CN107603354A - A kind of water-based reflectorized paint of exterior wall cooling - Google Patents
A kind of water-based reflectorized paint of exterior wall cooling Download PDFInfo
- Publication number
- CN107603354A CN107603354A CN201710935806.3A CN201710935806A CN107603354A CN 107603354 A CN107603354 A CN 107603354A CN 201710935806 A CN201710935806 A CN 201710935806A CN 107603354 A CN107603354 A CN 107603354A
- Authority
- CN
- China
- Prior art keywords
- mass parts
- water
- paint
- exterior wall
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of water-based reflectorized paint of exterior wall cooling, including following raw material and weight fraction：The mass parts of water 200~300；Antifreeze is 8~15 mass parts；Dispersant is 3~5 mass parts；Wetting agent is 1~3 mass parts；Defoamer is 1~3 mass parts；Preservative is 1~3 mass parts；Rutile titania titanium white is 30~50 mass parts；Kaolin is 50~80 mass parts；Coarse whiting is 150~200 mass parts；Fine particle calcium carbonate is 50~100 mass parts；Talcum powder is 50~100 mass parts；Coalescents are 3~5 mass parts；Thickener is 100~150 mass parts, styrene-acrylic emulsion is 80~100 mass parts, ultra micron glass dust is 10~20 mass parts and sunshade thermal insulation painting feed powder is 20~30 mass parts.Add ultra micron glass dust in present invention paint, when light is irradiated to bead surface, due to microballon high refraction action and optically focused and will not produce dazzle on the special reflecting layer of microballon focus, form good regression reflecting effect.
Description
Technical field
The present invention relates to aqueous paint preparing technical field, the especially a kind of water-based reflectorized paint of exterior wall cooling.
Background technology
With water as solvent, ample resources is saved；Fire risk when eliminating construction；Reduce to atmosphere pollution；Only adopt
With a small amount of hypotoxicity alcohol ethers organic solvent, operating environmental condition is improved.In general water paint organic solvent (accounting for coating)
Between 5%~15%, and cathode electrophoresis dope is reduced to less than 1.2%, notable to reducing pollution saving resource impact.
Traditional water-based reflectorized paint effectively can not be reflected sunshine so that sunshine is radiated on wall
Afterwards, interior is transferred heat to by wall, and then improves indoor temperature, and traditional water-based reflectorized paint can not be effective
Play a part of sunshade thermal insulation, after the paint long-time use on exterior wall, can natural aging, come off, enter from outer wall body
And improve the cost of External Wall wall plastering again.
The content of the invention
The present invention is for technical deficiencies such as existing preventing and treating Chinese medicine for treating diabetes formulas, there is provided a kind of exterior wall temperature lowering water
Property reflectorized paint.
The present invention, using modified technical scheme, specifically includes following raw material and weight point to solve above-mentioned technical deficiency
Number：The mass parts of water 200~300；Antifreeze is 8~15 mass parts；Dispersant is 3~5 mass parts；Wetting agent is 1~3 mass
Part；Defoamer is 1~3 mass parts；Preservative is 1~3 mass parts；Rutile titania titanium white is 30~50 mass parts；Kaolin be 50~
80 mass parts；Coarse whiting is 150~200 mass parts；Fine particle calcium carbonate is 50~100 mass parts；Talcum powder is 50~100 mass parts；Film forming
Auxiliary agent is 3~5 mass parts；Thickener is 100~150 mass parts, styrene-acrylic emulsion is 80~100 mass parts, ultra micron glass dust
It is 20~30 mass parts to apply feed powder for 10~20 mass parts and sunshade thermal insulation.
As a kind of preferred embodiment of the present invention, including following raw material and weight fraction：The mass parts of water 300；It is freeze proof
Agent is 5 mass parts；Dispersant is 5 mass parts；Wetting agent is 3 mass parts；Defoamer is 3 mass parts；Preservative is 3 mass parts；
Rutile titania titanium white is 50 mass parts；Kaolin is 80 mass parts；Coarse whiting is 200 mass parts；Fine particle calcium carbonate is 100 mass parts；Talcum powder is
100 mass parts；Coalescents are 5 mass parts；Thickener is 150 mass parts, styrene-acrylic emulsion is 100 mass parts, ultra micron glass
Powder is 20 mass parts and sunshade thermal insulation painting feed powder is 20 mass parts.
As a kind of preferred embodiment of the present invention, including following raw material and weight fraction：The mass parts of water 200；It is freeze proof
Agent is 5 mass parts；Dispersant is 5 mass parts；Wetting agent is 3 mass parts；Defoamer is 3 mass parts；Preservative is 3 mass parts；
Rutile titania titanium white is 50 mass parts；Kaolin is 80 mass parts；Coarse whiting is 200 mass parts；Fine particle calcium carbonate is 100 mass parts；Talcum powder is
100 mass parts；Coalescents are 5 mass parts；Thickener is 150 mass parts, styrene-acrylic emulsion is 100 mass parts, ultra micron glass
Powder is 10 mass parts and sunshade thermal insulation painting feed powder is 30 mass parts.
It is as follows as a kind of preferred embodiment of the present invention, manufacturing process steps：
A. above-mentioned raw materials are weighed according to parts by weight, put into after weighing in agitator, ceaselessly stirred with mixer, separately
Outer preparation putty and the water-based alkali-resistant sealing primers of Ya Shi；
B. basal plane flattens：With the slit and aperture of external wall special putty repairing metope, batch scrape until basic unit is smooth, batch
Scrape putty to be at least spaced 12 hours, must be maintained 3-5 days before priming, to reach suitable strength, the work after use
Tool is cleaned up with clear water；
C. roller coating priming paint：Using the water-based alkali-resistant sealing primer of sub- scholar, during construction generally need not dilution, can when construction is not easy
Pure water or deionized water are added, and is stirred, form of construction work can use the construction technology requirement of rolling, spray, brush equal
It is even unanimously, without leakage brush, without accumulation, instrument to be cleaned up using rear with clear water；
D. roller coating finish paint：Rolling, spray can be used, dataller's skill External Wall be constructed, it is desirable to uniformity, without leakage brush, without heap
Product；Repainting time is at least spaced 8 hours, and after maintaining about 5 days, complete film forming simultaneously reaches best adhesion state, after instrument use
Cleaned up immediately with clear water.
As a kind of preferred embodiment of the present invention, paint is during brushing described in step d, in agitator domestic demand
Ceaselessly to stir, in order to avoid reflective powder precipitates, cause reflective uneven.
The beneficial effect that is reached of the present invention is：The present invention adds ultra micron glass dust in paint, when light is irradiated to
During bead surface, due to microballon high refraction action and optically focused and will not be produced dizzy on the special reflecting layer of microballon focus
Light, form good regression reflecting effect；Sunshade thermal insulation is added in paint and applies feed powder, increases wall heat-proof quality, so it is right
Interior is cooled.
Embodiment
A kind of water-based reflectorized paint of exterior wall cooling, including following raw material and weight fraction：The mass parts of water 200~300；It is anti-
Jelly agent is 8~15 mass parts；Dispersant is 3~5 mass parts；Wetting agent is 1~3 mass parts；Defoamer is 1~3 mass parts；It is anti-
Rotten agent is 1~3 mass parts；Rutile titania titanium white is 30~50 mass parts；Kaolin is 50~80 mass parts；Coarse whiting is 150~200 matter
Measure part；Fine particle calcium carbonate is 50~100 mass parts；Talcum powder is 50~100 mass parts；Coalescents are 3~5 mass parts；Thickener is
100~150 mass parts, styrene-acrylic emulsion are 80~100 mass parts, ultra micron glass dust is that 10~20 mass parts and sunshade thermal insulation apply
Feed powder is 20~30 mass parts.
A kind of described water-based reflectorized paint of exterior wall cooling, including following raw material and weight fraction：The mass parts of water 300；It is anti-
Jelly agent is 5 mass parts；Dispersant is 5 mass parts；Wetting agent is 3 mass parts；Defoamer is 3 mass parts；Preservative is 3 mass
Part；Rutile titania titanium white is 50 mass parts；Kaolin is 80 mass parts；Coarse whiting is 200 mass parts；Fine particle calcium carbonate is 100 mass parts；Talcum powder
For 100 mass parts；Coalescents are 5 mass parts；Thickener is 150 mass parts, styrene-acrylic emulsion is 100 mass parts, ultra micron glass
Glass powder is 20 mass parts and sunshade thermal insulation painting feed powder is 20 mass parts.
A kind of described water-based reflectorized paint of exterior wall cooling, including following raw material and weight fraction：The mass parts of water 200；It is anti-
Jelly agent is 5 mass parts；Dispersant is 5 mass parts；Wetting agent is 3 mass parts；Defoamer is 3 mass parts；Preservative is 3 mass
Part；Rutile titania titanium white is 50 mass parts；Kaolin is 80 mass parts；Coarse whiting is 200 mass parts；Fine particle calcium carbonate is 100 mass parts；Talcum powder
For 100 mass parts；Coalescents are 5 mass parts；Thickener is 150 mass parts, styrene-acrylic emulsion is 100 mass parts, ultra micron glass
Glass powder is 10 mass parts and sunshade thermal insulation painting feed powder is 30 mass parts.
A kind of described water-based reflectorized paint of exterior wall cooling, manufacturing process steps are as follows：
A. above-mentioned raw materials are weighed according to parts by weight, put into after weighing in agitator, ceaselessly stirred with mixer, separately
Outer preparation putty and the water-based alkali-resistant sealing primers of Ya Shi；
B. basal plane flattens：With the slit and aperture of external wall special putty repairing metope, batch scrape until basic unit is smooth, batch
Scrape putty to be at least spaced 12 hours, must be maintained 3-5 days before priming, to reach suitable strength, the work after use
Tool is cleaned up with clear water；
C. roller coating priming paint：Using the water-based alkali-resistant sealing primer of sub- scholar, during construction generally need not dilution, can when construction is not easy
Pure water or deionized water are added, and is stirred, form of construction work can use the construction technology requirement of rolling, spray, brush equal
It is even unanimously, without leakage brush, without accumulation, instrument to be cleaned up using rear with clear water；
D. roller coating finish paint：Rolling, spray can be used, dataller's skill External Wall be constructed, it is desirable to uniformity, without leakage brush, without heap
Product；Repainting time is at least spaced 8 hours, and after maintaining about 5 days, complete film forming simultaneously reaches best adhesion state, after instrument use
Cleaned up immediately with clear water.
The paint will be stirred ceaselessly during brushing in agitator domestic demand, in order to avoid reflective powder precipitates, be caused anti-
Light is uneven.
Embodiment 1
A kind of water-based reflectorized paint of exterior wall cooling, including following raw material and weight fraction：The mass parts of water 200~300；It is anti-
Jelly agent is 8~15 mass parts；Dispersant is 3~5 mass parts；Wetting agent is 1~3 mass parts；Defoamer is 1~3 mass parts；It is anti-
Rotten agent is 1~3 mass parts；Rutile titania titanium white is 30~50 mass parts；Kaolin is 50~80 mass parts；Coarse whiting is 150~200 matter
Measure part；Fine particle calcium carbonate is 50~100 mass parts；Talcum powder is 50~100 mass parts；Coalescents are 3~5 mass parts；Thickener is
100~150 mass parts, styrene-acrylic emulsion are 80~100 mass parts, ultra micron glass dust is that 10~20 mass parts and sunshade thermal insulation apply
Feed powder is 20~30 mass parts.
Manufacturing process steps are as follows：
A. above-mentioned raw materials are weighed according to parts by weight, put into after weighing in agitator, ceaselessly stirred with mixer, separately
Outer preparation putty and the water-based alkali-resistant sealing primers of Ya Shi；
B. basal plane flattens：With the slit and aperture of external wall special putty repairing metope, batch scrape until basic unit is smooth, batch
Scrape putty to be at least spaced 12 hours, must be maintained 3-5 days before priming, to reach suitable strength, the work after use
Tool is cleaned up with clear water；
C. roller coating priming paint：Using the water-based alkali-resistant sealing primer of sub- scholar, during construction generally need not dilution, can when construction is not easy
Pure water or deionized water are added, and is stirred, form of construction work can use the construction technology requirement of rolling, spray, brush equal
It is even unanimously, without leakage brush, without accumulation, instrument to be cleaned up using rear with clear water；
D. roller coating finish paint：Rolling, spray can be used, dataller's skill External Wall be constructed, it is desirable to uniformity, without leakage brush, without heap
Product；Repainting time is at least spaced 8 hours, and after maintaining about 5 days, complete film forming simultaneously reaches best adhesion state, after instrument use
Cleaned up immediately with clear water.
Ultra micron glass dust in the present embodiment, sunshade thermal insulation, which apply to be used in conjunction with each other between feed powder and water, adjustable makes height
Imitate reflection and heat insulation aqueous paint.
Embodiment 2
A kind of water-based reflectorized paint of exterior wall cooling, including following raw material and weight fraction：The mass parts of water 300；Antifreeze is
5 mass parts；Dispersant is 5 mass parts；Wetting agent is 3 mass parts；Defoamer is 3 mass parts；Preservative is 3 mass parts；Rutile titania
Titanium white is 50 mass parts；Kaolin is 80 mass parts；Coarse whiting is 200 mass parts；Fine particle calcium carbonate is 100 mass parts；Talcum powder is 100 matter
Measure part；Coalescents are 5 mass parts；Thickener is 150 mass parts, styrene-acrylic emulsion is 100 mass parts, ultra micron glass dust is 30
It is 30 mass parts that mass parts and sunshade thermal insulation, which apply feed powder,.
Manufacturing process steps are as follows：
A. above-mentioned raw materials are weighed according to parts by weight, put into after weighing in agitator, ceaselessly stirred with mixer, separately
Outer preparation putty and the water-based alkali-resistant sealing primers of Ya Shi；
B. basal plane flattens：With the slit and aperture of external wall special putty repairing metope, batch scrape until basic unit is smooth, batch
Scrape putty to be at least spaced 12 hours, must be maintained 3-5 days before priming, to reach suitable strength, the work after use
Tool is cleaned up with clear water；
C. roller coating priming paint：Using the water-based alkali-resistant sealing primer of sub- scholar, during construction generally need not dilution, can when construction is not easy
Pure water or deionized water are added, and is stirred, form of construction work can use the construction technology requirement of rolling, spray, brush equal
It is even unanimously, without leakage brush, without accumulation, instrument to be cleaned up using rear with clear water；
D. roller coating finish paint：Rolling, spray can be used, dataller's skill External Wall be constructed, it is desirable to uniformity, without leakage brush, without heap
Product；Repainting time is at least spaced 8 hours, and after maintaining about 5 days, complete film forming simultaneously reaches best adhesion state, after instrument use
Cleaned up immediately with clear water.
Ultra micron glass dust and water usage amount are more in the present embodiment, and sunshade thermal insulation painting feed powder usage amount is less, is preparing
Into after aqueous paint, because ultra micron glass dust and water usage amount are more, the reflection to light can allow people's generation to dazzle the eyes sense, and
Because water is more so that paint is not easy to be attached on outer wall body, but also can not effectively play the effect to room temperature lowering
Fruit.
Embodiment 3
A kind of water-based reflectorized paint of exterior wall cooling, including following raw material and weight fraction：The mass parts of water 200；Antifreeze is
5 mass parts；Dispersant is 5 mass parts；Wetting agent is 3 mass parts；Defoamer is 3 mass parts；Preservative is 3 mass parts；Rutile titania
Titanium white is 50 mass parts；Kaolin is 80 mass parts；Coarse whiting is 200 mass parts；Fine particle calcium carbonate is 100 mass parts；Talcum powder is 100 matter
Measure part；Coalescents are 5 mass parts；Thickener is 150 mass parts, styrene-acrylic emulsion is 100 mass parts, ultra micron glass dust is 10
It is 30 mass parts that mass parts and sunshade thermal insulation, which apply feed powder,.
Manufacturing process steps are as follows：
A. above-mentioned raw materials are weighed according to parts by weight, put into after weighing in agitator, ceaselessly stirred with mixer, separately
Outer preparation putty and the water-based alkali-resistant sealing primers of Ya Shi；
B. basal plane flattens：With the slit and aperture of external wall special putty repairing metope, batch scrape until basic unit is smooth, batch
Scrape putty to be at least spaced 12 hours, must be maintained 3-5 days before priming, to reach suitable strength, the work after use
Tool is cleaned up with clear water；
C. roller coating priming paint：Using the water-based alkali-resistant sealing primer of sub- scholar, during construction generally need not dilution, can when construction is not easy
Pure water or deionized water are added, and is stirred, form of construction work can use the construction technology requirement of rolling, spray, brush equal
It is even unanimously, without leakage brush, without accumulation, instrument to be cleaned up using rear with clear water；
D. roller coating finish paint：Rolling, spray can be used, dataller's skill External Wall be constructed, it is desirable to uniformity, without leakage brush, without heap
Product；Repainting time is at least spaced 8 hours, and after maintaining about 5 days, complete film forming simultaneously reaches best adhesion state, after instrument use
Cleaned up immediately with clear water.
Ultra micron glass dust and water usage amount are less in the present embodiment, and sunshade thermal insulation painting feed powder usage amount is more, is stirring
In the later stage, because quantity of solvent is less, it can to paint the excessively sticky brushing so as to influence to wall.
Finally it should be noted that：The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention,
Although the present invention is described in detail with reference to the foregoing embodiments, for those skilled in the art, it still may be used
To be modified to the technical scheme described in foregoing embodiments, or equivalent substitution is carried out to which part technical characteristic.
Within the spirit and principles of the invention, any modification, equivalent substitution and improvements made etc., it should be included in the present invention's
Within protection domain.
Claims (5)
- The water-based reflectorized paint 1. a kind of exterior wall cools, it is characterised in that including following raw material and weight fraction：The matter of water 200~300 Measure part；Antifreeze is 8~15 mass parts；Dispersant is 3~5 mass parts；Wetting agent is 1~3 mass parts；Defoamer is 1~3 matter Measure part；Preservative is 1~3 mass parts；Rutile titania titanium white is 30~50 mass parts；Kaolin is 50~80 mass parts；Coarse whiting is 150 ~200 mass parts；Fine particle calcium carbonate is 50~100 mass parts；Talcum powder is 50~100 mass parts；Coalescents are 3~5 mass parts；Increase Thick dose is 100~150 mass parts, styrene-acrylic emulsion is 80~100 mass parts, ultra micron glass dust is 10~20 mass parts and sun-proof Insulating moulding coating powder is 20~30 mass parts.
- The water-based reflectorized paint 2. a kind of exterior wall according to claim 1 cools, it is characterised in that including following raw material and again Measure fraction：The mass parts of water 300；Antifreeze is 5 mass parts；Dispersant is 5 mass parts；Wetting agent is 3 mass parts；Defoamer is 3 Mass parts；Preservative is 3 mass parts；Rutile titania titanium white is 50 mass parts；Kaolin is 80 mass parts；Coarse whiting is 200 mass parts；Gently Calcium is 100 mass parts；Talcum powder is 100 mass parts；Coalescents are 5 mass parts；Thickener is 150 mass parts, styrene-acrylic emulsion For 100 mass parts, ultra micron glass dust be 20 mass parts and sunshade thermal insulation painting feed powder is 20 mass parts.
- The water-based reflectorized paint 3. a kind of exterior wall according to claim 1 cools, it is characterised in that including following raw material and again Measure fraction：The mass parts of water 200；Antifreeze is 5 mass parts；Dispersant is 5 mass parts；Wetting agent is 3 mass parts；Defoamer is 3 Mass parts；Preservative is 3 mass parts；Rutile titania titanium white is 50 mass parts；Kaolin is 80 mass parts；Coarse whiting is 200 mass parts；Gently Calcium is 100 mass parts；Talcum powder is 100 mass parts；Coalescents are 5 mass parts；Thickener is 150 mass parts, styrene-acrylic emulsion For 100 mass parts, ultra micron glass dust be 10 mass parts and sunshade thermal insulation painting feed powder is 30 mass parts.
- The water-based reflectorized paint 4. a kind of a kind of exterior wall prepared described in one of claims 1 to 3 cools, it is characterised in that make Processing step is as follows：A. above-mentioned raw materials are weighed according to parts by weight, put into after weighing in agitator, ceaselessly stirred with mixer, it is accurate in addition Standby putty and the water-based alkali-resistant sealing primers of Ya Shi；B. basal plane flattens：With the slit and aperture of external wall special putty repairing metope, batch scrape until basic unit is smooth, batch scrape Road putty is at least spaced 12 hours, must be maintained 3-5 days before priming, and to reach suitable strength, the instrument after use is used Clear water cleans up；C. roller coating priming paint：Using the water-based alkali-resistant sealing primer of sub- scholar, during construction generally need not dilution, when construction is not easy, can add Pure water or deionized water, and stir, form of construction work can use rolling, spray, the construction technology requirement uniform one of brush Cause, cleaned up without leakage brush, without accumulation, instrument using rear with clear water；D. roller coating finish paint：Rolling, spray can be used, dataller's skill External Wall be constructed, it is desirable to uniformity, without leakage brush, without accumulation；Weight The painting time is at least spaced 8 hours, and after maintaining about 5 days, complete film forming simultaneously reaches best adhesion state, is used immediately after instrument use Clear water cleans up.
- The processing technology of water-based reflectorized paint 5. a kind of exterior wall according to claim 4 cools, it is characterised in that step d The paint will be stirred ceaselessly during brushing in agitator domestic demand, in order to avoid reflective powder precipitates, cause reflective inequality It is even.