15
Part, 0.5~1 part of photoinitiator, 5~10 parts of cosolvent, 5~10 parts of conductive agent, 3~7 parts of surfactant, surplus is water.
As a preferred solution of the present invention, the hydrophilic antifogging coating is the component containing following parts by weight: modified
40 parts of acrylic emulsion, 1 part of nano silica, 5 parts of dispersing agent, 5 parts of defoaming agent, 10 parts of waterborne curing agent, photoinitiator 0.5
Part, 5 parts of cosolvent, 5 parts of conductive agent, 3 parts of surfactant, surplus is water.
As a preferred solution of the present invention, the hydrophilic antifogging coating is the component containing following parts by weight: modified
50 parts of acrylic emulsion, 5 parts of nano silica, 10 parts of dispersing agent, 10 parts of defoaming agent, 15 parts of waterborne curing agent, photoinitiator 1
Part, 10 parts of cosolvent, 10 parts of conductive agent, 7 parts of surfactant, surplus is water.
As a preferred solution of the present invention, the surfactant is neopelex.
As a preferred solution of the present invention, the modified acrylic acid emulsion be polyacrylic acid, it is polyvinyl alcohol, aqueous poly-
One of urethane, ethylhydroxyethylcellulose, carbomer are a variety of.
As a preferred solution of the present invention, the waterborne curing agent is aziridine crosslinker, diazomethane, maleic acid
One of acid anhydride, carbodiimides, vinyl sulfone are a variety of.
A kind of processing technology of antifog glass, includes the following steps:
Step a: clean glass body is taken;Purified treatment is carried out to the glass;
Step b: hydrophilic antifogging coating is coated on the glass after purified treatment;
Step c: the glass in step b being placed in drying oven and carries out curing and drying, finally carries out crosslinking Treatment;It obtains antifog
Glass.
As a preferred solution of the present invention, the hydrophilic antifogging coating can pass through the side of dip-coating, spin coating or spraying
Formula is coated in pretreated glass surface.
As a preferred solution of the present invention, in the step c, the drying temperature in drying oven is 20~40 DEG C.
As a preferred solution of the present invention, in the step c, the cured time is 15~25 minutes.
Compared with prior art, the beneficial effects of the present invention are: the present invention passes through scientific matching, optimization technique, so that raw
The antifog persistence of antifog glass that output is come, it is more practical and convenient.The transparency of final glassware can be with original glass simultaneously
Glass is suitable, and the light transmittance at 550nm wavelength is greater than 85%, to not influence the optical property of glass itself and its using model
It encloses.
Specific embodiment
It elaborates below to the embodiment of the present invention.
Embodiment 1, a kind of antifog glass, including glass body;Hydrophilic antifogging coating is coated on glass body, it is hydrophilic anti-
Mist coating is the component containing following parts by weight: 40 parts of modified acrylic acid emulsion, 1 part of nano silica, 5 parts of dispersing agent, being disappeared
5 parts of infusion, 10 parts of waterborne curing agent, 0.5 part of photoinitiator, 5 parts of cosolvent, 5 parts of conductive agent, 3 parts of surfactant, surplus is
Water.
Surfactant is neopelex.
Modified acrylic acid emulsion is polyacrylic acid, polyvinyl alcohol, aqueous polyurethane, ethylhydroxyethylcellulose, carbomer
One of or it is a variety of.
Waterborne curing agent is aziridine crosslinker, diazomethane, maleic anhydride, carbodiimides, one in vinyl sulfone
Kind is a variety of.
A kind of processing technology of antifog glass, includes the following steps:
Step a: clean glass body is taken;Purified treatment is carried out to the glass;Hydrophilic antifogging coating can pass through dip-coating, rotation
It applies or the mode of spraying is coated in pretreated glass surface.
Step b: hydrophilic antifogging coating is coated on the glass after purified treatment;
Step c: the glass in step b being placed in drying oven and carries out curing and drying, the drying temperature in drying oven be 20~
40 DEG C, the cured time is 15~25 minutes.Finally carry out crosslinking Treatment;Obtain antifog glass.
Embodiment 2,
A kind of antifog glass, including glass body;Be coated with hydrophilic antifogging coating on glass body, hydrophilic antifogging coating be containing
The component of following parts by weight: 50 parts of modified acrylic acid emulsion, 5 parts of nano silica, 10 parts of dispersing agent, 10 parts of defoaming agent, water
15 parts of curing agent of property, 1 part of photoinitiator, 10 parts of cosolvent, 10 parts of conductive agent, 7 parts of surfactant, surplus is water.
Embodiment 3,
A kind of antifog glass, including glass body;Be coated with hydrophilic antifogging coating on glass body, hydrophilic antifogging coating be containing
The component of following parts by weight: 45 parts of modified acrylic acid emulsion, 2 parts of nano silica, 7 parts of dispersing agent, 7 parts of defoaming agent, aqueous
11 parts of curing agent, 0.8 part of photoinitiator, 7 parts of cosolvent, 8 parts of conductive agent, 4 parts of surfactant, surplus is water.
Embodiment 4,
A kind of antifog glass, including glass body;Be coated with hydrophilic antifogging coating on glass body, hydrophilic antifogging coating be containing
The component of following parts by weight: 46 parts of modified acrylic acid emulsion, 2 parts of nano silica, 6 parts of dispersing agent, 8 parts of defoaming agent, aqueous
10 parts of curing agent, 0.5 part of photoinitiator, 6 parts of cosolvent, 6 parts of conductive agent, 3 parts of surfactant, surplus is water.
Embodiment 5,
A kind of antifog glass, including glass body;Be coated with hydrophilic antifogging coating on glass body, hydrophilic antifogging coating be containing
The component of following parts by weight: 44 parts of modified acrylic acid emulsion, 2 parts of nano silica, 10 parts of dispersing agent, 10 parts of defoaming agent, water
14 parts of curing agent of property, 0.8 part of photoinitiator, 7 parts of cosolvent, 7 parts of conductive agent, 7 parts of surfactant, surplus is water.
Embodiment 6,
A kind of antifog glass, including glass body;Be coated with hydrophilic antifogging coating on glass body, hydrophilic antifogging coating be containing
The component of following parts by weight: 50 parts of modified acrylic acid emulsion, 4 parts of nano silica, 9 parts of dispersing agent, 9 parts of defoaming agent, aqueous
12 parts of curing agent, 0.8 part of photoinitiator, 8 parts of cosolvent, 8 parts of conductive agent, 7 parts of surfactant, surplus is water.
The foregoing description of the disclosed embodiments enables those skilled in the art to implement or use the present invention.
Various modifications to these embodiments will be readily apparent to those skilled in the art, as defined herein
General Principle can be realized in other embodiments without departing from the spirit or scope of the present invention;Therefore, of the invention
It is not intended to be limited to the embodiments shown herein, and is to fit to and the principles and novel features disclosed herein phase one
The widest scope of cause.
Claims (10)
1. a kind of antifog glass, it is characterised in that: including glass body;Hydrophilic antifogging coating is coated on glass body, it is described
Hydrophilic antifogging coating is the component containing following parts by weight: 40~50 parts of modified acrylic acid emulsion, 1~5 part of nano silica,
5~10 parts of dispersing agent, 5~10 parts of defoaming agent, 10~15 parts of waterborne curing agent, 0.5~1 part of photoinitiator, cosolvent 5~10
Part, 5~10 parts of conductive agent, 3~7 parts of surfactant, surplus is water.
2. a kind of antifog glass according to claim 1, it is characterised in that: the hydrophilic antifogging coating is containing following weight
The component of amount part: 40 parts of modified acrylic acid emulsion, 1 part of nano silica, 5 parts of dispersing agent, 5 parts of defoaming agent, waterborne curing agent
10 parts, 0.5 part of photoinitiator, 5 parts of cosolvent, 5 parts of conductive agent, 3 parts of surfactant, surplus is water.
3. a kind of antifog glass according to claim 1, it is characterised in that: the hydrophilic antifogging coating is containing following weight
Measure the component of part: 50 parts of modified acrylic acid emulsion, 5 parts of nano silica, 10 parts of dispersing agent, 10 parts of defoaming agent, aqueous solidified
15 parts of agent, 1 part of photoinitiator, 10 parts of cosolvent, 10 parts of conductive agent, 7 parts of surfactant, surplus is water.
4. a kind of antifog glass according to claim 1, it is characterised in that: the surfactant is detergent alkylate sulphur
Sour sodium.
5. a kind of antifog glass according to claim 1, it is characterised in that: the modified acrylic acid emulsion is polypropylene
One of acid, polyvinyl alcohol, aqueous polyurethane, ethylhydroxyethylcellulose, carbomer are a variety of.
6. a kind of antifog glass according to claim 1, it is characterised in that: the waterborne curing agent is aziridine crosslinking
One of agent, diazomethane, maleic anhydride, carbodiimides, vinyl sulfone are a variety of.
7. a kind of processing technology of antifog glass described in claim 1, characterized by the following steps:
Step a: clean glass body is taken;Purified treatment is carried out to the glass;
Step b: hydrophilic antifogging coating is coated on the glass after purified treatment;
Step c: the glass in step b being placed in drying oven and carries out curing and drying, finally carries out crosslinking Treatment;It obtains antifog
Glass.
8. a kind of processing technology of antifog glass according to claim 7, it is characterised in that: the hydrophilic antifogging coating
Pretreated glass surface can be coated in by way of dip-coating, spin coating or spraying.
9. a kind of processing technology of antifog glass according to claim 7, it is characterised in that: in the step c, drying oven
In drying temperature be 20~40 DEG C.
10. a kind of processing technology of antifog glass according to claim 7, it is characterised in that: in the step c, solidification
Time be 15~25 minutes.